Influence of Heat Treatment on Microstructure and Wear of Aluminium 359.0 Alloys
تأثیر المعاملات الحراریة على البنیة المجھریة والبلى لسبیكة الألمنیوم 359.0

Authors: Mohammed Saead Wahead محمد سعید وحید --- Huwaidah Ibrahim Ahmed ھویدا ابراھیم احمد
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 6 Part (B) Scientific Pages: 126-138
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this work is to study wearing of alloy 359.0 which are (Al-9%Si) before and after heat treatment. First heat treatment is precipitation hardening ,Second Laser surface treatment ,The microstructure after precipitation process and laser application effected on the hardness and wear rate.

تضمن البحث دراسة خواص البلى للسبيكة 359.0 وهي من سبائك الألمنيوم الحاوية على 9%Si قبل وبعد اجراء المعاملات الحرارية,تضمن البحث محورين اولهما اجراء عملية الأصلاد بالترسيب , والمحور الثاني اجراء عملية الاصلاد السطحي باشعة الليزر، اظهرت النتائج ان طبيعة البنية المجهرية الناتجة بعد عملية الأصلاد بالترسيب والمعاملة السطجية باللليزر تؤثر تأثيرا كبيرا على الصلادة ومعدل البلى


Article
دراسة تأثير زمن القذف بالكرات الفولاذية على مقاومة البلى الانزلاقي الجاف لسبيكة الالمنيوم-نحاس Al-3.5%Cu

Author: عادل محمود باش
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2015 Volume: 22 Issue: 2 Pages: 34-39
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract


Article
Effect of Graphite Particles Addition on the Wear Resistance and Friction coefficient of Brass Alloy (α)
تأثير اضافة دقائق الكرافيت على مقاومة البلى ومعامل الاحتكاك لسبيكة البراص ألفا

Authors: سراء عبد القادر --- مريم عبد العظيم باقر
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 6 Pages: 218-233
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research is devoted to study the effect of different percentage of Graphiteparticles addition (5,10,15) wt% to Brass alloy (α) produced by stir casting using vortextechnique , on the wear resistance and the coefficient of friction under dry slidingconditions using pin-on-disk technique . Three loads (5, 10, 15) N were used at differentsliding speeds effect (2.7,3.7,4.7) m/sec . The results showed that the wear rate isincreased in general with increasing the applied load , but the composite materialreinforced with graphite particles showed wear rate lower than that of the base alloy .Thewear resistance of the composite material reinforced with graphite particles with 15 wt%was higher than that of reinforced with 5 wt% . When different sliding speeds were used, the results showed that , the wear rate is decreased with increasing sliding speed .Whenthe coefficients of friction was measured at high loads , It is clear that the compositematerial has low coefficient of friction as compared with that at low loads , while it isdecreased with increasing sliding distance at all used loads , and the composite materialreinforced with graphite particles showed remarkable decreasing in temperature whensurface temperatures were measured as compared with base alloy.

يهدف البحث الى دراسة تأثير اضافة دقائق الكرافيت بنسب وزني ة مختلفة ( 15،10،5 )% الى باتباع (Stir Casting) المنتجة بطريقة السباكة بالتحريك (Cu- 29.5% Zn) α سبيكة البراص نوع على مقاومة البلى والاحتكاك تحت ظروف الانزلاق الجاف (Vortex Technique) تقنية الدوامة باستعمال تقنية المسمار على القرص ، لقد تم استعمال ثلا ثة احم ال ( 15،10،5 ) نيوتن تحت تأثير سرع4.7 ) متر/ثانية ، وقد أظهرت النتائج بان معدل البلى يزداد بصورة عامة ، 3.7 ، انزلاقية مختلفة ( 2.7 بزيادة الحمل المسلط لكن أبدت المادة المتراكبة المقواة بدقائق الكرافيت معدل بلى أقل مما هو عليه 15 كانت أعلى wt% للسبيكة الاساس وان مقاومة البلى للمادة المتراكبة المقواة بدقائق الكرافيت بنسبة 5 . أما عند استخدام سرع انزلاقية مختلفة فأظهرت النتائج بان معدل wt% من تلك المقواة بنسبة البلى ينخفض مع ازدياد سرعة الانزلاق . وعند حساب معامل الاحتكاك عند الأحمال العالية للمادة المتراكبة وجد انه يكون أقل من معامل الاحتكاك عند الأحمال القليلة بينما يقل معامل الاحتكاك مع زيادة سرعة الانزلاق وعند جميع الأحمال المستخدمة ، وقد أبدت المادة المتراكبة المقواة بدقائق الكرافيت انخفاضاً ملحوظاً بدرجة الحرارة عند قياس درجة الحرارة السطحية بالمقارنة مع السبيكة الاساس .


Article
Study of Wear Sliding For Dezincification of Brass
دراسة البلى الانزلاقي لعينات البراص المزالة الزنك

Authors: محمد سعيد وحيد --- هناء عرير سميج
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 14 Pages: 484-499
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Given the emergence of cracks in a high proportion of clay product in the production phase of the plant Blocks in the laboratory Abu- Nuass which was reflected in the increase of damage from the permissible limits, as well as the high proportion of soluble salts that are on theexternal surfaces of the product, which negatively affect the properties of bricks in the future lead to the break in the walls and turned into a fragile strength, which affects the safety anddurability of origin and to address these negative phenomena and to identify causes and improve the properties of brick products to be within the specification has been adopted for this researchand to take practical steps in the development of a scientific program for the follow-up stages of the process of production and make the appropriate adjustments to it, starting with the initial article and the semi-final and ending with the product. The focus was on developing a program to modify the conditions of drying and burning and theadoption of the drying period of time not exceeding 72 hours and a gradual manner to control on the stresses generated by the sudden evaporation of water. As well as kaolin’s clay been added to the soil and in different proportions were different burning temperature was reached by adding the best results (30-40)% of kaolin’s clay degree burn (950-1000) m into the soil and following the step-by-step method of drying, where it was observed a significant improvement in the properties of bricks in terms of strength and absorption of water and effloresce phenomenon.

70 ) بتأثير الأوساط الأكالة / تضمن البحث دراسة عملية إزالة الزنك التي تحدث في سبيكة براص-الفا ( 30 2,1.5,1,0.5 )ولفترة غمر( 14 ) يوما,وقد كان اقل معدل M) (الحامضية والقاعدية والملحية) عند تراكيز مختلفة 3.37,90.14 ) للأوساط الأكالة الثلاثة الحامضية,القاعدية والملحية ppm)(0.5 M) لحدوث الإزالة عند التركيز 13.29,220,69 ) للأوساط الثلاثة. تم ppm)(2 M) على التوالي.أما أقصى معدل للإزالة فقد كان عند التركيز تعزيز النتائج أعلاه بفحص الخشونة السطحية للعينات التي عوملت بالأوساط أعلاه وللتراكيز نفسها.ولدراسة اثر الإزالة للزنك على خواص سبيكة البراص,تم دراسة تأثير الإزالة في خواص البلى الالتصاقي الجاف تحت تأثير أحمال وسرع مختلفة, وتبين من نتائج الفحص إن العينات المغمورة في الوسط القاعدي اقل مقاومة للبلى. أما العينات المغمورة في الوسط الملحي فأبدت مقاومة بلى أعلى من الوسط القاعدي في حين كانت أعلى مقاومة للبلى للعينات المعاملة بالحامض, ولكن تبقى مقاومة البلى للسبيكة الأصلية أعلى مما في حالة العينات التي تممعاملتها بالأوساط الأكالة.


Article
STUDY OF WEAR RESISTANCE AND HARDNESS PROPERTY FOR POLYMERIC BLENDS
دراسة مقاومة البلى وخاصية الصلاده لخلائط بوليمرية.

Authors: FAIK H. ANTER فائق حماد عنتر --- AHMED H. MAHMOOD احمد حسن محمود
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: ISSN: 19918941 Year: 2013 Volume: 7 Issue: 1 Pages: 194-203
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This work includes preparation binary and ternary polymeric blends by Hand lay-up molding from Epoxy resin, Unsaturated polyester and polyvinyl chloride ( PVC) with different weight ratios. The wear resistance (which includes change in applied load and hardness (shore)) were study before and after immersion in (HCL) solution with (0.3) normality. The experimental results show that the wear rate was increased with increasing applied load and immersion time. Also the results show that shore hardness was decreased after immersion in (HCL) solution.

تضمن البحث تحضير خلائط بوليمرية ثنائية وثلاثية بطريقة القولبة اليدوية من راتنج الايبوكسي وراتنج البولي استر غير المشبع والبولي فنيل كلورايد (PVC) وبنسب وزنية مختلفة .في هذا البحث تم دراسة مقاومة البلى التي تتضمن التغّير في الحمل المسلط وكذلك الصلادة قبل وبعد الغمر في المحلول الحامضي وبتركيز ( 0.3 N).اوضحت النتائج بأن مقاومة البلى تزداد مع زيادة الحمل المسلط ومع زمن الغمر .كذلك اوضحت النتائج بأن صلادة شور تقل بعد الغمر في المحلول الحامضي.


Article
دراسة تأثير السرعة الدورانية ودرجة حرارة الصب على مقاومة البلى والصلادة لسبيكة الالمنيوم (A380) المقواة بنسب حجمية مختلفة من دقائق الالومنيا

Authors: مهند عبدالخالق حميد --- نجيب عبطان سلمان --- فاروق منصور مهدي
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2016 Volume: 23 Issue: 4 Pages: 1-10
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In this study a cylindrical liner was produced by horizontal centrifugal casting process. The liner was composed from aluminum alloy (A380) matrix reinforced with alumina particles (Al 2O3)with grain size of (63−125)µ and volume percent of 10,15 and 20%. The die was rotated atdifferent speeds and its temperature was remained constant at (350)ºC. In this present study it was concluded that any increase in temperature difference between pouring and die temperature will reduce the surface defects. This study reveals that increasing the rotational speed refines the grain size but cause the alumina particles to be concentrated atthe outer surface. Finally it was found that the addition of alumina particles increases bothhardness and wear resistance of the alloy.


Article
Studying the Effect of Addition Particles of Alumina (Al2O3)
دراسة تأثير إضافة دقائق كل من الالومينا (Al2O3) والزركونيا (ZrO2) على بعض الخواص الميكانيكية لمتراكبات ذات أساس من سبيكة (Al-Si-Mg)

Author: Sarmad I. Ibrahim سرمد عماد إبراهيم حسين
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2011 Volume: 7 Issue: 3 Pages: 78-90
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study is concerned with the effect of adding two kinds of ceramic materials on the mechanical properties of (Al-7%Si- 0.3%Mg) alloy, which are zirconia with particle size (20μm > P.S ≥ 0.1μm) and alumina with particle size (20μm > P.S ≥ 0.1μm) and adding them to the alloy with weight ratios (0.2, 0.4, 0.6, 0.8 and 1%). Stirring casting method has been used to make composite material by using vortex technique which is used to pull the particles to inside the melted metals and distributed them homogenously.After that solution treatment was done to the samples at (520ºC) and artificial ageing at (170ºC) in different times, it has been noticed that the values of hardness is increased with the aging time of the original alloy and reached its highest value after (8hr).Mechanical tests were done to the original alloy and the composite material at the maximum hardness value and represented by tensile, hardness, and wear tests. It was found that the hardness value is increased with increment of the amount of added particles; also the increment in the hardness of the alloy which is reinforced with alumina is more than that reinforced with zirconia.Regarding the tensile test, results show that the strength and yield resistance of the composite material are more than that in the original alloy and these values are increased with increasing the amount of the added particles and they reached maximum values at (0.6%). Then they are decreased but these values remain at higher values than those in the original alloy. However, the ductility is decreased as compared with the original alloy and this decrement was more obvious with the increasing amount of the added particles. The increment of strength and yield resistance of the alloy reinforced by alumina was higher than that reinforced with zirconia, while the ductility of the alloy reinforced by zirconia was higher than that happened by the addition of alumina. Also zirconia and alumina addition to the original alloy decreased the wear rate, and the decrement would be more with the increased amount of adding particles. In addition the wear resistance of the alloy reinforced with alumina was larger than that reinforced with zirconia. X-rays testing proved that secondary phase (AlFeSi) appeared in both original alloy and the composite material. While heat treatment led to the appearance of phases (Mg2Al) and (Mg2Si) in original alloy. This was led to obvious improvement in the mechanical properties in addition to appearance ceramic particles in the microstructure of the composite material.This structure somewhat homogenous has fine grains as compared with large grains in the microstructure of the original alloy. .

يتنـاول البحـث دراسـة تأثيـر إضافـة نوعيـن مـن المـواد السيراميكيـة في الخواص الميكـانيكيـة لسبيكـة Al - Si - Mg)) وهمـا دقائق الالومينا بحجـم حبيبـي يتراوح بيـن (≥0.1μm 20μm>P.S) ودقائق الزركونيا بحجم حبيبي يتراوح بيـن (20µm>P.S≥0.1µm) وإضافتها إلى السبيكة بنسب وزنية (0.2 ,0.4 ,0.6 ,0.8and 1%). وتمت بطريقة السباكة بالمزج في تصنيع المادة المتراكبة باستخدام تقنية الدوامة والتي تعمل على سحب الدقائق إلى داخل المنصهر المعدني وتوزيعها خلاله بشكل متجانس. وتم بعد ذلك إجراء المعاملة المحلولية للعينات عند درجة حرارة 520˚C)) والتعتيق الاصطناعي عند درجة حرارة 170˚C)) في فترات مختلفة. حيث لوحظ أن قيم الصلادة للسبيكة الأساس تزداد مع مدة التعتيق لتصل إلى أعلى قيمة لها عند مدة 8hr)). تم إجراء الفحوصات الميكانيكية للسبيكة الأساس والمادة المتراكبة المنتجة والمتمثلة بفحص الشد والصلادة والبلى عند قيم الصلادة العظمى للنماذج المعاملة حرارياُ. حيث وجد ان قيم الصلادة تزداد مع زيادة النسب المضافة ولغاية (1%). وان الزيادة الحاصلة في قيم الصلادة للسبيكة المقواة بدقائق الالومينا اكبر من قيم الصلادة المقواة بدقائق الزركونيا. أما نتائج فحص الشد فقد بينت ان مقاومة الشد والخضوع للمادة المتراكبة أعلى مما هي عليه في السبيكة الأساس وتزداد هذه القيم مع زيادة النسب الوزنية للدقائق المضافة والى حد 0.6%)) ثم تسلك سلوكاً مغايراً لكنها تبقى محافظة على قيم أعلى مما هي عليه في السبيكة الأساس , في حين تنخفض قيم المطيلية مقارنة مع السبيكة الأساس ويزداد انخفاضها مع زيادة النسب الوزنية للدقائق المضافة. وان الزيادة الحاصلة في قيم مقاومة الشد ومقاومة الخضوع للسبيكة المقواة بدقائق الالومينا اكبر من تلك المقواة بدقائق الزركونيا. في حين أن قيم المطيلية للسبيكة المقواة بدقائق الزركونيا اكبر من المقواة بدقائق الالومينا. كما أدى إضافة دقائق الزركونيا والالومينا إلى تقليل معدل البلى للسبيكة الأساس مع تغير الحمل المسلط , وان النقصان يزداد مع زيادة النسب المضافة. وان النقصان الحاصل في قيم معدل البلى للسبيكة المقواة بدقائق الالومينا اكبر من المقواة بدقائق الزركونيا.أثبتت نتائج فحص الأشعة السينية ظهور الطور الثانوي AlFeSi)) في كل من السبيكة الأساس والمادة المتراكبة بينما أدت المعاملة الحرارية إلى ظهور الأطوارMg2Al )) و Mg2Si)) في البنية المجهرية للسبيكة الأساس والتي أدت إلـى تحسن واضح فـي الخواص الميكانيكيـة, فضلاً عن ظهور الدقائق السيراميكية في البنية المجهرية للمادة المتراكبة والتي كانت بشكل حبيبات ناعمة ومتجانسة نوعاٌ ما مقارنةُ بكبر الحبيبات في البنية المجهرية للسبيكة الاساس.


Article
The Effect of the Cerium Addition on the (Corrosion Fraction Wear) Properties of (Aluminum – Iron) Base Alloy
تأثير إضافة السيريوم على خاصيتي التآكل والبلى الاحتكاكي لسبيكة ذات أساس ( ألمنيوم – حديد )

Author: زهير طالب خليف الطائي
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 13 Pages: 642-657
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The present study deals with the effect of addition cerium in the corrosion–fraction wear behavior of with added (0.25%) cerium element. The solution used;salt solution ( 3%Wt.NaCl ) by weight , acidic solution (3%Vol.HCl ) by volume ,weight loss method ; electrochemical method ( Tafel Extrapolation ) andmicroscopic examination are used for study corrosion behavior of alloy . The resultof weight loss method showed different continues weight loss while the (B) alloyshowed weight loss at the first stage of the test then showed weight gain. The resultof electrochemical method ( Tafel Extrapolation ) showed the corrosion potentialand corrosion current of ( A ) alloy in the salt solution was E Corr.=-641.3 mv;ICorr. = 34.42μA/Cm2 while the corrosion potential and corrosion current for (B)alloy was E Corr. = -681.6 mv ; I Corr.= 51.50 μA/Cm2. The result of weight lossmethod in acid solution showed convergence in the result at first hour of the testafter that (A) alloy showed signification superiority on the ( B ) alloy . The resultof electrochemical method ( Tafel Extrapolation ) showed the corrosion potentialand corrosion current of ( A ) alloy in the acidic solution was E Corr.= -324.7 mv ;I Corr.=19.13 μA/Cm2 while the corrosion potential and corrosion current for ( B )alloy was E Corr. = -697.9 mv ; I Corr.=507.35 μA/Cm2. The result of fractionwear test showed significant superiority of alloy ( A ) on the alloy ( B )

البحث الحالي يمثل دراسة تأثير إضافة السيريوم في سلوك التآكل والبلى لسبيكة ذات( A ) أساس ( ألمنيوم – حديد ) تم استخدام وعين من السبائك في هذه الدراسة السبيكة الأساسالسبيكة الأساس مع إضافة السيريوم بنسبة ( % 25 ). المحاليل المستخدمة هي ( B ) والسبيكةاستخدمت طريقة فقدان (%Vol.HCl 3% ) والمحلول ألحامضي ( 3 Wt.NaCl ) المحلول الملحيالوزن, الطريقة الكهروكيميائية (استقطاب منحنى تافل) واستخدام التصوير بالمجهر الضوئيلدراسة سطح العينات من اجل دراسة السلوك التاكلي والبلى للسبائك.أظهرت نتائج طريقة فقدان الوزن اختلاف في السلوك التاكلي للسبائك في الوسط الملحيفقدان في ( B ) فقدان مستمر في الوزن في حين أظهرت السبيكة ( A ) حيث أظهرت السبيكةالفترة الأولى للاختبار ثم حصل بعد ذلك زيادة في الوزن المكتسب وهذه الزيادة كانت متذبذبة ,أما نتائج الطريقة الكهروكيميائية( استقطاب منحنى تافل ) أظهرت إن جهد التآكل وتيار التآكلI Corr. = 34.42 μA/Cm2; ECorr. = -641.3 mv. في المحلول الملحي كانت ( A ) للسبيكةI Corr. =51.50 μA/Cm2; E Corr. = - كانت ( B ) في حين جهد وتيار التآكل للسبيكة681.6 في المحلول الملحي .أظهرت نتائج فقدان الوزن في الوسط ألحامضي تقارب النتائج mv.B ) تفوق واضح على السبيكة ( A ) خلال الساعة الأولى من الاختبار بعد ذلك أظهرت السبيكة) أما نتائج الطريقة الكهروكيميائية ( استقطاب منحنى تافل ) في الوسط ألحامضي فقد أظهرتI Corr.=19.13 μA/Cm2; E Corr.= - كانت ( A ) إن جهد التآكل وتيار التآكل للسبيكة. I Corr.= 507.35 μA/Cm2; E Corr.= -697.9mv. كانت ( B ) 324.7 أما السبيكة mv.( A ) أظهرت نتائج اختبار البلى الذي اجري إلى السبيكتين تفوق واضح للسبيكة. ( B ) على السبيك


Article
The Effect of Liquid Nitriding and Carborizing on Adhesive Wear Resistance of Carbon Steel 1020
تأثير النتردة والكربنة السائلتين على مقاومة البلى الالتصاقي لفولاذ كربوني 1020

Authors: خيرية سلمان حسن --- رحاب حسين خنجر --- شذى محمد رجاء عبد الجبار
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 5 Pages: 231-240
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of this paper is to study the effect of Nitro carburizing on adhesivewear resistance of carbon steel (1020 AISI). Four groups of specimens weremanufactured (A, B, C, D) with dimensions (D20*10 mm) according to ASTMstandard . Liquid nitriding at 550 °C for one hour was applied for group B, liquidcarburizing at 950°C for one hour was applied for group C, and double process ofnitriding the carburizing in the same conditions as mentioned before was appliedfor group D. The hardness test, the adhesive wear resistance at different conditions(time, sliding velocity and load) and photo microstructure was checked by opticalmicroscope, then phases was examined by the X-ray diffraction technique for allthe specimens. It is found that the adhesive wear resistance was improved by allsurface heat treatment. Nitriding and carburizing but Nitro carburizing it found thatbest improvement.


Article
EFFECT OF GRAPHITE ON WEAR RESISTANCE OF ALUMINUM-SILICON ALLOY
تأثير الكرافيت على مقاومة البلى لسبيكة ألمنيوم - سيليكون

Loading...
Loading...
Abstract

This research deals with studying the effect of graphite on the wear resistance of aluminum – silicon alloy. Firstly this alloy (master alloy) is prepared using casting method then graphite particles added in weight ratio (5.5 %) by using vortex technique after that the master alloy and composite material casted in dies and prepared for sliding wear test , wear test was made under different conditions of applied load , sliding distance and surface roughness at the room temperature. The results show that wear rate increases with increasing any of the above conditions, also the composite material show higher resistance wear than of master alloy.

يتضمن البحث دراسة تأثير الكرافيت على مقاومة البلى لسبيكة ألمنيوم – سيليكون , إذ تم تحضير هذه السبيكة (السبيكة الأساس ) باستخدام طريقة السباكة بالمزج ثم إضافة دقائق الكرافيت بنسبة وزنية مقدارها (5.5%) باستخدام تقنية التحريك بتكوين دوامة (Vortex Technique) . بعدها تم صب السبيكة الأساس والمادة المتراكبة في قوالب معدنية وتحضيرها لاختبار البلى الانزلاقي حيث تم إجراء الاختبار تحت ظروف مختلفة من الحمل المسلط ومسافة الانزلاق وخشونة السطح وعند درجة حرارة الغرفة. من النتائج لوحظ إن معدل البلى يزداد في حالة زيادة أي من الظروف أعلاه وكذلك فان المادة المتراكبة تبدي مقاومة بلى أعلى منها في حالة السبيكة الأساس.

Listing 1 - 10 of 43 << page
of 5
>>
Sort by
Narrow your search

Resource type

article (43)


Language

Arabic (22)

English (17)

Arabic and English (2)