Article
Synthesis of Nanosilica Glass Activated by Erbium Ions, Spectroscopic studies
توليف زجاج النانو سليكا المطعم بايونات الاربيوم، دراسات طيفية

Loading...
Loading...
Abstract

Erbium, as optical probe, doped silicate sol-gel glass with different Er concentrations was formed by wet chemical synthesis method using ethanol, water and tetraethaylorthosilicate [Si(OC2H5)4] precursor. Erbium ions were incorporated into silica sol-gel matrix via dissolution of Erbium chloride solution into the initial Si(OC2H5)4 precursor sol. Aluminum (Al) as a co-dopant was added to the final precursor in the form of Aluminum chloride (AlCl3) solution. The prepared samples were analyzed using atomic absorption analysis, X-ray diffraction and spectroscopic tests. The experimental results concerned with the transmission spectra suggest that the final samples have a good transparency and homogeneity. Also, the X-ray diffraction test showed that they have amorphous structure. The absorption and fluorescence spectra, as a function of Er concentration, were recorded at room temperature. Fluorescence emission of the 4I13/2→4I15/2 transition at ~ 1.536 µm was observed. In addition, the high values of peak emission cross-section, which were calculated as a function of Er concentration, suggest that the Er in the sol-gel may be favorable as optical material

الاربيوم كمجس بصري تم تطعيمه بزجاج السيليكات Sol-gel وبتراكيز مختلفة بأستخدام الطريقة الكيميائية الرطبة بأستعمال كحول الايثانول, الماء و محلول التتراثيل اورثو سيليكات [Si(OC2H5)4]. ايونات الاربيوم تداخل في مصفوفة السيليكا بواسطة اذابة محلول كلوريد الاربيوم في محلول [Si(OC2H5)4] الاولي. الالمنيوم كشائب مشارك قد تم اضافته الى المحلول النهائي بصيغة محلول كلوريد الالمنيوم.حللت النماذج المحضرة باستخدام تحليل الامتصاص الذري، حيود الاشعة السينية بالاضافة الى الفحوصات الطيفية. اظهرت النتائج التجريبية المتعلقة باطياف النفاذية امتلاك النماذج المحضرة لنفاذية وتجانس جيدين، كذلك اظهرت اطياف حيود الاشعة السينية التركيب العشوائي لهذة النماذج.سجلت اطياف الامتصاص والفلورة للنماذج كدالة لتركيز ايون الاربيوم عند درجة حرارة الغرفة وقد لوحظ انبعاث الفلورة الخاص بالانتقال 4I13/2 4I15/2 عند تقريبا 1.536μm. اضافة الى ذلك فان القيم العالية لذروة المقطع العرضي للانبعاث والتي حسبت كدالة لتركيز ايون الاربيوم بينت أن الاربيوم المطعم بزجاج الـ Sol-gel قد يكون مفضلا كمادة بصرية ليزرية.

Keywords

Erbium --- silica sol-gel


Article
Two-dimensional Crystallization of Silica nanospheres using Coplanar DC Electric field
تكوين بلورة ثنائية الأبعاد من جسيمات السيليكا بتاثير المجال الكهربائي

Loading...
Loading...
Abstract

Two-dimensional crystal has been achieved and controlled with the aid of DC electric field applied between two electrodes at 5 millimeters separating distance between them. Sol-gel method has been used to prepared nanosilica particle which used in this work as well as TiO2 nanopaowder. The assembly of the silica particles is due to the interaction between the electrical force, the particles dipole, and the interaction between the particles themselves. When a DC voltage is applied, the particles accumulated and crystallized on the surface between the electrodes. The Light diffraction demonstrates that the hexagonal crystal is always oriented with one axis along the direction of the field. The particles disassemble when the field is turned off, and the process can be repeated many times. The diffraction patterns from all consecutively formed crystals are identical. This assembly is driven by forces that depend on the electric field gradient; the process can be controlled via the external field strength, and the viscosity of the liquid media.

تم الحصول على بلورة ثنائية الأبعاد من جسيمات السيليكا و التحكم بها بواسطة مجال كهربائي مسلط بين قطبين المسافة بينهما 5 مليمتر. تم تحضير جسيمات السيليكا المستخدمة في هذا العمل باستخدام تقنية السول–جل ،وكذلك تم استخدام مادة ثنائي اوكسيد التيتانيوم . هذا التجميع هو نتيجة التفاعل بين القوة الكهربائية وثنائيات القطب المتكونة من الجسيمات وكذلك التفاعل بين ثنائيات الأقطاب نفسها . عند تسليط الفولتية المستمرة تتجمع الجسيمات على السطح بين القطبين الكهربائيين .نمط الحيود الضوئي خلال لبلورة المتكونة يشير إلى الترتيب السداسي للجسيمات خلال البلورة بين القطبين . عند إزالة المجال الكهربائي تعود الجسيمات لحلة عدم التجمع وهذه العملية يمكن أعادتها عدة مرات . يمكن الحصول على نفس نمط الحيود من كافة مناطق البلورة . هذه العملية يمكن التحكم بها بواسطة قوة المجال الكهربائي وكذلك لزوجة السائل المستخدم.


Article
Some Properties of High Performance Carbon Fibres Cement Composites
بعض خواص الخرسانة عالية الأداء المسلحة بألياف الكاربون

Author: Nada Al – Jalawi
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2009 Volume: 15 Issue: 4 Pages: 4409 -4416
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The paper presents properties of high performance concrete reinforced with relatively high percentage of choped carbon fibers vol. fraction ranging from (1 to 5) %. The great advantage of such composites is their relatively high flexural strength. A low water to cement ratio of 0.3 with super plasticizer was used in order to keep the cement mix easily workable. To improve the properties, a locally existing pozzolan based on reactive meta- kaolin was used in the mixture together with silica sand. A high modulus carbon fibers (450 KN/mm2) were also used. In addition to the flexural strength, dynamic modulus of elastisity were found using dynamic methods. The results showed that the specimen failed in flexureal by a single crack although the ultimate tensile strength and the stiffness of the composite were increased as the fibers content was increased.

يقدم البحث خواص الخرسانة العالية الأداء المسلحة بألياف الكاربون بنسب حجمية عالية نسبياً تتراوح من (1 – 5) % . إن الفائدة الكبيرة لهذا النوع من الخرسانة هي مقاومتها العالية للشد في الانحناء.تم استخدام نسبة واطئة من الماء/السمنت تساوي (0.3) مع استخدام ملدن متفوق للحصول على قابلية تشغيل مقبولة كما تم استخدام بوزلان محلي متكون من دقيق الكاؤولين النشط واستخدام رمل ذو أساس سيليكي وكانت ألياف الكاربون من نوع ذات معامل المرونة العالية (450 كيلونت/ملم2), بلإضافة إلى الخواص الانحنائية فقد تم بحث الخواص الديناميكية باستخدام طرق ديناميكية, وبينت النتائج بأن نوع فشل النماذج كانت بشق منفرد (single crack) وأن كلاً من مقاومة الانثناء القصوى ومعامل المرونة تزداد بزيادة نسبة الألياف.


Article
Predicting Mechanical Properties of High Performance Concrete by Using Non-destructive Tests
التنبؤ بالخواص الميكانيكية للخرسانة عالية الأداء بإستخدام الفحوصات اللاإتلافية

Authors: Sura F. Al-Khafaji --- Waleed A. Al-Qaisi --- Shakir A. Al-Mishhadani
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 3 Pages: 425-444
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study, high performance concrete mixes were produced by using highrange water reducing agent and also by using 10% silica fume or 10% highreactivity metakaolin as a partial replacement by weight of cement. Three cementcontents (350, 450, and 550) kg/m3 were used through this study. A total of 330(100 mm) cubes, 132 (100×200 mm) cylinders, 132 (100×100×400 mm) prisms,and 66 (150×300 mm) cylinders were casted and cured to the required age of test .All specimens were cured in tap water except 165 cubes, which were submerged inCl ˉ + SO4ˉ ˉ solution at concentration identical to those present in severeaggressive environment to study the effect of this solution on the compressivestrength of high performance concrete mixes. Compressive strength, splittingtensile strength, modulus of rupture, static modulus, rebound number, ultrasonicpulse velocity, dynamic modulus, initial surface absorption, density ,and totalabsorption tests were investigated for all mixes at 7, 28, 90, and 120 days age.Results of the destructive tests (compressive tensile strength, strength, splittingmodulus of rupture, and static modulus) and non–destructive tests (hammer,ultrasonic pulse velocity, and dynamic modulus) are statistically analyzed by usingSPSS Ver.15 software to study the possibility of predicting the mechanicalproperties of high performance concrete by using non–destructive tests. Simple andmultiple linear regression analysis of the obtained results leads to the proposedstatistical models for evaluating the compressive strength, splitting tensilestrength, modulus of rupture, and static modulus by using one or two or three ofthe above mentioned non–destructive tests. Analysis of variance (ANOVA)and t–test was also used to investigate the adequacy of the statistical models.

تم في هذه الدراسة انتاج خلطات خرسانية عالية الاداء باستخدام مضاف مقلل للماء بدرجة متفوقةوكذلك باستخدام ابخرة السليكا المكثفة بنسبة ١% او الميتاكاؤولين عالي الفعالية بنسبة ١% كتعويضعن جزء من وزن الاسمنت ، كما و تم استخدام ثلاث محتويات من السمنت 426٤٥٠،٣٥٠ و ٥٥٠ ) كغم/م ٣. تم صب و تهيئة ٣٣٠ مكعب بابعاد ( ١٠٠ ملم) ، ١٣٢ اسطوانة )٤٠٠ ملم ) و ٦٦ اسطوانة بابعاد ×١٠٠× ٢٠٠ ملم) ، ١٣٢ موشور بابعاد ( ١٠٠ × بابعاد ( ١٠٠٣٠٠ ملم) و قد عولجت جميعها بالماء لغاية عمر الفحص المطلوب ما عدا ١٦٥ مكعب تم ×١٥٠)غمرها جزئياً في محلول الكلوريدات و الكبريتات بتراكيز مماثلة لتلك الموجودة في ظروف بيئيةقاسية لدراسة تأثير هذا المحلول على مقاومة الانضغاط للخلطات الخرسانية العالية الاداء .اجريت فحوصات مقاومة الانضغاط ، مقاومة الشد الانفلاقي ، مقاومة الانثناء ، معامل المرونةالاستاتيكي ، رقم الارتداد، سرعة الموجات فوق الصوتية، معامل المرونة الديناميكي ، فحصالامتصاص السطحي الاولي ، الكثافة ، وفحص الامتصاص الكلي باعمار ١٢٠،٩٠،٢٨،٧ يوم .تم تحليل نتائج الفحوص ات الإتلافية (مقاومة الانضغاط ، مقاومة الشد الانفلاقي ، مقاومة الانثناء، ومعامل المرونة الاستاتيكي ) و اللاإتلافية (رقم الارتداد، سرعةالموجات فوق الصوتية، معامللدراسة امكانية التنبؤ بالخواص (SPSS Ver. المرونة الديناميكي) احصائياً باستخدام برنامج ( 15الميكانيكية لخرسانة عالية الاداء باستخدام الفحوصات اللاإتلافية . التحليل الانحداري البسيطوالمتعدد الخطي للنتائج المستحصلة ادى الى النماذج الاحصائية المقترحة لتقييم الخواصالميكانيكية باستخدام فحص واحد او فحصين او ثلاثة من الفحوصات اللاإتلافية . كذلك تم استخداملتحري كفاءة النماذج الاحصائية. (t-test) و (ANOVA) تحليل التباين

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2009 (4)