Study on Vanadium Recovery from Spent Catalyst Used in the Manufacture of Sulfuric Acid

Safa K. Kouba --- Khalid M. Mousa

Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط
ISSN: 19974884/E26180707 Year: 2010 Volume: 11 Issue: 2 Pages: 49-54
Publisher: Baghdad University جامعة بغداد

Abstract

Spent catalysts for sulfuric acid production have large amount of vanadium and due to environmental authority it is required to reduce the vanadium contain of the spent catalyst. Experimental investigation was conducted to study the vanadium recovery from spent catalyst via leaching process using sodium hydroxide to study the effect of process variables (temperatures, sodium hydroxide molarities, leaching time and particle size) on vanadium recovery. The effect of process variables (temperature, particle size,molarities of sodium hydroxide and leaching time) on the percentages of vanadium recovery were investigated and discussed .It was found that the percentage of vanadium recovery increased with increasing temperature up to 100 , increasing sodium hydroxide molarity from 2 to 4M, increasing leaching time, decreasing particle size from mesh 150, 100 and 65. A complete vanadium recovery was achieved at the following conditions: temperature (100˚c), particle size (150 mesh ) molarity of Na OH(4 molar) and leaching time(5 h).

تعتبر عملية استرداد الفناديوم من العامل المساعد المستهلك والمستخدم في صناعة حامض الكبريتيك من الامور المهمة لكونة يعتبرمصدر جيد للحصول على الفتاديوم وكذلك لاهمية الموضوع من الناحية البيئية وذلك لظرورية خفض نسبة الفناديوم في المخلفات قبل طمرها. اهتم هذا البحث بدراسة استرداد الفناديوم من مخلفات المحفز المستهلك المستخدم في صناعة حامض الكبريتيك بواسطة محلول هيدروكسيد الصوديوم . تم دراسة تأثير عدة متغيرات هي درجة الحرارة ,الحجم الحبيبي للمخلفات , مولارية هيدروكسيد الصوديوم و زمن الهظم .

Keywords

vanadium --- spent catalysts --- sulfuric acid