Effect of Halogen Ions on The Corrosion of Brass In Na2SO4 Solution
تأثير أيونات الهالوجين على تأكل البراص في محلول كبريتات الصوديوم

Authors: Rana A. Majed --- Saad M. Elia --- Zahra`a Fadhel
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 7 Pages: 1386-1395
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research involves study effect of halogen ions presence in 0.2M sodiumsulphate on the corrosion of brass at room temperature (30oC). Three concentration ofhalogen ions (Fˉ, Clˉ, Brˉ, and Iˉ) were used 0.1, 0.2, and 0.3 M. The different incorrosion parameters before and after added the halogen ions interpreted anddiscussed which involves corrosion potentials (Ecorr), corrosion current densities(icorr), and Tafel slops (bc & ba) in addition to discuss the polarization curves.Polarization resistances (Rp) and the change in free energy (ΔG) werecalculated and interpreted, in addition to calculate the rate of corrosion (Rmpy).The results of this work indicates that the presence of halogen ions inexperimental solution increases the rate of corrosion, and the effect of halogen ionsfollows the sequence to increase the corrosion Iˉ > Clˉ > Fˉ > Brˉ.

يتضمن هذا البحث دراسة تأثير وجود ايونات الهالوجين في محلول 0.2 مولاري كبريتاتم). استخدمت ثلاثة تراكيز من ايونات o الصوديوم على تأكل البراص عند درجة حرارة الغرفة ( 30الهالوجينات (ايونات الفلوريد والكلوريد والبروميد واليوديد) وكانت 0.1 و 0.2 و 0.3 مولاري. تمتفسير ومناقشة متغيرات التاكل المقاسة والتي تضمنت جهود التأكل وكثافات تيار التأكل وميول تافلالكاثودية والانودية بالاضافة الى مناقشة منحنيات الاستقطاب.تم حساب قيم مقاومات الاستقطاب والتغير في الطاقة الحرة لكيبس وكذلك معدل سرعةالتاكل بوحدة المل لكل سنة. وقد بينت النتائج ان اضافة ايونات الهالوجين تؤدي الى زيادة معدلالتاكل والزيادة تتبع التسلسل التالي يوديد > كلوريد > فلوريد > بروميد.


Article
Effect of MnO-4 Anion Inhibition on Corrosion of (70%Cu-30%Zn) Brass in Salt and Basic Solutions

Author: Mervit M. Al-Jnabi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 16 Pages: 3320-3330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research involves study effect of MnO-4 anion addition as inhibitor on the polarization behavior of (70%Cu-30%Zn) alloy in salt and basic medium ( 0.6 M NaCl & 0.6 M NaOH) by potentiostatic method where Tafel slopes and corrosion rate (Rmpy) and inhibition efficiency (El%) for each salt and basic environments were measured .Result of the tests shows that the values of Tafel slopes and corrosion rate decreases with adding the MnO-4 anion in two solutions, the Inhibition efficiency of 70%Cu-Zn30% alloy in NaOH solution more than that observed in NaCl solution. which means that the basic media is more corrosive Cu-Zn alloy even after the addition of inhibitor.


Article
Synthesis , Identification and Study of Some New Schiff Bases as Inhibitors for Brass Corrosion

Author: Mouayed Y. Kadhum مؤيد يوسف كاظم الاسدي
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2011 Volume: 37 Issue: 2A Pages: 87-112
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

Three Schiff bases were synthesized namely (4-dimethyl amino benzaldene – 3-amino benzoic acid ) , ( piperonaldene – 4-amino – 2-nitro toluene ) and (4-dimethyl amino benzaldene - 4-amino – 2-nitro toluene ) . These Schiff bases have been identified by microanalysis ( CHN ) , infrared , 1H-NMR , 13C-NMR and GC-Mass spectroscopy . The study also included the use of these Schiff bases as inhibitors for corrosion of brass in acidic media ( 0.5 M HCl ) . The rate of corrosion was determined by two methods ( electrochemical and weight loss methods ) . It was found agreement between them . Different studies such as ; the effect of temperature on the corrosion rate at ( 298 ˚K , 308 ˚K and 318 ˚K ) , measurement of some thermodynamic parameters ( corrosion current , activation energy and free energy ) , and comparison of inhibition effect for prepared Schiff bases with their primary amines were achieved . The results indicated that these Schiff bases inhibited the corrosion efficiently . Furthermore , antibacterial activity of prepared Schiff bases and standard inhibitor (AK3) was also studied on the two types of bacteria ,Staphylococcus aureus and Escherichia coli . It was found that the Schiff bases under study were considered inhibitors for bacterial growth with variation extents .

تم تحضير ثلاث قواعد شف وهي ( 4-dimethyl amino benzaldene – 3-amino benzoic acid ) و piperonaldene– 4-amino–2-nitro toluene) ) و (4-dimethyl amino benzaldene-4-amino –2-nitro toluene). شخصت قواعد شف المحضرة بوساطة تحليل العناصر الدقيق (CHN) ومطيافية الاشعة تحت الحمراء والرنين النووي المغناطيسي للبروتون 1H-NMR)) والرنين المغناطيسي للكاربون 13(13C-NMR) ومطيافية الكتلة GC-Mas . تضمنت الدراسة ايضا استعمال قواعد شف المحضرة كمثبطات لتاكل البراص في الوسط الحامضي (0.5 M HCl) ، حيث قيس معدل سرعة التاكل بطريقتين هما الطريقة الكهروكيميائية وطريقة الفقدان بالوزن وقد وجد ان هناك توافق بين نتائج الطريقتين . فضلاً عن ذلك اجريت دراسات مختلفة في مجال التاكل وهي : تاثير تغيير درجة الحرارة على معدل سرعة التاكل عند ( 318 °K , 308 °K , 298 °K ) ، وحساب بعض الدوال الثرموديناميكية مثل تيار التاكل وطاقة التنشيط والطاقة الحرة اضافة الى مقارنة التاثير التثبيطي لقواعد شف المحضرة مع اميناتها الاولية وقد بينت النتائج بان قواعد شف المحضرة ذات كفاءة جيدة في تثبيط التاكل . ومن جانب اخر تم دراسة الفعالية المضادة للبكتيريا لقواعد شف المحضرة والمادة القياسية (AK3) على نوعين من البكتيريا وهما البكتيريا الموجبة لصبغة غرام و البكتيريا السالبة لصبغة غرام وقد اشارت النتائج ان قواعد شف قد ثبطت النمو البكتيري وباقطار تثبيطية مختلفة .


Article
Study of the influence of surface roughness, Sample heat and Sample shape on Wear rate measurements
دراسة تاثير خشونة السطح، درجة حرارة النموذج وشكل النموذج على قياسات معدل البلى

Authors: Abdulhadi k.Judran --- Najim Abd-Alkadhim --- Haithim T.Hussein
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 2 Part (B) Scientific Pages: 252-260
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Metal samples such as Copper and Aluminum and alloy as Brass were prepared and machined as discs (plane sample) and as a half rings (curvature sample). The samples were polished by using metallographic paper with different grades. The micro roughness and the initial weight were measured for all samples before wear tests, and then the samples were subjected to wear testing system under lubricated condition, fixed normal load of 15N, sliding time 30 min and sliding speed of 750 rpm. During the running of wear testing system the temperature of the samples were measured .The wear rate was calculated by employing the weighing method. It is clear from the results that micro roughness values increasing leads to increase in weight loss , wear rate and the temperature of samples .The effect of sample shape on weight loss , wear rate and sample heat is also obvious when noticing that the different measurements of weight loss, wear rate and sample heat of curvature samples are higher than that of plane samples .

تم في هذا العمل تحضير وتشغيل نماذج من المعادن كالنحاس والألمنيوم ونموذج من السبائك كالبراص وتشغيلها كأقراص (نماذج مستوية) وأنصاف حلقات (نماذج منحنية) . تم تنعيم جميع النماذج بأستخدام ورق تنعيم بمختلف الدرجات وتم قياس الخشونة المايكروية للسطح لجميع النماذج وكذلك قياس أوزانها الأبتدائية وبعدها تم اجراء فحص البلى تحت شرط التزييت وتحت حمل عمودي ثابت مقداره 15نيوتن ووقت انزلاق 30 دقيقة وسرعة انزلاق 750 دورة/دقيقة . خلال تشغيل منظومة فحص البلى قيست درجة حرارة النماذج وتم حساب معدل البلى بأستخدام الطريقة الوزنية . ومن النتائج التي حصلنا عليها يمكن ملاحظة ان الزيادة في قيم الخشونة المايكروية تؤدي الى زيادة في الوزن المفقود ومعدل البلى ودرجة حرارة النماذج. كذلك فأن تأثير شكل النموذج على الوزن المفقود , معدل البلى ودرجة حرارة النماذج يبدو واضحا حيث أظهرت قياسات الوزن المفقود, معدل البلى ودرجة حرارة للنماذج المنحنية انها اعلى من تلك التي قيست للنماذج المستوية .

Keywords

micro roughness --- Copper --- Aluminum --- Brass --- Wear


Article
Study on Corrosion Inhibition of Brass in Water Using Horse Tail Herb as Green Inhibitor
دراسة تثبيط تاكل الراصد المستخدم في المبادلات الحرارية باستخدام عينة ذنب الخيل

Authors: Sami Abualnoun Ajee --- Ali Yashar Zain Al-Abdein
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 8 Part (A) Engineering Pages: 1992-2008
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Brass used in heat exchanger is corroded in industrial water. The used inhibitor is extracted from horse tail herb added in different concentrations and temperature to industrial water in which heat exchanger if exposed to these conditions. Brass is studied under the above conditions using potentiodynamic polarization, scanning electron microscopy (SEM) and X-ray diffraction. Potentiodynamic polarization technique was used to evaluate the corrosion rate data. Inhibition efficiency of 92.1 % at 298 k was achieved with the addition of 1350 ppm of horse tail herb from potentiodynamic polarization measurements. Potentiodynamic curves show that the presence of extracted horse tail herb in industrial water affects both the anodic and cathodic processes, decreases the corrosion current density and shifts the corrosion potential towards more noble values; the inhibitors are mixed type inhibitors.

يتاكل البراص المستخدم في المبادلات الحرارية في المياه الصناعية. تم اضافة المثبط المستخلص من عشبة ذنب الخيل عند تراكيز و درجات حرارة مختلفة مشابهة للظروف المتعرضة لها المبادلات الحرارية. تمت الدراسة ضمن الظروف اعلاه باستخدام تقنية المجهاد الساكن, المجهر الالكتروني الماسح و حيود الاشعة السينية. من نتائج التي تم الحصول عليها من منحنيات الاستقطاب تبين ان كفائة التثبيط 92.1% عند 298 كلفن عند اضافة 1350 جزء بالمليون من المثبط اعلاه.


Article
Effect of the Laser Shock Processing onWear Resistance of Brass Alloy
تأثير الصدمة بموجة الليزر على زيادة مقاومة البلى لسبيكة البراص

Authors: Saeed M.Faydh --- Abdulhadi Kadhim Al-Ogaili --- Evan T.Salim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 5 Part (B) Scientific Pages: 998-1008
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Laser shock processing (LSP) is becoming an important surface treatment to induce a compressive residual stress field, which improves micro-hardness, fatigue and fracture properties of components. In this work, we examine the effect of laser shock processing on the surface micro-hardness and wear resistance of brass alloy. After LSP treatment, micro-hardness values increased by 97% at the metal surface and decreases gradually with distance below the surface. It is observed that LSP impact can improve the wear resistance of brass, where the wear rate is reduced by 79% compared with the untreated LSP specimens due to work hardening and compressive residual stress of LSP impact. From SEM micrograph analysis of worn surface, the grooves and compacted debris of LSP treated sample are smaller and less than these untreated LSP samples

المعاملة بواسطة موجة الصدمة المتولدة بالليزر اصبحت اكثر طرق المعاملة اهمية نضرا لما تضيففه للمادة من اجهادات انضغاط وصلادة ومقاومة الكلال والكسر. في هذا العمل , تم اختبار تاثير المعاملة بموجة الصدمة المتولدة بالليزر على صلادة ومقاومة البلى لسبيكة البراص.بعد اجراء المعاملة بموجة الصدمة المتولدة بالليزر لسطح السبيكة, قييم الصلادة ارتفعت 97% عند السطح وتنخفض تدريجيا كلما ابتعدنا عن السطح. تمت الملاحظة ان المعاملة بموجة الصدمة المتولدة بالليزر يمكن ان تزيد من مقاومة البلى لسبيكة البراص حيث قل معدل فقدان الكتلة بمقدار 79% مقارنة مع العينات الغير معاملة بالليزر بسبب عملية التصليد واجهادات الانضغاط المتولدة بالسطح. تصوير المجهر الالكترونيلسطح المادة المعرض لاختبار البلى اضهر ان الاغاديد والمخلفات المنضغطة على السطح اصغر واقل في العينات المصلدة بالليزر منها للغير مصلدة.


Article
Influence of Shot Peening on 70/30 Brass Residual Stresses Using Plasticity Theory
تأثير القذف بالكريات على الاجهادات المتبقية لسبيكة البراص 30/70 باستخدام نظرية اللدونة

Authors: Hussain J. M. Alalkawi --- Qusay Khalid Mohammed --- Abbas A. AL – Asadi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 16 Pages: 3064-3075
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Residual stresses play an important role in the behavior of structuressubjected to static and dynamic loads. The main aim of this study is to estimate experimentally the residual stresses in 70/30 brass material tested in bending and torsion using the plasticity theory. The influence of shot peening process on the tensile residual stresses is discussed. It is shown that the shot peening strongly influences the residual stresses, i.e. shot peening will reduce the tensile residualstresses by 13.6% of the yield strength in bending tests. While will reduce the tensile residual stresses by 22% of shear yield stress in torsion tests.

الاجهادات المتبقية تلعب دورا مهماً في تصرف التراكيب المسلط عليها أحمال ثابتة ومتحركة. الهدف الرئيسي من هذه الدراسة هو تقييم الاجهادات المتبقية عملياً في مادة البراص 70/30 تمت فحوصات الانحناء والالتواء باستخدام نظرية اللدونة. تأثير عملية القذف بالكريات على الاجهادات المتبقية تمت مناقشته . حيث تمت ملاحظة بأن القذف يالكريات سوف يؤثر على الاجهادات المتبقية بشكل ملحوظ وهذا يعني إن القذف بالكريات سوف يقلل من الاجهادات المتبقية الشدية بنسبة % 13.6 نسبة لاجهاد الخضوع في فحوصات الانحناء بينما سوف يقلل هذهالاجهادات المتبقية الشدية بنسبة % 22 من إجهاد الخضوع القصي في فحوصات الالتواء


Article
EFFECT OF ANNEALING ON MECHANICAL PROPERTIES OF BRASS ALLOY TYPE C38500
تأثير عملية التلدين على الخواص الميكانيكية لسبيكة البراصC38500

Author: Zuhal A. Kabash
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2015 Volume: 8 Issue: 1 Pages: 16-26
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The effect of annealing process on microstructure and mechanical properties of brass C38500 according to UNS was studied. The test samples were heated to (450, 500, 550 and 600) °C for 1 hour and in a furnace. The samples were cooled gradually to the room temperature. The microstructural change during annealing was studied by using optical microscope and mechanical properties such as tensile strength, yield strength, hardness and torsionl test were also studied. From the obtained results it was observed that annealing has a little effect on the microstructure and it reduces the mechanical properties (tensile strength, yield strength, hardness) as a result of elimination of the brittle phase or internal stress in microstructure, but it improves the torsional strength and increases the number of twisting angle it is also found that the annealing at (600)οC gives the best torsion test.

يهدف البحث الى دراسة تأثير عملية التلدين على البنية المجهرية والخواص الميكانيكية لسبيكة البراصC38500. تم تسخين عينات الاختبار في فرن كهربائي إلى درجات حرارة مختلفة 600,550,500,450)) مᵒ لمدة ساعة ثم التبريد البطيء داخل الفرن الى درجة حرارة الغرفة. تم فحص البنية المجهرية بعد التلدين باستخدام مجهر ضوئي وكذلك الخواص الميكانيكية من (مقاومة الشد و نقطة خضوع والصلادة) إضافة إلى إجراء اختبار الالتواء وقد وجد إن لعملية التلدين تأثير قليل على البنية المجهرية بينما ساهمت في تقليل الخواص الميكانيكية (مقاومة الشد و نقطة خضوع والصلادة) بسبب تقليل ترسيب الأطوار الهشة ولكنه حسّن من مقاومة الالتواء بسبب زيادة القوة اللازمة لمقاومة اللي من خلال زيادة عدد الدورات اللازمة للكسر وقد وجد إن درجة حرارة التخمير (600) م° أعطت أفضل انفعال قص.


Article
Surface Modification of Red Brass Alloy by Using Laser Technique

Authors: Abdulhadi Kadhim --- Inmar N.Ghazi --- Amjed Razzaq.Hussein
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 7 Part (A) Engineering Pages: 1439-1444
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Laser shock processing technique was performed on red brass alloy type C83300 specimens for the purpose ofstudy its effect on the mechanical properties such as micro-hardness and surface roughness. LSP experimental setup system involved Q-switched Nd:YaG laser of wavelength of 1064nm and 10 ns laser pulse . Double distilled deionized water (DDDW) is used as the transparent confining layer. The effects of the LSP parameters as laser pulse energy, number of laser pulses and thickness of confinement layer on the surface micro-hardness, and surface roughness were investigated. The experimental results show that, the surface roughness and micro-hardness values increased when the laser parameters (mentioned above) have been increased and the maximum value of micro-hardness generated near the surface due to LSP. The optimum thickness of DDDW layer was 4mm. After this thickness (4mm) ,the results of microhardness and surface roughness are reduced due to the absorption of laser pulse energy by the confinement layer .


Article
Practical Study on the Corrosion Rates of Alloys (Aluminum, Medium Carbon Steel, Copper & Brass) Using Dissolved Ozone
دراسة عملية لمعدل تاكل السبائك ( الالمنيوم، الحديد المتوسط الكاربون، النحاس والبراص) بأستخدام الاوزون المذاب

Loading...
Loading...
Abstract

Ozone is a strong oxidizing a gen, with a standard electrode potential of 2.07V.Oxidize materials, equipment a, surfaces wanted to clean. Ozone unfortunately, reacts with those materials and others leading to corrosion in those materials moreover those materials could lose their effectiveness. Because of multiple uses of Ozone, its effect on corrosion of Aluminum, Medium Carbon Steel, Copper & Brass in three different flow rates by weight losses method with benefits from linear fitting process was studied. The experimental shows that corrosion rates of Aluminum & Brass in three flow rates, decreasing with increasing the exposure time to corrosion, meanwhile the corrosion rates for Medium Carbon Steel & Copper decreasing only for (0.25 ft3/hr) and for another two flow rates (0.5 & 0.75 ft3/hr) the corrosion rates increasing with increasing the exposure time to corrosion, because of ozone gas flow rate positive& negative effected by forming oxide and hydroxide film which damage or not by increasing the corrosion intervals and ozone flow rates increasing. The average of total corrosion rates for the materials used in previous work increasing with increase the flow rate of Ozone in distilled water and the maximum value was (8.71×10-17MPY), meanwhile the minimum values was (4.08 ×10-17MPY).

الأوزون هو عامل مؤكسد قوي الذي جهد الاختزال له 2.07 فولت. يتفاعل الأوزون مع المعدات، المواد والأسطح المراد تنظيفها والمعقماتوبسبب امكانية حدوث التاكل والذي يسبب فقدانها لهذه الخاصية. بسبب الاستخدامات المتعددة للاوزون نم دراسة تاثيره على تاكل الالمنيوم، الفولاذ المتوسط الكاربون، النحاس وعلى البراص بثلاث معدلات تدفق للغاز بطريقة الفقدان بالوزن مع الاستفادة من عملية التقريب الخطي. اضهرت التجارب ان معدل التاكل لكل من الالمنيوم والبراص بثلاث معدلات تدفق للغاز يتناقص مع زيادة زمن التعرض للتاكل, بينما معدل التاكل لكل من الفولاذ المتوسط الكاربون والنحاس يتناقص فقط عند 0.25قدم مكعب /ساعة’, بينما لمعدلات التدفق (0.5و0.75 قدم مكعب/ساعة) معدل التاكل يتزايد مع زيادة زمن التعرض للتاكل. نتيجة للتاثير الايجابي والسلبي لمعدلات تدفق الاوزون بسبب تكوينها طبقات الاكاسيد والهيدروكسيدات التي ربما تتكسر او لا بزيادة فترة لتاكل وزيادة معدلات تدفق الغاز. ان معدل التاكل العام للمعادن المستخدمة في الدراسة الحالية يزداد مع زيادة تدفق غاز الاوزون في الماء المقطر والقيمة الاعلى كانت ( 8.71×10-17مل /سنة )بينما الادنى كانت ( 4.08×10-17 مل / سنة ).

Keywords

Aluminum --- Medium Carbon Steel --- Copper --- Brass --- Ozone --- Corrosion

Listing 1 - 10 of 17 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (17)


Language

English (17)


Year
From To Submit

2018 (1)

2016 (1)

2015 (2)

2014 (2)

2013 (2)

More...