Galvanic Corrosion of Carbon Steel –Copper in Aerated H2SO4 Under Agitation Conditions
التآكل الكلفاني للكاربون الفولاذي-نحاس في محلولالكبريتيك وفي ظروف الخلط بوجود الهواء

Authors: Muayad F. Hamad --- Huda D.Abdul Kader --- Basim O. Hasan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 9 Part (A) Engineering Pages: 2107-2118
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Galvanic and free corrosion experiments on carbon steel-copper couple in 3% H2SO4in the presence of NaCl salts were carried out under different operating conditions. The effect of temperature, agitation speed, and air bubbling (O2 concentration) on the free and galvanic corrosion was studied and discussed. The galvanic corrosion was investigated by both weight loss method and by determining the galvanic currents using zero resistance ammeter (ZRA). The results revealed that increasing temperature leads to increase the galvanic corrosion rate and also the free corrosion rate of each metal. Increasing agitation velocity enhanced the galvanic corrosion rate in a manner depending on temperature. The presence of air bubbling increased the corrosion rate and galvanic currents at low air pumping rate, while, at high pumping rate, air bubbling decreased the corrosion rate.

تم اجراء تجارب على عملية التآكل لكل من الحديد والنحاس بصورة منفردة وعند ربطهما معا في محلول ملحي من حامض الكبريتيك 3% وفي ظروف تشغيلية مختلفة وتم دراسة ومناقشة تأثير درجة الحرارة، سرعة الخلط، تركيز الاوكسجين المذاب على معدل التآكل الكلفاني.تم قياس معدل التآكل الكلفاني بطريقتين فقدان الوزن وقياس تيارات التآكل باستخدام الاميتر الصفري. اثبتت النتائج ان زيادة درجة الحرارة يؤدي الى زيادة معدل التآكل الكلفاني وايضا معدل التآكل لكل معدن على حدى. وكذلك فان زيادة سرعة الخلط يسبب زيادة في معدل التآكل الكلفاني اعتمادا على درجة الحرارة.ان زيادة نسبة الاوكسجين المذاب يسبب زيادة في معدل التآكل وكذلك تيارات التآكل الكلفاني عند معدل ضخ الهواء الواطىء بينما زيادة معدل ضخ الهواء اكثر يسبب تقليل في معدل التآكل عند سرع الخلط العالية.


Article
Enhancement of Heat Transfer using Aluminum Oxide Nanofluid on Smooth and Finned Surfaces with COMSOL Multiphysics Simulation in Turbulent Flow

Authors: Hasan S. Majdi --- Hussein A. Alabdly --- Muayad F. Hamad --- Basim O. Hasan --- et al.
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2019 Volume: 22 Issue: 1 Pages: 44-54
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

Both surface extension and nanofluid methods were used to enhance the heat transfer in a double pipe heat exchanger under turbulent flow conditions. Aluminum oxide nanoparticles were used with different concentrations(0.6-3 g/l)in hot water to increase the heat transfer rate on smooth tube and circular fins tube for a range of Reynolds number4240-19790. The simulation was also performed to predict the heat transfer coefficient and temperature profile for selected conditions in which COMSOL Multiphysics is used. The experimental results revealed that the heat transfer enhancement by both circular fin and nanofluid exhibited an increasing trend with Reynolds number and nanofluid concentration. The conjoint effect of Al2O3 of 3 g/l concentration and circular fin provided largest heat transfer enhancement of 53% for the highest Re investigated. Simulation results showed reasonable agreement with the experimental values of heat transfer coefficient. The simulation showed that the presence of nanofluid on finned surface influenced the temperature profile indicating the increased heat transfer rate.


Article
Corrosion of Carbon Steel in Oxygen and NaCl Concentration Cells: the Influence of Solution Temperature and Aeration
تاكل الفولاذ الكاربوني في خلايا تركيز الاوكسجين وكلوريد الصوديوم :تاثير درجة حرارة المحلول والتهوية

Loading...
Loading...
Abstract

Corrosion rate tests were carried out on carbon steel under concentration cells conditions of oxygen and sodium chloride. The effect of aeration in one compartment on the corrosion rate of both coupled metals was determined. In addition, the effects of time and temperatures on the corrosion rate of both coupled metals and galvanic currents between them were investigated. Corrosion potentials for the whole range of operating conditions under concentration cell conditions were also studied. The results showed that under aeration condition, the formation of concentration cell caused a considerable corrosion rate of the Carbon steel specimens coupled in different concentrations of O2 and NaCl due to the galvanic effect. Aerating one compartment caused a noticeable increase in the corrosion rate of the coupled specimen in the other compartment due to the galvanic effect. Increasing temperature caused unstable trends in the free and galvanic corrosion potentials. Increasing the temperature led to an increase in the corrosion rate for both metals.

اجريت عملية قياس معدل التاكل للحديد الفولاذي تحت ظروف خلايا التركيز للاوكسجين وملح كلوريد الصوديوم. وتم دراسة تاثير عامل التهوية لاحد اجزاء الخلية على معدل التاكل لكلا المعدنين المربوطين بالاضافة الى ذلك تم دراسة تاثير الوقت ودرجات الحرارة على معدل التاكل لكلا المعدنين المربوطين وايضا تم قياس التيارات الكلفانية بينهما .تم قياس ودراسة جهود التاكل للمدى الكلي للظروف التشغيلية لظروف خلية التركيز.اظهرت النتائج انه في حالة استخدام التهوية فان تَكُون خلية التركيز يسبب زيادة معدل التاكل للعينات المربوطة وفي تراكيز مختلفة للاوكسجين وملح كلوريد الصوديوم بسبب التاثير الكلفاني. استخدام التهوية لاحد اجزاء الخلية يسبب زيادة ملحوظة في معدل التاكل للعينة المربوطة في الطرف الاخر من الخلية نتيجة التاثير الكلفاني. زيادة درجة الحرارة يؤدي الى اتجاه غير مستقر في جهود التاكل الكلفانية والحرة وان زيادة درجة الحرارة يؤدي الى زيادة معدل التاكل الكلي للمعدنين .