Article
The Effect of Waste Ceramic Materials ( Iraqi Stones Dust Powders ) on The Mechanical Properties of Epoxy Resin

Author: Fadhil A.Chyad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 16 Pages: 3302-3312
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Using waste materials, which have a high pollution on the environment, as an improvement to the properties of a weaken material such epoxy resin become a good achievement. Iraqi stones dust powders have been used to improve the mechanical properties of epoxy resin. Impact strength and fracture toughness from impact test, Young`s modulus from tensile test, Shore hardness, fracture toughness and thermalconductivity have been investigated. The percentages of the ceramic powders have affected all the above properties and increased the values of them about twice. The highest values were at 12% and then decreased. Also the particle size of this powders has affected these properties, where the lowest particle size (25ìm) has the best values.


Article
Synthesize Nano ZnO-ZrO2 Composite by Combustion Method and Studying their Dielectric Properties
تحضير متراكب نانوي من اوكسيد الخارصين – الزركونيا بطريقة الانفجار ودراسة خواصها العزلية

Author: Fadhil A.Chyad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 8 Pages: 1342-1350
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Combustion method had been used to prepare a composite material from dopingZnO by 10 mol% ZrO2 . XRD showed a good crystalline powder comparing withASTM cards. Dielectric properties such dielectric strength, dielectric constant,dielectric loss and tangent loss have been measured .All the dielectric propertieshave decreased as the frequency increasing .The particle size has great effect on the dielectric properties of the compositewhich decreased as the particle size increased .

أستخدمت طريقة الانفجار ، لتحضير مادة متراكبة بأضافة 10 مول % من اوكسيدالزركونيوم الى اوكسيد الزنك. اكدت حيود الاشعة السينية للنماذج المحضرة بأنها متبلورة طبقاًالى المواصفات الاصلية . تمت دراسة الخواص العزلية للمتراكب والتي تمثلت بجهد او متانةالانهيار ، ثابت العزل ، معامل فقدان العزل وظل زاوية الفقدان .جميع الخواص العزلية قلت عند زيادة التردد . كان للحجم الحبيبي تأثير واضح على جميعالخواص العزلية حيث تقل هذه الخواص مع زيادة الحجم الحبيبي للمادة المتراكبة .


Article
Fracture Statistics of Porcelain Ceramic: The Influence of Zirconia Additive and Sintering Temperature
أحصائيات الكسر في سيراميك البورسلين : تأثير اضافة الزركونيا ودرجة حرارة التلبيد

Author: Fadhil A.Chyad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 6 Part (A) Engineering Pages: 1081-1091
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The knowledge of statistic characteristics in mechanical properties is important for designer in order to asses the reliability of the structure. Scatter characteristics of fracture strength (splitting strength) of porcelain toughened by zirconia and the effect of sintering temperature were investigated in this study. Many specimens were tested by Brazillian method to obtain the scatter data of fracture strength. The probability distribution of fracture strength is evaluated by using Weibull ddistribution function. Fracture strength is increased with zirconia content having the highest value (43MPa) at 10 wt.% and then decreased .The same behavior was for Weibull modulus, having the highest value (39) for 10 wt.% Zirconia . Fracture strength and Weibull modulus also affected by sintering temperature, they increased with the increasing of sintering temperature.

ان معرفة الخصائص الاحصائية في الخواص الميكانيكية مهمه للمصمم لكي يخمن الاعتمادية في التركيب . تمت دراسة خصائص التشتت لمتانة الكسر( متانة الانفلاق ) للبورسلين المقوى بالزركونيا وكذلك تأثير درجة حرارة التلبيد عليها. تم اختبار عدة نماذج لقياس متانة الكسر بالطريقة البرازيلية وكذلك تم دراسة توزيع الاحتمالية لمتانة الكسر حيث حسبت بداله توزيع ويبل.ان متانة الكسر ازدادت مع اضافة الزركونيا وكانت اعلى قيمة (43MPa) عند نسبة وزن 10% ومن ثم ومن ثم تناقضت ، كذلك الحال بالنسبة الى معامل ويبل حيث كانت أعلى قيمة (39) عند 10% زركونيا . اما عند زيادة درجة حرارة التلبيد فقد ازدادت كل من متانة الكسر ومعامل ويبل . متانة الكسر ومعامل ويبل ازدادت عند زيادة درجة حرارة التلبيد .


Article
Thermal and Structure Properties in Ferromagnetic INVAR Alloys Prepared by Powder Metallurgy Processes

Author: Ishmaeel K. Jassim Fadhil A. Chyad
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2005 Volume: 8 Issue: 1 Pages: 6-8
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In order to understand the INVAR, effect in 3D-transition metal alloys . the Fe3. * Nix alloys with x= 0.35.0.50,0.70 have been chosen .Experiments have been made on thermal and structural properties to study the physical origin of INVAR characteristics such as : thermal expansion . phase transition, and curie temperature Tc which are closely related to its ferromagnetism .Fe0.65 Ni0.35 shows an anomalously small thermal expansioncoefficient below the curie temperature with ( FCC ) structure . This behavior has not been found in other combination.The structural results show that the ( BCC ) phase occurs above 50% Ni and does not effect (lie INVAR behavior. The results are discussed with the relation between thermal and structural properties with respect to theSciencemagnetic transformation .

Keywords


Article
Microstructure of Free MgO Powder

Authors: Mahasin F. Hadi --- Fadhil A. chyad --- Etab F. Hussein
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2011 Issue: 1 Pages: 142-170
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The aim of this research is to study the Microstructure behavior of pure MgO free (uncompacted) powders and MgO added to magnesium chloride free powders with different doping rates (1% , 38% , 44% , and50%) . The sintering temperatures were taken from to in steps. The sintering times were taken 3 hr, 24 hr, and 48 hr. The essential contribution of this work consists of new results in microstructure development . First , increasing the concentration of magnesium chloride (50%) led to obtain single ultrafine grains at low temperatures . secondly , the formation of a new structure that is the fiber structure at sintering conditions (temperature and time) ; ,48hr for magnesium oxide added to 44% magnesium chloride powders . while reducing the ratio of the additive material ; magnesium chloride to (1%) led to decrease the sintering temperature and sintering time to and 3hr , respectively which is required to the fiber formation . An important structure is recognized at the intermediate stage of sintering, this is the Kelvin's tetrakaidecahedron. This occurred at sintering temperature , 24 hr sintering time for 44% magnesium chloride added with magnesium oxide powders.

يهدف البحث إلى دراسة التركيب الدقيق لمساحيق أوكسيد المغنيسيوم الحرة (غير المكبوسة) النقية والممزوجة بكلوريد المغنيسيوم وبنسب إضافة مختلفة (1% ، 38%، 44% و 50%) . أما درجات حرارة التلبيد المستخدمة أخذت من إلى لكل 100 ْم . وأزمان التلبيد هي 3، 24و 48 ساعة . ومن الإسهامات المهمة في هذا البحث احتوائه على نتائج جديدة في تطور التركيب الدقيق . أولاً , إن زيادة تركيز كلوريد المغنيسيوم (50%) أدى إلى إمكانية الحصول على حبيبات دقيقة جداً بشكل منفصل في درجات حرارة منخفضة . ثانياً , تشكيل تركيب جديد ألا وهو التركيب الليفي في ظروف تلبيد (درجة حرارة وزمن) , 48 ساعة لمساحيق 44% من كلوريد المغنيسيوم المضافة إلى أوكسيد المغنيسيوم . بينما أدى تقليل نسبة المادة المضافة كلوريد المغنيسيوم إلى انخفاض درجة حرارة التلبيد وزمن التلبيد المطلوب لتشكيل التركيب الليفي إلى , 3 ساعة . تم تمييز تركيب مهم آخر في المرحلة المتوسطة من التلبيد وهو تركيب (Kelvin's tetrakaidecahedron) . ولوحظ في درجة حرارة التلبيد وزمن تلبيد 24 ساعة لمساحيق 44% كلوريد المغنيسيوم المضافة إلى أوكسيد المغنيسيوم .

Keywords


Article
Microstructure of Free MgO powrler

Authors: Mahasin F. Hadi --- Etab F. Hussein --- Fadhil A. chyad
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2009 Issue: 3 Pages: 863-885
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The aim of this research is to study the Microstructure behavior of pure Mgo free (uncompacted) powders and Mgo added tomagnesium chloride(MgCtr)free powders with different dopingrates (lolo ,38Yo ,44yo, and50%) . The sintering temperatures weretaken from700'c to 1600"c in 100'c steps. The sintering timeswere taken 3hr,24 hr, and 48 hr.The essential contribution of this work consists of new results inmicrostructure development . First , increasing the concentration ofmagnesium chloride (*50%) led to obtain single ultrafine grains atlow temperatures . secondly , the formation of a new stmctr_rre that is uthe fiber structure at sintering conditions (temperature and time) ; 1100'c,48hr for magnesium oxide added to 44% magnesiumchloride powders . while reducing the ratio of the additive material ;magnesium chloride to (-l%) led to decrease the sinteringtemperature and sintering time to l000"cand 3hr , respectivelywhich is required to the fiber formation .An important structure is recognized at the intermediate stage ofsintering, this is the Kelvin's tetrakaidecahedron. This occurred atsintering temperaturelr00"c, 24 hr sintering time for 44%magnesium chloride added with magnesium oxide powders.

Keywords


Article
Synthesis of B4C/YTZP Composite Powder and Studying Effect of its Addition on Mechanical Properties of B4C
تصنيع مسحوق مركب من YTZPB4C ودراسة تأثير إضافته على الخواص الميكانيكية لكاربيد البورون

Authors: Fadhil A. Chyad --- Mohammed H. AL-Taie --- Hussein AlaaJaber
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 5 Part (A) Engineering Pages: 1158-1170
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research B4C powder have been coated with yttria stabilized tetragonal zirconia polycrystalline (YTZP) (ZrO2 – 6wt% Y2O3) by using sol-gel method in order to obtain on composite powder (B4C core/ YTZP shell, 1/1 wt%). Zirconium oxychloride (ZrOCl2.8H2O) and yttrium nitrate (Y(NO3)3.6H2O) were used as the precursors for synthesis of the YTZP compound. The coated B4C powder was then used as additive powder to B4C. It was mixed with different percentages for making ceramic–ceramic composite samples. The YTZP weight percentages added to the B4C were in the range (0–12.5) wt%. The samples sintered by using spark plasma sintering technique at 1800 and 1900°C for 5 min. Density and mechanical properties (Vickers microhardness, fracturetoughness and fracturestrength) for the sintered samples were measured. The results show that the best YTZP additions to the B4C that have good mechanical properties were ranged 5 – 7.5 wt%.

في هذا البحث تم طلاء مسحوق كاربيد البورون (B4C) بالزركونيا المثبتة جزئيا باليتيريا (YTZP) (ZrO2 – 6 wt% Y2O3) باستعمال طريقة السائل الهلامي للحصول على مسحوق متراكب (B4C القلب/YTZP القشرة, 1/1 نسبة وزنية). استعمل اوكسي كلوريد الزركونيوم(ZrOCl2.8H2O) ونترات اليتريوم(Y(NO3)3.6H2O) كمواد اوليةلإنتاج المركب .YTZP بعدها استعملمسحوقكاربيد البورون المطلي كمسحوق مضاف الى كاربيد البورون. حيث خلط عند نسب مختلة لعمل نماذج متراكبة سيراميكية. ان النسب الوزنية لمركب YTZP المضافة الى B4Cكانت بين (0 – 12.5)%. تم تلبيد النماذج بتقنية التلبيد بالبلازما بدرجة حرارة (1800 و 1900( درجة مئوية لمدة خمسة دقائق.تمقياس الكثافة والخواص الميكانيكية(الصلادة المجهرية بطريقة فيكرز, متانة الكسر ومقاومة الكسر) للنماذج الملبدة.وأظهرت النتائج أن أفضل الإضافات منYTZPإلىB4C والتي تضمنت خصائص ميكانيكية جيدة تراوحت بين 7.5 – 5 نسبة وزنية.


Article
Effect of Thermally Sprayed Ceramic Coating on Properties of Low Alloy Steel
تأثير طلاء الرش الحراري السيراميكي على خواص الفولاذ منحفض السبائكيه

Authors: Fadhil A. Chyad --- Abdalkalaq F. Hamood --- Lamees S. Faiq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 10 Part (A) Engineering Pages: 2568-2575
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thermal spraying technique was employed for coating low alloy steel specimens that have been used in a derrick oil well frames. Two types of ceramic materials were used as a coating material and two groups of steel samples were prepared for coating process. The first group was coated by zirconia while the second group was coated by alumina. Ni-Al composite powder was used forbonding the coating material on the substrate surface of the steel specimens. The hardness, adhesion strength of the coating layers as well as wear rateswere studied for the two steel group samples and compared with as received steel. The results showed an increase in the mechanical properties with a decrease in wear rate values for coated samples as compared to those of uncoated samples.

أستخدمت تقنية الرش الحراري لغرض طلاء نماذج من سبائك الفولاذ منحفض السبائكيه والتي تستخدم في برج حفر الابار النفطيه والغازيه . أستخدم نوعين من المواد السيراميكيه كماده طلاء لمجموعتين من نماذج الفولاذ منخفض السبائكيه . حيث كانت الاولى زركونيا والثانيه الالومينا كذلك أستخدم مسحوق متراكب من النيكل- الالمنيوم كماده رابطه. تم دراسه الصلاده ومتانه الالتصاق لطبقات الطلاء بالاضافه الى معدل البلى للمجموعتين ومقارنتها مع النماذج الغير مطليه. أظهرت النتائج زياده في الخواص الميكانيكيه ونقصان بقيم معدل البلى للنماذج المطليه مقارنة مع النماذج غيرالمطلية.


Article
Synthesis and Studying Dielectric Properties of Mixed Nanoferrites
تحضير ودراسة بعض الخواص الميكانيكية المتراكبة

Authors: Zainab I. Dhary --- Mohammed S. Hamza --- Fadhil A. Chyad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 1 Part (A) Engineering Pages: 154-164
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Based on a low temperature route (sol-gel autocombustion) a nano-ferrite CoFe2O4and Li0.5Fe2.5O4 and different percentages of cobalt-ferrite are synthesized. The crystalline structure by XRD and dielectric properties with TEM micrographs are presented. The XRD (crystallite size and lattice parameter) are determined which affected by cobalt content. TEM micrographs show a nano-particles in the range of (8-20) nm which correlate with crystallite size. Dielectric properties (dielectric constant, loss tangent and dielectric loss factor) are decreased with frequency and cobalt content.

استخدمت طريقة السول-جيل (الاحتراق الذاتي) لتحضير فيرايت الكوبلت والليثيوم النانوي وكذلك خلط نسب مختلفة من الكوبلت مع الليثيوم. تم دراسة التركيب البلوري باسنخدام حيود الاشعة السينية والتركيب المجهري باستخدام المجهر الالكتروني النافذ بالاضافة الى قياس الخواص العزلية .تم حساب الحجم البلوري و ثابت الشبكية حيث تاثر كليهما باضافة فيرايت-الكوبلت وان صور المجهر الالكتروني النافذ بينت ان معدل الحجم الحبيبي كان من(8-20)نانومتر والتي تكون متقاربة مع الحجم البلوري. اما الخواص العزلية (ثابت العزل, ظل فقدان الزاوية, معامل الفقدان العزلي) فقد تناقصت مع التردد مع محتوى الكوبلت.


Article
Preparation of Lead Free Piezoelectric Composite Based on Polyester Resin and (LKNN6-0.5%CeO2) Ceramic Particles

Authors: Fadhil A. Chyad --- Saad B.H. Farid --- Hamza M. Kamal
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 13 Part (A) Engineering Pages: 2464-2471
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

For the sake of guarding the environment from the vital problems that results from the toxic effects of lead components, lead free (LKNN6-0.5%CeO2/polyester) piezoelectric composite are prepared in this work using cold press technique. Firstly, the lead free (LKNN6-0.5%CeO2) piezoceramics are prepared using normal sintering technique. The dielectric and piezoelectric properties of the composites were examined as a function of the volume fraction of ceramic particles, all composites showed well dispersion of the piezoceramic particles in the polyester matrix as shown in SEM images. The piezoelectric and dielectric coefficients were found to be improved as the concentration of ceramic particles increases. Although the procedure is simple, the composite prepared in this study exhibited better piezoelectric and dielectric constants with (d33=41 and Ԑr=157) at (80%) volume fraction.

Listing 1 - 10 of 15 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (15)


Language

English (13)

Arabic and English (2)


Year
From To Submit

2016 (2)

2015 (2)

2014 (2)

2013 (2)

2012 (2)

More...