Optimization of Heat Treatment Parameters for the Tensile Properties of Medium Carbon Steel

Authors: Abbas Kh. Hussein --- Laith K. Abbas --- Wisam N. Hasan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2018 Volume: 36 Issue: 10 Part (A) Engineering Pages: 1091-1099
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The purpose of this study is designate quenching and tempering heat treatment by using Taguchi technique to determination optimal factors of heat treatment (tempering temperature, percentage of nanoparticles, type of base media, nanoparticles type and tempering time)for increasing ultimate tensile strength, yield strength and ductility properties of medium carbon steel. An (L18) orthogonal array was chosen for the design of experiment. The optimum process parameters were determined by using signal-to-noise ratio (larger is better) criterion. The importance levels of process parameters on tensile properties were obtained by using analysis of variance, which applied with the help of (Minitab18) software. Percentage of volumetric fractions of nanoparticles with three different levels(0.01, 0.03 and 0.08 %) were prepared by dispersing nanoparticles that are (α-Al2O3,TiO2 and CuO) with base fluids (De-ionized water, salt solution and engine oil).Medium carbon steel specimens were suffered to hardening and tempering heat treatment process. The variables of tempering heat treatment were temperatures (400 C˚, 550 C˚) and a soaking times (30, 45 and 60 minutes) respectively. Tensile testing performed on samples using united universal hydraulic machine. The results for ( S/N) ratios showed the order of the factors in terms of the proportion of their effect on ultimate tensile strength, yield strength and ductility properties as follow: Tempering temperature ( 400 C˚) ,Nanoparticles type (TiO2 ),Tempering time (30 min),Type of base media (salt solution, engine oil) and Percentage of nanoparticles ( 0.03%) was the least influence for ultimate strength and yield strength while for the elongation were as follows: Tempering temperature (550 C˚),Tempering time(60min), Nanoparticles type (CuO),Type of base media (deionized water) and last percentage of nanoparticles (0.08%).


Article
Effect of Quenching Media Variations on the Mechanical Behavior of Martensitic Stainless Steel
تأثير اختلاف وسط التقسية على السلوك الميكانيكي لفولاذ مقاوم للصدأ مارتنسياتي

Authors: Abbas Kh. Hussein عباس خماس حسين --- Laith K. Abbas ليث قيس عباس --- Wisam N. Hasan وسام ناجي حسن
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2019 Volume: 15 Issue: 2 Pages: 1-12
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The purpose of this study is designate quenching and tempering heat treatment by using Taguchi technique to determine optimal factors of heat treatment (austenitizing temperature, percentage of nanoparticles, type of base media, nanoparticles type and soaking time) for increasing hardness, wear rate and impact energy properties of 420 martensitic stainless steel. An (L18) orthogonal array was chosen for the design of experiment. The optimum process parameters were determined by using signal-to-noise ratio (larger is better) criterion for hardness and impact energy while (Smaller is better) criterion was for the wear rate. The importance levels of process parameters that effect on hardness, wear rate and impact energy properties were obtained by using analysis of variance which applied with the help of (Minitab18) software. The variables of quenching heat treatment were austenitizing temperature (985 C˚,1060 C˚),a soaking times (50,70 and 90 minutes) respectively, Percentage of volumetric fractions of nanoparticles with three different levels(0.01, 0.03 and 0.08 %) were prepared by dispersing nanoparticles that are (α-Al2O3,TiO2 and CuO) with base fluids (De-ionized water, salt solution and engine oil).The specimens were tempered at 700°C after quenching of nanofluids for (2 hours).The results for ( S/N) ratios showed the order of the factors in terms of the proportion of their effect on hardness, and wear rate properties as follow: Austenitizing temperature ( 1060 C˚),Type of base media (salt solution), Nanoparticles type (CuO), Percentage of nanoparticles (0.08%) and Soaking time(90min) was the least influence while for the impact energy were as follows: Type of base media (oil), Austenitizing temperature (985C˚), Percentage of nanoparticles (0.01%), Nanoparticles type (α-Al2O3) and last soaking time (50min).

الغرض من هذه الدراسة هو تصميم معاملة حرارية (اخماد ومراجعة) بوساطة استخدام تقنية تاغوتشي لتحديد العوامل المثلى للمعاملة الحرارية (درجة حرارة الاوستنايت النسبة المئوية للجسيمات النانوية و نوع وسط الأساسو نوع الجسيمات النانوية ووقت النقع) لزيادة الخواص (الصلادة,معدل البلى وطاقة الصدمة) لفولاذ مقاوم الصدأ المارتنسايتي 420. تم اختيار مصفوفة متعامدة(18L) لتصميم التجربة. عوامل العملية المثلى حددت باستخدام معيار (Signal/Noise) (الأكبر هو الأفضل) للصلادة وطاقة الصدمة بينما معيار (الأصغر هو الأفضل) كان لمعدل البلى. تم الحصول على مستويات الأهمية لعوامل العملية على خواص الصلادة,معدل البلى وطاقة الصدمة باستخدام تحليل التباين المطبق بمساعدة برنامج (منتاب18).المتغيرات للمعاملة الحرارية (اخماد) كانت درجة حرارة الأوستنايت (985 C˚، 1060C˚) ، وأوقات النقع (50،70 ، 90 دقيقة) على التوالي، النسبة المئوية للكسور الحجمية للجسيمات النانوية بثلاثة مستويات مختلفة (0،01،0.03و0.08%) تم تحضيرها من خلال تشتيت جسيمات نانوية التي هي (α-Al2O3،TiO2،CuO) بأوساط أساسية (الماء غير المتأين، محلول الملح، زيت المحرك).تم مراجعة العينات بدرجة (700(C˚ لساعتين بعد الاخماد بالموائع النانوية .أظهرت النتائج لنسب ( S/N) ترتيب العوامل من حيث نسبة تأثيرها على الخواص الصلادة ومعدل البلى على وفق النحو الاتي : درجة حرارة الاوستنايت (1060 C˚ ,(نوع وسط الاساس(محلول ملحي), نوع الجسيمات النانوية (CuO), وقت النقع(90 دقيقة) واخيرا النسبة المئوية للجسيمات النانوية (0.08%) بينما لطاقة الصدمة كانت على وفق النحو الاتي: نوع وسط الاساس(زيت المحرك), درجة حرارة الاوستنايت (985(C˚، نوع الجسيمات النانوية (α-Al2O3)، النسبة المئوية للجسيمات النانوية (01.0%) واخيرا وقت النقع (50 دقيقة).