Article
PREPARED THIXOFOROMED ALUMINUM ALLOYS BY HIGH-PRESSURE CAST AND STUDY THEIR WEAR PROPERTIE
تحضير سبائك ثايكسوفورميد الألمنيوم بواسطة سباكة الضغط العالي ودراسة خواص البلى لها

Author: Aqeel Ali Kadhim AL-Attar عقيل علي كاظم
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2010 Volume: 3 Issue: 2 Pages: 25-38
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Hypereutectic Al-Si casting alloys are attractive candidates for connecting rod applications in compressors. Several hypo- and hypereutectic Al-Si alloys were produced by pressure die casting and thixoforming in this search. Hypereutectic Al—Si alloys were less than the near-eutectic and hypoeutectic alloys under the sever were conditions encountered in compressors, confirming the impact of Si on were resistance. Cu also improves were properties. The thixoformed alloys were at comparable rates with pressure die cast alloys at lower Si levels, implying that the lower Si content of the former is compensated for by the thixoforming processing route. Hypereutectic composition, uniform dispersion of fine Si particles and thixoforming as the production route are all good for a superior wear performance, However, does not translate into a sizable improvement in wear resistance of the thixoformed alloys.

تعتبر سبيكة الألمنيوم-سيليكون المسبوكة من السبائك ذات التطبيقات الواسعة وخصوصاً في أنظمة الضاغطات. ولهذا السبب تم إنتاج العديد من سبائك Al-Si بطرق الضغط أو العصر أو بالطريقة الهلامية (العجينة) ودراسة تأثير البلى على هذه السبيكة ومعرفة مدى تأثير السيليكون على مقاومة البلى وكذلك معرفة مدى تحسين مقاومة البلى من خلال طريقة التصنيع بالحالة الهلامية، ومن خلال هذا البحث تم التوصل إلى زيادة البلى عن طريق التصنيع بالطريقة الهلامية .


Article
Investigation of the Tribological Behavior of Eutectic Al-Si Casting Alloy

Author: Riyadh Azzawi Badr
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2017 Volume: 24 Issue: 3 Pages: 42-46
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The effect of roughness of Al-Si alloy on the wear is investigated. Roughness average (Ra) was verified via different polishing, also was using a pin–on-disc of different loads (5, 10, 15) N, different speeds (100, 200, 300) rpm and relative humidity 74%. Different values of Ra are obtained with (3, 5 and 7) µm. Worn surface were characterized using SEM / EDX. The results show that the wear rate of Al-Si eutectic alloys increases with the roughness increase. It was noticed that the specific and wear decreases as roughness decreases. Severe wear was observed at all loads.


Article
Dry Sliding Wear Characteristics of EN 24 Steel Hardened by ND: YAG Laser

Author: Ihsan AlNaimi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2019 Volume: 27 Issue: 3 Pages: 84-91
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aims of this investigation is to survey influence of ND:YAG Laser surface treatment of dry sliding wear features of EN 24 steel, which is medium carbon low alloy steel.Many parts of automotive, railways, marine and electric power generators are made from this alloy with distinctive properties as high strength and good wear resistance.According to ASTM G99 standards, length and diameter of the samples were(2 and 1) cm prepared by lathe machining. The prepared specimens were heat treated by using pulse ND: YAG Laser of 1064 nm wavelengthand 6 Hz frequency with different energies as 500, 750 and 1000 mJ for 10 pulses. Whilst, wear inspect with dry slipping was carried out in pin–on–disc mechanism through changing loads and times from 5, to 25 N and 5 to 30 min in 5 intervals respectively.In addition, roughness and microhardness examinations were performed for the samples as received and after wear test. Photomicrographs were taken for the samplesbefore, after surface Laser treatment, before, and after wear test.Results obtained increasing in hardness with improving in wear resistance. Surface roughness of treated specimenswith 1000 mJ was more than with 500 and 750 mJ energies.

أهداف هذا البحث هي دراسة تأثير المعاملة السطحية بالليزر نيديميوم – ياك على خصائص البلى الانزلاقي الجاف للفولاذ EN 24 الذي هو عبارة عن سبيكة فولاذ متوسط الكربون منخفض السبائكية. وهي تستخدم في العديد من التطبيقات التي تتطلب مقاومة عالية ومقاومة بلى مثل بعض أجزاء المركبات، ســكك الحديد، مجالات البحرية ومولدات الطاقة الكهربائية. تم تحضير العينات بالتشـــغيل علـى المخرطة لقياس 2 سم طول و1 سم قطر بموجب المواصفة القياسية ASTM G99. تمت معاملة العينات المحضرة حرارياً باستخدام الليزر نيديوم – ياك النبضي بطول موجي 1064 نانومتر، وبتردد لمنظومة الليزر 6 هيرتز مع طاقات مختلفة 500،750،و1000 ملي جول لعشر نبضات. بينما أجري اختبار البلى الانزلاقي الجاف باستخدام تقنية المسمار– على– القرص بتغيير الأحمال والزمن بمقدار 5 إلى 25 نيوتن و5 إلى 30 دقيقة على التوالي وبخمسة فترات. كذلك أجريت اختبارات الصلادة الدقيقة وفحص الخشونة للعينات قبل وبعد اختبار البلى. وتم أخذ صور مجهرية للعينات قبل وبعد المعاملة السطحية بالليزر وأيضا قبل وبعد اختبار البلى. أظهرت نتائج هذا البحث تحسن مقاومة البلى وزيادة الصلادة. خشونة السطح للعينات المعاملة بـ 1000 ملي جول هي أكثر مما هو عليه للطاقات 500 و750 ملي جول.


Article
The Effect of Glass and Carbon Fibers and Powders Addition on the Sliding Wear Behavior of Unsaturated Polyester Resin
تأثير إضافة ألياف ومساحيق الزجاج والكاربون على سلوك البلى الأنزلاقي لراتنج البولي استر غير المشبع

Loading...
Loading...
Abstract

The current investigation is interested in studying the wear phenomenon for unsaturated polyester resin reinforced by a different weight fraction of glass and carbon fibers and powders. The prepared specimens were tested according to standard (ASTM-D5963) using a dvice pin-on-disk, at room temperature. The influence of wear parameter like, applied load, sliding speed on the wear rates were investigated. It was observed that the carbon and two types of glass fibers composite shows lower wear rates than the carbon and glass powders composites, under varying the loads and sliding speeds. In the case of sliding speed increased the results show that the increased of the weight fractions of carbon and glass powders will decrease the wear rates of composites prepared from this powders, while in the case of loading increase the wear rates increased when the weight fraction increased up to (4.16 Wt.%) for both carbon and glass powders.

يهتم بحثنا الحالي بدراسة آلية حدوث ظاهرة البلى لراتنج البولي أستر غير المشبع المقوى بكسور وزنية مختلفة بالياف ومساحيق الزجاج والكاربون. أختبرت العينات المحضرة وفقاً لنظام (ASTM-D5963) باستخدام جهاز المسمار على القرص، عند درجة حرارة الغرفة. تم حساب معدلات البلى تحت تاثير مَعْلَماتْ (متغيرات) البلى، كالحمل المطبق وسرعة الأنزلاق. حيث لوحظ ان متراكبات ألياف الكاربون والزجاج بنوعيه، أظهرت أقل معدلات البلى بالمقارنة مع متراكبات المساحيق الكاربونية والزجاجية، عند تغير كل من الاحمال وسرع الانزلاق. في حالة زيادة السرعة الانزلاقية، أظهرت النتائج أن زيادة الكسور الوزنية لمساحيق الزجاج والكاربون قلل من معدلات البلى للمتراكبات المحضرة من هذه المساحيق، أما في حالة زيادة الحمل، فان معدلات البلى ازدادت بزيادة الكسر ألوزني لأعلى من (4.16 Wt.%) لكل من مسحوق الزجاج والكاربون.