Influence of Nanoreinforced Particles (Al2O3) on Fatigue Life and Strength of Aluminium Based Metal Matrix Composite
تاتير حبيبات المادة النانوية المقواة (Al2O3) على عمر ومقاومة الكلال لمركب ذي الاساس المعدني

Loading...
Loading...
Abstract

In this investigation, Al2O3 nano material of 50nm particles size were added to the 6061 Al aluminium alloy by using the stir casting technique to fabricate the nanocomposite of 10wt% Al2O3. The experimental results observed that the addition of 10wt% Al2O3 improved the fatigue life and strength of constant and cumulative fatigue. Comparison between the S-N curves behaviour of metal matrix (AA6061) and the nanocomposite 10wt% Al2O3 has been made. The comparison revealed that 12.8% enhancement in fatigue strength at 107cycles due to 10wt% nano reinforcement. Also cumulative fatigue life of 10wt% nanocomposite was found to be increased by 33.37% and 39.58% for low-high and high-low loading sequences, respectively, compared to the metal-matrix cumulative life.

في هذا البحث تم اضافة المادة النانوية Al2O3 ذات حجم حبيبات 50 نانوميتر الى سبيكة الالمنيوم AA6061 باستخدام تقنية السباكة بالتحريك لتصنيع المركب النانوي ذو 10wt% من المادة النانوية Al2O3.النتائج المستخرجة عمليا اوضحت ان اضافة 10wt% Al2O3 بوصفه نسبة وزنية حسنت من عمر مقاومة الكلال الثابت والمتراكم .تمت مقارنة بين سلوك منحنيات S-N للمعدن الاساس AA6061 والمركب النانوي 10wt% Al2O3 .واوضحت المقارنة تحسن بمقدار 12.8% في مقاومة الكلال عند 107 دورة نتيجة 10w% للمادة المقواة. كذلك وجد ايضا ان عمر الكلال التراكمي ازداد نسبة 33.37% و% 39.58 للتحميل المتتابع من واطئ-عالٍ ومن عالٍ-واطئ على التوالي مقارنة مع العمر التراكمي للمعدن الاساس.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

Arabic and English (1)


Year
From To Submit

2017 (1)