Article
EFFECT OF CEMENT, LIMESTONE AND HYDRATED LIME ON SETTING TIME AND COMPRESSIVE STRENGTH OF LOCAL GYPSUM

Author: Sana Taha Abdul-Hussain
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2019 Volume: 23 Issue: 2 Pages: 120-132
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

This paper consists of studying the effect of adding different ratios of cement, limestone powder and hydrated lime on setting time and compressive strength of gypsum which available in local market which does not conform to Iraqi Standard Specification (I.Q.S) No.28/1988. The adding materials are low-cost and available in local market and can be used to improve setting time and compressive strength for gypsum which are considered as the most important properties if it used as mortar or in finishing. The adding ratios of cement were (10, 20, 30, 40 and 50) % from gypsum weight, the ratio of (50%) was the best ratio as regarded to setting time and compressive strength. They are (10.33 minutes), (8.04 N/mm2) respectively. For the limestone powder addition, the ratios were (10, 20, 30, 40, 50 and 60) % from gypsum weight. The results showed that, the ratio of (10%) was the best in compressive strength (6.2 N/mm2) and ratio of (60%) was the best in setting time. At adding hydrated lime, the ratio of addition (2.5%) gave compressive strength (7.51 N/mm2) and the ratio of (12.5%) gave setting time (14.15 min.).


Article
EFFECT OF OIL PRODUCTS ON COMPRESSIVE STRENGTH OF REACTIVE POWDER CONCRETE
تأثيرالمشتقات النفطية على مقاومة الأنضغاط لخرسانة المساحيق الفعالة

Author: Sana Taha Abdul-Hussain سنا طه عبد الحسين
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2013 Volume: 6 Issue: 4 Pages: 352-368
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The aim of this study is to investigate the effect of two of oil products (kerosene and fuel oilwhich is locally called as black oil) on compressive strength of reactive powder concrete (RPC).RPC was prepared using cement, silica fume, fine sand, steel fibers and superplasticizer to cast andtest 63 specimens of cubes with various steel fibers ratios of 0%, 1% and 2% at different exposuretimes in oil products (0, 30, 90 and 180) days. In general the results showed that RPC has goodresistance to the effect of kerosene and fuel oil. A slight decrease in compressive strength occurredas the time of exposure to the oil products increases. The RPC specimens of 2% steel fibers contenthad the lower decrease in compressive strength as a result of the denser microstructure. Thedecreasing ratio of RPC compressive strength exposed to fuel oil (1.33%) was lower than that ofkerosene (2.91%). This may be attributed to the lower viscosity of kerosene than fuel oil.

الهدف من هذه الدراسة هو التحري عن تأثير اثنين من المشتقات النفطية (النفط الابيض و نفط الوقود المعروف محليابالنفط الأسود) على مقاومة الأنضغاط لخرسانة المساحيق الفعالة. تم تحضير خرسانة المساحيق الفعالة من السمنت، الرمل الناعم،أبخرة السليكا, ألياف الحديد والملدن المتفوق لصب و فحص 63 نموذج من المكعبات بأستخدام نسب مختلفة من ألياف الحديد90 و 180 ) يوم. بشكل عام النتائج اظهرت ان ،30 ، %1 و 2%) عند اوقات تعرض مختلفة في المشتقات النفطية ( 0 ،%0)خرسانة المساحيق الفعالة ذات مقاومة جيدة لتأثيرالنفط الابيض و النفط الاسود. مقاومة الانضغاط انخفضت قليلا بزيادة زمنالتعرض للمشتقات النفطية. الخلطة التي تحتوي على 2% الياف حديد هي الاقل انخفاضا في المقاومة كنتيجة لهيكلها الاكثر كثافة.ان نسبة الانخفاض في مقاومة الانضغاط لخرسانة المساحيق الفعالة المتعرضة لنفط الوقود ( 1.33 %) أقل من تلك المتعرضةللنفط الابيض( 2.91 %). ان ذلك قد يعود لللزوجة الاقل للنفط الابيض مقارنة مع نفط الوقود


Article
Effect of Elevated Temperatures on Compressive and Tensile Strengths of Reactive Powder Concrete
تأثير ارتفاع درجات الحرارة على مقاومة الأنضغاط ومقاومة الشد لخرسانة المساحيق الفعالة

Author: . Sana Taha Abdul-Hussain سنا طه عبد الحسين
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 4 Pages: 259-278
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

An experimental investigation was conducted on the effect of elevated temperatures on mechanical properties of reactive powder concrete (RPC), mainly on compressive strength, flexural strength and splitting tensile strength. RPC was prepared using cement, silica fume, fine sand and steel fibers to cast and test 128 specimens (cubes, cylinders and prisms) with various steel fibers ratios of 0%, 1%, 2% and 3% at temperatures of 20°C, 200°C, 400°C and 600°C. Results generally show that the decrease in compressive strength, flexural strength and splitting tensile strength become larger when temperature exceeds 400°C. At 600°C the decreasing ratios were 17.8%, 38.87% and 58.58% for compressive strength, flexural strength and splitting tensile strength, respectively. Explosive spalling of RPC at elevated temperatures was also observed and discussed.

تم اجراء تحريات عملية على تأثير الأرتفاع في درجات الحرارة على الخصائص الميكانيكية لخرسانة المساحيق الفعالة و بشكل رئيسي على مقاومة الأنضغاط, مقاومة الأنثناء و مقاومة شد الأنفلاق. خرسانة المساحيق الفعالة المستخدم فيها السمنت,أبخرة السليكا, الرمل الناعم و ألياف الحديد لصب و فحص 128 نموذجا (مكعبات , أسطوانات ومواشير) مع نسب مختلفة من ألياف الحديد هي0%, 1%, 2%و 3% عند درجات حرارة 20 °م,200°م, 400°م و600°م. بشكل عام ,النتائج اظهرت ان مقدار الأنخفاض في مقاومة الأنضغاط, مقاومة الأنثناء و مقاومة شد الأنفلاق يكون أكبر عندما تتجاوز درجات الحرارة 400°م. عند درجة حرارة600°م نسبة الانخفاض17.8%, 38.87% و 58.57% لمقاومة الانضغاط, مقاومة الانثناء و مقاومة شد الانفلاق على التوالي. كذلك تم ملاحظة و مناقشة التشظي الأنفجاري لخرسانة المساحيق الفعالة عند ارتفاع درجات الحرارة.


Article
Effect Of Kerosene And Fuel Oil On Compressive Strength Of Reactive Powder Concrete
تأثیرالنفط الابیض ونفط الوقود على مقاومة الأنضغاط لخرسانة المساحیق الفعالة

Author: Sana Taha Abdul-Hussain سنا طھ عبد الحسین
Journal: AL-MANSOUR JOURNAL مجلة المنصور ISSN: 18196489 Year: 2013 Issue: 20 Pages: 51-71
Publisher: Private Mansour college كلية المنصور الاهلية

Loading...
Loading...
Abstract

The aim of this study is to investigate the effect of two of oil products(kerosene and fuel oil which is locally called black oil) on compressive strength ofreactive powder concrete. RPC was prepared using cement, silica fume, fine sand,steel fibers and superplasticizer to cast and test 63 specimens of cubes with varioussteel fibers ratios of 0%, 1% and 2% at different exposure periods in oil products (0,30, 90 and 180) days. In general the results showed that RPC has good resistance tothe effect of kerosene and fuel oil. A slight decrease in compressive strengthoccurred as the time of exposure to the oil products increase. The RPC specimens of2% steel fibers content had the lower decrease in compressive strength as a result ofthe denser microstructure. The decreasing ratio of RPC compressive strengthexposed to fuel oil (1.33%)was lower than that of kerosene (2.91%). This may beattributed to the lower viscosity of kerosene than fuel oil.

الھدف من ھذه الدراسة ھو التحري عن تأثیر اثنین من المشتقات النفطیة (النفط الابیض و نفط الوقود المعروفمحلیا بالنفط الأسود) على مقاومة الأنضغاط لخرسانة المساحیق الفعالة. تم تحضیر خرسانة المساحیق الفعالة من السمنت،الرمل الناعم، أبخرة السلیكا, ألیاف الحدید والملدن المتفوق لصب و فحص 63 نموذج من المكعبات بأستخدام نسب( 90 و 180 ،30 ، 1% و 2%) عند فترات تعرض مختلفة في المشتقات النفطیة ( 0 ،% مختلفة من ألیاف الحدید ( 0یوم. بشكل عاماظھرت النتائج ان خرسانة المساحیق الفعالة ذات مقاومة جیدة لتأثیرالنفط الابیض و النفط الاسود. مقاومةالانضغاط انخفضت قلیلا بزیادة زمن التعرض للمشتقات النفطیة. الخلطة التي تحتوي على 2% الیاف حدید ھي الاقلانخفاضا في المقاومة كنتیجةلھیكلھا الاكثر كثافة. ان نسبة الانخفاض في مقاومة الانضغاط لخرسانة المساحیق الفعالةالمتعرضة لنفط الوقود ( 1.33 %) أقل من تلك المتعرضة للنفط الابیض( 2.91 %). ان ذلك قد یعود للزوجة الاقل للنفطالابیض مقارنة مع نفط الوقود.