Optimization of Hot-Dip Aluminizing Process Parameters of AISI 303 Stainless Steel Using RSM
أمثلية متغيرات عملية الألمنة بالغمر الساخن للصلب المقاوم للصدأ AISI 303 بأستخدام RSM

Authors: Ahmed Naif Al-Khazraji --- Samir Ali Al-Rabii --- Hameed Shamkhi Al-Khazalli
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 9 Part (A) Engineering Pages: 2130-2145
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The coating thickness is an important factor to evaluate the coating quality and determining the properties of the hot-dip aluminizing (HDA)coating. In the present work, a hot dipping pure aluminum (99%) on stainless steel (AISI 303) rods was carried out for different diameters of rods (8, 10 and 12mm) and different lengths (250 and 500 mm) at different aluminizing conditions of temperature and time. The dipping temperature was set to 700, 740, 780, 820 and 860℃ .The dipping time was set to 1, 2, 3,4 and 5 minutes. A response surface methodology (RSM) using a central composite rotatable design (CCD) for a 2³ factorial, with 5 central points and α = ±2 approach, based on the experimental data, was used to obtain the optimum modelto get the best thickness of coating and the best conditions of dipping. A 2nd polynomial model was obtained with a confiding percentage of 95%.Analysis of the experiments using RSM indicated that 807℃ and3minare optimum dipping conditions for hot-dip aluminizing process with corresponding thickness of coating layers of 134 μmto Al layer,62.9 μm to intermetallic compound (IMC) layer and 197μm to total coating layer.

يعتبر سمك طبقة الطلاء في طريقة الالمنةبالغمرالساخن من العوامل المهمة لتقييم نوعية الطلاء وتحديد مواصفاته. في هذا البحث تم تنفيذ عملية الالمنة بالغمرالساخن باستخدام الالمنيوم النقي بنسبة (99%) لاعمدة دائرية المقطع مصنوعة من الصلب المقاوم للصدأ (AISI 303) ذات اقطار مختلفة (8, 10 and 12 mm) واطوال مختلفة (250 and 500 mm ) ولظروف ألمنة مختلفة من درجة الحرارة وزمن الغمر. تم تثبيت درجة حرارة الغمر الساخن لتكون 700, 740, 780, 820 and 860℃ .اما زمن الغمر فتم تثبيته ليكون 1, 2, 3, 4 and 5 minutes . تم استخدام طريقة الاستجابة السطحية (RSM), والتي تستعملتصميم المركز المركب (CCD) بعوامل 23و5 نقاط مركزية, لانتاج موديل رياضي لحساب سمك طبقة الطلاء وكذلك تحديد الظروف المثلى لعملية الالمنة وذلك بالاستناد الى النتائج العملية لقياس سمك الطلاء عند ظروف الالمنة المختلفة, حيث تم الحصول على موديل رياضي من الدرجة الثانية (a 2nd degree polynomial) بنسبة موثوقية تصل الى 95%.ان استخدام طريقة RSM لتحليل نتائج عملية الالمنة اظهر بأن ظروف الغمر المثلى هي 807℃ and 3minوان ما يقابلها من سمك طبقات الطلاء هو 134.0μm لطبقة الالمنيوم (Al) , 62.9 μm للطبقة الوسطية المركبة (IMC) و 197ΜM لسمك الطبقة الكلية للطلاء.


Article
Enhancement of Buckling Resistance of Aluminized Long Columns of Stainless Steel AISI 303
تحسين مقاومة الانبعاج للاعمدة الطويلة من الصلب المقاوم للصدأ AISI 303 المؤلمنة بطريقة الغمر الساخن (HDA)

Loading...
Loading...
Abstract

This paper has investigated experimentally the dynamic buckling behavior of AISI 303 stainless steel Aluminized and as received long columns. These columns, hot-dip aluminized and as received, are tested under dynamic buckling, 22 specimens, without aluminizing (type 1), and 50 specimens, with hot-dip aluminizing at different aluminizing conditions of dipping temperature and dipping time (type 2), are tested under dynamic compression loading and under dynamic combined loading (compression and bending) by using a rotating buckling test machine. The experimental results are compared with Perry Robertson interaction formula that used for long columns. Greenhill formula is used to get a mathematical model that descripts the buckling behavior of the specimens of type (1) under dynamic compression loading. The experimental results obtained show an advantageous influence of hot-dip aluminizing treatment on dynamic buckling behavior of AISI 303 stainless steel long columns. The improvement based on the average value of critical buckling stress, are as follow: (64.8 %) for long columns type (2), compared with columns type (1), under dynamic compression loading, and (56.6 %) for long columns type (2), compared with columns type (1), under dynamic combined loading, and (33.3 %) for long columns type (2) compared with Perry Robertson critical buckling stress.

تم في هذا البحث التحقق العملي لسلوك الانبعاج الديناميكي للاعمدة الطويلة المؤلمنة وغير المؤلمنة المصنوعة من الصلب المقاوم للصدأ AISI 303 . حيث فحصت هذه الاعمدة تحت تاثيرحمل الانبعاج الديناميكي، 22 عينة غير مؤلمنة (type 1) و 50 عينة مؤلمنة بطريقة الغمر الساخن (type 2)، وبظروف غمر مختلفة من درجة حرارة الغمر وزمن الغمر، بأستخدام ماكنة فحص الانبعاج الدوار ولحالة حمل الانضغاط الديناميكي وكذلك الحمل المركب (حمل انضغاط زائد حمل انحناء). تم مقارنة النتائج مع صيغة Perry Robertson interaction formula. تم استخدام صيغة Greenhill لغرض الحصول على موديل رياضي يصف سلوك الانبعاج تحت تأثير حمل الانبعاج الديناميكي. أظهرت النتائج الفائدة العملية المتحققة من عملية الالمنة بالغمر الساخن على سلوك الانبعاج تحت تأثير الاحمال الديناميكية. تمثل هذا التأثير الايجابي بتحسين مقاومة الانبعاج الديناميكي للاعمدة الطويلة المستخدمة في هذا البحث بنسب مئوية لمتوسط اجهاد الانبعاج الحرج، وهذه النسب كما يلي: (64.8 %) للاعمدة الطويلة نوع (2) مقارنة بالاعمدة نوع (1) وتحت تأثير التحميل الانضغاطي الديناميكي، و (56.6 %) للاعمدة الطويلة نوع (2) مقارنة بالاعمدة نوع (1) وتحت تأثير التحميل الديناميكي المركب، و (33.3%) للاعمدة نوع (2) مقارنة بقيمة اجهاد الانبعاج الحرج المحسوب من صيغة Perry Robertson.