Article
Effect of Aluminizing Process on The Mechanical Properties of Stainless Steel Type (305)
تأثير عملية الألمنة على الخواص الميكانيكية للصلب ألسبائكي ( 305

Author: صباح نوري محمود
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 9 Pages: 434-443
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this work is to study the thermal surface treatment by Aluminizingprocess of stainless steel (305) to modify the mechanical properties of the surfaceby pack cementation process. The coating process was done with various periodsof time (2, 4, 6, 8, 10) hours and temperatures (900 1000 1100)°C. The resultsshowed that the thickness of coating layer was increased with the increment oftime and temperature. The microhardness values of coating layer was reducedfrom the outer surface to the core, also the results showed that the highestmicrohardness of the coating was obtained at period of (6) hours and temperatureof (900, 1000, 1100)°C, also the highest bending stress was obtained at the periodof (6) hours and at all temperature.

تناول البحث أجراء معاملة حرارية سطحية لتحوير الخصائص الميكانيكية لسطح السبيكةالأساس وهو الصلب السبائكي السبيكة ( 305 ) باستعمال واحدة من طرق المعاملات الحراريةالكيميائية السطحية وهي عملية السمنتة وهي واحدة من طرق الطلاء الانتشاري حيث تمت عمليةالطلاء بالألمنيوم بدرجات حرارية ( 1100,1000,900 ) مْ وأزمان ( 10,8,6,4,2 ) ساعة وقد تمقياس سمك طبقة الطلاء المتكون وأظهرت النتائج إن سمك طبقة الطلاء يزداد بزيادة درجةالحرارة والزمن كما تم قياس الصلادة المايكروية ووجد إن مقدار الصلادة المايكروية يزداد عند( الأطراف ويقل كلما اتجهنا نحو القلب وان أفضل مقدار للصلادة حصلنا عليه عند زمن ( 61100 ) م وكذلك تم قياس إجهاد الانحناء ووجد إن , 1000, ساعة وللدرجات الحرارية ( 900أفضل قيمة لإجهاد الانحناء حصلنا عليها عند زمن ( 6) ساعة وللدرجات الحرارية الثلاث .


Article
Studying Some Of Mechanical properties Of (sawdust/Un Saturated Polyester) Composite in salt solution
دراسة بعض الخواص الميكانيكية لمتراكبات (نشارة الخشب /البولي أستر غير المشبع )في المحلول الملحي

Author: Sanaa A. A. Hafad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 16 Pages: 5238-5245
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Commercial sawdust is the most common wood filler used for polysterthermosetting and is produced from graduated particles of different sizes which has in general has a lower aspect ratio than wood and other natural fibers. Wood additives include a mixture of sawdust and short chopped fibers. To study how characteristics of fibers and sawdust influence the mechanical properties of unsaturated polyester composites .Investigations were made by studying the effects of different volumetric fractions from sawdust and fiber fillers (up to limitof 1.4mm), then these results were compared with the properties of sawdust –fiber filled composites immersed for different periods in a salt solution of (2 N) . wood volume fractions {(20, 30, 50) vf %} selected to be added for un saturated polyester were studied which gave improvement in their selected studied mechanical properties for all reinforced composites -(only impact is decreased)- and particularly at higher values of volume fractions ,were hardness showed an improvement by (15% ) , compressive strength gave obvious Improvement by(38% ) ,while impact resistance decreased by (16%) with the reinforcement of (50 vf %) sawdust . The above values were reduced when the items were immersed in asalt solution for (60days).

أن نشارة الخشب التقليدية ،تعد من أكثر الأخشاب التي تستخدم كمالئات للبوليمرات المتصلدة حراريا،يتم أنتاجها بهيئة مزيج متدرج من الحجوم الحبيبية ،وبشكل عام تمتلك نسبة باعية أوطأ من ألياف الخشب والمواد الطبيعية الأخرى ،أن إضافات الخشب تتضمن مزيجا من النشارة والألياف القصيرة المقطعة . ولدراسة تأثير مميزات نشارة وألياف الخشب على الخواص الميكانيكية لمتراكبات البولي أستر ،تم التحقق في تأثير دراسة الكسور الحجمية المختلفة لمالئات من ألياف و نشارة الخشب (ذات حد حبيبي 1,4 ملم) على الخواص الميكانيكية لمتراكبات البولي أستر المدعمة ،وبعدها تم مقارنة تلك النتائج مع نتائج لمتراكبات البولي أستر المدعمة بنفس المالئات بعد غمرها لفترات زمنية مختلفة في أوساط ملحية ذات عياريه ( 2) . تم اختيار كسورا 50 ) % } من البوليستر غير المشبع المختار . ) , (30) , ( حجميه للمالئات تراوحت بين { ( 20 أوضحت النتائج تطورا واضحا في الخواص الميكانيكية - (ماعدا مقاومة الصدمة) - وبالخصوص عند ارتفاع قيم الكسر ألحجمي حيث حققت الصلادة تطورا بنسبة ( 15 % ) , في حين حققت مقاومة الانضغاط تطورا ملحوظا وبنسبة ( 38 % ) ،بینما انخفضت مقاومة الصدمةبنسبة ( 16 %) عند التدعیم بنسبة ( 50 ) % حجما من نشارة الخشب.أن القیم أعلاه أنخفضت عند الغمر في المحلول الملحي لمدة ستون یوما.

Listing 1 - 2 of 2
Sort by
Narrow your search

Resource type

article (2)


Language

Arabic (1)

English (1)


Year
From To Submit

2010 (2)