Article
Adsorptive Removal of Furfural from Wastewater on Prepared Activated Carbon from Sawdust
الازالة الامتزازية للفرفورال من مياه الصرف الصناعية باستخدام الكاربون المنشط المحضر من نشارة الخشب

Authors: Rouaa Nadhum Ghazy رؤى ناظم غازي --- Ibtehal Kareem Shakir ابتهال كريم شاكر
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2019 Volume: 25 Issue: 1 Pages: 51-63
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Furfural is a toxic aromatic aldehyde that can cause a severe environmental problem especially the wastewater drown from petroleum refinery units. In the present work, a useless by-product from local furniture manufacturing industry; sawdust was used as raw material for the preparation of activated carbon which is chemically activated with phosphoric acid. The effect of adsorption variables which include initial pH of solution (2-9), agitation speed (50-250) rpm, agitation time (15-120) min, initial concentration of furfural (50-250) ppm, and amount of adsorbent material (0.5-2.5) g for the three adsorbents used (prepared activated carbon, commercial activated carbon and raw sawdust) were investigated in a batch process in order to obtain the maximum furfural removal from wastewater. The results obtained from the experimental investigation show that the percentage removal of furfural increases with increasing pH and agitation speed until a maximum value after that it decreased with increasing pH and agitation speed. Also increases with increasing amount of adsorbent material and agitation time until a maximum value then reaches a constant value approximately, and decreasing with increasing furfural concentration. The maximum removal percent of furfural was 97.8, 94.4 and 55.9% for prepared activated carbon, commercial activated carbon, and raw sawdust respectively, which is obtained at a pH of 7.0, agitation speed of 150 revolutions per minute, agitation time of 105 minutes, furfural concentration of 100mg/L, and adsorbent amount of 1.5gm. Langmuir model is best fitted the data than Freundlich model.

يعتبر الفورفورال من المواد الاروماتية السامة والتي تسبب مشاكل كبيرة للبيئة وخصوصا المياه المطروحة من وحدات المصافي النفطية, وفي هذا العمل استخدمت مواد عديمة الفائدة مطروحة من معامل النجارة وهي نشارة الخشب كمادة اولية لتحضير كاربون منشط كيميائيا باستخدام حامض الفسفوريك. أثر متغيرات الامتصاص والتي تشمل الرقم الهيدروجيني الأبتدائي للمحلول من (2-9), وسرعة الخلط من (50-250) دورة في الدقيقة, ووقت الخلط من (15-120) دقيقة، التركيز الأولي للفورفورال من (50-250) جزء بالمليون، وكمية المواد المازة من(0.5-2.5) غم, باستخدام الكاربون المحضر والكاربون التجاري ونشارة الخشب في العملية الدفعية من أجل الحصول على أقصى إزالة للفورفورال من مياه الصرف الصناعية حيث أظهرت النتائج التي تم الحصول عليها من التجارب أن نسبة إزالة الفورفورال تزداد مع زيادة درجة الحموضة وسرعة الخلط حتى تصل الى اعلى قيمة بعد ذلك تنخفض مع زيادة الرقم الهيدروجيني وسرعة الخلط ، وتزداد مع زيادة كمية المواد المازه ووقت الخلط حتى تصل الى اعلى قيمة ثم تصل الى قيمة ثابتة تقريبا، وتناقص مع زيادة تركيز الفورفورال. وكانت النسبة المئوية القصوى لإزالة الفورفورال 97.8٪ 94,4 ٪ و 55.9٪ باستخدام الكاربون المحضر والكابون التجاري ونشارة الخشب على التوالي والتي تم الحصول عليها عند درجة الحموضة = 7 ، وسرعة الخلط 150 دورة في الدقيقة الواحدة، وزمن الخلط 105 دقيقة، وتركيز الفورفورال 100ملغم / لتر, وكمية المادة المازة 1,5 غرام , نتائج الدراسة انطبقت على لانكماير موديل افضل من فريندلج موديل.


Article
The use of Prepared Zeolite Y from Iraqi kaolin for Fluid Catalytic Cracking of Vacuum Gas Oil
استخدام الزيولايت من نوع Y المحضر من الكاؤلين العراقي لعملية التكسير الحفازي المائع لمادة زيت الغاز الفراغي

Authors: Abdul Halim Abdul Karim Mohammed عبدالحليم عبدالكريم محمد --- Ibtehal Kareem Shakir ابتهال كريم شاكر --- Karim Khalifa Esgair كريم خليفة أزغير
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 10 Pages: 1256-1270
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The faujasite type Y zeolite catalyst was prepared from locally available kaolin. For prepared faujasite type NaY zeolite X-ray, FT-IR, BET pore volume and surface area, and silica/ alumina were determined. The X-ray and FT-IR show the compatibility of prepared catalyst with the general structure of standard zeolite Y. BET test shows that the surface area and pore volume of prepared catalyst were 360 m2/g and 0.39 cm3/g respectively. The prepared faujasite type NaY zeolite modified by exchanging sodium ion with ammonium ion using ammonium nitrate and then ammonium ion converted to hydrogen ion. The maximum sodium ion exchange with ammonium ion was 53.6%. The catalytic activity of prepared faujasite type NaY, NaNH4Y and NaHY zeolites was investigated by using the experimental laboratory plant scale of fluidized bed reactor. The cracking process was carried out in the temperature range 440 to 500 oC, weight hourly space velocity (WHSV) range 10 to 25 h-1 ,and atmospheric pressure . The catalytic activities of the prepared faujasite type NaY , NaNH4Y and NaHY zeolites were determined in terms of vacuum gas oil (VGO) conversion, and gasoline yield . The conversion at 500oC and WHSV10 hr-1 by using faujasite type NaY, NaNH4Y and NaHY zeolite were 50.2%, 64.1% and 69.5wt% respectively. The gasoline yield using the same operating conditions were 24.8%, 30.5% and 36.8wt% respectively.

تم تحضيرالعامل المساعد الفيوجيسايت نوع Y زيولايت من الكاؤلين المتوفر محليا. اجريت تحاليل الاشعة السينية , والاشعة تحت الحمراء , والمساحة السطحية و الحجم المسامي , وتحليل نسبة السليكا الى الالومينا للعامل المساعد فيوجيسايت نوع NaY زيولايت.اظهرت تحليلي الاشعة السينية , والاشعة تحت الحمراء توافق العامل المساعد المحضر مع التركيب العام للزيولايت القياسي و كانت المساحة السطحية 360م2 /غم والحجم المسامي 0.39 سم3 /غم .طور العامل المساعد المحضر فيوجيسايت نوع NaY زيولايت و ذلك باستبدال ايون الصوديوم بايون الامونيوم باستعمال نترات الامونيوم ومن ثم جرى تحويل ايون الامونيوم الى ايون الهيدروجين .كانت اعلى نسبة استبدال لايون الصوديوم 53.6% . درست الفعالية الحفازية للفيوجيسايت بصيغة الصوديوم NaY , و صيغة الامونيومNaNH4Y و صيغة الهيدروجين NaHY زيولايت باستخدام وحدة تجريبية بحدود درجات الحرارة بين 440 – 500 oC وسرعة فراغية بين 10 – 25 سا-1 .تم تعيين الفعالية الحفازية للفيوجيسايت بصيغة الصوديوم NaY , و صيغة الامونيومNaNH4Y و صيغة الهيدروجين NaHY زيولايت بصيغة تحويل المتفاعلات الى مختلف النواتج ونسبة الكازولين الناتج .لقد كانت نسبة تحويل المتفاعلات الى نواتج عند درجة حرارة 500 oC وسرعة فراغية 10 سا-1 50.2% و 64.1% و 69.5% على التوالي. وان انتاجية الكازولين لنفس الظروف التشغيلية كانت24.8% و 30.5% و 36.8% على التوالي .


Article
Pitting Corrosion Behavior of 304 SS and 316 SS Alloys in Aqueous Chloride and Bromide Solutions
سلوك التأكل النقري لسبائك الفولاذ المقاوم للصدأ 304 و316 في محاليل الكلور والبروم الملحية

Loading...
Loading...
Abstract

The importance of the present work falls on the pitting corrosion behavior investigation of 304 SS and 316 SS alloys in 3.5 wt% of aqueous solution bearing with chloride and bromide anion at different solutions temperature range starting from (20-50)oC due to the pitting corrosion tremendous effect on the economic, safety and materials loss due to leakage. The impact of solution temperatures on the pitting corrosion resistance at 3.5wt% (NaCl and NaBr) solutions for the 304 SS and 316 SS has been investigated utilizing the cyclic polarization techniques at the potential range -400 to1000 mV vs. SCE at 40 mV/sec scan rate followed by the surface characterization employing Scanning Electron Microscope. The results show that a significant decline in the pitting corrosion potential Ep values of both stainless steel alloys in chloride and bromide solution during temperature increase attributed to the pitting corrosion potential decreased arises from the modification of the passive film properties. The surface examination using optical microscope and scanning electron microscope prove the occurring of higher pitting density over 304 SS in chloride solution than that observed in bromide solution with a non-circular lacy cover pitfall out at the center and falls inside the pits hall in comparison to the isolated circular lacy cover pit formed on 316 SS in 3.5wt% NaBr solution at 50 oC.

يقع الاهتمام الكبير في هذا البحث على دراسة سلوك التأكل النقري لسبائك الفولاذ المقاوم للصداء 304 و316في3.5 نسبة مئوية وزنية لمحاليل مائية محملة بأيونات الكلور والبروم السالبة عند درجات حرا ره مختلفة تبدأ من 20 الى 50 درجه مئوية بسبب التأثير الهائل للتأكل النقري على الاقتصاد والسلامة وفقدان المواد الحاصل بسبب التسرب. قد تم دراسة تأثير درجة حرارة المحلول على مقاومة التأكل النقري لمحلول 3.5 نسبة مئوية وزنية لمحلول كلوريد الصوديوم وبروميد الصوديوم لسبائك الفولاذ 304 و316 باستخدام تقنينة الاستقطاب الحلقي عند معدل جهد يبدأ من -400 ملي فولت الى 1000 ملي فولت متبوعا بدراسة خواص السطح بأستخدام المجهرالالكتروني . لقد اظهرت النتائج ان انخفاض واضح في قيم جهد التأكل النقري للسبائك في محاليل الكلور والبروم بارتفاع درجة حرارة المحلول يعود السبب الى انخفاض مقاومة طبقة الحماية . فحوصات السطوح اثبتت حدوث تأكل نقري عالي الكثافة على سبيكة الفولاذ 304 في محلول كلوريد الصوديوم اعلى منه في محلول بروميد الصوديوم وان نقر كبيرة الحجم ذات غطاء شريطي متساقط من منتصف الغطاء الى داخل قعر الفجوة قد لوحظت مع سبيكة فولاذ 316 في محلول 3.5 %الكلوريد مقارنة بفجوات معزولة دائرية الشكل في محلول 3.5 % بروميد الصوديوم عند درجة حرارة 50 درجة مئوية.

Listing 1 - 3 of 3
Sort by
Narrow your search

Resource type

article (3)


Language

English (3)


Year
From To Submit

2019 (1)

2018 (1)

2013 (1)