Study the surface hardness for (UPE/SiO2) composites

دراسة الصلادة السطحية لمتراكبات (UPE/SiO2)

Areej Hatam Fareed أريج حاتم فريد --- Faik Hammad Anter فائق حماد عنتر

Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة
ISSN: ISSN: 19918941 Year: 2017 Volume: 11 Issue: 2 Pages: 37-43
Publisher: University of Anbar جامعة الانبار

Abstract

In this work the effect of adding SiO2 powder on the hardness property for UPE was studied. Three groups of samples were prepared (UPE/(SiO2-Micro)), (UPE/(Nano-SiO2) and (UPE/(Micro+Nano)SiO2) with weight fraction of additives (%2، %4، %6، %8). The surface hardness for all samples was measured before and after irradiation with Ultraviolet at time interval (10) hours. The experimental results showed that the surface hardness of all samples increases with increasing the weight fraction of SiO2 in the composite in natural conditions, and that the nano samples has higher hardness than other samples. After UV irradiation, the hardness values also increase with increasing the weight fraction of SiO2 in the composite for all samples, and their value is higher than in normal conditions.

في هذا البحث تم دراسة تأثير اضافة مسحوق ثاني اوكسيد السيليكون على خاصية الصلادة لراتنج البولي استر غير المشبع. تم تحضير ثلاث مجاميع من العينات هي (UPE/(SiO2-Micro)), ((UPE/(Nano-SiO2) وSiO2)(UPE/(Micro +Nano) وبنسب وزنية للمواد المضافة (%2، %4، %6، %8). وتم قياس الصلادة السطحية للعينات قبل وبعد التشعيع بالاشعة فوق البنفسجية ولمدة (10) ساعات, لقد اظهرت النتائج العملية ان الصلادة للعينات كافة تزداد مع زيادة النسبة الوزنية لمادة SiO2 في المتراكب في الظروف الطبيعية, وان العينات النانوية تمتلك صلادة اعلى من بقية العينات. بعد تشعيع العينات ب(UV) تزداد قيم الصلادة ايضاً مع زيادة النسبة الوزنية لمادة SiO2 في المتراكب ولكافة العينات وتكون قيمتها اعلى مما في الظروف الطبيعية.

Keywords

راتنج البولي استر غير المشبع --- ثاني اوكسيد السيليكون --- الصلادة --- الاشعة فوق البنفسجية.