Article
A Study of some Mechanical Behavior ona Thermoplastic Material

Authors: Zaid Ghanem M. Salih --- Awham M. H.
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2011 Volume: 14 Issue: 3 Pages: 58-65
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The aim of the current study is the investigation of mechanical behavior of thermoplastic material type (U-PVC) which may be subjected to effect of some mechanical stresses, because these materials are manufactured to use as drinking water, rainwater and heavy water pipelines.Some tests were carried out on it, included: The (impact, modulus of elasticity (bending), flexural and compression) tests. These tests were performed to determine the ability of the material under study for these stresses.The results which obtained from these tests at natural environments were analyzed and compared with other materials which were used in present studies.These results showed that (Unplasticised PVC, (U-PVC)) material has high impact strength at these ambient, but obviously that there is great effect of notches on this property, as well as that the flexural strength and its ability for sustaining the compression failure is considered suitable if its compared with other materials.

يهدف بحثنا الحالي الى دراسة السلوك الميكانيكي لمادة ثرموبلاستيكية نوع (U-PVC) اذا ما وقعت تحت تأثير بعض الاجهادات الميكانيكية لكونها تستعمل كأنابيب ماء الشرب ومياه الامطار والمياه الثقيلة. ولهذا الغرض أجريت لها مجموعة من الاختبارات شملت أختبار الصدمة ومعامل المرونة (الانحناء) ومقاومة الانحناء والانضغاط لاجل دراسة خصائص وسلوكية تلك المادة وتحديد مدى تحملها لمثل هذه الاجهادات والتي غالبا ما يتعرض لها هذا النوع من الانابيب اثناء الخدمة.وبعد اجراء تلك الفحوصات العملية عند الظروف المختبرية تم تحديد النتائج لكل أختبارعلى حدة ، وبعد تفسيرها ومقارنتها بمواد اخرى أستخدمت في بحوث سابقة، وجد انها ذات مقاومة جيدة للصدمة ولكن في الوقت نفسه تبين بأن هنالك تأثير كبير لوجود الحزوز في المادة على تلك الخاصية كما ان مقاومتها للانحناء ومدى قابليتها على تحمل الفشل تحت تأثير الحمل الانضغاطي تعد مناسبة اذا ما قورنت بمواد اخرى.


Article
Diffusivity of water in Unplasticised PVC
أنتشارية الماء في مادة (UPVC)

Authors: Awham M.H --- Zaid Ghanem M. Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 10 Pages: 1960-1966
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current study concerns an investigation of diffusion mechanism ofdifferent kinds of water into thermoplastic material (type unplasticised PVC,(UPVC)) that is often used as pipes for healthy draining purposes and otherservices.After preparation of samples from this material, they were immersed in glasscontainers which contain (sea water, river water, rain water, distilled water, andtap water), the weights of these samples are measured at periodic time of soaking.The aim of this work is introducing an idea about the diffusion behavior and thepenetration of water through the material under study, then, the values of diffusioncoefficient (Dx) are evaluated for each type of water mentioned above.After comparing the obtained results from these tests, it is found that the distilledwater has the higher value of (DX) into the (UPVC) material, it is followed by thesea water and then the rainwater, while each of the river and tap water record thelowest values.

يختص البحث الحالي بدراسة آلية الانتشار لنماذج مختلفة من المياه في مادة مطاوعةالتي غالبا ما تستعمل كأنابيب لأغراض الصرف الصحي والخدمات (UPVC) للحرارة من نوعالأخرى، حيث تم غمر نماذج من تلك المادة في حاويات زجاجية تحتوي على (ماء البحر، ماءالنهر، ماء المطر، الماء المقطر، الماء العادي), ومن ثم قيست اوزان تلك النماذج بعد فترات زمنية دورية من الغمر. الهدف من هذه الدراسة هو أعطاء فكرة عن السلوك الانتشاري وآلية لكل نوع من المياه (Dx) تغلغل الماء خلال المادة قيد الدراسة ومن ثم تحديد قيم معامل الانتشار المذكرة آنفا.وبعد مفارنة النتائج المستحصلة من الاختبار, وجد بان الماء المقطريمتلك اعلى قيمة لمعامل ويليه ماء البحر ثم ماء المطر في حين يسجل كل من (UPVC) الى داخل مادة (DX) الانتشار ماء النهر والماء العادي القيم الاوطأ.


Article
Effect of environmental conditions on Shore hardness values of polymer blend

Author: Dr. Awham M. H & Asist. Lecture. Zaynab N. R
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2011 Volume: 16 Issue: 69 Pages: 73-80
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The current investigation was carried to study and determine the values of shore D hardness for polymer blends at different environmental conditions. Epoxy (EP) and Unsaturated polyester (UPE) resins were used to prepare polymer blends(EP/UPE) with various weight ratios (95/5)% , (90/10)% . After determining Shore hardness values, the specimens of both ratios of mixing were subjected to different environments included: sunlight for times) 1,2,3,4,5) hours, the immersion into diverse types of waters (distilled, tap and rain) for the same previous periods for comparing the two cases. Other samples were immersed into the mentioned water kinds but for longer times (1,2,3,4) weeks. The results showed that the shore hardness values increase of both ratios after the subjecting to the sunlight at the above period while decease when the specimens were immersed into the different water sorts at the same period. The obtained results showed that the rate of dropping of hardness values was increased clearly at longer times of the immersion (4 weeks).
Keywords: Polymer blends, Shore hardness, sunlight, immersion

Keywords


Article
Study of The Wear Rate of Some Polymer Materials In Different Conditions
دراسة معدل البلى لبعض المواد البوليمرية في ظروف مختلفة

Authors: Awham M. H --- Sadeer M. M --- Bushra H. M.
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 16 Pages: 5165-5170
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current investigation is interested by study of the wear phenomenon for two polymeric materials (Epoxy and Unsaturated polyester) resins, the prepared specimens were tested at room temperature by using two different loads(10,20)N for various testing times with different sliding distances. The resulted wear rates were calculated for each sample apart with. Variation the previous variables. To produce more precise idea about the wear characteristics of both above materials when immersed them in water environment, the study of wear rates was carried out for different immersion times at different temperatures when the above mentioned variables were fixed. It was found after comparing the results which obtained from the wear test in air thatEpoxy resin undergoes higher wear rates than unsaturated polyester resin in general with variation the testing parameters, while the results of immersion in water which acts as plasticizing factor for polymers exhibited different effect on the wear behavior of the materials under study.

یھتم بحثنا الحالي بدراسة آلیة حدوث ظاھرة البلى لمادتین بولیمریتین وھما راتنجي الایبوكسي والبولي استرغیرالمشبع , وبعد تحضیر النماذج وفحصھا عند درجة حرارة الغرفة باستخدام حملین وعند ازمان اختبارمختلفة ولمسافات انزلاق مختلفة , تم حساب معدلات البلى N ( مختلفین ( 20,10 الحاصلة لكل نموذج على حدة مع أختلاف المتغیرات السابقة . ولاعطاء صورة (Wear rate) ادق عن خصائص البلى للمادتین اعلاه عند غمرھما في بیئة مائیة, اجریت دراسة معدلات البلىعند ازمان غمر مختلفة وبدرجات حراریة مختلفة مع تثبیت المتغیرات المذكورة اعلاه .وقد وجد بعد مقارنة النتائج المستحصلة من اختبارالبلى في الھواء بان راتنج الایبوكسي بعاني من معدلات بلى اعلى من راتنج البولي استرغیرالمشبع بشكل عام مع تغیرمحددات الفحص. في حین اظھرت للبولیمرات تأثیرا متباینا" على (plasticizing factor) نتائج الغمربالماء الذي یمثل عامل ملدنسلوك البلى للمادتین قید البحث.