Effect of GAMMA Rays on some types of viscosity and optical properties for polycarbonate in chloroform at room temperature

Harith Hasoon Jasim

University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية
ISSN: 26645564/26645572 Year: 2013 Volume: 4 Issue: 1 Pages: 47-57
Publisher: Thi-Qar University جامعة ذي قار

Abstract

Some types of viscosity for polycarbonate aqueous solution in Chloroform with concentration of 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5 and 5% were determined for two kinds of samples, first non-radiated & the second, irradiated with source for a rate of 508 rad/min for 20 minutes.The results show that the values of shear, relative, specific & reduced viscosity were increased with increasing the concentration of polycarbonate in chloroform, Also the properties which had been determined in this work, increased after radiation, this could be attributed to penetration of ionizing radiation in the polymer structure & cross linking the chains.

تم تعيين قيم بعض أنواع اللزوجة لبولي كاربونيت المذاب في الكلوروفورم وبتراكيز 1 ,1.5 ,2, 2.5 ,3, 3.5, 4, 4.5 و 5% قبل وبعد تشعيعها بمصدر وبمعدل 508 راد لكل دقيقة ولمدة 20 دقيقة.أظهرت النتائج إن قيم كل من اللزوجة القصية ، اللزوجة النسبية، اللزوجة النوعية، اللزوجة المختزلة تزداد بزيادة تركيز البولي كاربونيت في الكلوروفورم.كذلك تزداد قيم الخصائص المقاسة والمحسوبة بعد التشعيع وقد يكون ذلك بسبب التشابك في التركيب الجزيئي لهذا البوليمر لاختراق أشعة كاما لبنية مولدتا حالة التشابك في البنية التركيبية للبوليمر .

Keywords

GAMMA Rays --- Polycarbonate --- Viscosity