FORMATION OF NI-SB PHASES BY ELECTRO-CODEPOSITION DIFFUSION COATING
تكوين أطوار Ni-Sb بطريقة الترسيب الكهربائي _ الانتشاري للطلاء

Loading...
Loading...
Abstract

Electrodeposited metal matrix/metal particle composite coatings (EMMC’s) were deposited, heat treated and characterized. Nickel matrix/ antimony particulate coatings deposited on Inconel 600 substrate (Ni-base superalloy) was chosen as a model system. The microstructure of the plated and heat treated coatings was characterized using light optical microscope (LOM) and X-ray diffraction analysis (XRD).Results showed that Ni5Sb2, Ni3Sb, and NiSb phases are presented in the coated layer. Further NiSb is a good source for Sb2O4 compound formation under open heating. This oxide has good stability at high temperatures.

تم في هذا البحث إجراء ترسيب كهربائي مزدوج لأرضية معدنية / دقائق معدنية وهذا ما يصطلح عليه ( EMMC’s ) ثم تلى ذلك إجراء معاملة حرارية . حيث تم ترسيب أرضية نيكل / دقائق الانتيمون على سطح سبيكة الانكونيل 600 وهي احد أنواع السبائك الفائقة ذات أساس نيكل والتي تتمتع باستخدامات واسعة وقد تم تحديد التركيب المجهري لطبقة الطلاء المعالجة حرارياً باستخدام المجهر الضوئي ، حيود الأشعة السينية .أظهرت النتائج تكون الأطوار NiSb, Ni3Sb, Ni5Sb2 عند سطح الطلاء. كما بينت النتائج إن طور NiSb مصدر جيد لتكوين Sb2O4 عند تسخينه في الهواء. هذا الأوكسيد يتمتع باستقرارية جيدة عند درجات الحرارة المرتفعة.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2009 (1)