Article
INFLUENCE OF ADDING DIFFERENT FILLERS ON POLY ETHYLENE PROPERTIES
تأثير إضافة مالئات مختلفة على خواص البولي أثيلين

Author: Dr. Abdulla Abd Al-Shakoor Dr. Ame'r H. Majeed Saba A. Ghani
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2006 Volume: 13 Issue: 2 Pages: 26-38
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

The aim of this study was focused on the improvement of pouring, mechanical and thermal properties of high density polyethylene using chemically treated kawaline as a filler which is composed of 10% carbamide and 90% kawaline.A composed had been made among the new filler (kawaline-carbamide), alumina and the pure kawaline in improving the latter properties of polyethylene.It was found that all the mentioned properties affect deeply by filler type and its content. Also it was found that the suitable filler is alumina and kawaline –carrbamide in less performance.

إن الهدف من هذه الدراسة يتركز على تحسين خواص الانسكاب، الميكانيكية و الحرارية للبولي أثيلين عالي الكثافة باستخدام الكاؤلين المعامل كيميائياً كمالئ و الذي يتكون من 10% كاربامايد و 90% كاؤلين.تم إجراء مقارنة بين المالئ الجديد (كاؤلين- كاربامايد) ، الألومينا و الكاؤلين النقي و ذلك من خلال قيام كل منها بتحسين مواصفات البولي أثيلين.وجد أن جميع الصفات المذكورة في أعلاه تتأثر بحدة بنوع المالئ و بكميته. ووجد أيضاً أن المالئ الأكثر ملاءمة هو الألومينا و بدرجة أقل في الأداء الكاؤلين-كارباميد .


Article
Experimental Determination of Ballistic Performance of Composite Material Kevlar 29 and Alumina Powder/ Epoxy by Spherical Projectile

Author: Luay Hashem Abbud
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 4 Pages: 991-1004
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

In this study, a response of hybrid composite laminate woven fiber Kevlar29 – Al2O3 Powder/ Epoxy subjected to high velocity impact loading is presented. The energy absorbed due to impact of small rigid projectile on composite materials targets is determined experimentally. The energy absorbed due to impact of hemispherical projectiles on the developed composite laminates is investigated. The results revealed the maximum ballistic limit at impact velocity is found to be 390.87 ± 6 m/s for an the 18 mm target thickness. The ballistic limit velocity predictions are based on the theoretical method presented from another article. The initial velocity and residual velocity results showed good is agreement compared with the predicted results of Ipson and Recht equations. With 5.4 % of accuracy based on the experimental value for the theoretical model for ballistic limit velocity.

يتضمن البحث دراسة عمل مركب هجين من ليف Kevlar29 ومسحوق اوكسيد الألمنيوم و الأيبوكسي لتحملها الصدمة من المقذوفات الصلدة النصف كروية ذات السرعة العالية التي تصل اقصى سرعة بالستية لها 390.87±6 مثا لسمك مقدارة 18 ملم وان السرعة البالستية معتمدة على الجزء النظري الذي قدم من قبل باحث أخر وقد ركزت الدراسة على الطاقة الممتصة بسبب تأثير المقذوفات الصلدة على الاهداف المركبة التي حسبت بشكل تجريبي. وقد تم مقارنة نتائج السرعة الابتدائية والسرعة النهائية مع النتائج المتوقعة لمعادلة Ipsonو Recht وكانت النتائج متقاربة جداً ونسبة الخطأ اكثر دقة 5.4% من القيمة التجريبية للنموذج النظري لسرعة الحد البالستي.


Article
Effect of Wood Flour Addition on the Pore Volume and BET Surface Area Properties of the Prepared Gamma Alumina (ɤ-Al2O3) Extrudates Used in Catalyst Carriers
تأثير إضافة طحين نشارة الخشب على خواص حجم المسام والمساحة السطحية نوع BET لمبثوقات الكاما ألومينا المستخدمة كحامل للعوامل المساعدة

Author: Alaa D. Jawad Al-Bayati علاء ضاري جواد البياتي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2015 Volume: 21 Issue: 11 Pages: 179-191
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The effect of Wood Flour addition to the gamma alumina powder used in the preparation of gamma alumina (ɤ-Al2O3) catalyst carrier extrudates on the pore volume and BET surface area physical properties was investigated. Two parameters which are size of wood flour particles and its quantity were studied. The sizes of wood flour particles used are 150 µm, 212 µm and 500 µm and the weight percentage added to the gamma alumina powder during the preparation of the extrudates are (1%, 3%, 5% and 10%). The results showed that the addition of wood flour to the gamma alumina powder in order to get gamma alumina extrudates used as catalyst carrier is one of the successful methods to improve the pore volume and BET surface area of the alumina extrudates. The size of wood flour particles and its quantity have main effect on the above texture properties. The smaller the size of wood flour leaded to higher BET surface area, where maximum BET surface area of 127.3 m2/g was got with addition 10% by weight wood flour of 150µm particle size. BET surface area for the same addition percentage of 10% resulted to 114.5m2/g and 105.2m2/g when adding wood flour of 212 µm and 500 µm particle sizes respectively. The weight percentage of wood flour addition has an effect on the BET surface area, where the 3% addition gives maximum BET surface area when the size of the wood flour particles is 500 µm. Regarding the pore volume property for the gamma alumina prepared extrudates, the results showed that the pore volume of the extrudates increased to 0.83 cm3/g and 1.0 cm3/g when 10% wood flour of 150 µm and 500 µm particle sizes were added respectively. The maximum BET surface area was reached when 10% wood flour of 150 µm particle size was added, and the maximum pore volume was reached when 10% wood flour of 500 µm particle size was added, the increase percentage for the BET surface area and pore volume is more than 40% and 400% respectively.

تم إجراء هذا البحث لمعرفة تأثير إضافة طحين نشارة الخشب إلى مسحوق ألكاما ألومينا ( ɤ-Al2O3) المستخدم في تحضير مبثوقات الحامل للعوامل المساعدة الكاما ألومينا على خاصيه المساحة النوعية (BET) وحجم المسام . تم دراسة تأثير متغيرين وهما الكمية وحجم الدقائق لطحين نشارة الخشب المضافة الى مسحوق الكاما الومينا ، حيث تم استخدام حجوم دقائق طحين النشارة بمقدار 150 µm، 212 µm و 500 µm، بينما النسب الوزنية المضافة الى مسحوق الكاما الومينا المستخدم في تحضير العجينة لانتاج مبثوقات الكاما ألومينا كانت (1%، 3%،5% و 10%). أظهرت النتائج إن إضافة طحين نشارة الخشب الى مسحوق الكاما الومينا عند تحضير العجينة المستخدمة لانتاج مبثوقات الكاما الومينا من اجل استخدامها كحامل للعوامل المساعدة ومن اجل تحسين خواص حجم المسام والمساحة السطحية نوع BET هي عملية ناجحة في تحسين الخواص النسيجية أعلاه عند تحضير المبثوقات، وإن حجم دقائق طحين النشارة المستخدمة وكميتها لها تأثير أساسي على الخواص النسيجية اعلاه. كلما كان حجم دقائق طحين الخشب أصغر يؤدي إلى مساحة سطحية نوع BET أعظم ، حيث تم الحصول على أعظم مساحة BET بمقدار127.3 م2/غم عند اضافة 10% وزنا نشارة خشب ذات حجم 150 µm عندما كان حجم دقائق طحين النشارة 150 µm ومساحة نوعيه (BET) بقيم 114.5 م2/غم و 105.2 م2/غم عندما كانت حجوم دقائق طحين نشارة الخشب هي 212 µm و 500 µm على التوالي. إن متغير نسبة طحين نشارة الخشب المضافة له تأثير على المساحة السطحية نوع BET ، حيث تم الحصول على مساحة عظمى عند اضافة 3% طحين خشب ذو حجم دقائق µm .500 فيما يخص خاصية حجم المسام للمبثوقات كاما الومينا المحضرة فقد أظهرت نتائج الدراسة أن حجم المسام ازداد الى 0.83 سم3/غم و1.0 سم3/غم عند إضافة 10% طحين خشب ذو حجم دقائق 150 µm و500 µm على التوالي. أعظم مساحة نوعية (BET) تم التوصل اليها كانت عند اضافة 10% طحين خشب ذو حجم دقائق 150 µm واعظم حجم مسام تم التوصل اليه كان عند اضافة 10% طحين خشب ذو حجم دقائق 500 µm ، أن نسبة الزيادة في المساحة النوعية كانت اكثر من 40% ونسبة الزيادة في حجم المسام كان اكثر من 400%.