Article
Fabrication and Characterization of Chromium Nanotube Using (AAO) Template

Authors: Rana Afif Anaee --- Ahmed Rajih Hassan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 2 Pages: 152-159
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In the current research, the fabricating of Cr nanotubes was done by electrochemical deposition in anodic aluminum oxide (AAO) as template. Characterization of fabricated Cr nanotubes were a achieved by XRD, SEM/EDS and TEM. These techniques indicated that the deposited chromium nanotubes have high purity within experimental conditions, the peaks in XRD was good agreement with JCPDS cards, SEM images showed the growth of ordered nanotubes in one plane perpendicular to the template (AAO). The purity of fabricating nanotubes was confirmed by EDS analysis, while the produced single walled nanotubes was shown from TEM images with open ends of tubes. 60 nm as diameter was obtained for fabricating Cr nanotubes.The fabrication of Cr nanotubes suggests producing quintuple bonds (Cr ≡ Cr) to form tubes without any chance to deposit chromium as particles.

في البحث الحالي تم تصنيع Cr Nanotube بعملية الترسيب الكهروكيميائي وذلك بترسيبها على أساس من الألمنيوم المؤنود AAO كذلك تم تشخيص الأنابيب الكروم النانوية بواسطة XRD, SEM/EDS and TEM . وقد تبين من خلال هذه التقنيات إن الأنابيب الكروم النانوية كانت تمتلك نقاوة عالية جدا , ومن خلال تقنية SEM لوحظ نمو منتظم للأنابيب النانوية على مستوى عمودي للـ AAO. وكذلك يتضح ذلك من خلال تقنية TEM والتي يظهر فيها الأنابيب ذات جدار منفرد single wall بقطر مقارب إلى 60nm.


Article
Estimation the Efficiency of Nano Particles Coating on Carbon Steel by Atomization

Authors: Rana Afif Anaee --- Ahmed M. Al- Ghaban --- Douaa A. Abdullah
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 5 Part (A) Engineering Pages: 876-886
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, three nanoparticles were applied as coatings on carbon steel using atomization method (cold spraying) by airbrush.The coatings includednano Al2O3,nanoSiC and nanoZrO2 materials. The characterization of coated surfaces has been investigated by AFM and SEM. All these inspections indicated that the deposition of nanoparticles on carbon steel surface was uniform and homogeneous. Thethickness of coated layers was calculated using gravimetric method, while the particle size and roughness were measured from the analysis of atomic force microscopy.With constant conditions of coating, nano alumina coating gave the highest thickness (6.2216 nm) due to agglomeration of these particles compared with others as illustrated in SEM images. Corrosion test was performed to estimate the corrosion resistance, protection efficiency and porosity percentage which indicated the role of nano particle coating on corrosion control. These data showed that the nano alumina was better than other coatings and gave PE 99.69%.Cyclic polarization was also estimated to show the probability of pitting corrosion. The coating with alumina gave the best data for decreasing the chance of pitting corrosion.


Article
CHEMICALLY TREATED SACCHARUM AS REINFORCEMENT FOR POLYESTER COMPOSITE

Authors: Rana Afif Anaee --- Aseel Mahmmod Abdulah --- Sura Salim Ahmed
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2017 Volume: 10 Issue: 1 Pages: 81-86
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This work involves using Saccharum short fibers as reinforcement for unsaturated polyester before and after chemical treatment for fibers. The chemical treatment was done in NaOH solution with different concentrations include 0.125, 0.25, 0.375, 0.5 and 0.625 M at room temperature. The prepared composites were characterized by FTIR spectra to confirm the improvement of interaction between reinforcement and matrix through the reduction in hydrophilic groups. The investigation by FTIR showed the improving of the adhesion between reinforcement and polyester as matrix because of reduction of absorption the water. The impact toughness was tested for polymeric composites and the results indicated that the chemical treatment with NaOH led to increasing impact energy due to increasing bonding force between treated Saccharum fibers and matrix.


Article
Binary and Ternary Nanoceramic Coatings to Protect Carbon Steel in Artificial Seawater

Authors: Rana Afif Anaee --- Ahmed M. Al- Ghaban --- Douaa A. Abdullah
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2016 Volume: 34 Issue: 15 Part (A) Engineering Pages: 2854-2863
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Binary and Ternary nanoparticles coatings have been applied on carbon steel using atomization method (cold spraying) to corrosion control in seawater. Nanoparticles were included Nano Al2O3, SiC and ZrO2. The characterization of coated surfaces has been investigated by AFM and SEM in addition to calculate the coating thickness. The binary coatings deal with 50%Al2O3-50%SiC, 50%Al2O3-ZrO2 and 50%SiC-50%ZrO2, while the ternary coating was 60%Al2O3-20%SiC-20%ZrO2. The results showed that 50%Al2O3-50%SiC had the lowest thickness and most uniform distribution in AFM and SEM due to closing in particle sizes. Corrosion test achieved to estimate the corrosion resistance, protection efficiency and porosity percentage which indicated the role of Nano particle coating to corrosion control. These data showed that the Nano 50%Al2O3-50%SiC coating had the most noble corrosion potential, lowest corrosion current density (lowest corrosion rate), highest corrosion resistance, highest efficiency 99.651 % and lowest porosity percent 1.438×10-11. Cyclic polarization also estimated to show the probability for pitting corrosion. The coating with 50%Al2O3-50%SiC gave the highest breakdown potential equal to +69mV.


Article
Electrodeposition of NiCr Nanowires Using Anodic Aluminum Oxide

Authors: Rana Afif Anaee dr.rana_afif@yahoo.com --- Alaa H. Ali --- Ahmed Rajih Hassan
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2018 Volume: 26 Issue: 1 Pages: 55-59
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This research highlights fabrication of NiCr nanowires by electrochemical deposition. The deposition was achieved using anodic aluminum oxide AAO template with 70 nm diameter of pores. The anodization was performed using oxalic acid with two steps to obtain AAO template. 72.3Ni27.7Cr nanowires were obtained using nickel and chromium sulfate. The nanowires were characterized by SEM and TEM. The obtained nanowires with 70 nm diameter and 420-500 nm length.

يشير هذا البحث الى تصنيع اسلاك نانوية لسبيكة نيكل-كروم بواسطة الترسيب الكهروكيميائي. انجز الترسيب الكهروكيميائي على اساس من اوكسيد الالمنيوم المؤنود ( AAO ) ذات ثقوب نانوية قطرها ( 70 nm ). تمت عملية الانودة للالمنيوم بأستعمال حامض الاوكزالك وذلك بخطوتين من الانودة للحصول على الاساس AAO ثم تلاها ترسيب سبيكة نيكل-كروم من املاح كبريتات النيكل وكبريتات الكروم وكانت نسب العناصر الناتجة للسبيكة هي 72.3Ni27.7Cr . الاسلاك النانوية الناتجة تم تشخيصها بأستعمال المجهر الالكتروني SEM والمجهر الالكتروني TEM.ان الاسلاك النانوية الناتجة تمتلك قطر بمقدار( 70 nm ) وطول ( 420-500 nm ).


Article
Effect of tempering on thermal analysis of Al-Ti-Si alloy and its composites
تأثير المراجعة على التحلل الحراري لسبيكة المنيوم – تيتانيوم – سليكون والمواد المتراكبة العائدة لها

Authors: Rana Afif Anaee رنــا عفيف مجيد --- Wafaa Mahdi Salih وفــاء مهدي صالح --- Ban Farhan Dawood بان فرحان داود
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2016 Volume: 14 Issue: 31 Pages: 89-98
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The investigation of the effect of tempering on thermal analysis of Al-Ti-Si alloy and its composites with MgO and SiC particles was performed. Thermal analysis was performed before and after tempering by DSC scan. Optical microscopy was used to identify the phases and precipitations that may be formed in base alloy and composites. X-ray diffraction test indicated that the Al3Ti is the main phase in Al-Ti-Si alloy in addition to form Al5Ti7Si12 phase. Some chemical reactions can be occurred between reinforcements and matrix such as MgO.Al2O3 in Al-Ti/MgO, and Al4C3 and Al(OH)3 in Al-Ti/SiC composite. X-ray florescence technique is used to investigate the chemical composition of the fabricated specimens. Heat treatment (Tempering) changes the microstructure of base alloy and its composites which was assessed by DSC scan. Generally, three main peaks appeared in DSC represented by GP zone, S phase (precipitations) and dissolution of phases or precipitations. After tempering, composite with SiC particles showed better results than base alloy and composite with MgO. Since the optical microscopy revealed reforming the stable phase Al3Ti with evaporation some gases from composite. DSC analysis showed the stability ofcomposite with SiCwas up to 270oC.DSC, Al-Ti-Si alloy, Composite, SiC, MgO, Al3Ti phase, Al5Ti7Si12.

لقد تم الكشف عن تأثير المراجعة على التحليل الحراري لسبيكة المنيوم – تيتانيوم – سليكون مع مواده المتراكبة المدعمة باوكسيد المغنيسيوم وكاربيد السليكون بنسبة وزنية 1% من خلال فحص المسعر التفاضلي الحراري. اجري فحص البنية بالمجهر البصري لتشخيص الاطوار المتكونة في السبيكة الاساس والمواد المتراكبة المدعمة وقد اثبت فحص الحيود بالاشعة السينية تكون الطور الرئيسي Al3Ti بالاضافة الى تكوين الطور Al5Ti7Si12 بالاضافة الى اطور اخرى تتكون ضمن المواد المتراكبة مثل MgO.Al2O3و Al4C3 و Al(OH)3واطوار اخرى. ان المعاملة الحرارية تغير من تفاعلات التبلور والانصهار الظاهرة في فحص التحلل الحراري باستخدام المسعر الماسح التفاضلي. ان قمم التبلور الرئيسية الظاهرة في فحص التحلل الحراري هي ظهور طبقة GP وقمة الطور البيني S وقمة الاطوار غير المتماسكة. ان المادة المتراكبة المدعمة بدقائق كاربيد السليكون تظهر من خلال الفحص بالمسعر الماسح التفاضلي استقراراً حرارياً واظحاً الى حد 270 درجة مئوية.


Article
Experimental and Numerical Study of Thermal Properties for Amalgam Reinforced by NiCrMo Nanowires
دراسة نظرية وتجريبية للخواص الحرارية للملغم المقوى باسالك ثانوية ذات اساسNiCrMo

Authors: Ahmed Rajih Hassan احمد راجح حسن --- Farooq Hassan Ali --- Alaa Hassan Ali --- Rana Afif Anaee رنا عفيف
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2018 Volume: 6 Issue: 1 Pages: 20-28
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

NiCrMo nanowires with four weight percents include 0.3, 0.6, 0.9 and 1.2 wt% have been added to conventional amalgam to improve its properties especially thermal conductivity which is represented important property to reduce the sensation of root for hot and cold foods and beverages. NiCrMo nanowires were selected because they closed in composition to the known dental alloy (Ni-Cr alloy). SEM technique was used to characterize the modified structure of nanocomposites.The thermal conductivity was decreased after adding NiCrMo nanowires to amalgam and the reduction is increases with increasing wt% of nanowires, this is due to the dominance of smooth temperature dependence by nanowires which suggest a phononphonon or phonon-defect scattering.AFM inspection also was achieved to show the morphology of surface in addition to measure roughness, and the results showed the decreasing in roughness of amalgam/nanowires composites compared with amalgam due to decreasing in surface irregularities by adding nanowires. This reduction in roughness leads to decrease the accumulation of bacteria on amalgam and then reducing biocorrosion. Also, microhardness of amalgam/NWs composites was increased compared with conventional amalgam and the increment increased with increasing wt% of nanowires. The increment in microhardness is suggested the filling of vacancies within amalgam by nanowires and getting more coherent for components in amalgam especially with Hg which is the main cause of the reduction in hardness. On the other word, in present work, we improved thermal conductivity in addition to get more microhardness and less surface roughness by adding nanowires. Simulation study was achieved for thermal properties to confirm the role of NiCrMo nanowires to reduce heat

تم إضافة أربعة نسب مختلفة من األسالك النانوية المصنعة من سبيكة 1.2 NiCrM ,الحشوات الزئبقية التقليدية لتحسين خواصها وخصوصا خواص التوصيل الحرارية لتقليل تحسس جذر السن للمأكوالت او المشروبات الحارة او الباردة. وتم اختيار أسالك نانوية من سبيكة NiCrMo وذلك لكونها إحدى السبائك الطبية التي يتم استخدامها في تطبيقات األسنان.نالحظ انخفاض التوصيل الح ارري للحشوات الزئبقية بعد إضافة األسالك النانوية ويزداد االنخفاض بزيادة النسب المضافةوذلك بسبب االستطارة التي تحدث بين فوتون – فوتون او فوتون – العيوب.في فحص AFM تم دراسة طبيعة السطح لعينات الحشوات الزئبقية وقد لوحظ انخفاض الخشونة السطحية بزيادة نسبة األسالك النانوية المضافة وهذا االنخفاض في الخشونة السطحية مفيد لمنع تجمع البكتريا على سطح الحشوات الزئبقية وبذلك يقلل معدل التآكل البايلوجي , كذلك زادت نسبة الصالدة للحشوات الزئبقية بزيادة نسبة األسالك النانوية المضافة وذلك


Article
CORROSION BEHAVIOR AND ROUGHNESS OF NI-CR/AL2O3 COMPOSITES AS DENTAL RESTORATIVE
السلوك التآكلي والخشونة لمتراكبات Ni-Cr/Al2O3 كمواد تعويضية في الاسنان

Loading...
Loading...
Abstract

This work investigated on the corrosion behavior and roughness of Ni-Cr alloy as dental restorative. Alumina with three weight percentages (1, 5 and 10%) added as reinforcement to fabricate Ni-Cr/alumina composites. Corrosion behavior was tested in artificial saliva at 37+1 oC and pH=4.4. The data of corrosion indicated that the addition of alumina led to reduce the dissolution of metals in base alloy due to the enhancing of Cr2O3 passive film and producing Ni3Al phase in matrix. The roughness of surface was reduced for composites compared with base alloy (Ni-Cr) which is important factor to reduce the accumulation of bacteria on restorative materials in mouth; this reduction is due to the formation of ductile Ni3Al compared with brittle Ni2Cr3 in composites.

يتضمن البحث الحالي التقصي عن السلوك التآكلي والخشونة لسبيكة نيكل – كروم، كما اضيقت الالومينا بثلاث نسب وزنية 1 و5 و 10% كتقوية للسبيكة الاساس. اجري فحص التآكل في محلول اللعاب الصناعي عند اس هيدروجيني 4.4 ودرجة حرارة 37+1 درجة مئوية وقد اظهرت النتائج بان اضافة الالومينا يؤدي الى تقليل الذوبان المعدني للسبيكة الاساس بسبب تعزيز طبقة اوكسيد الكروم الحامية وتكوين الطور Ni3Al. كما بينتْ نتائج فحص الخشونة السطحية بان المواد المتراكبة تمتلك خشونة اقل من السبيكة الاساس وهذا ما يعد عامل اساسي لتقليل تجمع البكتريا على المواد التعويضية المستخدمة داخل الفم. ان النقصان الحاصل في الخشونة سببه تكوين Ni3Al اللدن مقارنة مع الطور Ni2Cr3 الهش.


Article
Antibacterial Inhibitor as an Expired Metoclopramide in 0.5M Phosphoric Acid
المثبط المضاد للبكتريا كميتوكلوبراميد منتهي الصلاحيه في 0.5 مولاري من حامض الفسفوريك

Loading...
Loading...
Abstract

Expired drug Metoclopramide was investigated as an antibacterial corrosion inhibitor for carbon steel in 0.5M H3PO4 solution using the electrochemical method at 30oC and 60oC. The results showed that this drug is an efficient inhibitor for carbon steel and the efficiency reached to 82.244 % for 175 ppm at 30oC and 76.146% for 225 ppm at 60oC. The adsorption of drug on carbon steel surface follows Langmuir adsorption isotherm with small values of adsorption-desorption constant. The polarization plots revealed that Metoclopramide acts as mixed-type inhibitor. Some parameters of inhibition process were calculated and discussed. The surface morphology of the carbon steel specimens was analyzed using scanning electron microscope and energy dispersive X-ray analysis. Antibacterial activity of inhibitor was also tested. Fourier-transform infrared (FTIR) spectroscopy confirmed the inhibitive role of Metoclopramide drug.

الدواء المنتهي الصلاحيه ميتوكلوبراميد تم اختباره كمثبط التأكل المضاد للبكتريا للفولاذ كاربوني في محلول 0.5 مولاري من حامض فسفوريك بأستخدام الطريقة الكهروكيميائية في 30 و 60 درجة مئوية. وأظهرت النتائج أن هذا الدواء هو مثبط فعال للفولاذ كاربوني والكفاءة وصلت إلى 82.244 % لل 175 جزء من مليون عند 30 درجه مئويه و76.146 % لل 225 جزء من مليون عند 60 درجه مئويه. امتزاز الدواء على السطح فولاذ كاربوني يتبع متساوي الحراره الامتزاز مع القيم الصغيره لثابت امتصاص الامتزاز. كشفت سير الاحداث في الاستقطاب ان ميتوكلوبراميد يعمل كمثبط من نوع المختلط . بعض معامل عمليه التثبط تم حسابها ومناقشتها. التشكل السطحي للعينات فولاذ كاربوني تم تحليلها بأستخدام المجهر المسح الألكتروني و تحليل الأشعة السينية المشتتة للطاقة. تم اختبار المثبط الفعال المضاد للبكتريا. أكد التحليل الطيفي دور المثبط للدواء ميتوكلوبراميد.

Listing 1 - 9 of 9
Sort by
Narrow your search

Resource type

article (9)


Language

English (7)

Arabic and English (1)


Year
From To Submit

2019 (1)

2018 (3)

2017 (2)

2016 (3)