Study of Adding Cement to Hardened Powdered Novolac Resin Matrix for Manufacturing Novel Concrete in the Presence of Heat and Pressure
دراسة إضافة السمنت الى مصفوفة مسحوق راتنج النوفولاك المصلد لصناعة خرسانة مبتكرة بوجود عاملي الحرارة والضغط

Loading...
Loading...
Abstract

In this study, a new concrete has been manufactured by mixing powdered hardened novolac resin with cement in equal proportions and in the presence of heat (150-200) 0C and pressure (100 kN) as catalysts. The results of laboratory tests showed that the new concrete have a compressive strength of (92 MPa) and a density of (1761.1 kg/m3 ) while the compressive strength of the normal concrete at the age (28) days (25 MPa) and the density was (2368 kg/m3). It can be seen from the images taken by the scanning electron microscopy that there is a correlation between concrete components (hardened powdered novolac resin with cement) in the presence of heat and pressure as catalysts (Bakelite concrete).

تم في هذا البحث صناعة خرسانة متكونة من ( سمنت ومطحون راتنج النوفولاك المصلد بنسب متساوية مع وجود حرارة تتراوح من (150- 200 ) درجة مئوية وضغط (100 كيلو نيوتن) كعوامل مساعدة. أظهرت النتائج المختبرية ان قوة الانضغاط للخرسانة الجديدة قد بلغت (92 ميكا باسكال) اما الكثافة فقد بلغت 1761.1)كيلوغرامم3) , بالمقارنة مع الخرسانة الاعتيادية عند عمر (28) يوم والتي كانت قوتها الانضغاطية (25 ميكا باسكال) وذات كثافة بلغت (2368 كغمم3) . ومن خلال صور المجهر الالكتروني الماسح SEM)) نلاحظ ترابط بين راتنج النوفولاك المصلد مع السمنت مما يعطي قوة انضغاط ممتازة.


Article
Study the Effect Different Radioactive Dose on MechanicalProperties of Composite Material from Novolak ResinExposure to High – Energy Radiation
دراسة تأثير اختلاف الجرع الإشعاعية على بعض الخصائص الميكانيكية لمادة متراكبة من الراتنج النوفولاك متعرضة لأشعة ذات طاقة عالية

Authors: Muhammad Slab Hamza محمد صَلاب حمزة --- Muzher Ali Sahib مزهر علي صاحب --- Rula Abdul Khider Abbas رولا عبد الخضر عباس
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2009 Volume: 5 Issue: 2 Pages: 72-82
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The research involves using phenol – formaldehyde (Novolak) resin as matrix for making composite material, while glass fiber type (E) was used as reinforcing materials. The specimen of the composite material is reinforced with (60%) ratio of glass fiber.The impregnation method is used in test sample preparation, using molding by pressure presses.All samples were exposure to (Co60) gamma rays of an average energy (2.5)Mev. The total doses were (208, 312 and 728) KGy. The mechanical tests (bending, bending strength, shear force, impact strength and surface indentation) were performed on un irradiated and irradiate samples.All of the mechanical properties were improved with an increase in radioactive dose of up to (312) KGy to be decreased afterwards.The topography of some physically tested specimens was studied using optical microscopy.

تضمنت هذه الدراسة تحضير مادة متراكبة من راتنج الفينول- فورمالديهايد نوع (نوفولاك) كمادة أساس للمادة المتراكبة, بينما استعملت ألياف الزجاج نوع (E-glass) بشكل ألياف قصيرة كمواد مقوية. وقد كانت نسبة الكسر ألوزني للألياف تقدر ب (60%), كما استخدم طريقة التشرب (method Impregnation) في تحضير هذه المادة المتراكبة باستعمال القولبة بمكابس الضغط. وأن هذه المادة المتراكبة المحضرة شُععت بأشعة گاما المنبعثة من النظير المشع (Co60) ذات معدل طاقة (1.25Mev) وبجرع أشعاعيه مختلفة هي KGy(728, 312,208).
ومن ثم تمت مقارنة خواص هذه المادة المتراكبة المتمثلة بفحص (الانحناء, متانة الثني, مقاومة القص الداخلية, الصلادة السطحية و مقاومة الصدمة) مع تلك الخواص لهذه المادة المتراكبة غير المشععة وذلك لملاحظة تأثير التشعيع على المقاومة الإشعاعية لهذه المادة.
أظهرت النتائج المقارنة إن تدعيم الراتنج النوفولاك بألياف الزجاج يعمل على تحسين مقاومته الإشعاعية, وأن زيادة الجرع الإشعاعية إلى KGy(312) تؤدي إلى زيادة جميع الخصائص الميكانيكية المدروسة في بداية الأمر لتنخفض بعد ذلك هذه الخصائص مع الاستمرار بزيادة الجرع الإشعاعية.
هذا ومن الجدير بالذكر تم الاستعانة بالمجهر الالكتروني الضوئي لدراسة السمات السطحية للنماذج الخاضعة لبعض من الفحوصات السابقة الذكر.