Article
EFFECT OF CURING CONDITIONS ON THE MECHANICAL PROPERTIES OF STEEL FIBER REINFORCED SELF COMPACTING CONCRETE
تأثير طرق المعالجة على الخصائص الميكانيكية للخرسانة ذاتية الرص المقواة بألألياف الحديدية

Author: Ilham Hatim Khuthair Alubaidi الهام حاتم خضير العبيدي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2011 Volume: 4 Issue: 4 Pages: 528-536
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Fiber-reinforced self compacting concrete (FRSCC) is a type of concrete mix that can mitigate two opposing weaknesses: poor workability in fiber reinforced concrete and cracking resistance in plain SCC concrete. This research investigates the influence of curing conditions and effect of steel fiber on shrinkage and mechanical properties of self compacting concrete. Test results showed that water cured specimens always give the highest values followed by this cured as in dry condition irrespective of type and age of concrete and test methods. For flexural, splitting tensile strength and modulus of elasticity tests, the SCC concrete with steel fiber reinforced gives the highest values than plain SCC for all curing conditions. Steel fibers in the early stage, didn’t show any improvement in shrinkage.

تعد الخرسانة ذاتية الرص المسلحة بالألياف نوع من الخلطات الخرسانية ، وهذه الخلطة مع استخدام الألياف المسلحة تعاني من ضعف في قابلية التشغيل وبدونها تعاني من ضعف مقاومتها للتشقق . لقد سلط هذا البحث الضوء على تأثير طرق المعالجة وتأثير ألألياف الحديدية على الخصائص الميكانيكية للخرسانة ذاتية الرص ، وبينت نتائج الفحص أن معالجة النماذج بالماء ذات قيم عالية مقارنة بطرق المعالجة الجافة ، بغض النظر عن عمر وطريقة فحص النموذج . وأن الخرسانة ذاتية ألرص المسلحة بالألياف أعطت قيم عالية لكل من مقاومة ألانثناء وألأنشطار ومعامل المرونة مقارنة بالخرسانة ذاتية الرص لكل طرق المعالجة . وان ألياف الحديد في المراحل المبكرة لم تعطي أي تحسن في ألانكماش .


Article
Some Mechanical Properties of Reactive PowderLight Weight Concrete
دراسة بعض الخواص الميكانيكية لخرسانة المساحيق الفعالة خفيفة الوزن

Author: Ibrahim A. S. Al-Jumaily إبراهيم احمد سرحان الجميلي
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2011 Volume: 4 Issue: 1 Pages: 47-61
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

In General, original reactive powder concrete (RPC) consists of a superplasticized cement mixture with silica fumes, steel fiber and ground fine sand (150-600 ىm). The main purpose of the present work is to produce and study some mechanical properties of lightweight reactive powder concrete using a superplasticized cement mixture with high reactivity metakaolin (HRM) instead of silica fume, steel fiber (with different ratios ) with ground fine sand (150-600 ىm) and light weight material called (Perlite ) also with different ratios .
This investigation was carried out using several tests, these tests were compressive strength, modulus of rupture, modulus of elasticity, density and absorption, and performed for specimens at ages of 3, 7, 28 days, respectively. The tests results were compared with a reference mix. The experimental results shows that , with different ages, (for constant Perlit ratio for 0% to 10% as additional cementtitious materials) addition of 1% steel fiber will improve about (8.3%-10% , 3.2%-11%and 0.25%- 8%) for compressive strength , modulus of rupture, and modulus of elasticity respectively, and increase density, absorption about (0.8%-1.8%,4.5%-8.2%) respectively. Also an increase of steel fiber ratio to 2% will improve about (16.5%-20.3%, 9.0%-17%, and 1.7%-11.5%) for compressive strength , modulus of rupture and modulus of elasticity respectively, and increase density, absorption about (1.7%-2.3% , 7.3%-8.3%) respectively. For same steel fiber ratio about 0% to 2%, increasing Perlite ratio to 2.5% will decrease about (17.3%-18.8%, 9.5%-15.5%, 4.4%-16.6%, and 4.98% - 6.9%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption to about (55.5% - 66.5%). Increasing the ratio to 5% will also make a decrease of about (36%-36.77%, 33.7%-37%, 16.5%- 21.88%and 15.91%-19.74%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption for about (106%- 110.5%) . Increasing the ratio to 10% will also decrease about (45.98%-47.2%, 46.5-54.2%, 30.6%- 35.57%and 19.4%-23.36%) for compressive strength, modulus of rupture, modulus of elasticity and density respectively and increase absorption about(183%- 192.6%). To produce structural lightweight concrete, the tests results show that the optimum steel fiber is 1% by volume and optimum Perlite ratio is 2.5% by weight of cement as additional materials.

بصورة عامة, تتكون خرسانة المساحيق الفعالة الأصلية من خليط السمنت وملدن متفوق مع المايكرو سليكا (بخار السليكا), ألياف الحديد والركام الطبيعي فائق النعومة بمقاس (150-600 مايكرومتر). إن الغرض الرئيسي من العمل إنتاج ودراسة بعض الخواص الميكانيكية للخرسانة خفيفة الوزن ذات المساحيق الفعالة باستخدام خليط الاسمنت مع الميتاكؤلين عالي الفعالية بدلا" من بخار السليكا , ملدن فائق الفعالية , ألياف الحديد بنسب مختلفة والركام الطبيعي فائق النعومة بمقاس (150-600 مايكرومتر) ومادة البرلايت خفيفة الوزن بنسب مختلفة أيضا".لغرض دراسة الخواص الميكانيكية لهذا النوع من الخرسانة تم اعتماد عدة فحوصات مختبربة شملت مقاومة الانضغاط , معايير الكسر , معامل المرونة, الكثافة والامتصاص ولأعمار 3, 7, 28 يوم. تم اعتماد خلطة مرجعية بدون استعمال مادة البرلايت أو ألياف الحديد (خلطة رقم1) لغرض مقارنة النتائج العملية. بينت النتائج العملية (لنسبة برلايت ثابتة تتراوح بين 0% - 01%) إن إضافة ألياف الحديد بنسبة 1% يؤدي إلى تحسن الخواص الميكانيكية بنسب ( 8.3 – 10%, 3.2 – 11% و 0.25%-8%) لمقاومة الانضغاط, معايير الكسر ومعامل المرونة على التوالي وتزيد بحوالي( 0.8- 1.8%) للكثافة وكذلك للامتصاص بحوالي( 4.5- 8.2%). كذلك فان زيادة هذه النسبة إلى 2% فان تلك الخواص تتحسن بنسب ( %16.5-20.3% و 9-17% و 1.7-11.5%) لمقاومة الانضغاط, معايير الكسر ومعامل المرونة وتزيد بحوالي( 1.7%-2.3% ) للكثافة وكذلك للامتصاص بحوالي (7.8%-8.3%). كذلك بينت النتائج العملية (لنسبة ألياف حديد ثابتة تتراوح بين 0%-2%) إن زيادة نسبة البرلايت بنسبة 2.5% تتأثر الخواص الميكانيكية بنسب متفاوتة حيث تقل بنسب تتراوح بين (17.3-18.8% , 9.5-15.5%, 4.4-16.6% و 4.98-6.9%) لمقاومة الانضغاط, معايير الكسر, معامل المرونة والكثافة على التوالي, والامتصاص يزداد بنسبة (55.5-66.5%). كذلك فان زيادة هذه النسبة إلى 5% فان تلك الخواص تتأثر بصورة واضحة حيث تقل بنسب تتراوح بين ( 36%- 36.77%, 33.7%-37%, 16.5%-21.88% و 15.91%-19.74%) لمقاومة الانضغاط, معايير الكسر, معامل المرونة والكثافة على التوالي أما الامتصاص فيزداد بنسبة (106%-110.5%), ويزداد التأثير في الخواص الميكانيكية عند زيادة نسبة البرلايت إلى 10% حيث تزداد بنسب تتراوح بين (45.98%-47.2%, 46.5%-54.2% , 30.6 %-35.57% و 19.4%-23.36%) لمقاومة الانضغاط, معايير الكسر, معامل المرونة والكثافة على التوالي أما الامتصاص فيزداد بنسبة (183-192.6%). ولغرض الحصول على خرسانة خفيفة الوزن إنشائية ذات مقاومة جيدة بينت الدراسة إن النسب المثلى لألياف الحديد هي 1% ونسبة البرلايت 2.5%.