Article
Study of Differential Scanning Calorimetry on Phase Precipitation in Various Heat Treatments of AlZnMgCu Aluminum Alloys
دراسة مسعر المسح التبايني على أطوار الترسيب في معاملات حرارية متنوعة لسبائك الألمنيوم (الألمنيوم-زنك-مغنيسيوم-نحاس)

Author: Haider Tawfiq Naeem
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2017 Volume: 5 Issue: 1 Pages: 10-15
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

Powers compensation of the differential scanning calorimetry (DSC) have been utilized to revealed ‎and analyze the phases of precipitations in the complex quaternary of Zinc (6.7wt. %) _ Magnesium (2.8 wt. %) _ Copper (1.8 wt. %) _Aluminum alloys ‎manufactured by the process of the Semi-Direct Chill Casting. The casted Al-Zn-Mg-Cu alloys slabs were homogenizing at the different temperatures. Firstly under treatment 450°C for 2 hours follow by treatment 470°C for 1 day and then treatment at 480°C for 40 minutes, then all casted samples have quenched in cold water after each step. The treated homogenized Al-Zn-Mg-Cu samples that were underwent the artificial ageing at 120 °C for 1 day, and then retrogression at 180°C for 2400sec. and then re-ageing at 120°C for 1 day. The outcomes proved that the X-ray diffraction (XRD) analyses confirmed information of the DSC thermal analyses which were obtained through various heat treatments of the three samples AlZnMgCu alloy. The outcomes have explained that the DSC data are helping in understanding the changes the peaks of temperatures as well the enthalpy values for the forming and dissolution the equilibrium phase’s and precipitation compounds within the artificial againg (with the pea-temper) and the Retrograession and Re-Againg-(RRA) treatments were conducting for Al_Zn_Mg_Cu alloy samples.

في هذه الدراسة تم استخدام معادلة القدرة التفاضلية لمسعر المسح التبايني (Differential Scanning Calorimetry-DSC) لكشف وتحليل مركبات الترسيب في الرباعية معقدةالالمنيوم- 6.7٪ الزنك -2.8٪ المغنيسيوم- 1.8٪ النحاس سبائك , التي تنتجها عملية السباكة ذات التبريد السريع شبه المباشر.خضعت ألواح مسبوكة من خلائط آلامنيوم - الزنك- المغنيسيوم- النحاس الى معاملة المجانسة الحرارية عند درجات حرارة مختلفة .كانت هذه اولى تحت 450 درجة مئوية لمدة 2 ساعة يتبعها 470 درجة مئوية لمدة 24 ساعة واخيرا 480 درجة مئوية لمدة 40 دقيقة، بعدها تم اخماد العينات في الماء البارد بعد كل خطوة من عمليات التجانس. بالاضافة الى ذلك خضعت الواح السبيكة لمعاملة التعتيق الصناعي عند درجة حرارة 120 مئوية لمدة 24 ساعة ، وايضا على حرارة 180 درجة مئوية لمدة 40 دقيقة ثم إعادة التعتيق عند 120 درجة مئوية لمدة 24 ساعة خضعت كل العينات الى التبريد بالماء البارد بعد كل عملية حرارية. أثبتت النتائج أن معلومات تحليل حيود الأشعة السينية (XRD) تؤكد المعلومات الحاصلة من التحاليل الحرارية للمسعر المسح التبايني ((DSC لعينات الالمنيوم الخاضعة للمعالجات الحرارية المختلفة.من جانب اخر اوضحت النتائج ان البيانات الحرارية للمسعر المسح التبايني ((DSC ساعدت في فهم المتغيرات و قيم المحتوى الحراري لاطوارومركبات الترسيب عند التشكيل والانحلال الناتجة بتاثير التعتيق الصناعي عند 120 درجة مئوية وايضا عند عملية اعادة التعتيق في 120 درجة مئوية وثم عند 180 درجة مئوية تليها عند 120 درجة مئوية.


Article
Characterizations Particulates of Crushed Particles (Al_Zn_Mg_Cu_Ni) for Fabrication of ‎Surface Composites Al-Alloy Using Friction Stir Processing Route
توصيف جسيمات الدقائق المطحونة (ألمنيوم-زنك-مغنيسيوم-نحاس-نيكل) لتصنيع سطح متراكب لسبيكة المنيوم بأستخدام عملية الأحتكاك الفائق

Author: Haider Tawfiq Naeem
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2016 Volume: 4 Issue: 2 Pages: 56-65
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

Productions of surfaces composites have high mechanical properties and altered microstructural is attracting considerable attention. One of the methods of fabricating composite surfaces of aluminium matrix alloys are the procedure of Friction Stir Process (FSP). In this investigation, the producing for the surface composites of Aluminum_Zinc_Magnesium_Copper ‎alloy ‎(7000 series) with the pulverizing particulates of (Al_5wt%Zn_2.5wt%Mg_1.5wt%Cu_4wt%, 6%, 8% Ni), ‎as the reinforcement particles using FSP was discussed. ‎The reinforcements were from Al_Zn_Mg_Cu particulates as well various nickel powder (mass percentages) synthesized using the high-energy, ball milling alloying process. Composites samples underwent for the homogenizing treatment through various temperatures. These samples have subjected the ageing treat with 120 °C for one day. Results showed a 70% decrease in the grain sizes of the surface of composites Al-alloys compared with as-received Al-alloy. The grain refinement and uniform dispersion of the reinforcements during the Al-matrix were obtained because of the optimized parameters of FSP. The intensity of precipitations intermetallic, which as reinforcements increased after heat treatments along with the phases of the precipitates. The effects of the grain reduction and intercompounds with the precipitation phases led to a ‎valuable rise in the hardness property of surface of aluminium 7000 alloy-reinforced composities. ‎

أنتاج سطح متراكب للألمنيوم بخواص ميكانيكة عالية بالاضافة الى خواص مجهرية معدلة اجتذب اهتماما كبيرا ولذا تعتبر طريقة ألاحتكاك الفائق (Friction Stir Processing) من إحدى الطرق المتميزة لتصنيع (لافتعال) سطح مركب معدني .في هذه الدراسة، يتم إنتاج سطح متراكب من سبائك الألومنيوم-زنك-مغنيسيوم-نحاس (السلسلة 7000) مع دقائق من مسحوق مطحون بنسب مختلفة من التكوين التالي ]المنيوم-- 5%) زنك -2.5%)( مغنيسيوم) -1.5%) نحاس)- 4%)- 8% نيكل‎)[ بأستخدام طريقة طريقة الأحتكاك الفائق , دقائق المسحوق(المتكونة من ألمنيوم-زنك-مغنيسيوم-نحاس-نسب مختلفة من النيكل) تم توليفها باستخدام عمليات الطحن السبكي بالكرات ذات الطاقة العالية. بعد ذلك تم وضع دقائق المسحوق في داخل شق صفيحة من سبيكة الالمنيوم ثم ضغطت مع تثبيت العينة على ماكنة الفارزة العمودية واجريت عملية الاحتكاك الفائق لتكوين سطح مقوى متراكب من سبيكة الألمنيوم. عمليات التجانس الحراري تمت عند درجات مختلفة وكذلك معاملات التعتيق الصناعي الحرارية في 120 درجة مئوية لمدة 24 ساعة اجريت على العينات. أظهرت النتائج انخفاضا كبيرا بنسبة 70٪ في أحجام الحبيبات المجهرية لسبيكة الالمنيوم المتراكبة المعززة بالجسيمات بالمقارنة مع سبيكة الالمنيوم الاصلية. النتائج اوضحت سبب تنعيم البلورات المجهرية وكذلك التجانس الحاصل في المركبات الوسطية داخل سبيكة الالمنيوم المعززة يعزى الى المقاييس الجيدة لظروف عمل طريقة ألاحتكاك الفائ . كثافة المركبات الوسطية من الاطوار المترسبة التي تعتبر كمقويات للسبيكة تزداد بعد المعاملات الحرارية.أثار تنعيم الحبيبات بألاضافة الى المترسبات قاد الى زيادة الصلادة السطحية للسبيكة المتراكبة.


Article
Preparation and Characterization of Polymer Blend (PVA/PEO) Filled with Methyl Orange Thin Films

Authors: Ahmed Namah Mohamed --- Jafer Fahdel Odah --- Haider Tawfiq Naeem
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2018 Volume: 14 Issue: 02 Pages: 221-234
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Polymers blend PVA/PEO filled with different weight percent ratios of methyl orange was used to prepare films via casting method. Structural properties of the final thin films were carried out using XRD technique, FTIR and optical microscope. While the absorption spectra of these films were measured using UV-VIS double beam spectrometer in the wavelength range of (190-1100) nm. The optical coefficients such absorption coefficient and extinction coefficient were calculated from the optical absorption. Direct and indirect allowed electronic energy transitions were studied under the influence of MO weight percent variation (0, 10, 20, 30, 40 and 50) wt %.

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2018 (1)

2017 (1)

2016 (1)