Article
Study the Effect of Nano-Al2O3 and Fiber Glass on Mechanical and Physical Properties of PMMA Composites for Prosthetic Denture

Author: Qahtan A. Hamad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 7 Part (A) Engineering Pages: 715-722
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In the present research, investigate the effect of adding some reinforcing materials which include nano-aluminum oxide (nano-Al2O3) particles that added with different volume fractions of (1%, 2%, 3% and 4%), and random fiber glass that added with fix volume fractions of (4%), into the PMMA matrix as new cold cure resin, and study some mechanical and physical properties of these hybrid laminated composite as prosthesis denture base material. Specimens’ of this project were prepared by using (Hand Lay-Up) method to form a hybrid laminated composites materials. The mechanical tests were performed on these specimens include (tensile test, impact test, flexural test and hardness test), while the physical test was thermal behavior test. Results of this study showed the values of (tensile strength, hardness, thermal conductivity and thermal diffusivity) properties increased when adding the (nano-Al2O3) particles in PMMA composite materials for prosthetic denture base materials. While, the values of impact strength and flexural strength properties were decreased.


Article
Numerically and Theoretically Studying of the Upper Composite Complete Prosthetic Denture
دراسة تحليلية ونظرية لطقم الاسنان الاصطناعي الكامل المتراكب العلوي

Authors: Sihama I. Salih --- Jawad K. Oleiwi --- Qahtan A. Hamad
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 5 Part (A) Engineering Pages: 1023-1037
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current study focused on the manufacturing and development properties of upper prosthesis complete denture from composite materials with the basis cold cured resin of poly methyl methacrylate as new fluid resin and reinforced materials by two different types of particles (nano-hydroxyapatite (nHA), micro zirconia (ZrO2)), that added with different volume fractions of (1%, 2% and 3%), and the different types of woven fibers (Glass fiber, Kevlar fiber), it were added with a fixed volume fraction of (5%) to PMMA composites.Specimens’ consist of a six groups where prepared by using (Hand Lay-Up) method from the composites materials and hybrid laminated composites materials. This research includes theoretical and numerical studies by using finite element method to confirming the experimental results of the effect of selected volume fractions of theseparticles and fibers on the (total deformation distribution, equivalent elastic strain and equivalent Von Mises stress) of the composite prosthetic dentures.The theoretical part included calculations the values of theoretical safety factor and Poisson's ratio. While the numerical part based on finite element method (F.E.M), which was performed by using program (ANSYS-15) to analyze the prepared of denture composite materials and evaluate its characteristics which represent total deformation distribution, equivalent stress and equivalent elastic strain. This was performed by obtaining twenty one models for the PMMA composite dental prostheses which were treated as three dimension structure. The numerical results of the F.E.A showed coincided with some of the experimental results.

في هذا البحث تم التركيز على تصنيعوتطوير مواصفات طقم أسنان أصطناعي كامل علوي من مواد متراكبة. وقد حضرت هذه المواد المتراكبة من راتنج البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية تم اضافتهما بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج والياف الكفلر والتي تمت اضافتها الى المواد المتراكبةبكسر حجمي ثابت هو (%5)الى المواد المتراكبة. تتكون العينات من ستة مجاميع تم تحضيرها باستخدام طريقة الصب اليدوي تمثل مواد متراكبة ومواد متراكبة طبائقية هجينية. تضمن البحث دراسة نظرية وتحليلية باستخدام طريقة العناصر المحددة للتاكد من النتائج العمليةلتأثير الكسور الحجمية المختارة لهذه الألياف والدقائق على (توزيع التشوه الكلي، الانفعال المرن المكافيء والاجهاد المكافيء) لأطقام الاسنان الأصطناعية المتراكبة.تضمنتنتائج الجانب النظري حساب قيم معامل الامان النظريونسبة بويزن. أما الجانب التحليلي فيتضمن أستخدام أستخدام طريقة العناصر المحددة والتي أنجزت بأستخدام برنامج(ANSYS-15) لغرض تحليل المواد المتراكبة المحضرة لطقم الأسنان وحساب خصائصه والتي تمثل (توزيع التشوه الكلي، الاجهاد المكافيء والانفعال المرن المكافيء)، وقد تم انجاز ذلك عن طريق الحصول على واحد وعشرون موديل لطقم الاسنان الأصطناعي باعتبارها أطقام أسنان متراكبة مكونة من راتنج البولي مثيل ميثا اكريليت ذات هيكل ثلاثي الابعاد، وقد أظهرت النتائج التحليلية لطريقة العناصر المحددة تطابق مع بعض النتائج العملية.


Article
Effects of Irradiation by UV- Acceleration on Mechanical Properties of Polymer Blends (Polyester: Starch)

Authors: Sihama I. Salih --- Qahtan A. Hamad --- Safaa N. Abdul Jabbar --- Najat H. Sabit
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2018 Volume: 21 Issue: 1 Pages: 147-152
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This work covers mixing of unsaturated polyester (un- polyester) with starch powders as polymer blends and study the effects of irradiation by UV-acceleration on mechanical properties of its. The unsaturated polyester was mixing by starch powders at particle size less than (45 μm) at selected weight fraction of (0, 0.5, 1, 1.5, 2, 2.5 and 3%). These properties involve ultimate tensile strength, modulus of elasticity, elongation percentage, flexural modulus, flexural strength, fracture toughness, impact strength and hardness. The results illustrate decrease in the ultimate tensile strength at and elongation percentage, while increasing modulus of elasticity, with increasing the weight ratio of starch powder to 3 % weight fraction, whereas the maximum value of hardness and flexural, impact properties happened at 1 % weight fraction for types of polymer blends.


Article
COMPARATIVE STUDY THE FLEXURAL PROPERTIES AND IMPACT STRENGTH FOR PMMA REINFORCED BY PARTICLES AND FIBERS FOR PROSTHETIC COMPLETE DENTURE BASE
دراسة مقارنة حول خصائص الانحناء ومقاومة الصدمة للبولي مثيل ميثا اكريليت المقوى بالدقائق والألياف لمادة قاعدة طقم أسنان أصطناعي كامل

Loading...
Loading...
Abstract

In the present search, attempts are made to develop the properties of PMMA resin that used for upper and lower prosthesis complete denture, by addition two different types of particles, which included: nano-hydroxyapatite (nHA) particles and micro-zirconia (ZrO2) particles that added with different volume fractions of (1%, 2% and 3%) to poly methyl methacrylate (PMMA) cold cured resin as new fluid resin matrix. Also woven glass fiber kind (E-glass) and woven Kevlar fiber kind (49), it were added with a fixed volume fraction of (5%) to PMMA composites. In this work the composite prosthetic dentures specimens preparation was done by using (Hand Lay-Up) method as six groups which includes: the first group consists of PMMA resin reinforced by nHA particles, the second group consists of PMMA resin reinforced by ZrO2 particles, the third group consists of (PMMA-nHA) and glass fiber layer as laminated composite , the fourth group consists of (PMMA-ZrO2) and glass fiber layer, the fifth group consists of (PMMA-nHA) and Kevlar fiber layer and the sixth group consists of (PMMA-ZrO2) and Kevlar fiber layer.The experimental part of this study included performing many mechanical tests which, includes (Flexural, Maximum Shear Stress and Impact) tests. The result of this study showed the values of most properties increased with increasing of the volume fraction of (nHA and ZrO2) particles in polymer composite materials. While, the impact strength decreased. The ZrO2 particle and woven mat Kevlar fiber had shown greater values for the most composite materials properties for all groups’ specimens except the flexural strain.Also the results showed the maximum values for hybrid laminated composite properties (flexural modulus and impact strength) were obtained in hybrid laminated composite materials for sixth group specimens. While, the maximum value for properties (flexural strength and max shear stress) were obtained in hybrid laminated composite materials for fourth group specimens.

تم في هذا البحث أجراء عدة محاولات لغرض تطوير مواصفات راتنج البولي مثيل ميثا اكريليت المستخدم كطقم أسنان أصطناعي كامل علوي أو سفلي. وقد حضرت هذه المواد المتراكبة من البولي مثيل ميثا اكريليت على شكل راتنج سائل جديد معالج ذاتياً كمادة أساس وقد تم تقويتها بنوعين مختلفين من الدقائق تضمنت دقائق الهيدروكسي اباتايت النانوية ودقائق الزركونيا الميكروية اضيفت بكسور حجمية مختلفة هي (1%, 2% and 3%)، ونوعين مختلفين من الالياف الحصيرية الثنائية الاتجاه هي الياف الزجاج نوع (E-GLASS) والياف الكفلر نوع (49) وقد اضيفت الى المواد المتراكبة بكسر حجمي ثابت هو (%5). في هذا البحث حضرت عينات من أطقام الاسنان الأصطناعية المتراكبة بطريقة (الصب اليدوي) على شكل ستة مجاميع هي: المجموعة الاولى تضم راتنج البولي مثيل ميثا اكريليت ودقائق الهيدروكسي اباتايت النانوية، المجموعة الثانية تضم راتنج البولي مثيل ميثا اكريليت ودقائق الزركونيا، المجموعة الثالثة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الهيدروكسي اباتايت النانوية، المجموعة الرابعة تضم راتنج البولي مثيل ميثا اكريليت والياف الزجاج مع دقائق الزركونيا، المجموعة الخامسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الهيدروكسي اباتايت النانوية، المجموعة السادسة تضم راتنج البولي مثيل ميثا اكريليت والياف الكفلر مع دقائق الزركونيا.يتضمن الجزء العملي من هذا البحث اجراء العديد من الاختبارات الميكانيكية والتي شملت فحوصات (الانحناء، اجهاد القص الأعظم والصدمة(. وقد بينت النتائج بان قيم اغلب الخواص ازدادت مع زيادة الكسر الحجمي لدقائق الهيدروكسي أباتايت النانوية ودقائق الزركونيا، بينما قلت مقاومة الصدمة. وان دقائق الزركونيا والياف الكفلر الحصيرية تعطي قيم أعلى لاغلب خواص المواد المتراكبة ولكافة مجاميع العينات ماعدا الانفعال الأنحنائي. كذلك أظهرت النتائج بان اعلى قيم لخصائص (معامل الانحناء ومقاومة الصدمة) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة السادسة. بينما اعلى قيم لخصائص (مقاومة الانحناء واجهاد القص الأقصى) وجدت في المواد المتراكبة الطبائقية الهجينية لعينات المجموعة الرابعة.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (3)


Year
From To Submit

2018 (2)

2015 (2)