STUDY THERMAL BEHAVIOR OF HEAT CURE POLY (METHYL METHACRYLATE) REINFORCED BY BAMBOO AND RICE HUSK POWDERS FOR DENTURE APPLICATIONS

Authors: Jawad K. Oleiwi --- Qahtan Adnan Hamad --- Hadil Jabbar Abdul Rahman
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2018 Volume: 11 Issue: 4 Pages: 417-425
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The present research, studies the effect of adding two different types of reinforcing powders, which included: Bamboo (Ba) and Rice Husk (RH), that added with different weight fractions (2, 4, 6 and 8 wt. %), and with the selected size particles of (25µm and 75µm) on thermal behavior of heat Cure Poly (Methyl Methacrylate) such as thermal conductivity and thermal diffusivity in addition to the differential scanning calorimetry (DSC) analysis and these tests were accomplished at temperature of laboratory. The poly Methyl Methacrylate properties which reinforced by (Bamboo and Rice Husk) powders are mainly influenced by the interfacial adhesion strength between the powders and the matrix, and in order to get better correlation between the natural powder and PMMA matrix, so the powders were treated with alkali (sodium hydroxide NaoH) solution prior to use as reinforcement materials. The results showed that the values of the thermal conductivity and thermal diffusivity increased with increasing of the weight fraction for both particle sizes (25 µm and 75 µm) of natural powders.


Article
Studying the Mechanical Properties of Denture Base Materials Fabricated from Polymer Composite Materials
دراسة الخصائص الميكانيكية لمادة قاعدة طقم الأسنان مصنعة من مواد متراكبة بوليمرية

Authors: Jawad Kadhim Oleiwi جواد كاظم عليوي --- Qahtan Adnan Hamad قحطان عدنان حمد
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2018 Volume: 14 Issue: 3 Pages: 100-111
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, the effect of adding two different types of reinforcing particles was investigated, which included: nano-zirconia (nano-ZrO2) particles and micro-lignin particles that were added with different volume fractions of 0.5%, 1%, 1.5% and 2% on the mechanical properties of polymer composite materials. They were prepared in this research, as a complete prosthesis and partial denture base materials was prepared, by using cold cure poly methyl methacrylate (PMMA) resin matrix. The composite specimens in this research consist of two groups according to the types of reinforced particles, were prepared by using casting methods, type (Hand Lay-Up) method. The first group consists of PMMA resin reinforced by (nano-ZrO2) particles, while the second group consists of PMMA resin reinforced by (micro-lignin) particles. The mechanical tests performed in this research includedtensile test, compression test, impact test and hardness test. The results of this study showed that the values of tensile modulus of elasticity, compressive strength and hardness properties increased with increasing the volume fraction of these particles in PMMA composite materials. While, the values of tensile strength, elongation and impact strength properties decreased. Also, the addition of (nano-ZrO2) particles showed greater effect than that of (micro-lignin) particles in some properties of PMMA composite materials for prosthesis denture base materials specimens, while they have lower effect for the other properties.

في هذا البحث تم التقصي عن تاثير اضافة نوعين مختلفين من دقائق التقوية تضمنت دقائق الزركونيا النانوية ودقائق اللكنين المايكروية والتي تمت اضافتهما بكسور حجمية مختلفة هي (0.5 %, 1 %، 1.5 %, و 2 %)، على بعض الخواص الميكانيكية للمواد المتراكبة البوليمرية المحضرة في هذا البحث بوصفها مادة لقاعدة طقم الاسنان الأصطناعية الكاملة او الجزئية, وذلك باستخدام راتنج البولي مثيل ميثا اكريليت المعالج ذاتياً بوصفها مادة أساساَ. وقد تم تحضير عينات المواد المتراكبة باستخدام طرائق السباكة, وقد استخدمت طريقة (الصب اليدوي) على شكل مجموعتين هما : المجموعة الاولى تضم راتنج البولي مثيل ميثا اكريليت مقواة بدقائق الزركونيا النانوية، وا الثانية تضم راتنج البولي مثيل ميثا اكريليت مقواة بدقائق اللكنين المايكروية وتضمنت الاختبارات الميكانيكية التي تم اجرائها في هذا البحث فحوصات الشد و الانضغاط، الصدمة، والصلادة. وقد أظهرت نتائج هذه الدراسة بان قيم خواص (معامل مرونة الشد, مقاومة الانضغاط والصلادة) ازدادت مع زيادة الكسر الحجمي لهذه دقائق في المواد المتراكبة البوليمرية. بينما قلت قيم خواص (مقاومة الشد و الاستطالة ومقاومة الصدمة). كذلك ان دقائق الزركونيا النانوية تمتلك تاثيراَ اكبر من دقائق اللكنين المايكروية على بعض خواص المواد المتراكبة البوليمرية لعينات مادة قاعدة طقم الاسنان الأصطناعية بينما تمتلك تاثيراَ اقل على الخواص الاخرى لهذه المادة.