Article
Properties Of Hardened Concrete Using Crushed Clay Brick As Aggregates
خصائص الخرسانة المتصلبة باستخدام مكسر الطابوق الطيني

Author: Osama M. Ghazi
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 4 Pages: 1022-1038
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This paper provides the result of an investigation to use of crushed clay brick as aggregates in producing concrete. Eight different crushed clay brick aggregate concretes were used in this investigation. Compressive strength, splitting tensile strength and pulse velocity of crushed clay brick aggregates concrete were determined and compare to natural aggregate concrete. The compressive strength of crushed clay brick aggregates concretes were always lower than the compressive strength of natural aggregates concrete regardless the age of concrete, but the crushed clay brick aggregates concrete showed better performance as the age of concrete increases and average reduction in compressive strength were 33.5% at the age of 7 days but it becomes only 20% at the age of 56 days compared to natural aggregates concrete. The splitting tensile strength of crushed clay brick aggregates concrete were always lower than natural aggregate concrete, the reduction in splitting tensile strength of crushed clay brick aggregates concrete is ranging between 11 and 26% with an average reduction of about 18.5% compared to natural aggregates concrete. The pulse velocity of crushed clay brick aggregates concrete were also lower than natural aggregates concrete, the reduction in pulse velocity of crashed clay brick aggregates concrete is ranging between 6 and 22% with an average reduction of about 14% compared to natural aggregates concrete.

يبين هذا البحث نتائج استخدام مكسر الطابوق الطيني كركام في إنتاج الخرسانة ثمانية نسب من مكسر الطابوق الطيني استخدمت في إنتاج الخرسانة . تم فحص مقاومة الانضغاط باعمار (56,28,7) مقاومة الشد غير المباشر بعمر 28 يوم وفحص سرعة الذبذبات فوق الصوتية بعمر 28 يوم ايضاً لخرسانة مكسر الطابوق الطيني ومقارنتها مع خرسانة الركام الاعتيادي ووجد إن مقاومة الانضغاط لخرسانة مكسر الطابوق الطيني كانت دائماً أقل من مقاومة الانضغاط لخرسانة الركام الطبيعي بغض النظر عن عمر الخرسانة لكن وجد ايضاً أن مقاومة الانضغاط لخرسانة مكسر الطابوق الطيني تزداد مع تقدم عمر الخرسانة ، حيث وجد أن معدل انخفاض مقاومة الانضغاط هي 33.5% بعمر 7 أيام ولكنها تصبح 20% بعمر 56 يوم مقارنة بخرسانة الركام الطبيعي . أما مقاومة الشد غير المباشر لخرسانة مكسر الطابوق الطيني كانت هي الاخرى أقل بنسبة تتراوح ما بين 26%) - 11) أي بمعدل % 18.5مقارنة بخرسانة الركام الاعتيادي . في حين كان فحص سرعة الذبذبات فوق الصوتية لخرسانة مكسر الطابوق الطيني أقل من سرعة الذبذبات لخرسانة الركام الطبيعي و كانت نسبة الانخفاض تتراوح ما بين (6-22%)أي بمعدل 14%


Article
The Effect of Elevated Temperature of Compressive Strength of Steel Fiber Concrete

Author: Osama M. Ghazi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2013 Volume: 21 Issue: 3 Pages: 1006-1012
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This study presents the benefit gained from using steel fiber reinforcement on concrete mixture. The effect of fire on compressive strength is investigated. Two different tests, one of them is the non destructive test which is the ultrasonic pulse velocity (UPV) test and the other is the destructive compression test, are carried out using (10cm) cubes. Forty-eight cubes (half of them are with steel fiber reinforcement of fiber/concrete ratio of (0.01) by volume and the remaining cubes are without fiber reinforcement) are heated to temperature levels of (100,200,300,400,500,600 and 700°C). Then after that specimens are air cooled and (UPV) test is done, the specimens are destructively tested. The results indicated that the addition of steel fiber increases the compressive strength at all tested heating levels with a maximum percentage increase of (56.9%) at a temperature level of (500°C), in spite of that they have the same behavior but the residual compressive strength decreases with the addition of steel fiber for the tested heating levels lower than (400°C) and increases for the heating levels above this degree

الدراسة الحالية تسلط الضوء على الفائدة الحاصلة من تسليح الألياف الفولاذية في تكنولوجيا الخرسانة حيث بحث تاثير الحرارة على مقاومة انضغاطها.اجري نوعان من الفحص احدهما لااتلافي وهو فحص سرعة الأمواج فوق الصوتية (UPV)والأخر إتلافي باستعمال نماذج مكعبة بطول ضلع(10سم).تم تسخين(48) نموذج (نصفها مقواة بألياف الفولاذ بنسبة حجمية للالياف الفولاذية إلى الخرسانة مقدارها(0.01)والنماذج الأخرى المتبقية غير مقواة) إلى مستويات من درجات الحرارة هي(100و200و300و400و500و600و700)درجة سيليزية.فحصت النماذج لا اتلافيا بعد تبريدها بتعريضها للهواء ثم فحصت اتلافيا.بينت النتائج ان إضافة الألياف الفولاذية يزيد من مقاومة الانضغاط في كل مستويات درجات الحرارة التي قيست فيها باعلى نسبة زيادة مقدارها (56.9%) من تلك غير المقواة عند درجة حرارة (500) درجة سيليزية بالرغم من ان لهما نفس السلوك ولكن نسبة ما تبقى من المقاومة بعد الحرق من المقاومة الاصلية يقل باضافة الالياف الفولاذية عند كل مستويات درجات الحرارة الأقل من (400)درجة سيليزية ولكنها تزداد بعد تلك الدرجة.