Synergistic Effect of Some Inorganic Corrosion Inhibitors for Carbon Steel in Cooling Water
تأثير اضافة خليط متجانس من مثبطات التأكل اللاعضوية على الفولاذ الكاربوني في ابراج التبريد

Authors: Mudhaffar Y. Hussein مظفر يعقوب حسين --- Haider J.Mohammed حيدر جاسم محمد --- Alaa A. Nagy ألاء عبدالزهرة ناجي
Journal: Basrah Journal for Engineering Science مجلة البصرة للعلوم الهندسية ISSN: Print: 18146120; Online: 23118385 Year: 2012 Volume: 12 Issue: 2 Pages: 81-88
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

The current approach to cooling water treatment is to use a multi – component inhibitors. Coolingwater formulations containing mixtures of inhibitors usually offer better and increased protection toferrous metals than similar concentrations of either of the individual components. Such mixtures aresynergistic in their action .But; the synergistic effects between nitrites, molybdates and inorganicphosphate were not investigated until recently. A weight loss technique was used to investigate suchmixture and to optimize the concentrations of the components in the blend.Consequently; anefficient and effective blend was developed as a corrosion inhibitor for carbon steel in aerated Al–Daura refinery re-circulating cooling water in the pH range 6.75 to 7.25. The preferredconcentrations of components in the multi- component inhibitor blend (as ppm ) were: (SN + SM):SHMP = 800: 20 with SN: SM weight ratio =3:2.The reduction in corrosion rate was 97.6 % .

السياق الحالي في معاملة مياه التبريد هو باستخدام مثبطات متعددة العناصر. خليط مثبط التآكل هذا يمنح وقاية أحسن وأكثر للمعادن الحديدية مما يمنحهأي من عناصر الخليط لوحده وبنفس تركيز الخليط . هذه التراكيب متدائبة في عملها ، ولكن لم يتم دراسة التأثيرات المتدائبة مابين النتريتات والموليبداتوالفوسفات المتعددة الغير عضوية إلا في الفترة الاخيره . تم استخدام طريقة فقدان الوزن لدراسة هذا الخليط وإيجاد التركيز الأمثل لعناصره. وبناء عليه تم7.25 . إن افضل تركيز - تطوير خليط مثبط تآكل كفوء وفعال للحد من تاكل الفولاذ ألكاربوني في مياه تبريد مصفى الدورة في مدى حامضية 6.7520 ،وان النسبة : لعناصر خليط مثبط التآكل (جزء بالمليون ) هو : ( نتريت الصوديوم +موليبدات الصوديوم ) : فوسفات الصوديوم السداسية = 80097 %باستخدام هذا الخليط . . الوزنية لنتريت الصوديوم إلى موليبدات الصوديوم تساوي 2:3 . تم تقليل معدل التآكل بنسبة

Keywords


Article
دراسة تأثير إضافة الزجاج على الخواص الفيزيائية للبوليمر PVC والمتراكب PVC/PMMA
دراسة تأثير إضافة الزجاج على الخواص الفيزيائية للبوليمر PVC والمتراكب PVC/PMMA

Loading...
Loading...
Abstract

Thermal analysis techniques were conducted for testing and evaluation of different polymeric samples. Pure samples (such as PVC and PMMA) and composites (with soda-lime glass; powder as filler ) were examined and tested for Tg, thermal expansion and Young modulus (E). Two updating instruments where used for this purpose. Differential scanning calometry (DSC) for pure polymers and thermomechanical analyzer (TMA) for composites. Differential scanning calometry (DSC) testing for sample of polyvinyle chloride (PVC) explain decrease of glass temperature (Tg) from (80.6°C) to (31°C) for the same polymer solved by (THF) solvent and dry it at (100°C). Thermomechanical analysis (TMA) for (PVC/glass) composites appears increase of glass temperature (Tg) with high decrease of Young modulus (E) and transform its mechanical properties from elastic to plastic. Adding the polymer poly mathylemethacrylate to composites (PVC/glass) was lightly effect to glass transition (Tg) and elastic modulus at low ratio of (PMMA) in composite, while the composite (PVC/PMMA/glass) appears elastomer properties when the (PMMA) ratio was 37% in in composite.

الفحوص الحرارية بواسطة التحليل الحراري المسعري DSC)) لعينات البوليمر بولي كلوريد الفنايل (PVC) أظهرت انخفاض في درجة حرارة التحول الزجاجي ((Tg من (80.6) °م الى (31)°م بعد إذابته بواسطة المذيب تتراهيدرفيوران ((THF ومن ثم تجفيفه بدرجة حرارة (100) °م . أما متراكبات البوليمر(PVC)مع الزجاج (PVC/glass)فقد أظهرت التحاليل الحرارية الميكانيكية (TMA) لها , ارتفاع في درجة حرارة التحول الزجاجي (Tg) مع انحدار كبير في قيم معامل يونك (E) لدرجة حرارة أكبر من Tg وتحول المتراكب من الصفة المرنة الى الصفة اللدنة. إن تأثير إضافة البوليمر بولي مثيل ميثا اكريلات (PMMA) بنسب واطئة إلى المتراكب ( (PVC/glassكان طفيفا" على درجة التحول الزجاجي (Tg) ومعامل يونك في حين إن تحول المتراكب (PVC/PMMA/glass) من الصفة اللدنة الى الصفة المطاطية كان واضحا" عندما تكون نسبة البوليمر PMMA)) مقدارها ( 5.37 %) من المتراكب. هذه الصفة المطاطية المميزة لهذا المتراكب يمكن ان تفتح أفاقا جديدة في مجال بحوث تحول المواد البوليميرية.