Studying the Effect of Annealing Temperature on some Physical Properties of In2O3 Thin Films

Authors: Duaa A. Mohammed --- Muslim F. Jawad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 2 Part (B) Engineering Pages: 124-127
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this study, In2O3 thin films were deposited on quartz substrates bypulsed laser deposition technique at room temperature and followed bythermally annealing at 300℃, 400℃ and 500℃ for 1 hour. The optical bandgap was found to increase with the annealing temperature from 3.5 to 3.85 eVand the transmittance was observed above 90%. XRD results show that the filmsare polycrystalline in nature and crystallizes with preferred orientation (222).SEM images show that the films are high homogenous and they containeduniformly distributed small grains.


Article
Study the Effect of oblique Deposition on Electrical and Thermoelectric Properties of Zn thin films.

Authors: Wafaa K. Khalef --- Muslim F.Jawad --- Ali M .Mousa
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2012 Issue: 1 Pages: 666-690
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The effect of deposition angle on the electrical and thermoelectric properties of deposited thin zinc film was studied. The films was deposited using oblique angle deposition method (OAD) by vaccum evaporation with resistive heating technique at different deposition angles (0, 50, 60, 70and 80). Electrical properties revealed a dependence on deposition angle, dark conductivity decreases from 7.5×104 to1.5 × 104 (Ω cm) −1 when deposition angle increases from 0◦ to 80◦. I-V characteristic shows ohmic behavior and the dark current decreases with increases deposition angle. The decrease in electrical conductivity is mainly due the columnar structure accompyined oblique deposition films. Thermoelectric properties were studied, the seeback coefficient, figure of merit, and power factor (PF) dependence on deposition angle (Ө◦), and the Seeback coefficient shows a positive value.

في هذا البحث تمت دراسة تاثير زاوية الترسيب على الخصائص الكهربائية والكهروحرارية لاغشية الخارصين(Zn) المرسبة بتقنية الترسيب المائل (oblique angle deposition technique) بالمقاومة الحرارية في الفراغ و بزوايا مختلفة (80⁰ ,50⁰,60⁰,70⁰ ,◦0 ) . حيث وجد ان الخصائص الكهربائية دالة لزاوية الترسيب .خصائص تيار –جهد اظهرت التصرف الاومي و التيار يقل مع زيادة زاوية الترسيب , كذلك تناقص التوصيلية الكهربائية من7.5×104 to 1.5 × 104 (Ω cm)−1 مع زيادة زاوية الترسيب من 0◦ الى 80◦, وذالك بسبب زيادة الانماء العمودي الناتج عن الترسيب بالوضع المائل , مما يؤدي الى زيادة مقاومة الغشاء , وبالتالي نقصان التوصيلية .في هذا البحث ,تم دراسة الخصائص الكهروحرارية لاغشية الخارصين المرسبة بالوضع المائل . اظهرت نتائج الخصائص الكهروحرارية ان معامل سيبكSeeback Coefficient ,معامل النوعية Figure of Merit ,وعامل القدرةpower factor دالة لزاوية الترسيب , وان قيم معامل سيبك كانت موجبة لجميع النماذج.


Article
Study the Effect of Deposition Angle on Structural Properties of Zn thin films
دراسة تاثيرزاوية الترسيب على الخصائص التركيبية لاغشية الخارصين

Authors: Ali M .Mousa --- Muslim F.Jawad --- Wafaa K. Khalef
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2012 Issue: 3 Pages: 32-53
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The effect of deposition angle on the structural properties of deposited Zn thin metallic film was studied. The films were deposited obliquely at different angles (0º, 50º, 60º, 70ºand 80º) by vaccum evaporation with resistive heating technique at different deposition angles. XRD technique used to study the crystalline structure of these films .confirm the polycrystalline nature of these films and the higher intensity accompanied that deposited with (70˚). Some structural parameters such as grain size, micro strain, shape factor, number of layers as a function of deposition angle were calculated. The surface morphology of the deposited materials has been studied using atomic force microscopes (AFM) and optical reflection microscope. The AFM results revel an increase in the film's roughness from (33.7 to 39.2) nm when Ө◦ change from 0◦ to 80◦. Reflection microscope results showed that the smoothness and homogeneity of the films are decreasing with increasing the deposition angle Ө˚, and the surface roughness increased with increasing angle.

في هذا البحث تمت دراسة تاثير زاوية الترسيب على الخصائص التركيبية لاغشية الخارصين(Zn) المعدنية المرسبة بتقنية الترسيب المائل (oblique angle deposition technique) بالمقاومةالحرارية في الفراغ و بزوايا مختلفة (º80 , º 50,60,70 , º 0) . تم استخدام تقنية حيود الاشعة السينية لقياس الخصائص التركيبية ,وظهر ان غشاء الخارصين هو من النوع المتعدد البلورات وان الترسيب بزاوية (º 70 ) اعطى اعظم شدة حيود . بالإضافة إلى ذلك فقد تم حساب بعض الخصائص التركيبيه مثل الحجم الحبيبي والإجهاد المايكروي وعامل الشكل وعدد الطبقات بدلاله تغيير زاوية الترسيب وتأثير ذلك على هذه الخصائص. استخدم مجهر القوة الذري(AFM ) للتحليل السطحي لاغشية المواد المرسبة بشكل رئيسي بالاضافة الى استخدام المجهر البصري العاكس. اظهرت نتائج التركيب السطحي للاغشية المرسبة زيادة في خشونة السطح من (33.7 -39.2 ) نانومتر لمادة الخارصين عندما تزداد زاوية الترسيب من(º0-º80). واظهرت نتائج المجهر الضوئي هنالك نقصان في نعومة وانتظامية سطح الغشاء مع زيادة زاوية الترسيب , وان خشونة السطح تزداد مع زيادة زاوية الترسيب .