Article
Synthesis of Nano Compound (Ba1-xSrxTiO3) by Sol-Gel Method and Study its Structural Properties
تحضير المركب (Ba1-x Srx TiO3) النانوي بطريقة السول- جل ودراسة خصائصه التركيبية

Author: Farouq I. Hussain فاروق أبراهيم حسين قادر
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042/ 25213407 Year: 2016 Volume: 29 Issue: 1 Pages: 417-427
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The Nano compound (Ba1-xSrxTiO3) as (X=0,0.26,0.28,0.30,0.32,0.34) was synthesized by using sol-gel method, the structural properties of result compound were studied by using x-ray diffraction test (XRD) and scanning electron microscope (SEM). the results were exhibited and by using software indexing to x-ray diffraction pattern that all prepared samples possess tetragonal phase and there is not any other phases were existed. also the substitution process didn't change the phase of compound and increase in (Sr+2) ion concentration leads to decrease lattice parameters (a,c) then the unite cell volume was decreased, as the particle size calculated from Debye-Scherrer and Williamson-Hall equations , and the calculated density from x-ray diffraction spectrum exhibited they were decreased with increase of (Sr+2) ion concentration, and scanning electron microscope pictures showed that prepared particles take a shape-like spherical shape.

حضر المركب النانوي (Ba1-xSrxTiO3) لقيم ( x=0.26,0.28,0.30,0.32,0.34) باستعمال طريقة السول – جل وتمت دراسة الخواص التركيبية للمركب الناتج باستعمال فحص حيود الاشعة السينية ( XRD) وكذلك المجهر الالكتروني الماسح (SEM) . وأظهرت النتائج لجميع العينات المحضرة من خلال الفهرسة البرمجية لطيف حيود الاشعة السينية انها تمتلك الطور الرباعي ولا توجد اطوار اخرى ظاهرة وان عملية استبدال ايون (Sr+2) بدل ايون (Ba+2) لم يغير طور المركب , كما تبين ان زيادة تركيز أيون (Sr+2) ادى الى نقصان ثوابت الشبيكة (c,a) ومن ثمَ نقصان حجم خلية الوحدة كما ان الحجم الحبيبي المحسوب من معادلتي ديباي شرر و وليامسون-هول والكثافة المحسوبة من طيف حيود الاشعة السينية تنقص بزيادة تركيز أيون (Sr+2) . ومن خلال صور المجهر الالكتروني الماسح تبين ان حبيبات المسحوق المحضر تتخذ شكلا شبه الكروي .


Article
The Structural and Surface Morphology Properties of Aluminum Doped CdO Thin Films Prepared by Vacuum Thermal Evaporation Technique.
الخواص التركيبيةومورفولوجية السطح لأغشية(Al) النقيةوالمشوبة ب(CdO)والمحضرة بتقنية التبخير الحراري في الفراغ

Loading...
Loading...
Abstract

Undoped and Al-doped CdO thin films have been prepared by vacuum thermal evaporation on glass substrate at room temperature for various Al doping ratios (0.5, 1 and 2)wt.% . The films are characterized by XRD and AFM surface morphology properties. XRD analysis showed that CdO:Al films are highly polycrystalline and exhibit cubic crystal structure of lattice constant averaged to 0.4696 nm with (111) preferred orientation. However, intensity of all peaks rapidly decreases which indicates that the crystallinity decreases with the increase of Al dopant. The grain size decreases with Al content (from 60.81 to 48.03 nm). SEM and AFM were applied to study the morphology and to estimate the surface roughness of the obtained films. All films were homogeneous and smooth, with a characteristic spherical grain size depending on Al content. The )RMS) roughness of the films increases with the increase of Al dopant.The improvement of the structural and surface morphology properties of Al-doped CdO has potential applications for different optoelectronic device applications

حضرت أغشية أوكسيد الكادميومCdO)) الرقيقة النقية والمشوبة ب(Al) بنسب تشويب (0.5, 1, 2)% وبإعتماد تقنية التبخير الحراري الفراغي على أرضيات زجاجية بدرجة حرارة الغرفة. دُرست الخواص التركيبية بأستخدام تقنية (XRD), وكذلك مواصفات مورفولوجية السطح للأغشية المحضرة بإستخدام تقنية (AFM) و(SEM) . أظهرت نتائج قياسات حيود الأشعة السينية XRD)) إن جميع الأغشية المحضرة النقية والمشوبة كانت ذا تركيب بلوري متعدد التبلور ومن النوع المكعب الذي يمتلك ثابت شبيكة طوله nm 0.4696مع هيمنة النمو بالإتجاه (111) للأغشية النقية والمشوبة كافة مع إزاحة في زاوية الحيود, وحدوث أنخفاض في شدة القمم المقاسة مما يدل على نقصان التبلور وتناقص واضح أيضاً يظهر في معدل الحجم الحبيبي nm (60.81-48.03) عند زيادة التشويب بالألمنيوم (Al). أستخدمت تقنية مجهر القوة الذرية (AFM) والمجهر الإلكتروني الماسح (SEM) لدراسة طوبوغرافية وخشونة سطوح الأغشية الرقيقة المحضرة. أظهرت نتائج فحوصات المجهر أن جميع الأغشية متجانسة وناعمة وأن شكل الحجم الحبيبي المتكون أشبه بالشكل الكروي بالأعتماد على نسبة التشويب, مع زيادة معدل خشونة السطح (RMS) بإزدياد نسبة التشويب. وأظهرت النتائج أن الخواص التركيبية ومورفولوجية السطح تتحسن لأغشيةCdO بعد تشويبها بنسب قليلة جداً من Al مما يجعل هذه الأغشية واسعة التطبيقات في مجال النبائط الالكتروضوئية.


Article
Preparation and Study of Cadmium Oxide Doped Gallium Oxide Thin Films and application of Gas Sensor
تحضير ودراسة الخصائص التركيبية والبصرية لأغشية أوكسيد الكادميوم النقيوالمطعم بأوكسيد الكاليوم وتطبيقها كمتحسس غاز

Authors: Salah sh.hamd صلاح شهاب حمد --- Asmiet Ramizy عصمت رمزي عبد الغفور --- Isam M. Ibrahim عصام محمد ابراهيم
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2017 Volume: 9 Issue: 2 Pages: 10-20
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

In this paper, the structure and optical properties of pure cadmium oxide films, and doped with gallium oxide have been achieved, the films were deposited on glass and silicon substrates, with different ratios (1,3,5,7)% via spry pyrolysis method, at the substrate temperature of ̊ C300. XRD results showed that all prepared films had a cubic polycrystalline structure, with preferred orientation of (111) for cadmium oxide. Surface morphology was studied using atomic force microscope (AFM), the grain size of the thin films was about 105.42-69.07 nm, with surface roughness is about (3.32-0.901) nm and root mean square (RMS) (3.97-1.05) nm for cadmium oxide films. The optical properties were studied using UV-VIS spectroscopy at wavelength (300-1100 nm), It was observed that the value of transmittance increases when the gallium doping are increasing and the films have a direct energy gap about (2.3-4) eV that increases with the increase in gallium concentration. Sensitivity properties of pure cadmium oxide films, and doped with gallium oxide was deposed on silicon substrates of NO2 gas at different operation temperatures was found that the films of CdO doped with Gallium oxide on silicon substrate has greater sensitivity than the films than the undoped and that the doping has improved the sensitivity of the membranes CdO.

جرى في هذا البحث مناقشة الخصائص التركيبية والبصرية والتحسسية لأغشية رقيقة من أوكسيد الكادميوم النقية والمطعمة بأوكسيد الكاليوم المرسبة على قواعدالزجاج والسيلكون بتراكيز مختلفة من اوكسيد الكاليوم %(1,3,5,7) بواسطة تقنية التحلل الكيميائي الحراري في درجة حرارة ̊ C300. أظهرت نتائج حيود الاشعة السينية (XRD) أن جميع الاغشية المحضرة تمتلك تركيب مكعبي (cubic) متعدد التبلور (polycrystalline) وان الاتجاه المفضل هو (111) لأوكسيد الكادميوم. درست طبوغرافية السطح من خلال مجهر القوة الذرية (AFM) وقد تبين أن الحجم الحبيبي للأغشية الرقيقة المحضرة حوالي(69.07-105.42)nm ،مع خشونة السطح(0.901-3.32) nm وكان متوسط الجذر التربيعي (RMS)(1.05-3.97)nm لأغشية أوكسيد الكادميوم، وقد تمت دراسة الخصائص البصرية بواسطة ﻣﻄﯿﺎفاﻟﻨﻔﺎذﯾﺔﻟﻼﺷﻌﺔاﻟﻤﺮﺋﯿﺔ –ﻓﻮقاﻟﺒﻨﻔﺴﺠﯿﺔ (UV-VIS)عند طول موجي ,(300 - 1100 nm) ولوحظ أن قيمة النفاذية تزداد عند التطعيم وان الأغشية تمتلك فجوة طاقة مباشرة تزداد بزيادة التطعيم(2.3-4) eV , الخصائص التحسسية لأغشية أوكسيد الكادميوم المطعم باوكسيد الكاليوم والمرسبة على قواعد السيلكون اتجاه غاز NO2 بدرجات حرارة مختلفة, وجد أن أغشية CdO المطعمة باوكسيدالكاليوم والمرسبة على قواعد السيلكون تمتلك تحسسية أكبر من الأغشية غير المطعمة اتجاه غاز NO2 أي أن التطعيم أدى الى تحسين الخواص التحسسية لأغشية CdO..


Article
Structure,RietveldRefinement Study of BaCoxTixFe12-2xO19 ferrite Using Powder XRD Analysis
دراسة تركيب وتصفية ريتفيلد للفيرايت السداسي بصيغة BaCoxTixFe12-2xO19 باستخدام تحليل حيود الاشعة السينية (PXRD)

Author: Farouq I.HussainQader فاروق ابراهيم حسين قادر
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042/ 25213407 Year: 2014 Volume: 27 Issue: 2 Pages: 70-77
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

BaCoxTixFe12-2xO19(x=0.1, 0.5, 0.7, 0.9, 1.7) were prepared using powder technology technique . X-ray diffraction with diffractometerCuKα radiation analysis and Rietveld refinement of the samples were studied and showed a single phase of hexagonal structure with SP63/mmc space group . Lattice parameters, cell volume, crystallite size and x-ray density weredetermined .The hexagonal structure was represented by using PowderCellprogram showing the atomic positions of Co ,Ti, and Fe ions.

تم تحضير الفيرايت ذو الصيغة الكيميائية BaCoxTixFe12-2xO19 باستخدام تقنية تكنولوجيا المساحيق وبنسب تطعيم مختلفة لكل منالكوبلت والتيتانيوم (x=0.1 0.5 ,0.7 ,0.9 ,1.7) واجريت فحوصات حيود الاشعة السينية وممقارنتها مع ملفات JCPDS التابعة للمركز الدولي لبيانات الحيود (ICDD) واظهرت جميع النماذج طور سداسي واحد وقيست الابعاد البلورية لها (a=b , c, c/a) وكذلك الحجم الحبيبي والكثافة باستخدام تحليل الاشعة السينية لها والمعادلات الخاصة بهذا التحليل , واعادة القياسات باستخدام تصفية ريتفيلد ودراسة المواقع للذرات في شبيكة الباريوم فيرايت المطعم بالكوبلت والتيتانيوم ورسم الشبيكة باستخدام البرامج الحاسوبية Fullprof و PowderCell.


Article
Formation of Compressive Residual Stress by Face Milling Steel AISI 1045
توليد الاجهادات الضغطية المتبقية بواسطة التفريز السطحي للصلب (AISI 1045)

Authors: Samir Zidan Al-Fahadawy سمير زيدان خلف --- Samir Ali Al-Rabii سمير علي امين --- Ahmed Naif Al-Khazraji احمد نايف الخزرجي
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2015 Volume: 11 Issue: 1 Pages: 40-50
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Machining residual stresses correlate very closely with the cutting parameters and the tool geometries. This research work aims to investigate the effect of cutting speed, feed rate and depth of cut on the surface residual stress of steel AISI 1045 after face milling operation. After each milling test, the residual stress on the surface of the workpiece was measured by using X-ray diffraction technique. Design of Experiment (DOE) software was employed using the response surface methodology (RSM) technique with a central composite rotatable design to build a mathematical model to determine the relationship between the input variables and the response. The results showed that both the feed rate and the cutting speed are the significant factors controlling the surface residual stress, while the depth of cut had no influence. A quadratic empirical model was developed with a 95% confidence level, and a good agreement was found between the experimental and predicted results. A numerical optimization was then conducted through DOE program to find the optimum surface residual stress at the optimum cutting parameters, depending on the maximum desirability obtained. The optimum compressive surface residual stress (-224.361 MPa) was found at cutting speed of 69.2 m/min, feed rate of 0.4 m/min and depth of cut of 0.4 mm.

ترتبط أجهادات التشغيل بشكل وثيق جدا" مع عوامل القطع والاشكال الهندسية لأدوات القطع . يهدف عمل هذا البحث الى التحقق من تأثير سرعة القطع ومعدل التغذية وعمق القطع على الاجهاد المتبقي السطحي للصلب (AISI 1045) بعد عملية التفريز الوجهي . تم قياس الاجهاد المتبقي على سطح المشغولة بعد كل عملية تفريز بأستخدام تقنية حيود الاشعة السينية (XRD). تم تطبيق برنامج تصميم التجارب (DOE) بأستخدام تقنية منهجية الاستجابة السطحية (RSM) بتصميم دوارمركب مركزي (CCD) لبناء نموذج رياضي لأيجاد العلاقة بين المتغيرات الداخلة والاستجابة . أظهرت النتائج بأن كلا" من معدل التغذية وسرعة القطع عوامل مهمة تتحكم بالاجهاد المتبقي السطحي بينما لم يكن لعمق القطع تأثير . تم عمل نموذج تجريبي من الدرجة الثانية بموثوقية 95% ووجد توافق جيد بين النتائج العملية والمتنبئة . بعد ذلك ، تم عمل أمثلية عددية خلال برنامج تصميم التجارب لأيجاد أمثل اجهاد متبقي سطحي عند أمثل عوامل قطع أعتمادا" على أقصى مطلوبية مستحصلة . وفقا" لذلك ، وجد أن الاجهاد المتبقي السطح الضغطي الامثل (-224.361) ميجاباسكال عند سرعة قطع (69.2) م/ دقيقة ومعدل تغذية (0.4) م/ دقيقة وعمق قطع (0.4) ملم .


Article
Fabrication and Characterization of Tri Metal Oxides by Chemical Spray Pyrolysis Technique as a Gas Sensor
تصنيع و توصيف اكاسيد ثلاثية معدنية بتقنية الرش الكيميائي الحراري كمتحسس غازي

Authors: Farhad M. Othman فرهاد محمد عثمان --- Alaa A. Abdul-hamead ألاء علاء الدين --- Noor M. Ali نور محمد علي
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 4 Pages: 132-140
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research tri metal oxides were fabricated by simple chemical spray pyrolysis technique from (Sn(NO3)2.20 H2O, Zn(NO3)2.6 H2O, Cd(NO3)2.4 H2O) salts at concentration 0.1M with mixing weight ratio 50:50 were fabricated on silicon substrate n-type (111). (with & without the presence of grooves by the following diemensions (20μm width, 7.5μm depth) with thickness was about ( 0.1 ±0.05 µm) using water soluble as precursors at a substrate temperature 550 ºC±5, with spray distance (15 cm) and their gas sensing properties toward H2S gas at different concentrations (10,50,100,500 ppmv) in air were investigated at room temperature which related with the petroleum industry. Furthermore structural and morphology properties were inspecting. Experimental results show that the Zn2SnO4 and Cd2SnO4 thin films were achieved from the used salts and samples gas sensitivity which improved with the presence of substrate grooves. Which make the sensor suitable for the detection of lower .concentrations of hazard H2S gas in the petroleum industry.

في هذا البحث حضرت اكاسيد ثلاثية بطريقة الرش الكيميائي الحراري البسيطة من املاح (نترات القصدير والزنك والكادميوم) بتركيز(0.1M) وبنسب خلط وزنية 50:50 على قاعدة من السيليكون من النوع (n) بأتجاه (111) (بوجود وبعدم وجود الحزوز وبالأبعاد الآتية:عرض20μm, عمق7.5μm وبسمك حوالي (0.1 ±0.05 µm) بأستخدام الماء مذيبا وبدرجة حرارة ترسيب بلغت 550 ºC±5 وبمسافة رش (15 cm) ككاشف للغاز بتراكيز مختلفة (10,50,100,500 ppmv) في الهواء وبدرجة حرارة الغرفة والمرتبطة مع الصناعة النفطية.تم تشخيص التبلور ومورفولوجية سطح الاغشية المحضرة بواسطة قياسات حيود الاشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذري لها. اظهرت النتائج ان اغشية الاكاسيد المحضرة من الاملاح المستخدمة هي Zn2SnO4 و Cd2SnO4 وحساسية الغازات تحسنت بوجود الحزوز على السطح والتي تجعل من الكاشف مناسبا لكشف التراكيز القليلة من غازH2S الخطر في الصناعة النفطية.


Article
Preparation of Silver Nanoparticles by Sol - Gel Method and Study their Characteristics
تحضير الفضة النانوية بطريقة السول - جل ودراسة خصائصها

Loading...
Loading...
Abstract

Powder of silver nanoparticles was prepared by Sol - Gel method successfully using silver nitrate , (AgNO3) gesture is added to sodium citrate (C6H5O7Na3) as a reducing agent and by using Magnetic Stirrer to mix the solutions and heated then using centrifuge machine to separate the silver nanoparticles from solution .It is then dried in an oven at a temperature 40oC for 24 hours.Structure characteristics was studied , the synthetic silver powder was prepared through the use of an (XRD). Results showed the composition of silver nanoparticles is a (fcc) and a constant lattice (4.086 ± 0.006 Å) by comparing it with standard tables (JCPDS) which is found perfectly matched to file with a number 04-0783, which is due to the space group Fm3 ̅m No. 225.Particle size of nanoparticles was calculated for samples prepared using the Scherrer equation where the average grain size of (18.84 nm - 50.23 nm) was also found using the equation Williamson - Hall and ranged from (10.11 nm - 39.60 nm). As well as the mass density, density of dislocations, texture factor and the surface area of nano-particles were calculated. In addition samples prepared with an atomic force microscope (AFM) were examined and had the average diameter of the grains between (84.32 nm - 97.35 nm), and the average height ranged between (1.54 nm - 5.02 nm).

حُضر مسحوق الفضة النانوية بطريقة السول - جل بنجاح باستخدام نترات الفضة (AgNO3) بصفته بادرة يضاف لها سترات الصوديوم (C6H5O7Na3) عاملاً مختزلاً وبإسخدام المحرك المغناطيسي (Magnetic Stirrers) لخلط المحاليل وتسخينها ثم إستخدمت آلة الطرد المركزي ( (centrifuge machine لفصل الفضة النانوية عن المحلول ومن ثم تجفيفها في فرن بدرجة حرارة 40oC مدة 24 ساعة . دُرست الخصائص التركيبية لمسحوق الفضة المحضرة من خلال استخدام جهاز حيود الاشعة السينية (XRD). اظهرت نتائج (XRD) إن تركيب الفضة النانوية هو مكعب متمركز الاوجه (fcc) وبثابت شبيكة (4.086 ± 0.006 Å)وبمطابقتها مع الجداول القياسية (JCPDS) وجدت مطابقة تماماً للملف ذي الرقم 04-0783الذي يعود للمجموعة الفضائية (space group)Fm3 ̅m رقم 225)). حُسب حجم الحبيبات النانوية للعينات المحضرة باستعمال معادلة شيرر , إذ كان متوسط حجم الحبيبات من (18.84 nm – 50.23 nm) كما تم ايجادها باستعمال معادلة وليمسون - هول وكانت تتراوح من (10.11 nm –39.60 nm) . كذلك حُسبت الكثافة الكتلية وكثافة الإنخلاعات وعامل التشكيل والمساحة السطحية للحبيبات النانوية . فضلاً عن ذلك فحصت العينات المحضرة بمجهر القوة الذرية (AFM) وقد كان متوسط قطر الحبيبات يتراوح بين (84.32 nm – 97.35 nm) , ومتوسط ارتفاعها تراوح بين (1.54 nm – 5.02 nm) .


Article
Influence of Thickness and Annealing on Some Physical Properties of Zinc Oxide Films
تأثير السمك والتلدين على بعض الخصائص الفيزيائية لاغشية اوكسيد الزنك

Author: Ammar Ayesh Habeeb عمار عايش حبيب
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2018 Volume: 14 Issue: 4 Pages: 114-125
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Zinc oxide transparent conductive films were deposited on glass substrates at 400 °C using chemical spray pyrolysis method. The effect of annealing of ZnO samples with the increase in thickness has been studied. The X-ray diffraction results indicate that the polycrystalline films exhibited a distinguished orientation along (002) direction with a hexagonal wurtzite phase type. It is found that good crystallinity is obtained in the samples annealed at 500 °C. All films showed an average transmittance of about 85% measured by UV/VIS/NIR spectrophotometer. The grain size and lattice parameters of films were computed. The grain size increases as thickness increases. Hence the values of the optical gap energy (Eg) are found to be in the range of 3.238 to 3.273 eV without annealing and in the range of 3.252 to 3.280 eV with annealing when the thickness varies from 355 to 445 nm.

حضرت اغشية اوكسيد الزنك شبه الموصلة باستخدام تقنية التحلل الكيميائي الحراري على ركائز الزجاج في محلول مائي على قواعد من الزجاج بدرجة حرارية 400 درجة سيليزية. وقد تم دراسة تأثير التلدين وسمك الاغشية على الخصائص التركيبية والبصرية. بينت نتائج حيود الاشعة السينية أن الاغشية المحضرة متعددة التبلوروتمتلك تر كيبا من النوع السداسي المتراص (Heaxagonal Wurtzite). وجد أن الحصول على تبلور جيد للاغشية المحضرة يكون عند تلدين العينات في 500 درجة سيليزية. أظهرت جميع الاغشية معدل نفاذية حوالي 85٪ حيث تم قياسها بجهاز مقياس طيف الأشعة فوق البنفسجية- المرئية – تحت الحمراء القريبة. تم حساب الحجم الحبيبي وثوابت الشبيكة للاغشية. حيث وجد ان الحجم الحبيبي يزداد مع زيادة السمك. ومن ثم وجد ان قيم فجوة الطاقة البصرية بين 3.238 إلى 3.273 الكترون فولت بدون التلدين ومن 3.252 إلى 3.280 الكترون فولت مع التلدين ولسماكات مختلفة بين 355 إلى 445 نانومتر.

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

Arabic and English (8)


Year
From To Submit

2018 (1)

2017 (1)

2016 (2)

2015 (2)

2014 (2)