Calculation the mass attenuation coefficient of beta-particles through Polyvinyl chloride
حساب معامل التوهين الكتلي لجسيمات بيتا خلال بولي كلوريد الفاينيل

Authors: Harith I. Jaafer حارث ابراهيم جعفر --- Ban M. Alshabander بان مازن مزاحم الشابندر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2010 Volume: 8 Issue: 12 Pages: 50-53
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The mass attenuation coefficient for beta particles through pure Polyvinyl chloride (PVC) and flax fibers- reinforced PVC composite were investigated as a function of the absorber thickness and the absorber to source distance. The beta particles mass attenuation coefficients were obtained using a NaI(Tl) energy selective scintillation counter with 90Sr/ 90Y beta source having an energy range from (0.546-2.275) MeV. Pure PVC polymer samples were prepared by compacting the PVC powder in a mould at high pressure (10bar) and temperature about 140°C for 30 minutes. A hot press system was used for this process. The experimentally obtained values of mass attenuation coefficients for 90Sr and 90Y were found to be 7.72 cm2.g-1and 0.842 cm2.g-1 respectively, and the measured mass attenuation coefficients values decrease with increase of the absorber to source distance .

تمت دراسه معامل التوهين الكتلي لجسيمات بيتا خلال عينات من مادة بولي كلوريد الفاينيل (PVC) ومتراكب الياف الكتان المدعمة بــ (PVC) كدالة لسمك المادة الماصة وللمسافة بين المادة الماصة والمصدر المشع. تم قياس معامل التوهين الكتلي لجسيمات بيتا باستخدام منظومة الكاشف الوميضي NaI(Tl) مع مصدر أشعة بيتا 90Sr/90Y بمدى طاقة تتراوح بين (0.546-2.75) ميكا الكترون فولت. حضرت عينات (PVC) النقي عن طريق كبس مسحوق الـ (PVC) في قالب معدني تحت ضغط عالي مقداره 10 بار وبدرجة حرارة 140 درجة مئوية ولمدة 30 دقيقة ولقد استخدمت منظومه الكبس الحراري لهذا الغرض. وجد ان القيم العملية المستحصلة لمعامل التوهـين الكتلي لـ 90Sr و 90Y هي 7.72 cm-2.g-1 و 0.842 cm-2.g-1 على التوالي. وان قيم معاملات التوهين الكتلي تتناقص مع زيادة المسافة بين المادة الماصة والمصدر.


Article
POLYVINYL ALCOHOL/POLYVINYL CHLORIDE (PVA/PVC) HOLLOW FIBER COMPOSITE NANOFILTRATION MEMBRANES FOR WATER TREATMENT

Authors: Sufyan Algebory --- A. Figoli --- Qusay Alsalhy --- Ghanim M. Alwan --- et al.
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2010 Volume: 11 Issue: 4 Pages: 23-32
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Two different polyvinyl alcohol/polyvinyl chloride (PVA/PVC) hollow fiber composite nanofiltration membranes were prepared after PVC hollow fiber membranes were coated using dip-coating method with PVA aqueous solution, which was composed of PVA, fatty alcohol polyoxyethylene ether (AEO9), and water [PVA/AEO9/water (4:0.5:95.5) wt%]. Effect of two different PVC hollow fiber immersion times in coating solution were studied. Cross-section, internal and external surfaces of the PVC hollow fibers and PVA/PVC composite nanofiltration membranes structures were characterized by scanning electron microscopy (SEM), pure water permeation flux and solutes rejection. It was found that, the coating layer thickness on the outer surface of the 19 wt% PVC hollow fiber was thin and about (6µm), while the coating solution penetrates through the outer edge of the PVC hollow fiber and it looks like sponge-like structure with increase of the dip-coating time from 20 to 30 sec. Besides, the pure water permeation flux decreases and solutes rejection increases with an increase of the coating time from 20 to 30 sec for the two PVA/PVC composite nanofiltration membranes.Molecular weight cut-off (MWCO) of the PVA/PVC composite nanofiltration membranes were in the range of NF (i.e. 200-3000 Mw).

تم تحضير نوعين من اغشية الالياف المجوفة والنانوية المكونة من PVA/PVC بواسطة طريقة الاكساء بالتغطيس في محلول PVA المائي المكون من بولي فنيل الكحول PVA, الماء و(AEO9) Fatty Alcohol Polyoxyethylene Ether وبنسب وزنية مئوية(0.5, 95.5, 4) على التوالي.تم دراسة تاثير وقتين مختلفين لزمن اكساء اغشية الالياف المجوفة على التركيب الداخلي والخارجي لاغشية الياف PVA/PVC المركبة والنانوية باستخدام جهاز المجهر الالكتروني الماسح (SEM) وايضا على اداء الاغشية في فصل المذابات وانتاج الماء النقي. وجد ان سمك طبقة الاكساء للالياف المحضرة من19% PVC كان رقيقا وبسمك µm6بينما يدخل محلول الاكساء خلال السطح الخارجي ويسد التراكيب الاصبعية الشكل عندما يزداد زمن الاكساء من 20-30 ثانية. بالاضافة الى ذلك, تقل نفاذية الماء النقي ويزداد فصل المذابات بزيادة زمن الاكساء من 20-30 ثانية لكلا نوعي الالياف المجوفة النانوية. ان الوزن الجزيئي للمذابات المفصولة(MWCO) لاغشية اليافPVA/PVC المجوفة النانوية كان ضمن مدى اغشية الفصل النانوية (200- 3000Da ).