The molar ratio)x( of Li-Ni ferrites in the formula Li0.5-0.5xNixFe2.5-0.5xO4 was varied in range 0.1-1.0 by hydrothermal process. The XRD, SEM, and TEM tests were conducted to examine the samples crystalline phase and to characterize the particles shapes and sizes. Thehigh purity spinel structure was obtained atmed and high x values.SEM and TEMimages showed the existence of different ferrite particles shapes like nanospheres and nanorods.The maximum particle size is around (20nm). These size encourage occurrence of super paramagnetic state. The reflection loss and insertion loss as microwave losses of Li-Ni ferrite-epoxy composite of 1mm thickness and mixing ratio 39.4 wt was investigated. The minimum reflection loss in x-band and in Ku band was about -8dB around 10GHz and lower than -18dB respectively. The insertion loss exceeded -6dB in the two band for some samples.

تم تغيير النسبة المولارية(x) لفررايت الليثيوم-نيكل بالصيغة Li0.5-0.5xNixFe2.5-0.5xO4وضمن المدى 0.1-1.0 بالعملية المائية الحرارية hydrothermal. أُنجزت أختبارات XRD و SEM و TEM لفحص الطور البلوري وتشخيص اشكال الجسيمات و أحجامها. تم الحصول على طور السبنل النقي عند القيم القيم الوسطى والعليا لقيم x. أظهرت صور SEM و TEM أشكال جسيمات فيررات مختلفة مثل الكرات النانوية والقضبان النانوية. الحجم الجسيمي الأعظم كان بحدود (20nm). أن هذه الحجوم تعزز حصول حالة البارامغناطيسية الفائقة superparamagnetic. تم تحري خسائر الانعكاس و خسائر الأدخال كخسائر مايكروويف للمادة المركبة من فيررايت الليثيوم-نيكل والايبوكسي بسمك 1mm ونسبة خلط وزنية 39.4. أن أدنى خسائر أنعكاس في حزمة-x وحزمة-Ku كانت تقريبا -8dB عند حوالي 10GHz وأقل من -18dB على التوالي. تجاوزت خسائر الأدخال لبعض العينات -6dB في الحزمتين.

NanoLi-Ni ferrites --- hydrothermal --- particle size --- reflection loss --- insertion loss.