Assessment of shear bond strength of glass ionomer cement reinforced by different amounts of Hydroxyapatite

Author: Mohammed R. Hameed* BDS, MSc, PhD
Journal: Journal of the Faculty of Medicine مجلة كلية الطب ISSN: 00419419 Year: 2009 Volume: 51 Issue: 2 Pages: 151-154
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: This study was done to assist bond strength of glass ionomer cement reinforced by different amount of Hydroxyapatite Materials and methods: In this study a hydroxyapatite materials were added to glass ionomer cement at different ratios; 10%, 15%, 20%, 25% and 30% (by weight) and the bond strength was detected by construction a cylinders from these mixed materials, constructed on exposed dentine of human extracted premolar teeth and by Zwick’s universal testing machine the bond strength were detected for these mixed materials.Results: Results showed that the glass ionomer cement reinforced by hydroxyapatite has higher bond strength than conventional glass ionomer cement and the hydroyapatite powder to glass ionomer cement powder ratio by weight best to be 25%. Conclusion: The addition of hydroxyapatite to conventional glass ionomer cement increased its bond strength to dentine.


Article
Effect of Hydroxyapatite layer Coating on Corrosion Behavior for Ti-20%Co alloy.
تأثير طبقة الطلاء بمادة الهايدروكسي ابتايت على سلوك التآكل لسبيكة Ti-20%Co.

Loading...
Loading...
Abstract


Abstract :Electrochemical corrosion of Ti-20%Co alloy coated with hydroxyapatite (HAP) performance depends on various parameters like applied potential, time, thickness and sintering temperature thus, the optimum parameters required for development of stable HAP coating was found by using electrophortic deposition (EPD) technique. This study discusses the result obtained from XRD and potentiodynamic polarisation, the measured corrosion potential in the synthetic blood plasma for the HAP coated specimens are more noble than the uncoated specimens. The specimen coated for (3) minutes was found to be the best corrosion resistance in comparison with the un coated specimens.

الخلاصةالمطلية بمادة الهايدروكسي ابتايت يعتمد على معلمات الطلاء الم ْ خَتلِفةِ مثل Ti-20%Co التآكل الكهروكيمياوي لسبيكةالفولتية المسلطة، والزمن، والسمك ودرج َ ة حرارة التلبيد. إذ تعد هذه أفضل المعلمات المطّلوبة لتطويرِ الطلاء بمادة الهايدروكسيابتايت المستقر كما أنها قد وجِد ْ ت باستعمال تقنية الترسيب بالهجرة للدقائق العالقة المشحونة.تُناقشُ هذه الدراسةِ النتائج التي حصلعليها مِ  ن منحيات الاستقطاب، إذ تمت قياسات ألتآكل في محلول بلازما الدم الصناعيِ إذ أظهرت النماذج المطلية بمادةالهايدروكسي ابتايت سلوك أكثر نبلاُ مِ  ن النماذجِ غير المطلية. كما وجد أن الأنموذج المطلي بزمن 3 دقائقِ له أفضلية من حيثالمقاومةِ للتآكلِ بالمقارنة بالنماذجِ غير المطلية.


Article
Synthesis of Fibrous Hydroxyapatite through Sol-Gel Route
تصنيع مادة الهيدروكسي ابتايت الشعيرية باستخدام طريقة السائل الهلامي

Loading...
Loading...
Abstract

The sol-gel route using an agar gel with calcium nitrate and phosphate solution as starting materials for producing hydroxyapatite (HAP). The product formed were needle like, zigzag and straight fibres. The fibrous products on sintering transformed into stoichiometric HAP with a biological Ca/P ratio of 1.67. The influences of pH, temperature, nature of base and phosphate solution on the growth of fibrous HAP were studied. The pH of the solution was found to greatly influence the growth rate and morphology of the resultant product. The optimum gel temperature was found to be 60oC and sintering temperature of 900oC for 1 hour. The crystalline, thermal, functional and morphological characteristics of the fibrous HAP were investigated.

أن العمل المعروض في هذا البحث يتضمن طريقة جديدة لتصنيع مادة الهيدروكسي ابتايت (هاب) الشعيرية ذات الاستخدام البايولوجي. محلول نترات الكالسيوم ]المخلوط بنسبة محسوبة لمادة (agar) الهلامية[ وفوسفات الامونيوم تمثلان المواد الرئيسية في التحضير، والتي ينتج عنها مادة (هاب) وبالاشكال (الابري، المتعرج والمستقيم) مع الاخذ بنظر الاعتبار المحافظة على البنية الاساسية لمادة الهاب وبالنسبة المعتمدة بايولوجيا (1.67). لاجل الحصول على تلك المادة وبالمواصفات البايولوجية الدقيقة، يجب السيطرة على المتغيرات الحاكمة وبمنتهى الدقة (الدالة الحامضية، درجة حرارة التفاعل، طبيعة المادة القاعدية وتركيز محلول الفوسفات). الفحوصات الطورية والحرارية والصور المجهرية بينت بان المادة المحضرة مطابقة للمواصفات القياسية.


Article
Influence of Immersion Period on the Corrosion Behavior of Heat Treated Biomedical Alloy Ti -5Al - 2.5Fe
تأثير فترة الغمر على سلوك التأكل السبيكة الطبية Ti -5Al - 2.5Fe المعاملة حراريا

Loading...
Loading...
Abstract

Heat treatment by solid solution method in the + phase region was used at 970°C for Ti-5Al-2.5Fe alloy. The specimens cooled under different cooling media [water quenched (WQ), air cooled (AC) and furnace cooled (FC)], and subsequently aged at 550°C for 4 hours. Five specimens from each treatment were immersed in simulated body fluid SBF for a period of time (3 months). The dependence of corrosion rate on compositional variation in the phases resulted from various type of cooling rates are discussed based on immersion tests. The EDXA results show the precipitation of phosphate and calcium compounds on the alloy after 3 months of immersion in blood plasma solution forming a bone-like apatite, which enhanced the alloy biocompatibility making it more suitable to use as biomedical implant.

تم استخدام السبيكة (Ti-5Al-2.5Fe) المعاملة حراريا (المحلول الصلب) والمدرفلة في طور(+) وبدرجة 970 م °وبثلاث أوساط للتبريد هي (الماء ، الهواء وداخل الفرن) ثم اجريت عملية التعتيق لمدة أربع ساعات للنماذج التي بردت بالماء والهواء وبدرجة550 م °.تم غمر خمسة نماذج من كل معاملة حرارية تم غمرها في مشبهات محاليل الجسم لمدة 3 أشهر. الدراسة اوضحت تاثير نوع التبريد للمعاملة الحرارية على سلوك التاكل للنماذج المغمورة في محول بلازما الدم. أظهرت فحوصات EDXRF ترسب الكالسيوم والفوسفور على السبيكة مكوناً طبقة شبيهة بالعظم مما يساعد في زيادة ملائمتها البايولوجية للاستخدامات الطبية.