Article
Comparing the Flexural Strength Values for Polymeric Material and other Fibrous Composite in 3 and 4 Point Bending Methods
مقارنة قيم متانة الانحناء لمادة بوليمرية واخرى متراكبة ليفية بطريقتي الانحناء ثلاثي ورباعي النقطة

Author: Awham M. Hameed اوهام محمد حميد
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2017 Issue: 1 Pages: 163-178
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This research aims to determine the flexural strength (F.S) values for epoxy material before the reinforcement and after it by carrying out 3and 4 bending tests then comparing the results that obtained from the two mentioned test methods. For this purpose, the casts of materials under study were prepared by using molds prepared previously for this objective. Epoxy resin reinforced with chopped glass fibers with volume fraction is (20%). After the solidification process, the samples were cut with length (10cm), width (1cm) and thickness (0.5cm), and then some tests were performed at room temperature. It was found from the results of tests that epoxy reinforced with glass fibers has higher (F.S) with less strain than that for un reinforced epoxy. It can be also noticed in 4-point bending test, the force needed for the sample failure of pure epoxy is higher than that required for failing the same sample subjected to 3- point bending test. Optical microscope was used for imaging the fracture surfaces and failure regions of samples.

يهدف بحثنا هذا الى تحديد قيم متانة الانحناء لمادة الايبوكسي قبل وبعد تسليحها بالالياف وذلك باجراء اختباري الانحناء ثلاثي النقطة (3-point bending test) واختبار الانحناء رباعي النقطة (4-point bending test) ومن ثم مقارنة النتائج المستحصلة من طريقتي الاختبارالمذكورة.ولهذا الغرض تم تحضير مصبوبات المواد قيد الدراسة باستخدام قوالب اعدت لهذا الغرض مسبقا علما بان الكسر الحجمي للالياف قدره (%20) وتم تسليح الايبوكسي بالياف الزجاج المقطعة (chopped glass fibers) وبعد عملية التصلب تم تقطيع العينات بطول (10cm) ، عرض cm) 10 (وسمك (0.5cm) وقد تم اجراء الاختبارات عند درجة حرارة الغرفة ، ولوحظ من نتائج الفحوصات ان الايبوكسي المسلح بالياف الزجاج يمتلك متانة انحناء اعلى من تلك للايبوكسي غير المسلح وكذلك اقل انفعال وقد لوحظ في اختبار الانحناء رباعي النقطة ان القوة اللازمة لفشل العينة من الايبوكسي النقي تكون اعلى من تلك اللازمة لفشل نفس العينة المعرضة لاختبار الانحناء ثلاثي النقطة ، تم تصوير سطوح الكسر ومنطقة الفشل الحاصل للعينات باستخدام المجهر الضوئي .


Article
Using the plastic wastes in fabrication of composite materials for different applications
استخدام النفايات البلاستيكية في تصنيع مواد متراكبة متعددة التطبيقات

Authors: Awham M. Hameed اوهام محمد حميد --- Ahmed Ali Talib احمد علي طالب
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 36 Pages: 123-133
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study suggests using the recycled plastic waste to prepare the polymer matrix composite (PMCs) to use in different applications. Composite materials were prepared by mixing the polyester resin (UP) with plastic waste, two types of plastic waste were used in this work included polyethylene-terephthalate (PET) and Polyvinyl chloride (PVC) with varies weight fractions (0, 5, 10, 15, 20 and 25 %) added as a filler in flakes form. Charpy impact test was performed on the prepared samples to calculate the values of impact strength (I.S). Flexural and hardness tests were carried out to calculate the values of flexural strength and hardness. Acoustic insulation and optical microscope tests were carried out. In general, it is found that UP/PVC composite exhibit the optimum values compared to UP/PET composite in all properties under test. From the experimental results, it can be concluded that the prepared composites from the waste could be utilized as precast or partitions inside the buildings with improved mechanical properties.

يقترح هذا البحث اعادة التدوير للمخلفات البلاستيكية لغرض استعمالها في تصنيع متراكبات ذات اساسات بوليمرية (PMCs) من الممكن استخدامها في تطبيقات متعددة. حضرت المواد المتراكبة بخلط راتنج البولي استر غير المشبع مع المخلفات البلاستيكية وقد استخدم نوعين من المخلفات اضيفت كحشوة بشكل قشور في هذه الدراسة شملت البولي اثيلين ترفثاليت (PET) والبولي كلوريد الفاينيل ((PVC وبكسوروزنية مختلفة (0، 5، 10،15 ، 20 و (25%. نفذ اختبار صلادة نوع جاربي على النماذج المحضرة لتحديد قيم مقاومة الصدمة لها. كما اجري اختباري الانحناء والصلادة لتحديد قيم مقاومة الانحناء والصلادة. اختبار العزل الصوتي والفحص بالمجهر البصري تمت على النماذج القياسية. بشكل عام، وجد ان المتراكب المدعم بمخلفات الPVC يظهرقيم مثلى مقارنة بالمتراكب المدعم بمخلفات الPET في جميع الخواص قيد الدراسة. ومن النتائج التجريبية يمكن الاستنتاج بان المتراكبات المحضرة من التدعيم بالمخلفات يمكن استخدامها كمصبوبات اولية جاهزة أو كقوطع داخل المباني وبخواص ميكانيكية محسنة.