Some Properties of High Performance Carbon Fibres Cement Composites
بعض خواص الخرسانة عالية الأداء المسلحة بألياف الكاربون

Author: Nada Al – Jalawi
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2009 Volume: 15 Issue: 4 Pages: 4409 -4416
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The paper presents properties of high performance concrete reinforced with relatively high percentage of choped carbon fibers vol. fraction ranging from (1 to 5) %. The great advantage of such composites is their relatively high flexural strength. A low water to cement ratio of 0.3 with super plasticizer was used in order to keep the cement mix easily workable. To improve the properties, a locally existing pozzolan based on reactive meta- kaolin was used in the mixture together with silica sand. A high modulus carbon fibers (450 KN/mm2) were also used. In addition to the flexural strength, dynamic modulus of elastisity were found using dynamic methods. The results showed that the specimen failed in flexureal by a single crack although the ultimate tensile strength and the stiffness of the composite were increased as the fibers content was increased.

يقدم البحث خواص الخرسانة العالية الأداء المسلحة بألياف الكاربون بنسب حجمية عالية نسبياً تتراوح من (1 – 5) % . إن الفائدة الكبيرة لهذا النوع من الخرسانة هي مقاومتها العالية للشد في الانحناء.تم استخدام نسبة واطئة من الماء/السمنت تساوي (0.3) مع استخدام ملدن متفوق للحصول على قابلية تشغيل مقبولة كما تم استخدام بوزلان محلي متكون من دقيق الكاؤولين النشط واستخدام رمل ذو أساس سيليكي وكانت ألياف الكاربون من نوع ذات معامل المرونة العالية (450 كيلونت/ملم2), بلإضافة إلى الخواص الانحنائية فقد تم بحث الخواص الديناميكية باستخدام طرق ديناميكية, وبينت النتائج بأن نوع فشل النماذج كانت بشق منفرد (single crack) وأن كلاً من مقاومة الانثناء القصوى ومعامل المرونة تزداد بزيادة نسبة الألياف.


Article
PREPARATION OF INSULATOR MATERIAL AND STUDY ITS THERMAL AND MECHANICAL PROPERTIES
تحضير عازل حراري ودراسة خواصه الحرارية والميكانيكية

Author: د. علي هوبي حليم
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2009 Volume: 9 Issue: 1 Pages: 119-124
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Due to increasing the importance of search about materials which have the capability to resistance generated flame from fires and in the same time acts as an insulator material so, this research introduced a material combined between these characteristics. In the present research, the preparation method of an insulator material, which composed of phenol – formaldehyde reinforced by carbon fibers up to 40% weight percentages, was expressed, as well as described thermal and mechanical properties. Thermal erosion test was indicated the performance of the insulator material efficiency to thermal insulation and flame retardancy. Thermal Erosion rate is 0.166mm /Sec. Mechanical properties (compression test, impact test, flexural test) indicated high toughness of insulator material.

نتيجة للأهمية المتزايدة في البحث عن مواد لها القدرة على مقاومة اللهب الناجم عن الاشتعال وفي نفس الوقت تعمل كمادة عازلة , لذلك جاء هذا البحث لتصنيع ماده تجمع بين هاتين الصفتين . استخدم في هذا البحث راتنج الفينول فورمالديهايد وتقويته بألياف الكاربون بحيث تصل نسبتها إلى 40% نسبة وزنيه . كما تم تحديد خواصه الحرارية والميكانيكية . ولتقييم كفاءة العازل الحراري وإعاقة اللهب فقد تم إجراء عدة اختبارات ميكانيكية و حرارية. لقد أظهرت النتائج التي تم الحصول عليها من اختبار ألشعله الحرارية الذي تم قي درجات حرارية عالية كفاءة راتنج الفينول فورمالديهايد المقوى بألياف الكاربون كمادة معيقة للهب وفي الوقت نفسه كفاءته في العزل الحراري عند هذه الدرجات العالية. إذ كان معدل التعرية الحراري ( Erosion Rate ) sec. 0.166 mm ∕. كما بينت نتائج الفحوصات الميكانيكية ( مقاومة الانضغاط , مقاومة الصدمة , مقاومة الانحناء ) تمتع هذا العازل بمتانة عالية .