Article
Surface Preparation of (2024-T4) AluminumAlloy by ElectrolessPlating

Authors: Nabaa S. Radhi --- Baraaalkhaqani
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 8
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study dealt with the process of coating (immersion) and the factors affecting this process stability of the solution and change the time andtemperature of immersion. In this study, aluminum alloy (2024-T4) was applied with a solution consisting of zinc oxide and sodium hydroxide (81g/lNaOH+81 g/lZnO). Thus, zinc sulphate formed by immersing the sample with nitric acid solution (50%HNO3+50%water). Then immersed in distilled water. The immersion process was carried out at a different temperature between(25, 55 and 65) °C and different time periods. The results showed an increase in the growth of the deposition layer with increasing duration of the sample and the electrical resistance of the samples and for the same periods.A correlation was drawn between time change and oxide layer growth. Curvature growth was shown with increasing time period for sample exposure to air. The correlation between electrical resistance and time period change was also determined. Simulation between the experimental results and theoretical calculated by using ANSYS version 15. Finally, to confirm the formation and growth of the oxide layer draw by using MATLAB version 15A, Topographic test was examined and XRD.

تهدف الدراسة الحالية الى عملية تغطية (بالغمر البسيط)، ان العوامل المؤثرة على هذه العملية بثبوت المحلول وتغير درجة الحرارة وزمن الغمر. في الدراسة الحالية استخدمت سبيكة الالمنيوم من نوع (2024-T4) وغمرت بمحلول يتكون من (81 g/l NaOH+81 g/l ZnO). بظروف درجة حرارة تراوحت (25,55 and 65) °C وزمن غمر تراوح min (5, 10, 15 and 30) تخرج العينات حسب ظروف الترسيب من زمن ودرجة حرارة تغسل بالماء المقطر ثم تغمر في محلول مخفف من حامض النتريك (50 % HNO3+50%water ) تبقى العينة لحين انتهاء التفاعل الحاصل بين الزنك والحامض من (10-15) ثانية تؤخذ النماذج وتغسل بالماء المقطر وتجفف بتيار من الهواء الساخن ثم توزن نستمر بأخذ قراءات الوزن مع الزمن كل يوم مدة 15 يوم ونحسب مقدار الزيادة بالوزن مع الزمن الذي يمثل معدل نمو طبقة الاوكسيد، كما درسنا مقدار الموصلية الكهربائية مع الزمن لكل عينة، رسمت المخططات باستخدام برنامج MATLAB version 15A، اخيرا اجري اختبار طوبوغرافية السطح وحيود الاشعة السينية. تم عمل محاكاة للنماذج المطلية باستخدام برنامج ANSYS version 15 لدراسة السلوك الميكانيكي لطبقة الطلاء.


Article
A Review for Functionally Gradient Materials Processesand Useful Application

Author: Nabaa S. Radhi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 9 Pages: 42-47
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In the science of materials, the term Functionally Graded Materials (FGMs) which could be recognized by the gradual changes in structure and composition leading to variation in the characterization of materials. (FGMs) is considered one of the recent development of composite materials to enhance the strengths and reduce the weaknesses of these materials. (FGMs) were used for the first tiMe in Japan in 1984 via an airplane project because these materials could be used and designed for many roles and applications. The reasons that make (FGMs) are multi-function materials due to the variation in the chemical composition, microstructure and design features depending on the requirements. In this review,the functionally graded materials are studied on many different sides such as the application (the field of implementation) of this new technology and the reason of each use. Moreover, discuss the manufacturing processes for functionally graded materials and discuss the reason of choosing each process. On the other hands, discuss the limitation of the using functionally graded materials were taking in the consideration.

المواد المتدرجة وظيفيا (FGM) هي أجيال جديدة من المواد المركبة حيث يتم تغيير خصائصها خطيا وفقا للتغير في التركيب مما يؤدي الى تغيير خواص المادة الناتجة. تعتبر المواد المتدرجة وظيفياًالجيل الجديد من المواد المركبة مع تطورات لزيادة المقاومة والتخلص من عيوب هذه المواد. استخدمت المواد المتدرجة لاول مرة في اليابان في عام 1984 في الطائرات وبما ان هذه المواد تمتلك خواص تصميم مميزة اهلها للقيام بادوار وتطبيقات كثيرة. هذه الاسباب جعلت المواد المتدرجة متعددت الوظائف عند تغيير التركيب الكيميائي، او البنية المجهرية او التصميماعتمادا على متطلبات الاستخدام، تطرق المقال الى طرق تصنيع هذه المواد واسباب الاستخدام. اضافة الى ذلك ناقش المقال عمليات تصنيع المواد المتدرجة واسباب اختيار كل طريقة. من جانب اخر ناقش المحددات من استخدام المواد المتدرجة.


Article
Investigation the Coating of Hydroxyapatite on Titanium Substrateby Pulse Laser Deposition

Authors: Rasha Safaa Hadi --- Haydar H. Jamal Al-deen --- Nabaa S. Radhi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 10 Pages: 299-311
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study investigated and prepared a coating for surgical implants by using hydroxyapatite (HA) empowers characteristic bone that developed at a medium for prosthetic the parts of human body. HA is the generally manufactured from both Calcium (Ca) and Phosphate (P) to produce (Ca10(PO4)6(OH)2) that used as a base material for covering mineral embeds because of its incredible biocompatibility and comparable the synthesis and structure to sclerous tissues of the human body. HA, coatings on titanium substrates have been produced by Pulses laser deposition (PLD) techniques. HA used in this search pressed at pressure (150MPa) with particle size (2.745 µm) and used as a target in coating by (PLD) techniques. Surface characterization studies of the coatings such as XRD, SEM, AFM and EDX to detect the amount of (Ca) and (P) in coating layer were carried out. Then test the micro-hardness, surface roughness for HA coating .Corrosion behavior for uncoated and coated samples with various number of pulses in Hank’s solution by using OCP and the potentially static polarization test were achieved also, , in this test we obtained a greatly improved in corrosion resistance of the samples B1 after coating by 99.88%.

بحثت هذه الدراسة وأعدت طلاء مركب للمزروعات الجراحية باستخدام المواد السيراميكيه النشطه بايولوجيا (bioactive) مثل الهيدروكسيابتايت كطلاءات للمزروعات المعدنيه التي تشجع النمو الطبيعي للعظام عند نقاط التماس بينها وبين العظم الحي. ان الهيدروكسيابتايت (Ca10(PO4)6(OH)2)) او فوسفات الكالسيوم يستخدم كطلاء للمعادن بسبب توافقيته الحياتيهالممتازه كما انه ذو هيكل مشابه للانسجه الصلبه في جسم الانسان. إن تطبيق الطلاء HA على ركائز التيتانيوم أنتجت باستخدام تقنية الترسيب بالليزر النبضي (Pulsed Laser Deposition). في هذا البحث استخدم (HA) كهدف ((Target تم كبسه عند ضغط (150MPa) مع حجم حبيبي مقداره 2.745 µm)) واستخدامه في عملية الطلاء بواسطة تقنية(PLD). أجريت عدة اختبارات لتوصيف طبقة الطلاء مثل XRDوSEM وAFM وEDX لتحديد كمية كلا من الكالسيوم (Ca) والفسفور (P) في طبقة الطلاء. وبعدها تم اختبار الصلاده وخشونة السطح لطبقه الطلاء HA)). تم اجراء اختبار التآكل باستخدام طريقة استكمال منحني تافل في محلول Hank's solution لكل النماذج المطليه وغير المطليه، حيث حصلنا في هذا الاختبار على تحسن كبير في مقاومة التآكل للعينات المطليه عند عدد نبضات 4000 نبضة بمقدار 99.88%.


Article
INVESTIGATION SOME PROPERTIES OF (ZN-NI-SIC) COMPOSITES COATING ON LOW CARBON STEEL
تحري بعض خواص طبقة الطلاء (Zn-Ni-SiC) المترسبة على نماذج من الفولاذ واطئ الكاربون

Loading...
Loading...
Abstract

This work represents an attempt to introduce further improvement on the properties of these coatings, although the (Zn-Ni) deposition is known to be an anomalous electrodeposited process , where added Ceramic materials is (silicon carbide) ,with very good mechanical properties.Carbon steel samples were coated with (Zn-Ni) and (Zn-Ni-SiC) particles with different particles size of silicon carbide once microscale (73µm) and another nanoscale (70-100nm) .After electroplating, these samples were analyzed by X-ray fluorescent to confirm all the content for each alloy.

يهدف هذا البحث لادخال تحسينات إضافية على خواص طبقة الطلاء (Zn-Ni) ، حيث تم أضافة مادة سيراميكية هي كاربيد السيليكون التي تمتاز كمثيلاتها من المواد السيراميكية بخواصها الميكانيكية الجيدة . تتضمن هذه الدراسة التحري عن بعض خواص طلاء (Zn-Ni) بعد اضافة مادة كاربيد السيليكون بحجميها المايكروي (≈73µm) والنانوي(70-100nm) المترسبة على نماذج من الفولاذ منخفض الكاربون.تضمنت الخواص المدروسة كلا من اختبار فلورة الاشعة السينية والخشونة والمسامية واختبار الصدمة الحرارية وقد ظهر تطابق بين نتائج اختبار المسامية والخشونة حيث إن هنالك علاقة بينهما إذ ان الخشونة العالية تسبب مسامية عالية وبذلك يكون تسلسل المسامية والخشونة الموجودة في طبقة الطلاء كالاتي: (Zn-Ni) >(Zn-Ni-nSiC) >(Zn-Ni-mSiC). كما أظهرت طبقة الطلاء (Zn-Ni-nSiC) نتائج جيدة في إختبار الصدمة الحرارية.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2018 (4)