Article
انتاج خرسانة عالية الاداء باستخدام انواع مختلفة من البوزولانات المحلية

Authors: علياء فالح حمد --- ندى مهدي فوزي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2009 Volume: 15 Issue: 1 Pages: 620-632
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

High Performance Concrete (HPC) is considered as one of the most important products known by the construction industries during the last years in the field of producing new and improved types of concrete. This new type of concrete has an essential importance due to its high compressive strength, superior resistance for external salt attack and its low permeability.This paper is concerned with experimental investigations for evaluation of high performance concrete using a new type, locally available pozzolan. The results are compared with that obtained from using well known micro silica. The experimental work also includes the possibility of activation in order to improve the quality of HPC; the experiments mainly deal with the chemical analysis and the selection for the optimum dosages of additive. The properties of HPC are studied in both fresh and hardened stages. The effect of pozzolan additive on shrinkage was also considered to provide an index for the durability of concrete.

تعتبر الخرسانة عالية الاداء واحدة من اهم المنتجات التي شهدتها الصناعة الانشائية في السنوات الاخيرة في مجال انتاج انواع جديدة ومتطورة من الخرسانة. وان لهذا النوع الجديد من الخرسانة اهمية بالغة لما لها من خواص عالية من ناحية مقاومة الانضغاط والديمومة ومقاومة مهاجمة الاملاح الخارجية حيث لها نفاذية واطئة للغاية.يتناول هذا البحث تجارب مختبرية لتقييم أداء خرسانة عالية الأداء بإستخدام نوع جديد من البوزولان المتوفر محليا مثل الميتاكاؤولين وخبث الافران ومقارنة تأثير إضافته مع أنواع أخرى من البوزولان المعروفة مثل دقيق السليكا. كأمكانية تنشيطها لتحسين نوعيته وتشمل التجارب دراسة المادة من حيث التحليل الكيمياوي وايجاد النسبة المثلى للإضافة ومدى تأثيرها على الخواص الميكانيكية وخواص الخرسانة في الحالة الطرية والمتصلبة وتأثير المضاف على الانكماش والتي تعطي فكرة عن ديمومة الخرسانة.

Keywords


Article
Influence of Temperature Upon Permanent Deformation Parameters of Asphalt Concrete Mixes
تأثير درجات الحرارة على معاملات التشوهات الدائمية للخلطات الإسفلتية

Authors: Amjad Hamad Albayati أمجد حمد البياتي --- Aliaa Faleh Hamd Al.ani علياء فالح حمد العاني
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 7 Pages: 14-32
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The performance of asphalt concrete pavement has affected by many factors, the temperature is the most important environmental one which has a large effect on the structural behavior of flexible pavement materials. The main cause of premature failure of pavement is the rutting, Due to the viscoelastic nature of the asphalt cement, rutting is more pronounced in hot climate areas because the viscosity of the asphalt binder which is inversely related to rutting is significantly reduced with the increase in temperature resulting in a more rut susceptible paving mixtures. The objective of this study is to determine the effect of temperatures variations on the permanent deformation parameters (permanent strain (p), intercept (a), slope (b), Alpha and Mu) as well as resilient strain (r) and resilient modulus (Mr). To achieve this objective, one aggregate gradation with 12.5mm nominal maximum size, two grades of asphalt cements (40-50 and 60-70) brought form Al- Daurah refinery, limestone dust filler has been used to prepare the asphalt concrete mixtures. 30 Marshall specimens were prepared to determine the optimum asphalt cement content. Thereafter, 30 cylindrical asphalt concrete specimens (102mm in diameter and 203 mm in height) are prepared in optimum asphalt cement and optimum ±0.5 percent. The prepared specimens were used in uniaxial repeated load test to evaluate the permanent deformation parameters of asphalt concrete mixes under the following testing temperature (5, 15, 25, 40 and 60̊c). The test result analyses appeared that Mr is decrease 51 percent when temperature increased from 5 ̊c to 25 ̊c and then decrease 22 percent with further increase in temperature from 25 ̊c to 60 ̊c. Also, the Alpha value decreases by a factor of 1.25 and 1.13 when temperature increases from 5 ̊c to 25 ̊c and 25 ̊c to 60 ̊c, respectively. Finally, statistical models were developed to predict the Alpha and Mu parameters of permanent deformation.

أداء التبليط الإسفلت يتأثر بعدة عوامل و درجة الحرارة هي واحدة من العوامل المناخية المهمة التي لها اكبر تأثير على أداء السلوك الانشائي لمواد الرصف المرنة .ان السبب الرئيسي للفشل المبكر للطرق هو التخدد ونظرا لطبيعة الاسفلت اللزجة/المرنة فالتخدد يظهربكثرة في المناطق المناخية الحارة لان لزوجة الاسفلت ترتبط عكسيا مع التخدد الذي يقل بشكل ملحوظ مع ارتفاع درجات الحرارة وبالنتيجة يعطي حساسيه اكبر للتخدد لطبقات التبليط . ان الهدف من هذه الدراسة هو لتحديد تأثير درجات الحرارة المختلفة على معاملات التشوهات الدائمية ومعامل المرونة ولتحقيق هذا الهدف تم اختيار تدرج واحد للركام بمقاس اسمي اقصى(12.5) ملم ونوعين اسفلت ذو اختراق (40-50)(60-70) من مصفى الدورة وقد تم استخدام الحجر الجيري المطحون كمادة مالئة. استخدمت هذه المواد لتحضير( 30) نموذج مارشال لغرض تعيين نسبة الاسفلت المثلى, وكذلك تم تحضير( 30) نموذج اسطواني من الخرسانة الاسفلتية ( 102ملم قطر,203ملم ارتفاع) تم تهيئتها بنسبه الاسفلت المثلى وكذلك نسبة ±0.5% من النسبةالمثلى . استخدم في الاختبار جهاز الحمل المتكرر لتقييم معاملات التشوه الدائمي لخلطات الاسفلت بدرجات حرارة (60,40,25,10,5)ºم .نتائج الفحوصات وتحليل النتائج اظهرت ان معامل المرونة يقل بمقدار 51% عند زيادة درجة الحرارة من5 الى25º م ونقصان 22% مع زيادة درجة الحرارة من 25 الى 60ºم وايضا قيمة الفا تقل بمقدار 1.25و1.13 عند زيادة درجة الحرارة (5-25)ºم و(25-60)ºم على التوالي. واخيرا تم تطوير موديلات احصائية للتنبؤ بقيم المعاملات الفا وMu للتشوهات الدائمية.