Article
Study of ZnO, SnO2 and Compounds ZTO Structures Synthesized for Gas-Detection
دراسة تراكيب ZnO , SnO2و مركباتها ZTO المؤلفة على الكشف الغازي

Authors: Farhad M. Othman --- Alaa A. Abdul-Hamead --- Alaa S. Taeeh
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 6 Part (A) Engineering Pages: 1328-1340
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Semiconductor-based metal oxide gas detector of five mixed Z:S from zinc chloride salt (0,25,50,75,100%) ratios with tin chloride salt, were fabricated on glass substrate by a spray pyrolysis technique with thickness were about ( 0.2 ±0.05 µm) using water soluble as precursors at a substrate temperature 500 Cº±5, 0.05 M ,and their gas sensing properties toward (CO2 , NO2 and SO2 gas at different concentration (10,100,1000 ppm) in air were investigated at room temperature which related with the petroleum industry. Furthermore structural and morphology properties was inspecting. Experimental results show that the mixing ratio affect the composition of formative oxides (ZnO,Zn2SnO4,Zn2SnO4+ZnSnO3,ZnSnO3, SnO2) ratios mentioned in the above respectively, and related with the sensitivity of the tested oxidation gases.

في هذا البحث حضر كاشف شبه موصل اوكسيدي من خمس خلطات Z:S من ملح كلوريد الزنك (100, 75 ,50, 25,0%) مع ملح كلوريد القصديرحضرت و بطريقة الرش الكيميائي الحراري و بسمك حوالي (0.2 ± 0.05 µm) على قواعد من الزجاج و باستخدام الماء كمذيب , و بدرجات حرارة ترسيب بلغت(500 ±5) C° و بتراكيز (0.05) M ككاشف للغازات الملوثة مثل(CO2 , NO2و SO2) و بتركيز ((10,100,1000 ppm في الهواء و بدرجة حرارة الغرفة والمرتبطة مع الصناعة النفطية. تم تشخيص التبلور و مورفولوجية سطح الأغشية المحضرة بواسطة قياسات حيود الأشعة السينية XRD و المجهر الالكتروني الماسح SEM ومجهرة القوة الذري AFMلها . بينت النتائج أن نسبة الخلط تؤثر على تبلور الأكاسيد المتكونة و المركبات الثلاثية المتكونة حيث كانت (ZnO,Zn2SnO4,Zn2SnO4+ZnSnO3,ZnSnO3, SnO2) للنسب المذكورة في أعلاه على التوالي وترتبط مع حساسية الغازات المؤكسدة المفحوصة.


Article
Studying the Effect of Nano Additives and Coating on Some Properties of Cement Mortar Mixes
دراسة تأثير الطلاءات والمضافات النانوية على بعض الخواص لخلطات مونة الاسمنت

Authors: Sarmad.I.Ibrahim --- Alaa.A.Abdul Hameed --- Farhad. M. Othman
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 3 Part (A) Engineering Pages: 553-566
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The experimental work is divided in two parts, in the first part was prepared the mortar samples and mixing proportions cementsand (1:3)they were mixing these samples with nano scale ceramic powders (ZrO2 and TiO2) respectively the percentages by weight are taken from cement ratio (0.1, 1, 2.5, 5, and 10%) at particle size (50nm) and curing time (28day). The second part has included the preparation of mortar samples and then coated with a mixture of methanol alcohol, cement and ceramic nano-powders by cold spray technique by using compressed air at room temperature with pressure (8bar) and the spray distance (20Cm) and heating of the samples at (75C°), and then study mechanical thermal physical and structural properties for prepared samples. The results of mechanical and physical tests showed large and significant improvement for all mixed and coated samples with nanoparticles, and that the highest value of the mechanical and physical properties obtained from cement coated samples with (%5ZrO2), reaching the rate of increase in values of Vickers hardness by (%54), and wear resistance increased by (%66), while reaching the rate of decrease in values of total water absorption by (%79), The porosity has decreased at a rate of (%65), With regard to the dry density has increased at a rate of (%2.3). The higher values for the mixed samples reaching the rate of increase in values of Vickers hardness by (%38), and wear resistance increased by (%58), while reaching the rate of decrease in values of total water absorption by (%67), The porosity has decreased at a rate of (%51.68), With regard to the dry density has increased at a rate of (%1.9). The thermal conductivity test results have shown that there is a marked decrease in values conductivity for all mixed and coated samples with nanoparticles and that the minimum value of conductivity obtained from coated and mixed samples with (%5TiO2) as the value decreases conductivity for coated samples by (%64), while the lowest value for conductivity to the mixed samples by (%49). Results of Characterizations tests showed images of all of (SEM and AFM) Mortar reference sample that a high roughness as well as having to structure Ca(OH)2 a needle shaped structures with the presence of large pores, while after adding and coating by nanoparticles shows the disappearance of structures needle and produce a homogeneous structure of compounds (C-S-H) and the disappearance of the pores and gaps further decrease in surface roughness this explains the clear improvement in the properties.

ينقسم الجانب العملي الى جزئين، في الجزء الاول تم تحضير نماذج المونة وبنسبة خلط اسمنت/رمل (1:3) حيث تم خلط هذه النماذج مع مساحيق سيراميكية نانوية (ZrO2,TiO2) على التعاقب وبنسب وزنية مأخوذة من نسبة الاسمنت (10,5,2.5,1,0.1%) وبحجم حبيبي (50) نانومتر ووقت معالجة لمدة (28) يوم، اما الجزء الثاني فقد تضمن تحضير نماذج المونة ومن ثم طلاؤها بخليط من كحول الميثانول والاسمنت والمساحيق النانوية وبتقنية الرش البارد بأستخدام الهواء الجوي المضغوط بدرجة حرارة الغرفة عند ضغط (8) بار ومسافة رش بمقدار (20) سم، وتسخين اولي للقواعد لدرجة (75) درجة مئوية، ومن ثم دراسة الخصائص الميكانيكية والحرارية والفيزيائية والتركيبية للنماذج المحضرة.نتائج الفحوصات الميكانيكية والفيزيائية اظهرت تحسن كبير وملحوظ لجميع النماذج المخلوطة والمطلية مع الدقائق النانوية، وان القيمة الاعلى للخواص الميكانيكية والفيزيائية تم الحصول عليها من النماذج المطلية والمخلوطة مع (%5ZrO2)، حيث بلغت معدل الزيادة في قيم صلادة فيكرز بنسبة (%54)، ومقاومة البلى ازدادت بمعدل (%66)،بينما بلغ معدل النقصان بالامتصاص الكلي للماء بنسبة (%79)، اما المسامية فقد تناقصت بمعدل (%65)، وفيما يخص الكثافة فقد تزايدت بمعدل %2.3)). أما القيم الاعلى بالنسبة للنماذج المخلوطة ، حيث بلغت معدل الزيادة في قيم صلادة فيكرز المايكروية بنسبة (%38)، ومقاومة البلى ازدادت بمعدل (%58)، بينما بلغ معدل النقصان بالامتصاص الكلي للماء بنسبة (%67)، اما المسامية فقد تناقصت بمعدل (%52)، وفيما يخص الكثافة فقد تزايدت بمعدل %1.9)).أما نتائج فحص التوصيلية الحرارية فقد اظهرت ان هنالك نقصان ملحوظ في قيم التوصيلية ولجميع النماذج المخلوطة والمطلية مع الدقائق النانوية، وان القيمة الادنى للتوصيلية الحرارية تم الحصول عليها من النماذج المطلية والمخلوطة مع (%5 TiO2)، حيث بلغت قيمة النقصان بالتوصيلية للنماذج المطلية بنسبة (%64). اما بالنسبة للنماذج المخلوطة فقد بلغ مقدار النقصان (%49). نتائج الفحوصات التركيبية اظهرت صور كل من المجهر الالكتروني الماسح، ومجهر القوة الذرية لنموذج المونة المرجع انه ذا خشونة عالية وكذلك وجود لتركيب هيدروكسيد الكالسيوم Ca(OH)2 بشكل تراكيب ابرية الشكل مع وجود مسامات كبيرة، بينما اظهرت الصور بعد الاضافة والطلاء بالدقائق النانوية اختفاء التراكيب الابرية وانتاج تركيب متجانس من مركبات (C-S-H) واختفاء المسامات والفجوات علاوة على نقصان في خشونة السطح وهذا ما يفسر التحسن الواضح في الخواص.


Article
Characterization of Nano Powder Incorporated for Building Applications
توصيف مسحوق نانو المدمج في تطبيقات البناء

Authors: Alaa A. Abdul-Hamead --- Farhad M. Othman --- Mustafa M .Salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 6 Part (B) Scientific Pages: 1027-1039
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this paper Nano powders were used a mono; copper oxide CuO and di metal oxides powder; titanium dioxide (TiO2) in fabrication of mortar. Powder particle size about (67.8 nm) for TiO2 and (55.7nm) for CuO with crystal structure tetragonal and monoclinic system respectively have been used. These Nano powders were used as additives to the mortar material (0.5, 2.5, 5, 7.5 wt %) in order to be used in construction application including covering building, and studies on these mortar. Investigation was done on the mortar including XRD, AFM, optical microscopy, physical and some mechanical properties, micro hardness and wear rate). Results shows that where there an increase in micro hardness and decrease in wear rate in the mortar with the addition of Nano powder. Also be reduced Ca(OH)2 soft crystals and formation fine grains structure and homogeneous and the abolition of flaws or cracks. And the mortar with the Nano addition has been improved, which make the addition of Nano material beneficial and have a promising future in modern construction application.

في هذا البحث مساحيق نانويه استخدمت. مساحيق أكاسيد أحاديه واوكسيد النحاس أكسيد CuO وثنائيه المعدن ثنائي أوكسيد التيتانيوم (TiO2) في تصنيع المورتر(الملاط) . كانت الحجوم الحبيبية للمساحيق حوالي (67.8) nm لTiO2 و( 55.7) nm للCuO ,مع تراكيب بلورية رباعي الزوايا و أحادي الميل على التوالي قد استخدمت.وقد استخدمت هذه المساحيق النانويه كأضافه لماده المورتر (0.5،2.5، 5 ، 7.5٪ بالوزن) من وزن المورتر لأجل استخدامها في أغراض البناء بما في ذلك تغليف المبناني، و دراستها.تم اجراء الفحوصات على المورتر بما في ذلك XRD، AFM ، المجهري الضوئي والخواص الفيزيائية و بعض الخواص الميكانيكية ،( فحص الصلاده المايكروية وفحص معدل البلى ) .بينت النتائج أن حيث هناك زيادة في الصلادة الدقيقة وانخفاض في معدل البلى في المورتر مع إضافة مسحوق النانو. كما أن انخفاض تكون بلورات هدروكسيد الكالسيوم Ca(OH)2 وتشكيل حبيبات الدقيقة بلورات ناعمة هيكل ومتجانس وإلغاء عيوب أو الشقوق. والهاون مع إضافة نانو قد تحسنت، والتي تجعل من إضافة مواد نانو مفيدة ولها مستقبل واعد في أغراض البناء الحد.

Keywords

Nano powder --- TiO2 --- CuO --- mortar --- micro hardness --- wear rate


Article
Investigation the Effect of Nano–Particles and Recycling Mortar Additives on Physical and Mechanical Properties of Concrete

Authors: Raeid K. Mohammed --- Farhad M. Othman --- Alaa A. Abdul-Hamead
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 3 Part (A) Engineering Pages: 295-303
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this paper a lower ratio of nano powder were used from (Al2O3 and ZrO2) (0.5, 1.5and 2. 5 wt %) from cement weight, the average particle size of nano-powder were (20nm). These powders were used in fabrication of Concrete with recycle fine aggregate was replaced Natural fine aggregate(sand) in order to be used in construction application and studies the effect on the concrete. Investigation were done on the concrete including dry density, water absorption%, porosity%, compression strength, and wear rate. The results shows that The nano-Al2O3, nano-ZrO2, and recycle aggregate were adding causes difference effect in the physical and mechanical properties of concrete. Compared with control concrete specimens (Co) results for same curing time, the density, and compression strength of concrete were decreased with addition recycle fine aggregate(RFA), while wear rate, water absorption, and porosity % were increased, the lower values of density, compression strength were decreased by (2.3%, 10.8% ), respectively, while the higher values wear rat for 7 and 28 day curing time, water absorption and porosity % were increased by (19.8%, 21.4%, 8.8%, and 5.6%), respectively were obtained with addition (50%)RFA. While, the addition nano-Al2O3 and ZrO2 with RFA were increasing the density, and compression strength, but decreasing wear rate, water absorption, and porosity %, the higher values of compression strength was increased by (9.8%), while the lower values water absorption and porosity % were decreased by (24.1%, and 16.6% ), respectively were obtained with addition (1.5%) of nano-Al2O3 and 50% RFA. But the higher values of density was increased by (9.8% ) and lower values of wear rate for 7 and 28 day curing time were decreased by (71.1%, and 66.9%), respectively was obtained with addition (1.5%) of nano-ZrO2 and 50% RFA.


Article
A study of the Zn:Sn mixing ratio effect on the gas detector properties
دراسة تأثير نسبة خلط Zn:Sn على خصائص الكاشف الغازي

Authors: Alaa A. Abdul-Hamead ألاء علاء الدين --- Farhad M. Othman فرهاد محمد عثمان --- Alaa S. Taeeh ألاء صبيح تايه
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2015 Volume: 13 Issue: 27 Pages: 50-62
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Semiconductor-based metal oxide gas detector of five mixed from zinc chloride Z and tin chloride S salts Z:S ratio 0, 25, 50, 75 and 100% were fabricated on glass substrate by a spray pyrolysis technique. With thickness were about 0.2 ±0.05 µm using water soluble as precursors at a glass substrate temperature 500 ºC±5, 0.05 M, and their gas sensing properties toward CH4, LPG and H2S gas at different concentration (10, 100, 1000 ppm) in air were investigated at room temperature which related with the petroleum refining industry. Furthermore structural and morphology properties were scrutinize. Results shows that the mixing ratio affect the composition of formative oxides were (ZnO, Zn2SnO4, Zn2SnO4+ZnSnO3, ZnSnO3, SnO2) ratios mentioned in the above respectively, and related with the sensitivity of the reduction tested gases, best sensitivity was for H2S gas, have sensitivity about 80.61% and a response time of 10 seconds for the binary oxides and 89.57% and a response time of (5-2) seconds for the mixed ternary oxides.

في هذا البحث حضر كاشف شبه موصل اوكسيدي من خمس خلطات من أملاح كلوريد الزنك Z و كلوريد القصديرS و بنسب خلط Z:S بلغت %100, 75, 50 ,25 ,0 بطريقة الرش الكيميائي الحراري و بسمك حوالي (0.2 ± 0.05 µm) على قواعد من الزجاج و باستخدام الماء كمذيب, و بدرجات حرارة ترسيب بلغت500 ±5 C° و بتراكيز 0.05 M ككاشف للغازات الملوثة مثل(CH4 ,LPG و H2S ) و بتركيز(10, 100, 1000 ppm) في الهواء و بدرجة حرارة الغرفة والمرتبطة مع صناعة تكريرالنفط. تم تشخيص التبلور و مورفولوجية سطح الأغشية المحضرة بواسطة قياسات حيود الأشعة السينية XRD و المجهر الالكتروني الماسح SEM ومجهرة القوة الذري AFMلها. بينت النتائج أن نسبة خلط تؤثر على تبلور الأكاسيد المتكونة و المركبات الثلاثية المتكونة حيث كانت ZnO, Zn2SnO4, Zn2SnO4+ZnSnO3, ZnSnO3, SnO2)) للنسب المذكورة في أعلاه على التوالي وترتبط مع حساسية الغازات المختزلة المفحوصة, وكانت أفضل حساسية للغازH2S 80.61 ٪ وزمن الاستجابة 10 ثانية للأكاسيد الثنائية و89.57٪ وزمن الاستجابة من (5-2) ثانية لخليط الأكاسيد الثلاثية.


Article
Fabrication and Characterization of Tri Metal Oxides by Chemical Spray Pyrolysis Technique as a Gas Sensor
تصنيع و توصيف اكاسيد ثلاثية معدنية بتقنية الرش الكيميائي الحراري كمتحسس غازي

Authors: Farhad M. Othman فرهاد محمد عثمان --- Alaa A. Abdul-hamead ألاء علاء الدين --- Noor M. Ali نور محمد علي
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 4 Pages: 132-140
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research tri metal oxides were fabricated by simple chemical spray pyrolysis technique from (Sn(NO3)2.20 H2O, Zn(NO3)2.6 H2O, Cd(NO3)2.4 H2O) salts at concentration 0.1M with mixing weight ratio 50:50 were fabricated on silicon substrate n-type (111). (with & without the presence of grooves by the following diemensions (20μm width, 7.5μm depth) with thickness was about ( 0.1 ±0.05 µm) using water soluble as precursors at a substrate temperature 550 ºC±5, with spray distance (15 cm) and their gas sensing properties toward H2S gas at different concentrations (10,50,100,500 ppmv) in air were investigated at room temperature which related with the petroleum industry. Furthermore structural and morphology properties were inspecting. Experimental results show that the Zn2SnO4 and Cd2SnO4 thin films were achieved from the used salts and samples gas sensitivity which improved with the presence of substrate grooves. Which make the sensor suitable for the detection of lower .concentrations of hazard H2S gas in the petroleum industry.

في هذا البحث حضرت اكاسيد ثلاثية بطريقة الرش الكيميائي الحراري البسيطة من املاح (نترات القصدير والزنك والكادميوم) بتركيز(0.1M) وبنسب خلط وزنية 50:50 على قاعدة من السيليكون من النوع (n) بأتجاه (111) (بوجود وبعدم وجود الحزوز وبالأبعاد الآتية:عرض20μm, عمق7.5μm وبسمك حوالي (0.1 ±0.05 µm) بأستخدام الماء مذيبا وبدرجة حرارة ترسيب بلغت 550 ºC±5 وبمسافة رش (15 cm) ككاشف للغاز بتراكيز مختلفة (10,50,100,500 ppmv) في الهواء وبدرجة حرارة الغرفة والمرتبطة مع الصناعة النفطية.تم تشخيص التبلور ومورفولوجية سطح الاغشية المحضرة بواسطة قياسات حيود الاشعة السينية والمجهر الالكتروني الماسح ومجهر القوة الذري لها. اظهرت النتائج ان اغشية الاكاسيد المحضرة من الاملاح المستخدمة هي Zn2SnO4 و Cd2SnO4 وحساسية الغازات تحسنت بوجود الحزوز على السطح والتي تجعل من الكاشف مناسبا لكشف التراكيز القليلة من غازH2S الخطر في الصناعة النفطية.


Article
Fabrication of Advanced Cement Mortar for Building Anti-Bacterial Applications
تصنيع مونة الاسمنت المتقدمة لتطبيقات البناء المضادة للبكتريا

Authors: Noor A. Hmeed نور عبد الناصر حميد --- Alaa A. Abdul-hamead ألاء علاء الدين --- Farhad M. Othman فرهاد محمد عثمان
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2019 Volume: 15 Issue: 1 Pages: 89-96
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, we have added nano anatase TiO2 as a partial replacement of Portland cement by a weight percentage of (0.25 to 1%) for the development of properties for protection against bacteria. The control mix was made by using "the cement to sand" proportion about (1: 2.75) with the "water to cement" proportion of (0.5) to study the structure, porosity, water absorption, density, mechanical properties, as well as anti-bacterial behavior. Inspections have been done such as scanning electron microscopy (SEM), and atomic force microscope (AFM) for mortar. Experimental results showed that after the addition of Nano powders in cement mortar, the structural properties improved significantly with the development of hydration of cement mortar at early age, reduction of porosity and the increase of density as well as enhancement in compressive and anti-bacteria properties that make the preparation of nano material very suitable for protection against bacteria.

في هذا البحث تم اضافة نانو تيتانيه طور (anatase) بوصفه كمادة استبدال جزئي للسمنت البورتلاندي بنسب وزنية ( 1% to 0.25 ) لأجل تطوير خصائص (الحماية ضد البكتريا) وتم إجراء مزيج مرجعي مع نسبة الأسمنت إلى الرمل 2.75:1)) . تم الحفاظ على نسبة المياه في الاسمنت عند 0.5 و تم اجراء فحوصات الكثافة، المسامية، معامل الامتصاص فظلا عن الى ذلك الخواص التركيبية AFM ,SEM وفحوصات Anti-bacteria بينت النتائج ان الملاط الاسمنتي يمتلك بنية منتظمة ومعامل خشونة انخفظت بعد اضافة الماده النانوية وتحسنت الكثافة و انخفاض في معامل الامتصاص والمسامية مما يجعل الملاط المحضر ملائماً لتطبيقات (الحماية ضد البكتريا).


Article
FABRICATION OF ADVANCED MORTAR FOR BUILDING APPLICATION
تصنيع مونه إسمنتية متقدمة لتطبيقات البناء

Loading...
Loading...
Abstract

In this research, cement mortar specimens were prepared with sand to cement (1:2.75) and (1, 2, and 3 wt%) of ceramic oxides (MgO, ZnO and Al2O3) at different particle sizes (11.8, 38.8, 109.8 nm), respectively. At curing time (7days), the (structural, thermal and physical) characteristics of the mortar specimens were investigated.The dry density and porosity results show that the values of density increased by (23.4, 15.6, and 9.5%), and the values of porosity decreased by (76.2, 63.8, and 56.2%) for (MgO, ZnO, and Al2O3), respectively with respect to the reference mortar specimen. The thermal conductivity results show that the values of thermal conductivity decreased by (47.27, 40.66, and 51.16%) for (MgO, ZnO and Al2O3) respectively, with respect to the reference mortar specimen . Results of characterizations tests (XRD and optical microscope) showed that the reference mortar specimen has high roughness with large number of Ca(OH)2 crystals, as well as the presence of pores, while after adding the nanopowders, it showed a decrease or disappearance of Ca(OH)2 and produced homogeneous structure of calcium silicate hydrate compound (C-S-H), in addition to a large decrease in the pores and surface roughness. This explains the significant improvement in the properties of cement mortar mixed with nanopowders, hence these mortars were very appropriate for covering walls, buildings and other outdoor building applications.

في هذا البحث تم إعداد نماذج المورتر بنسبة خلط الرمل إلى الاسمنت (1:2.75) مع (3,2,1 % ( اكاسيد سيراميكية هي: اوكسيد المغنيسيوم (MgO) واوكسيد الزنك ((ZnO واوكسيد الألمنيوم (Al2O3) بحجوم حبيبية (10911.8,38.8,109.8 ) نانومتر على التوالي. عند الزمن (7 يوم), تم إجراء فحوصات مثل التوصيل الحراري والفحوصات التركيبية والحرارية والفيزيائية على نماذج المونه المحضرة. اظهرت نتائج فحوصات الكثافة والمسامية زيادة في قيم الكثافة بنسب (9.5,15.6, 23.4%), وقيم المسامية زادت بنسب 56.2,63.8,76.2)%) عند اضافة لوكسيد المغنيسيوم واوكسيد الخارصين والالومينا على التوالي نسبة إلى نموذج المورتر المرجع. أما نتائج التوصيلية أظهرت إن هناك نقصان واضح في قيم التوصيلية الحرارية باستخدام تلك المواد بنسب (%51.16,40.66,47.27 ) على التوالي, نسبة إلى نموذج المورتر المرجع. اظهرت نتائج الفحوصات التركيبية (حيود الاشعة السينية و المجهر البصري) إن لنموذج المونة المرجع خشونة عالية وكذلك وجود عدد كبير من بلورات هيدروكسيد الكالسيوم Ca(OH)2 مع وجود مسامات، بينما بعد إضافة المساحيق النانوية, أظهرت نقصان أو غياب للبلورات الكبيرة ل Ca(OH)2وانتاج تركيب متجانس من سيليكات الكالسيوم المماهة (C-S-H), إضافة إلى ذلك نقصان كبير في المسامات والخشونة السطحية. هذا ما يفسر التحسن الواضح في خواص المورتر الأسمنتي المخلوط بمساحيق نانوية, مما يجعلها مناسبة في تغليف الجدران, والبنايات, وتطبيقات البناء الخارجي الاخرى.


Article
Synthesis and characterization of Iron tungstate oxide films by advanced controlled spray pyrolysis technique
تحضير وتشخيص أغشية اوكسيد تنغستات الحديد بواسطة تقنية الرش الحراري الكيميائي المطورة المسيطر عليها

Loading...
Loading...
Abstract

For the first time Iron tungstate semiconductor oxides films (FeWO4) was successfully synthesized simply by advanced controlled chemical spray pyrolysis technique, via employed double nozzle instead of single nozzle using tungstic acid and iron nitrate solutions at three different compositions and spray separately at same time on heated silicone (n-type) substrate at 600 °C, followed by annealing treatment for one hour at 500 °C. The crystal structure, microstructure and morphology properties of prepared films were studied by X-ray diffraction analysis (XRD), electron Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM) respectively. According to characterization techniques, a material of well-crystallized monoclinic phase FeWO4 films with spindle and aggregated fine plates microstructures were obtained from using this advance technique, with thickness about 500 nm. Such these structures have been recognized as one of the most efficient microstructures due to their large specific surface area especially in gas sensor applications.

لاول مرة أغشية أوكسيد تنغستات الحديد الشبة موصلة (FeWO4) حضرت بنجاح بواسطة استخدام تقنية الرش الكيميائي الحراري المحدثة المسيطر عليها ذلك باستخدام فوهة مزدوجة بدلا من فوهة واحدة حيث استعمل حامض التنغستن ونترات الحديد كمحاليل للرش بثلاث نسب مختلفة وتم رش المحاليل بصورة منفصلة على شريحة سيليكون نوع مانح مسخنة بدرجة حرارة 600 م°، يليها معاملة حرارية التلدين بدرجة حرارة 500 م° لمدة ساعة واحدة. خصائص التركيب البلوري والبنية المجهرية و طوبوغرافية السطح للطبقة المحضرة تم دراستها بواسطة حيود الاشعة السينية، مجهر المسح الالكتروني و مجهر القوة الذرية على التوالي. وفقا لتقنيات التشخيص تشير الى تكون اغشية متبلورة من (FeWO4) على شكل صفائح ناعمة متجمعة ناتجه من استخدام هذه التقنية المطورة، مثل هذه البنية تم التعرف عليها باعتبارها واحدة من أكثر البنى المجهرية كفاءة لامتلاكها مساحة سطحية كبيرة خاصة في تطبيقات المتحسس الغازي.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (7)

Arabic and English (2)


Year
From To Submit

2019 (2)

2018 (2)

2016 (2)

2015 (3)