Wear Behavior Performance of Polymeric Matrix Composites Using Taguchi Experiments
أداء سلوك البلى للانسجة البوليمرية المركبة باستخدام تجارب تاكوجي

Loading...
Loading...
Abstract

This research estimates the effect of independent factors like filler (3%, 6%, 9%, 11% weight fraction), normal load (5N, 10N, 15N), and time sliding (5,7 , 9 minutes) on wear behavior of unsaturated polyester resin reinforced with jute fiber and waste eggshell and, rice husk powder composites by utilizing a statistical approach. The specimens polymeric composite prepared from resin unsaturated polyester filled with (4% weight fraction) jute fiber, and (3%, 6%, 9%, 11% weight fraction) eggshell, and rice husk by utilizing (hand lay-up) molding. Dry sliding wear experiments were carried utilizing a standard (pin on disc test setup) following a well designed empirical schedule that depends on Taguchi’s experimental design L9 (MINITAB 16) with the determined (S/N) ratio and analysis of different (ANOVA) optimal factors to minimize the wear rate. Results exhibit that the presence the of 11% weight fraction eggshell and rice husk powder with 4% weight fraction jute fiber improves the wear resistance of unsaturated polyester composite materials significantly. The filler content was observed to be the major significant factor influencing the wear rate followed by time sliding and normal load. From the results of the S/N ratio, the optimization of wear parameters is obtained at specimens A3, A6, A7, and A10 as to minimize wear rate.

يقيم هذا البحث تأثير العوامل المستقلة مثل الحشو (3%، 6%، 9%، 11% كسر وزني) ، الحمل العادي (5N، 10N ، 15N) ووقت الانزلاق (5، 7، 9 دقائق) على سلوك البلى لمتراكبات راتنج البوليستر غير المشبع المدعم بألياف القنب ونفايات مسحوق قشور البيض وقشور التمن بوساطة استخدام نهج إحصائي. يتم تحضير العينات البوليمرية المتراكبة من راتنجات البوليستر غير المشبعة المحشوه مع 4 % كسر وزني ألياف القنب و (3٪ ، 6٪ ، 9٪ ، 11٪ كسراً وزنياً) قشور البيض وقشور التمن باستخدام القولبة اليدوية واجريت تجارب البلى الانزلاقي باستخدام (دبوس على إعداد اختبار القرص) القياسي باتباع جداول تجريبية مصممة جيدا تعتمد على تصاميم تجارب تاكوجي (L9) ( مني تاب 16) مع حساب نسبة الاشارة الى الضوضاء (S/N) وتحليل التباين (الانوفا) الامثل للمتغيرات لتقليل معدل البلى. أظهرت النتائج أن وجود 11 % كسراً وزنياً من مسحوق قشور البيض وقشور التمن مع 4 % كسراً وزنياً ليف القنب يحسن من مقاومة البلى للمواد المتراكبة من البوليستر غير المشبعة بشكل كبير. لوحظ أن محتوى الحشو هو العامل الرئيسي الهام الذي يؤثر على معدل البلى يليه (وقت الانزلاق) و (الحمل العادي). ايضا من نتائج نسبة الاشارة الى الضوضاء (S/N) تم الحصول على الأمثل لمتغيرات البلى عند العينات (A10, A7, A6, A3) لتقليل معدل البلى.


Article
The Effect of Glass and Carbon Fibers and Powders Addition on the Sliding Wear Behavior of Unsaturated Polyester Resin
تأثير إضافة ألياف ومساحيق الزجاج والكاربون على سلوك البلى الأنزلاقي لراتنج البولي استر غير المشبع

Loading...
Loading...
Abstract

The current investigation is interested in studying the wear phenomenon for unsaturated polyester resin reinforced by a different weight fraction of glass and carbon fibers and powders. The prepared specimens were tested according to standard (ASTM-D5963) using a dvice pin-on-disk, at room temperature. The influence of wear parameter like, applied load, sliding speed on the wear rates were investigated. It was observed that the carbon and two types of glass fibers composite shows lower wear rates than the carbon and glass powders composites, under varying the loads and sliding speeds. In the case of sliding speed increased the results show that the increased of the weight fractions of carbon and glass powders will decrease the wear rates of composites prepared from this powders, while in the case of loading increase the wear rates increased when the weight fraction increased up to (4.16 Wt.%) for both carbon and glass powders.

يهتم بحثنا الحالي بدراسة آلية حدوث ظاهرة البلى لراتنج البولي أستر غير المشبع المقوى بكسور وزنية مختلفة بالياف ومساحيق الزجاج والكاربون. أختبرت العينات المحضرة وفقاً لنظام (ASTM-D5963) باستخدام جهاز المسمار على القرص، عند درجة حرارة الغرفة. تم حساب معدلات البلى تحت تاثير مَعْلَماتْ (متغيرات) البلى، كالحمل المطبق وسرعة الأنزلاق. حيث لوحظ ان متراكبات ألياف الكاربون والزجاج بنوعيه، أظهرت أقل معدلات البلى بالمقارنة مع متراكبات المساحيق الكاربونية والزجاجية، عند تغير كل من الاحمال وسرع الانزلاق. في حالة زيادة السرعة الانزلاقية، أظهرت النتائج أن زيادة الكسور الوزنية لمساحيق الزجاج والكاربون قلل من معدلات البلى للمتراكبات المحضرة من هذه المساحيق، أما في حالة زيادة الحمل، فان معدلات البلى ازدادت بزيادة الكسر ألوزني لأعلى من (4.16 Wt.%) لكل من مسحوق الزجاج والكاربون.