Analysis of Linearity Response and Spectral Responsivity in CdS Photoconductive Detector
تحلیل الاستجابة الخطیة والاستجابة الطیفیة لكاشف التوصیلیة الضوئیة CdS

Authors: Ali M. Mousa --- Selma M. H. Al- Jawad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 3 Pages: 584-591
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thin films of cadmium sulfide have been deposited by chemical bath deposition.The effect of temperature and time deposition on spectral responsivity for CdSphotoconductive investigation. The effect of temperature bath and time depositionwhere study. Linearity response of photoconductive detector were carry on analyzingthe light current with incident power curves. The results show that high spectral nonsaturated responsivity was achieved, further the detector were manufacture with lowcost.

حضرت أغشية كبريتيد الكادميوم بطريقة الترس يب بالحمام الكيميائي . إذ درس تأثير درجة حرارةوكذلك درس تأ ثير .CdS الحمام وزمن الترسيب على الاستجابة الطيفية لكاشف التوصيلية الضوئيةدرجة حرارة الحمام وزمن الترسيب على الاستجابة الخطية لكاشف التوصيلية الضوئية بتحليل منحنياتالتيار الضوئي مع القدرة الساقطة . حيث أبدى الكاشف المصنع بأقل كلفة استجابة عالية واستجابة خطيةدون حصول أي استقرارية للتيار الضوئي مع القدرة الساقطة.


Article
Correlation between Thickness, Grain Size and Optical Band Gap of CdI2 Film
الترابط بين السمك والحجم الحبيبي مع فجوة الطاقة البصرية لأغشية يوديد الكادميوم

Author: Modaffer A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 6 Pages: 1174-1183
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Structural and optical property was studied as a function of film thickness forthermally evaporated CdI2 films. Stoichiometric films (up to 250 nm thickness) showinghexagonal structure, and good c-axis alignment normal to glass substrate plane. Theoptical absorption data indicate an allowed direct inter – band transition near theabsorption edge with optical energy gap varies continuously from 2.9 eV to 3.6 eV.Partof the optical data was fitted to an indirect type transition to determine the indirect opticalenergy gap which also varies continuously from 2.2 eV to 3.1 eV . Both energy gapsshow thickness dependences, which can be explained qualitatively by a thicknessdependence of the grain size through the decreasing of the grain boundary barrier heightwith grain size.

درست الخصائص البصرية والتركيبية كدالة لسمك أغشية يو ديد الكادميوم المحضرة بالتبخير250 ) تركيبا سداسيا وترصيف جيد في nm الحراري.أظهرت الأغشية المتوازنة كيماوي ا(لحد سمكالعمودي على القواعد الزجاجية .بينت قيم الامتصاص البصري انتقالات مباشرة (c-axis) المحور.(2.9eV to 3.6eV) مسموحة بين الحزم قرب حافة الامتصاص وبفجوة طاقة بصرية متغيرة ما بينجزء من القيم البصرية كانت مطابقة للانتقالات غير المباشرة وبها حددت فجوة طاقة بصرية غير2.2 ).أظهرت كلا فجوتي الطاقة اعتمادا على السمك,والذي eV to 3.1eV) مباشرة متغيرة أيضا مابينيمكن تفسيره كميا بأعتماد الحجم الحبيبي على السمك من خلا ل تناقص ارتفاع حاجز الجهد عند الحدودالبلورية مع الحجم الحبيبي.


Article
Interfacial Adhesion of PZT Ferroelectric Thin Films Determined by Nano-Indentation Method

Authors: X.J. Zheng --- Y.C. Zhou
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2009 Volume: 5 Issue: 1 Pages: 46-48
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

We propose an elastic groundsill beam model with piezoelectric effectconsidered to assess the interfacial adhesion of ferroelectrics thin films,complemented and validated by nano-indentation fracture test onPb(Zr0.52Ti0.48)O3 (PZT) thin films. It was observed from the loadindentationdepth curves and atomic force microscopy (AFM) images thatthe fracture failure of PZT thin films induced by nano-indentations can bedivided into three typical stages: no damage, bulging and spallation. Thedelamination of thin film systems was modeled as an interfacial crackpropagation problem, with the energy release rate determined from theelastic groundsill beam model. For PZT thin films deposited on single Sisubstrate with thickness of 350nm and 450nm, the energy release rates perunit new crack area are in the range of 3.399~52.432J/m2 and the phaseangles are constant of 13.3570.


Article
Studies on solution – growth thin films of CdS : Zn for photovoltaic application
دراسة أغشية CdS:Zn المرسبة بطريقة النمو بالمحلول المستخدم في تطبيقات الفوتولتائية

Author: Selma M. H. Al- Jawad سلمى محمد حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2009 Volume: 6 Issue: 1 Pages: 135-140
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Structural, optical, and electrical properties of thin films of CdS : Zn prepared by the solution – growth technique are reported as a function of zinc concentration. CdS are window layers influencing the photovoltaic response of CIS solar cells. The zinc doping concentration was varied from 0.05 to 0.5 wt %, zinc doping apparently increase the band gap and lowers the resistivity. All beneficial optical properties of chemically deposited CdS thin films for application as window material in heterojunction optoelectronic devices are retained. Heat treatment in air at 400 °C for 1h modify crystalline structure, optical, and electrical properties of solution growth deposited CdS : Zn films.

درست الخصائص التركيبية والبصرية والكهربائية للاغشية الرقيقة CdS : Zn المحضرة بتقنية النمو بالمحلول كدالة لتركيز شوائب الزنك. اذ توثر اغشية ال CdS المستخدمة كنافذة للخلايا الشمسية CIS على الاستجابية الفوتوفولتائية. حيث غيرت تراكيز شوائب الزنك من 0.05 الى 0.5% , اذ عملت شوائب الزنك على زيادة فجوة الطاقة مع تقليل المقاومية الكهربائية, مع الحفاظ على نفاذية عالية للاغشية الرقيقة المرسبة بتقنية النمو بالمحلول اللازمة لاستخدام غشاء CdS كنافذة للتركيب الهجيني المستخدم في النبائط الالكترونية – البصرية. كذلك اجري تلدين للاغشية الرقيقة بدرجة حرارة 400 درجة مئوية ولمدة ساعة ، الذي ادى الى تغير التركيب البلوري والخصائص البصرية والكهربائية لاغشية CdS:Zn .


Article
Analytical Equivalent Optical Properties of CdS-CuxS Thin Films Deposited on Glass Substrate by Spray Pyrolysis

Authors: H.I. Nacsu --- V. Paposcu
Journal: Iraqi Journal of Applied Physics Letters الرسائل العراقية في الفيزياء التطبيقية ISSN: 1999656X Year: 2009 Volume: 2 Issue: 4 Pages: 37-40
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

Multi-layered, firmly adherent, optically clear CdS/CuxS films were deposited by spray pyrolysis on glass substrate. The glass/CdS/CuxS system was investigated. Firstly, CdS films were deposited using a solution containing CdCl2 and thiourea. For CuxS films deposition the solution used consisted on CuCl2 and thiourea. Multilayered films were also deposited. Mixed films of copper and cadmium sulfides were also deposited from solutions containing both copper and cadmium salts and thiourea on heated glass substrates, by spray pyrolysis. Visible transmission spectra were recorded for CdS/CuxS films. The film characteristics depend on the concentration and the molar ratio of cadmium and copper salts. These thin layers may be applied in solar control coatings, leading to important energy saving for air conditioning devices used for cars or other closed spaces.


Article
Power Reduction in Flexible Silicon Thin Film Digital Circuits

Authors: T.J. Alward --- K.R. Wissmiller --- J.E. Knudsen
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2009 Volume: 5 Issue: 2 Pages: 19-23
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

Amorphous silicon (a-Si) thin-film circuits promise robust, lightweight, flexible displays and digital computation. Here, several methods for reducing standby-power while retaining logic state are investigated for such circuits. Lacking a PMOS load transistor, the conventional approach for retaining state is to dynamically shift values through memory elements. We investigate other methods and demonstrate 36x power savings by introducing a non-shifting, refresh based operating mode.


Article
Increasing the Conductivity of Cadmium Telluride Films
زيادة توصيلية أغشية تولورايد كادميوم

Authors: Muslm Fadhel Al-Zubadi --- Waseem Najeeb Ibrahim
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 14 Pages: 2682-2691
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The structural , optical and electrical properties of vacuum-evaporated CdTe thin films were investigated as a function of post-deposition annealing without and with CdCl2 treatment at 300˚C for 15min . X-Ray diffraction studies of the asdeposited films revealed polycrystalline in nature with cubic structure . The intensity of the (111) peak increased with the CdCl2 annealing treatment , and there is an increasing in the grain sizes after the CdCl2 annealing treatment with voids around the grain boundaries from the surface morphologies after the CdCl2 annealing treatment . The optical band gap values , Eg , were 1.56, 1.54 and 1.38 eV for film deposited at room temperature and after annealing without and with CdCl2 treatment at 300˚C for 15min respectively . Furthermore , the activation energy decreases after heat treatment without and with CdCl2 for CdTe thin films.

CdTe تم دراسة الخصائص التركيبية والبصرية والكهربائية لأغشية تولورايد كادميوم الرقيقة المحضرة بطريقة التبخير الحراري في الفراغ وتاثيرعملية التلدين والمعالجة الحرارية بمحلول كلوريد الكادميوم عند درجة حرارة ( 300 ) درجة مئوية ولمدة ( 15 ) دقيقة على خواص الأغشية المحضرة . اوضحت نتائج حيود الاشعة السينية ان جميع الأغشية المحضرة متعددة التبلور وذات تركيب بلوري مكعب . حيث ان شدة المستوي ( 111 ) تزداد بعد عملية المعالجةالحرارية بمحلول كلوريد الكادميوم وحصول زيادة في الحجم الحبيبي بعد اجراء المعالجة الحرارية مع وجود مناطق عشوائية حول الحدود الحبيبية من خلال دراسة طوبغرافية سطوح 1.38,1.54,1.56 ) لأغشية مرسبة عند درجة حرارة ) eV الأغشية . وبلغت قيم فجوة الطاقة ( الغرفة وبعد عملية تلدينها ومعالجتها حرارياً بمحلول كلوريد الكادميوم بدرجة حرارة ( 300 درجة مئوية ولمدة ( 15 ) دقيقة على التوالي . اضافة الى نقصان في قيم طاقة التنشيط بعد اجراء. CdTe عملية التلدين والمعالجة الحرارية بمحلول كلوريد الكادميوم لأغشية


Article
Structural and Optical Characteristics of CdSe Thin Films Prepared by Chemical Bath Deposition Technique

Authors: J. Chandrasekaran --- S.M. Mohan --- S. Thirumalairajan --- K. Girija
Journal: Iraqi Journal of Applied Physics Letters الرسائل العراقية في الفيزياء التطبيقية ISSN: 1999656X Year: 2009 Volume: 2 Issue: 4 Pages: 21-24
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

Cadmium selenide thin films were deposited on glass substrate using chemical bath technique for different bath temperatures 313K, 333K and 353K. Polycrystalline nature of the material was confirmed by X-ray diffraction technique and various structural parameters were calculated. The optical properties were revealed by UV-Visible transmittance spectra and the band gap energy was determined.


Article
The structure and optical properties of CdSe:Cu Thin Films
الخواص التركيبية والبصرية للأغشيةالرقيقة CdSe:Cu

Authors: Ikbal S. Naji اقبال سهام ناجي --- Tariq. J. Alwan طارق جعفر علوان --- Eman M.N.Al-Fawadi ايمان مزهر ناصر الفوادي
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2009 Volume: 6 Issue: 1 Pages: 141-149
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

A polycrystalline CdSe thin films doped with (5wt%) of Cu was fabricated using vacuum evaporation technique in the substrate temperature range(Ts=RT-250)oC on glass substrates of the thickness(0.8μm). The structure of these films are determined by X-ray diffraction (XRD). The X-ray diffraction studies shows that the structure is polycrystalline with hexagonal structure, and there are strong peaks at the direction (200) at (Ts=RT-150) oC, while at higher substrate temperature(Ts=150-250) oC the structure is single crystal. The optical properties as a function of Ts were studied. The absorption, transmission, and reflection has been studied, The optical energy gap (Eg)increases with increase of substrate temperature from (1.65-1.84)eV due to improvement in the structure. The amorphousity of the films decreases with increasing Ts. The films have direct energy gap and the absorption edge was shift slightly towards smaller wavelength for CdSe:Cu thin film with increase of substrate temperature.it was found that the absorption coefficient was decreased with increasing of substrate temperature due to increases the value of(Eg). The CdSe:Cu films showed absorption coefficient in the range (0.94 x104-0.42x104)cm-1at Ts=RT-250 oC. Also the density of state decreases with increasing of substrate temperatures from (0.20-0.07)eV, it is possibly due to the recrystallization by the heating substrate temperatures.. Also the extinction coefficient, refractive index and dielectric constant have been studied.

حضرت الأغشية الرقيقة CdSe:Cu المتعددة البلورات والمطعمة بالنحاس بنسبة (5wt%) بأستعمال تقنية التيخير الفراغي بمدى درجة حرارة اساس (Ts=RT-250)oC على قواعد زجاجية. حدد تركيب تلك الاغشية بواسطة الفحص بالأشعة السينية (XRD) . بينت دراسات حيود الاشعة السينية بان التركيب يكون من النوع المتعدد البلورات السداسي, وهناك قمة قوية بالاتجاه (200) عند(Ts=RT-250) oC بينما عند درجات حرارة الأساس العالية(Ts=150-250) oC يتحول التركيب الى البلورة المفردة . درست الخصائص البصرية كدالة لدرجة حرارة الأساس(Ts) ودرست النفاذية والأمتصاصية والأنعكاسية. فجوة الطاقة تزداد بزيادة درجة حرارة الأساس من(1.65-1.84)eV وتقل العشوائية نتيجة للتحسن بالتركيب البلوري. تمتلك الأغشية فجوة طاقة مباشرة و تزاح حافة الأمتصاص بأتجاه الأطوال الموجية القصيرة لأغشية CdSe:Cu بزيادة درجة حرارة الأساس وجد بأن معامل الأمتصاص يقل بزيادة درجة حرارة الأساس من(0.94 x104-0.42x104)cm-1at Ts=RT-250 oC, كذلك تقل كثافة الحالات بزيادة درجة حرارة الأساس (0.20-0.07)eV ذلك نتيجة لاعادة التبلور بواسطة التسخين بدرجة حرارة الأساس..كذلك درس معامل الخمود ومعامل الأنكسار وثوابت العزل كدالة لدرجة حرارة الأساس .


Article
The Effect of Humidity on the Optical Storage BDK/MR and PMMA/BDK/MR Systems Using the Spectroscopic Eillpsometry
تأثير الرطوبة على أنظمة الخزن البصري BDK/MR و PMMA/BDK/MR باستخدام مطيافية القطع الناقص

Author: Taha. M. AL – Maula طه مصطفى خضر المولى
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2009 Volume: 20 Issue: 3A Pages: 95-102
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

The effect of humidity on the two optical storage systems PMMA/BDK/MR, BDK / MR has been studied by preparing the system of BDK/MR from the Azo – dye of the methyl red (MR) and it is mixed with benzyl dimethyl ketal (BDK) in certain rates of size. But the other system PMMA/BDK/MR has been prepared from the Azo – dye of methyl red (MR) doped with poly methyl methacylate (PMMA) benzyl dimethyl ketal (BDK) and was used as a photoinitiartor at certain rates of size. The effect of humidity has been studied by using device of spectroscopical Eillipsometry which has different angles on the two systems of optical storage, and its become clear that the effect of humidity on the system BDK/MR is greater than that of PMMA/BDK/MR. From this we conclude that the thin films which were prepared from PMMA / BDK / MR system are better than those of the BDK/MR system and adding these information to the programming library for spectroscopical device .

في هذا البحث تمت دراسة تأثير الرطوبة على نظامي الخزن البصري BDK/MR وPMMA/BDK/MR. إذ تم تحضيـر النظـام BDK/MR مـن صبغة المثيل الأحمـر MR مثـال (Azo – dye) وخلطها مع البادئ الضوئي BDK مثال (Benzyl dimethyl Ketal ) بنسب حجمية معينة. أما النظام PMMA/BDK/MR تم تحضيرها من صبغة المثيل الأحمر مثال (Azo – dye) وبوليمر PMMA مثال(Poly methyl methacylate) مطعم بالبادئ الضوئي BDK مثال (Benzyl dimethyl ketal) بنسب حجمية معينة. أن تأثير الرطوبة درست باستخدام جهاز مطيافية القطع الناقص متغير الزوايا على نظامي الخزن البصري وتبين أن تأثير الرطوبة على نظام الخزن BDK/MR اكبر بكثير من النظام الخزن البصري PMMA/BDK/MR ومن هنا نستنتج بان الأغشية الرقيقة المحضرة من النظام PMMA/BDK/MR أفضل من الأغشية الرقيقة المحضرة من النظام BDK/MR وإضافة هذه المعلومات إلى المكتبة البرمجية لجهاز المطيافية

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (10)

Arabic (1)


Year
From To Submit

2009 (12)