Studying The Properties of PP/LDPE polymer blend

Lina Fadhil Kadhim --- Zainab Fadhil Kadhim

Journal of University of Babylon مجلة جامعة بابل
ISSN: 19920652 23128135 Year: 2017 Volume: 25 Issue: 1 Pages: 193-201
Publisher: Babylon University جامعة بابل

Abstract

This research studies some of the mechanical, thermaland physical properties for a polymer blend of polypropylene(PP)&low density polyethylene (LDPE). The blend compositions under studying were(pure PP, 25LDPE/75PP,50LDPE/50PP,75LDPE/25LDPE,pure PP). From the results it can be observed that the addition of LDPE to PP has been declined the tensile strength, flexural strength, flexural modulus and hardness while the density improved . the superior tensile strength was obtained at (25LDPE/75PP) composition while preferable flexural strength was ascribed to (50LDPE/50PP) blend composition.

يدرس هذا البحث مجموعة من الخواص الميكانيكية والحرارية والفيزيائية لخليط بوليمري من البولي بروبلين والبولي اثيلين الواطئ الكثافةوتم دراسة نسب الخلط التالية (25/75، 50/50، 75/25) بالأضافة الى البولي بروبيلين والبولي أثيلين واطئ الكثافة النقيين، اظهرت النتائج ان اضافة البولي اثيلين الواطئ الكثافة الى البولي بروبلين ساهمت في تقليل مقاومة الشد ومقاومة الأنحناء ومعامل الانحناء والصلادة وتحسن الكثافة ، عند النسبة (25/75) من الخليط تم الحصول على أعلى مقاومة شد بينما أفضل مقاومة انحناء تعطيها نسبة الخلط (50/50).

Keywords

polypropylene --- blend --- low density polyethylene --- differential scanning calorimeter --- tensile and flexural properties. --- البولي بروبيلين --- خليط --- البولي اثيلين الواطئ الكثافة --- المسعر الماسح التفاضلي --- خواص الشد و الانحناء.