Growth andcharacterization of Mn2O3nano thin films by spin coating technique
باستخدام Mn2O أنماء ومعرفة خواص الأغشیة النانویة الرقیقة لمادة اوكسید المنغنیز 3 Spin coating تقنیة تدویر الطلاء

Author: Ayad Hatim Karim أیاد حاتم كریم
Journal: Journal of Education for Pure Science مجلة التربية للعلوم الصرفة ISSN: 20736592 Year: 2018 Volume: 8 Issue: 1 Pages: 247-254
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

AbstractMn2O3 nano thin films were preparedon glass substrates using spin coating technique by takingmanganese acetate (Mn(CH3COO)2.4H2O) as starting martial for different molar solutions. Solutionwas prepared by dissolving Mn(CH3COO)2.4H2O as precursor and monoethanolamine (MEA) asstabiliser agent and 2-methoxyethanol as solvent. The mixture was stirred at 80oC until to get highviscous transparent solution. A small portion was taken and dropped on to corning glass substratewhich was rotated at (3000) rpm for (30) sec and dried at 300oC. The process was repeated for threetimes to get desired thickness of the film.also Prepared films were characterized by using XRD,SEM, UV-Vis spectrophotometer.

الخلاصةبأخذ مادة منغیز ( spin coating ) النانویھ على ركیزة من الزجاج باستخدام تقنیة Mn2O تم تحضیر أغشیة رقیقة من مادة 3كسلائقومونوا بثانولامین MN ( CN3COO) كمادة ابتداء ل لمحالیل المختلفة،تم تحضیر المحلول بإذابة 2 MN ( CN3COO)280 ) حتى الحصول على محلول عالي اللزوجةثم c ) كمذیب ھذا الخلیط خفق عند درجة ( Methoxythanol ) كعامل استقرار و30 ) ثم see ) 3000 ) دورة بالدقیقة لمدة rpm ) وضع جزء صغیر من المحلول على زاویة ركیزة زجاجیة دورت بمقدار300 ) وكررت العملیة ثلاث مرات للحصول على السمك المطلوب كذلك الغشاء المحضر تم فحصھ باستخدام c ) خفقت عند درجة. XRD _ SEM _UV –VIS