Article
Fabrication temperature sensing by using ZnO Nanoparticles
تحضير متحسس حراري باستخدام اوكسيد الزنك ذو الجسيمات النانوية

Author: Ausama I. Khudiar اسامة اسماعيل خضير
Journal: JOURNAL OF THI-QAR SCIENCE مجلة علوم ذي قار ISSN: 19918690 Year: 2013 Volume: 4 Issue: 4 Pages: 75-78
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

A present study is reported for the synthesis and characterization of ZnO nanoparticles and its application as a temperature sensor. ZnO nanoparticles thin film was prepared the by Sol: Gel method and deposition on a glass substrate. Structural and optical properties of ZnO films were studied. Structural investigation including microstructure was carried out by X-ray diffraction (XRD) analysis. The films gave a hexagonal wurtzite structure. Optical properties of the thin films were determined by using UV-Vis spectrometer. It was found the value of the band gap of the thin film is 3.18 eV. The variations in resistance of sensing with different temperatures were recorded. The relative resistance was decreased linearly with increasing temperature over the range (120- 250)°C.

أفادت دراسة الحالية حول امكانية تحضير ودراسة خصائص جزيئات أكسيد الزنك ذوالتركيب النانوي واستخدامة كمتحسس للحرارة. تم تحضير اوكسيد الزنك ذو التركيب النانوي حضر بطريقة صل – جل ورسب بعد ذلك على الزجاج. تم دراسة الخواص التركيبية للاغشية المحضرة باستخدام حيود الاشعة السينية حيث كان التركيب البلوري هو سداسي. تم دراسة الخواص البصرية باستخدام جهاز الطيف للاشعة الفوق البنفسجية و المرئية حيث تم احتساب فجوة الطاقة وذلك من خلال طيف الامتصاص للغشاء المحضر . تم تسجيل تغير المقاومة مع ارتفاع درجة الحرارة للغشاء المحضر حيث لوحظ ان المقاومة تقل بصورة خطية مع ارتفاع درجة الحرارة للغشاء المحضر


Article
Effect of Sputtering pressure and partial pressure on Structural Properties of TiO2thin Films
تاثير ضغط الترذيذ والضغط الجزيئي على الخصائص التركيبية لأغشية ثنائي اوكسيد التيتانيوم المحضرة باستخدام الترذيذ بالتيار المستمر

Authors: Mahdya A.Yeser مهدية احمد يسر --- Raaed S.Atea رائد ستار عطية
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2013 Volume: 5 Issue: 2 Pages: 15-20
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Effect of sputtering pressure and partial pressure on structural properties of TiO2 films prepared using DC-sputtering to glass substrate was investigated. sputtering pressures are changed (1.8,2.8,3.8,4.3 pa) at constant O2 /Ar Ratio(5%). Measurements reveal that the TiO2 films at the sputtering pressure 1.8 pa is amorphous , while at increasing pressure to 2.8 pa becomes crystalline with Rutile phase (110) and when we increase the pressure to 4.3 pa get crystalline structure with anatas phase ( 101) .Grain size is calculated per crystalline structure of the anatas and rutile (15.7) nm and(14.2) nm respectively. For constant sputtering pressure (2.8pa) and changedO2/Ar Ratio(10% ,15% ,20% ,25% ,30% , 35%),TiO2 thin films are a amorphous, except percentage (25%) is crystalline with anatas phase (101) and with grain size (15.7 nm).

تم في هذا البحث دراسة تاثير كل من ضغط الترذيذ والضغط الجزيئي على الخصائص التركيبة لاغشية ثنائياوكسيد االتيتانيوم المحضرة باستخدام منظومة الترذيذ بالتيار المستمر على ارضيات زجاجية . الخطوة الاولىفي البحث تم تثبيت الضغط بتثبيت الضغط الجزيئي للاوكسجين عند النسبة 5%) ( وتغير ضغط غاز الترذيذ( 1.8,2.8,3.8,4.3pa ( وثانيا تم تثبيت ضغط الترذيذ عند الضغط ) 2.8 pa ( وتغير الضغط الجزيئيللاوكسجين (10%,15%,20%,25%,30%,35% ) . من قياسات حيود الاشعة السينية تبين ان الاشعة عندالضغط ) 1.8 pa ( عشوائية التركيب ولكن عند الضغط ) 2.8 pa ( تصبح بلورية التركيب وبطور الروتيلوبزيادة الضغط اكثر تصبح الاغشية وبالتحديد الضغط ) 4.3 pa ( بلورية التركيب وبطور الاناتاس وبتوجيهية( 101 ) , بينما عند تثبيت النسبة وزيادة الضغط سوف نحصل على تركيب بلوري وبطور الاناتاس وبتوجيهة( 101 ( عند النسبة .25%قمنا بحساب الحجم الحبيبي للاغشية المحضرة كدالة لكل من ضغط الترذيذ مرة والضغط الجزيئي مرة اخرى