Article
Physical Adsorption of Reforming Catalyst by Nitrogen

Authors: Tariq M.Naife --- Hussain K.Hussain --- Abdul Halim A.K. Mohammed
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2006 Volume: 12 Issue: 2 Pages: 345-359
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Physical adsorption by nitrogen gas was studied on seven commercial platinum reforming catalysts (RG-402, RG-412, RG-432, RG-451, RG 422,RG-482, PS-10), four prepared platinum catalysts (0.1%Pt/alumina, 0.2 %Pt/alumina, 0.45 %Pt/alumina and 0.55% Pt/alumina), and γ-alumina support.Physical adsorption was carried out by using Accelerated Surface Area and Porosimetry (ASAP 2400 device) at 77 K . The results indicate that the surface area in general decreases with increasing platinum percentage,high platinum loaded (0.45% and 0.55%) it was found that the percent increasing in surface area was lower than those obtained for low platinum loaded catalysts , and at very higher platinum loading 0.6 %Pt , some reduction in surface area was observed . The precipitation of Re and Ir metals with 0.35 % and 0.6 % platinum increases the surface area , while precipitation of 0.57% Sn with 0.375% Pt/ γ-alumina deceases the surface area catalyst .

تم دراسة الإمتزاز الفيزياوي باستخدام غازالنتروجين للعوامل المساعدة التالية: سبعة عوامل مساعدة تجارية(RG-402, RG-412, RG-432, RG-451, RG 422,RG-482, PS-10) أربع عوامل مساعدة محضرة (0.1، 0.2، 0.45 و 0.55) % وزنا بلاتين (نسبة وزنية مئوية) محمل على الألومينا, اضافة الى كاما اوكسيد الالمنيوم.تم إجراء الإمتزاز الفيزياوي في درجة حرارة النيتروجين السائل (77)كلفن باستعمال جهاز قياس المساحة السطحية والمسامية (ASAP 2400). أظهرت النتائج أن المساحة السطحية تنخفض مع زيادة نسبة البلاتين المحمل على الألومينا بشكل عام وفي نسب البلاتينيوم العالية (0.55,0.45)% وجد بأن نسبة الزيادة في المساحة السطحية هي أقل من التي تم الحصول عليها في نسب البلاتينيوم الواطئة للعوامل المساعدة ،وجد ايضا بانه عندما تكون نسبة البلاتين عالية جدا 0.6% لوحظ أنخفاض بسيط في المساحة السطحية.أن ترسيب Re و Ir للعوامل المساعدة الثنائية المعدن بنسبة 0.35 % و 0.6 % من البلاتينيوم أدى الى زيادة في المساحة السطحية مقارنة بالعوامل المساعدة الاحادية المعدن , بينما ترسيب Sn بنسبة 0.57 % للعامل المساعد 0.357%البلاتين / كاما-الومينا أدى الى أنخفاض المساحة السطحية.


Article
Thermodynamics and Kinetics study of Lead Ions Adsorption on Iraqi Bentonite
دراسة ديناميكية وحركية امتزاز ايونات الرصاص على البنتونايت العراقي

Author: Khulood A. S. AL – Saadi خلود عبد صالح السعدي1
Journal: Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة ISSN: 18131662 Year: 2006 Volume: 11 Issue: 2 Pages: 150-153
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

Evaluation of adsorption parameters of Iraqi bentonite for lead ions (Pb2+) was investigated in a temperature range (10 – 50 oC) and pH values range (2-10). The method was based on the calculation of Langmuir adsorption maximum (b), and the bonding energy term (KL). The parameters were the outcome of well – established linear relationships of Ce/Q versus Ce (Ce, equilibrium concentration and Q, amount of lead adsorbed). The Q values increased with temperature and pH increasing. Kinetics study was conducted by using Lagergreen equation and a first order equation was obtained at time ranging from 5 mints to equilibrium time, and the rate constant of adsorption was calculated. The study included the adsorption of lead ions attached to EDTA as a complex (Pb – EDTA) on bentonite.

تم تقدير دوال امتزاز ايونات الرصاص على البنتونايت العراقي عند المدى الحراري (50 – 10 ) درجة مئوية ومدى من الرقم الهيدروجيني (10 –2 ) . تعتمد الطريقة على حساب الامتزاز الأعظم من معادلة لنكماير المعروفة (b) ومن حساب ثابت (KL) الخاص بطاقة الارتباط على السطح. وتم الحصول على هذه الدوال من العلاقة المستقيمة بين قيم Ce/Q مقابل Ce ( حيث أن Ce هو التركيز عند الاتزان, Q كمية الرصاص الممتزة على البنتونايت ) , ووجد ان قيمة Q تزداد بزيادة درجة الحرارة والرقم الهيدروجيني. استخدمت معادلة لاﮔركرين الخاصة بقياس سرعة الامتزاز وكانت النتيجة الحصول على معادلة من المرتبة الأولى عند الفترة الزمنية بين خمس دقائق وزمن الاتزان , ثم تم حساب ثابت سرعة للامتزاز. تم دراسة امتزاز الرصاص الموجود بشكل مرتبط مع EDTA أي بهيئة (Pb – EDTA) على سطح البنتونايت.


Article
Adsorption of Some Blood Components on Bentonite

Loading...
Loading...
Abstract

AbstractDifferent weights at (10, 20, 30,40,50,60, and 70milligrams) of bentonite clay were incubated with 1milliliters of serum, mixed vigorously at room temperature. Serum total protein (STP), albumin, aspartate aminotransferase (AST), alanine aminotransferase (ALT), and alkaline phosphatase (ALP) were estimated before and after adsorption. Desorption processes were carried out by mixing one milliliter of distilled water with the clay that produced from adsorption process and measurement of the substances that released to the water. Albumin showed the highest adsorption capability followed by STP, ALP, ALT, and AST. The desorption process revealed that there are more than one half of the quantities adsorbed on bentonite were able to be eluted by distilled water. In conclusion, the bentonite clay has the ability to adsorb and extract of some blood component from human serum.

الخلاصةأخذت أوزان مختلفة من طين البنتونايت (60, 70 10, 20, 30, 40, 50, مللغرام) ورجت مع واحد مليلتر من مصل الدم عند درجة حرارة الغرفة. تم قياس تراكيز مكونات الدم الآتية قبل وبعد الامتزاز: بروتين الدم الكلي STP, الألبومين, أنزيم الانين امينوترانسفريز ALT, أنزيم اسبارتيت امينوترانسفريز AST, أنزيم الفوسفاتيز القاعدي ALP. كما أجريت دراسة لمعرفة كمية المادة المستخلصة وذلك بمزج الطين الناتج من عملية الامتزاز مع واحد مليلتر من الماء المقطر وقياس كمية المواد المتحررة من الطين الى الماء. اظهر الألبومين أعلى قابلية على الامتزاز على سطح طين البنتونايت يليه ALT, ALP, STP ثم AST. في تجارب الامتزاز ظهر أن أكثر من نصف كمية المواد الممتزة تتحرر الى الماء من سطح الطين. يمكن الاستنتاج ان لطين البنتونايت القدرة على امتزاز واستخلاص بعض المكونات الحيوية من مصل دم الانسان.مفاتيح الكلمات: بروتين الدم الكلي STP, الألبومين, أنزيم الانين امينوترانسفريز ALT, أنزيم اسبارتيت امينوترانسفريز AST, أنزيم الفوسفاتيز القاعدي ALP، طين البنتونايت، الامتزاز، الابتزاز.


Article
امتزاز دواء الميترونيدازول على سطح طين البنتونايت

Authors: . حسين كاظم عبد --- وسام عبد الجليل --- إحسان مهدي شهيد
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2006 Volume: 4 Issue: 1 Pages: 190-200
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Metronidazole drug (Flagyl) is widely used in as antiprotozoal drug in bowel parasitic diseases. Bentonite in medicine used as antidiarrheal, suspending agent, and as additives. Drug overdose may treated by adsorbents especially by activated charcoal suspension to prevent further absorption, but usually it is unacceptable to drink. Hence, an attempt was made in this work to estimate the ability of bentonite as adsorbent for metronidazole overdose in vitro as a possible alternative for activated charcoal. UV-Visible spectrophotometry technique was used to follow the quantity adsorbed after incubation of bentonite with a known concentration of metronidazole solutions. The adsorption experiments were repeated at (12, 25, 37.5, and 50ºC) to measure the thermodynamical parameters (ΔHº, ΔGº, ΔSº) of the adsorption process. The results showed that, there are small amounts of metronidazole ready to adsorb on bentonite. The thermodynamic parameters values were (ΔHº=18.68 KJ.mol-1, ΔGº=-10.03 KJ.mol-1, ΔSº=96.33 J.mol-1.ºK-1). The amount of the adsorbed drug was increased as the pH of the drug solution decreased.It can be concluded that the adsorption of metronidazole on bentonite is endothermic process with low thermodynamic parameters values. The adsorption enhanced by increasing temperature and by increasing acidity of the medium.

يستعمل دواء الميترونيدازول (فلاجيل) كمضاد للأوالي و الأميبا المسببة لأمراض الأحشاء الطفيلية. أما البنتونايت فيستعمل في الطب كمضاد للإسهال وكعامل للانتشار و كمضافات للأدوية. إن التسمم بالجرعات الزائدة من الأدوية يعالج بواسطة المواد ألمازة مثل معلق الفحم المنشط الذي يمتز على سطحه الأدوية ويمنع امتصاصها لكن هذا المعلق غير مستساغ عادة من قبل المرضى. لذلك أجريت هذه الدراسة لتقدير قابلية طين البنتونايت للعمل كمادة مازة لدواء الميترونيدازول كبديل محتمل لمادة الفحم المنشط.استخدمت تقنية المطيافية فوق البنفسجية لمتابعة الكميات الممتزة بعد مزج محلول الدواء مع طين البنتونايت. أعيدت التجربة عند أربعة درجات حرارية ( 12 و 25 و37.5 و50 درجة مئوية) وذلك لقياس الدوال الثرموداينمكية (ΔHº, ΔGº, ΔSº) لعملية الامتزاز.اظهر تحليل النتائج أن هناك كمية قليلة فقط من الميترونيدازول هي قابلة للامتزاز وان الكميات الثرموديناميكية كانت كالأتي:ΔHº=18.68 KJ.mol-1, ΔGº=-10.03 KJ.mol-1 , ΔSº=96.33 J.mol-1.ºK-1.كما وجد ان كمية المادة الممتزة تزداد بزيادة حامضية المحلول. إن عملية امتزاز الميترونيدازول على سطح البنتونايت هي عملية ماصة للحرارة مع قيم دوال ثرموديناميكية صغيرة. إن عملية الامتزاز تحفز بزيادة درجة الحرارة و زيادة حامضية المحلول.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)

Arabic (1)


Year
From To Submit

2006 (4)