Deposition Angle Effect on the Optical Properties of Obliquely Deposited (SnTe) Thin Films Prepared by Thermal Evaporation

تأثير زاوية الترسيب على الخواص البصرية لأغشية (SnTe) المرسبة بشكل مائل والمحضرة بطريقة التبخير الحراري

Raad S.A.Al – Rawie رعد سعيد عبد --- Ahmed I. Jawad احمد ابراهيم جواد

Journal of College of Education مجلة كلية التربية
ISSN: 18120380 Year: 2016 Issue: 1 Pages: 65-77
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Abstract

The Tin Telluride thin films of obliquely and normal deposited were prepared using thermal evaporation method at pressure of 10-6 torr on glass substrates at room temperature. The optical band gap of films has been determined from the transmission and absorption spectra. The optical band gap of as-grown films has been found to have direct band gap of ~(1.8, 1.62, 1.47) eV for deposition angle θ = (0 ̊ , 40° , 70 ̊ ) respectively. The optical band gap of SnTe thin films decreases with angle of deposition increases.

تم في هذا البحث دراسة الخصائص البصرية لأغشية (SnTe) المحضرة بطريقة الترسيب الحراري الفراغي تحت ضغط (10-6 Torr) على قواعد زجاجية عند درجة حرارة الغرفة وبزوايا ترسيب مختلفة θ=(0°,40°,70°) وبسمك10 nm) (50nm±. وقد تم تحديد فجوة الطاقة المسموحة من أطياف الامتصاصية و النفاذية وان زيادة زاوية الترسيب له تأثير واضح في تقليل النفاذية وزيادة الامتصاصية مع إزاحة نحو الأطوال الموجية الطويلة. أما بالنسبة لفجوة الطاقة المباشرة المسموحة فتقل بين eV (1.8) و eV (1.47) على التوالي عند زيادة زاوية الترسيب بين (70°,0°).

Keywords

Thin films --- SnTe --- Obliquely Deposited --- Optical band gap --- transmission analysis.