Removal of SO2 over Modified Activated Carbon in Fixed Bed Reactor: I, Effect of Metal Oxide Loadings and Acid Treatment

Loading...
Loading...
Abstract

The removal of SO2 from simulated gas stream (SO2 + air) in a fixed bed reactor using Modified Activated Carbon (MAC) catalysts was investigated. All the experiments were conducted at atmospheric pressure, initial SO2 concentration of 2500 ppm and bed temperature of 90oC. MAC was prepared by loading a series of nickel and copper oxides 1, 3, 5, 7, and 10 wt% on AC. In some of the experimental runs, the original activated carbon was pretreated with two different concentrations of nitric acid 10 and 45 wt%. The results showed that the SO2 removal efficiency, breakthrough time (τ0.05) and sorption capacity increase with increasing metal oxides loadings up to a value of 7 wt% beyond which the desulfurization performance decreases. The pretreatment of the original AC with HNO3 enhanced the removal efficiency of SO2. The copper supported catalysts showed higher flue gas desulfurization activity as compared to the nickel supported catalysts


Article
PREPARATION AND ADSORPTION STUDY (MONO AND DI- VALENT IONS) OF SELECTED TYPES OF ZSM-ZEOLITES.
دراسة تحضير وامتصاص (ايونات أحادية وثنائية) لبعض أنواع الزيولايت المنقاة

Loading...
Loading...
Abstract

Experimental studies have been carried out on three types of crystalline zeolites which were prepared and used as supports catalysts. All were synthesized in the laboratory (ZSM-5, -11, and –23) with SiO2/Al2O3 ratio of 37, 86 and 94 respectively. The adsorption process was investigated to characterize the catalysts performance toward adsorption parameters (percent of extraction and distribution factor). The performance of catalysts was studied over the range of temperature (room, 50 and 80 ºC) for mono and di-valent ions respectively (H+, Li+, K+, Rb+, Cs+, Sr+2 and Ba+2). The prepared catalysts exhibited that the percent of extraction and distribution factor for both mono and di-valent ions (H+, Li+, K+, Rb+, Cs+, Sr+2, and Ba+2) used on adsorption increase with increasing temperature and also showed different to the framework structure and type of ions used. The maximum percent of extraction and distribution factor is in the order ZSM-11˃ ZSM-5˃ ZSM-23 respectively.

تـضمن البحث اعداد دراســة شاملة عمليــة لثلاثة انواع من الزيولايتات واستخدمت كحوامل٬ جميع هذه الانواع تم تحضيرها في المختبر وهي (ZSM-5, -11, and –23) ٬ حيث كانت نسبة السيلكا / الالومينا لهذه الانواع من الزيولايتات هي (94, 86, 37) على التوالي. تم خلال البحث دراســة معاملات الامتصاص (معامل الاستخلاص ومعامل التوزيع للايونات) لعملية الامتصاص للعوامل المساعدة (الزيولايتات) المحضرة. وقد حسبت معاملات الامتصاص (معامل الاستخلاص ومعامل التوزيع للايونات) على مدى درجات حرارة (درجة حرارة الغرفة,50, 80 مº) بالنسبة الى الايونات الاحادية والايونات الثنائية على التوالي وهي (الهيدروجين, الليثيوم, البوتاسيوم, الربديوم, السيزيوم, والسترونيوم, والباريوم). كذلك بينت النتائج أن معامل الاستخلاص والتوزيع للأيونات المستخدمة في عملية الامتصاص كمتغيرات للأمتصاص تختلف تبعا لكل من البناء التركيبي للزيولايت وكذلك نوع الأيون المستخدم. بينت النتائج ان معامل الاستخلاص والتوزيع للايونات المستخدمة في عملية الامتصاص للزيولايتات المستخدمة كانت كالتاليZSM-11˃ ZSM-5˃ ZSM-23