Article
Synthesis, Characterization and Textural Analysis of Functionalized Mesoporous Silica Using Sodium Silicate as Precursor and Silicone Surfactant as Template
تحضير وتشخيص وتحليل سطح سيليكا مسامية محورة بأستخدام سيليكات الصوديوم كمصدر سيليكوني ومادة فعالة سطحيا سيليكونية كقالب

Authors: Moayed G. Jalhoom مؤيد كاصد جلهوم --- Inaam H. Ali انعام حسين علي --- Sameer H. Kareem سمير حكيم كريم
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2014 Volume: 11 Issue: 2 عدد خاص بالمؤتمر النسوي الثاني Pages: 419-428
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Three mesoporous silica with different functional group were prepared by one-step synthesis based on the simultaneous hydrolysis and condensation of sodium silicate with organo - silane in the presence of template surfactant polydimethylsiloxane - polyethyleneoxide (PDMS - PEO). The prepared materials were characterized by Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), atomic force microscopy (AFM) and nitrogen adsorption/desorption experiments. The results indicate that the preparation of methyl and phenyl functionalized silica were successful and the mass of methyl and phenyl groups bonded to the silica structure are 15, 38 mmol per gram silica. The average diameter of the silica particles are 103.51, 167.25 , and 86.41 nm while the average pore diameter are 6.7, 16.4, and 2.7 nm for unfunctionalized, methyl, and phenyl functionalized silica respectively.

تم تحضير ثلاثة سطوح لمواد مسامية سيليكونية محورة وذلك بأدخال مجاميع عضوية مختلفة بأستخدام طريقة الخطوة الواحدة المبنية على اساس التحلل المائي والتكثيف لسيليكات الصوديوم باستخدام المادة الفعالة سطحيا متعدد ثنائي مثيل سايلوكسان – متعدد اوكسيد الاثلين كقالب. تم تشخيص المواد المحضرة بأستخدام طيف الاشعة تحت الحمراء (FT-IR) والتحليل الوزني الحراري (TGA) ومجهر القوة الذرية (AFM) وقياس امتزاز/ ابتزاز النايتروجين. بينت النتائج نجاح ارتباط مجموعة المثيل والفنيل بسطح السيليكا وان الكتلة المولية لمجموعة المثيل والفنيل كانت 15 و 35 ملي مول لكل غرام من السليكاعلى التوالي. اما معدل قطر الدقائق فكان 103.51 ، 167.25 و 86.41 نانومتر بينما معدل قطر المسام فكان 6.7 ، 16.4 و 2.7 نانومتر لكل من السيليكا غير المحورة والمحورة بمجموعة المثيل ومجموعة الفنيل على التوالي.


Article
PREPARATION AND ADSORPTION STUDY (MONO AND DI- VALENT IONS) OF SELECTED TYPES OF ZSM-ZEOLITES.
دراسة تحضير وامتصاص (ايونات أحادية وثنائية) لبعض أنواع الزيولايت المنقاة

Loading...
Loading...
Abstract

Experimental studies have been carried out on three types of crystalline zeolites which were prepared and used as supports catalysts. All were synthesized in the laboratory (ZSM-5, -11, and –23) with SiO2/Al2O3 ratio of 37, 86 and 94 respectively. The adsorption process was investigated to characterize the catalysts performance toward adsorption parameters (percent of extraction and distribution factor). The performance of catalysts was studied over the range of temperature (room, 50 and 80 ºC) for mono and di-valent ions respectively (H+, Li+, K+, Rb+, Cs+, Sr+2 and Ba+2). The prepared catalysts exhibited that the percent of extraction and distribution factor for both mono and di-valent ions (H+, Li+, K+, Rb+, Cs+, Sr+2, and Ba+2) used on adsorption increase with increasing temperature and also showed different to the framework structure and type of ions used. The maximum percent of extraction and distribution factor is in the order ZSM-11˃ ZSM-5˃ ZSM-23 respectively.

تـضمن البحث اعداد دراســة شاملة عمليــة لثلاثة انواع من الزيولايتات واستخدمت كحوامل٬ جميع هذه الانواع تم تحضيرها في المختبر وهي (ZSM-5, -11, and –23) ٬ حيث كانت نسبة السيلكا / الالومينا لهذه الانواع من الزيولايتات هي (94, 86, 37) على التوالي. تم خلال البحث دراســة معاملات الامتصاص (معامل الاستخلاص ومعامل التوزيع للايونات) لعملية الامتصاص للعوامل المساعدة (الزيولايتات) المحضرة. وقد حسبت معاملات الامتصاص (معامل الاستخلاص ومعامل التوزيع للايونات) على مدى درجات حرارة (درجة حرارة الغرفة,50, 80 مº) بالنسبة الى الايونات الاحادية والايونات الثنائية على التوالي وهي (الهيدروجين, الليثيوم, البوتاسيوم, الربديوم, السيزيوم, والسترونيوم, والباريوم). كذلك بينت النتائج أن معامل الاستخلاص والتوزيع للأيونات المستخدمة في عملية الامتصاص كمتغيرات للأمتصاص تختلف تبعا لكل من البناء التركيبي للزيولايت وكذلك نوع الأيون المستخدم. بينت النتائج ان معامل الاستخلاص والتوزيع للايونات المستخدمة في عملية الامتصاص للزيولايتات المستخدمة كانت كالتاليZSM-11˃ ZSM-5˃ ZSM-23