PHOTODEGRADATION OF GAS OIL USING NANO CLAY(BENTONITE) AS SUPPORTED SURFACE OF TITANIUM DIOXIDE (TIO2)
التكسير الضوئي لزيت الغاز باستخدام طين البنتونايت النانوي كسطح ساند لثاني اوكسيد التيتانيوم(TiO2).

Loading...
Loading...
Abstract

This research was conducted for photodegradation of gas oil using nano clays (bentonite) by 30% of TiO2 loaded on the clay , for the purpose of fragmentation chains hydrocarbon long polluting the environment and converted to short chains and gas, and carried out operations cracking through the design of a photocell according to the specifications laboratory, using xenon lamp wave length (200-800 nm) and by passing the air for a specific time periods (4,6,10) hours, after which the components of the models were measured by a gas chromatography (GC), as well as the use of a radiation infrared (FT-IR) to identify groups effective of gas oil before and after degradation , The results obtained from the analysis (GC) that there is a change in the percentage of some compounds hydrocarbon paraffin such as(Nonan, Dodecane, Hexadecane) that is to know the time of Retention solutions( standard compounds), as was observed decrease ratio compound Hexadecane and increasing the percentage Alnonan gradually in the gas oil over time of irradiation and this shows the transformation of long chains in gas oil into shorter chains ,As for analysis by (FT-IR) the appearance of the carbonyl group (C=O) which indicates the occurrence of oxidation process of some organic compounds during degradation .

أجري في هذا البحث عملية التكسير الضوئي لزيت الغاز باستخدام الأطيان الطبيعية ( البنتونايت ) نانوية التركيب المحمل عليها 30% من TiO2 , لغرض تجزئة السلاسل الهيدروكاربونية الطويلة الملوثة للبيئة وتحويلها إلى سلاسل قصيرة وغازات , ونفذت عمليات التكسير من خلال تصميم خلية ضوئية حسب المواصفات المختبرية , باستخدام مصباح الزنون بطول موجي من (200-800 nm) وبإمرار الهواء ولفترات زمنية محددة( 4,6,10 ) ساعة , بعدها تم متابعة عملية التكسير الضوئي للنماذج بواسطة جهاز كروماتوغرافيا الغاز(GC) وكذلك بجهاز الأشعة تحت الحمراء(FT-IR) للتعرف على مجاميع الفعالة لزيت الغاز قبل وبعد التكسير , وقد بينت النتائج المستحصل عليها من تحليل مخططات ال(GC) إن هناك تغير في نسب بعض المركبات الهيدروكاربونية البرافينية مثل ( نونان , دوديكان , هكساديكان) التي تم معرفة زمن الاحتجاز لها من محاليلها القياسية , حيث لوحظ نقصان نسبة المركب هكساديكان وزيادة نسبة النونان تدريجياً في زيت الغاز بمرور زمن التشعيع وهذا يدل على تحول السلاسل الطويلة الموجودة في زيت الغاز إلى سلاسل اقصر , أما بالنسبة لتحليل (FT-IR) فقد بين ظهور مجموعة الكاربونيل فعالة(C=O) التي تدل على حدوث عملية أكسدة للمركبات العضوية أثناء عملية التكسير .


Article
EFFECT OF OPERATING CONDITIONS ON HYDRODESULFURIZATION OF VACUUM GAS OIL
تأثير الظروف التشغيلية على المعاملة الهيدروجينية لزيت الغاز الفراغي

Author: Abdul Mun’em A. Karim عبد المنعم عباس كريم
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2008 Volume: 1 Issue: 1 Pages: 19-31
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The study deals with the hydrotreating of vacuum gas oil with boiling range (611-833K) using trickle bed reactor and a commercial cobalt – molybdenum on alumina as a catalyst with temperature range (583-643K) , liquid hourly space velocity range (1.5-3.75 hr-1) , hydrogen to oil ratio about 250 lt / lt , and hydrogen pressure kept constant at 3.5 MPa. The results showed that the aromatic content of vacuum gas oil decreased while sulfur removal increased with increasing temperature and decreasing space velocity. The properties, viscosity, density, flash point, and carbon residue of the products are decreased with temperature increasing but the aniline point did the otherwise.

لقد تمت الدراسة بموجب عقد مع شركة مصافي الشمال في بيجي و التي تتناول دراسة المعاملة الهيدروجينية لزيت الغاز الفراغي ذو مدى غليان(833 - 611) كلفن باستخدام المفاعل الخريري (Trickle bed reactor) والعامل المساعد الصناعي كوبلت – موليبدنيوم (Cobalt – Molybdenum) المحمل على ثالث أوكسيد الألمنيوم ومدى درجات حرارة (583 – 643 ) ;كلفن وسرعة سائل فراغية (1.5- 3.75 ) ساعة -1 ونسبة الهيدروجين الى الزيت حوالي (250)لتر / لتر وضغط (3.5) ميكا باسكال . لقد بينت النتائج المستحصلة بان المحتوى الاوروماتي و نسبة الكبريت المزال تزداد مع زيادة درجة الحرارة وانخفاض السرعة الفراغية وان الخصائص اللزوجة والكثافة و نقطة الوميض و المتخلف الكار بوني للنواتج ينخفض مع زيادة درجة الحرارة آلا آن نقطة الانيلين عكس ذلك.


Article
Some Properties of Polymer Modified Self-Compacting Concrete Exposed to Kerosene and Gas Oil
بعض خواص الخرسانة المعدلة بالبوليمر ذاتية الرص المعرضة إلى النفط وزيت الغاز

Authors: Nada Mahdi Fawzi ندى مهدي فوزي --- Aqeel Kareem Weli عقيل كريم ولي
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2016 Volume: 22 Issue: 1 Pages: 31-48
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This thesis aims to study the effect of addition polymer materials on mechanical properties of self-compacting concrete, and also to assess the influence of petroleum products (kerosene and gas oil) on mechanical properties of polymer modified self-compacting concrete (PMSCC) after different exposure periods of (30 ,60 ,90 ,and 180 days).Two type of curing are used; 28 days in water for SCC and 2 days in water followed 26 days in air for PMSCC.The test results show that the PMSCC (15% P/C ratio) which is exposed to oil products recorded a lower deterioration in compressive strength's values than reference concrete. The percentages of reduction in compressive strength values of PMSCC (15% P/C ratio) was (6.03%) and (9.61%) up to 180 days of exposure to kerosene and gas oil respectively, relative to the same mix immersed in water, while the percentages of reduction in compressive strength values of SCC (reference concrete) was (21.18%) and (25.19%) up to 180 days of exposure to kerosene and gas oil respectively, relative to the same mix immersed in water. Flexural strength results present improvement for all ages and for all concrete mixes with all percentages of polymer content. The total water absorption values of PMSCC (15% P/C ratio) showed a better performance than reference concrete mix when exposed to oil products. It was (1.34, 2.21, 2.17) % up to 180 days with samples immersed in water, kerosene, and gas oil respectively, with percentages of reduction of (23.86%), (33.83%), and (31.33%) relative to the SCC (reference concrete).

الهدف من هذا البحث هو دراسة تأثير أضافه مواد بوليمرية على الخواص الطرية والميكانيكية للخرسانة ذاتية الرص, وكذلك أيجاد تأثير المشتقات النفطية (النفط الأبيض وزيت الغاز) على الخواص الميكانيكية للخرسانة المعدلة بالبوليمر ذاتية الرص والخرسانة ذاتية الرص بــعد التعرض لفترات مختـلفــة ( 30 ،60،90،180) يوم. نوعين من الانضاج تم استعمالهما حيث كانت 28 يوم غمر بالماء للخرسانة ذاتية الرص بينما 2يوم غمر بالماء متبوعة 26 يوم بالهواء للخرسانة المعدلة بالبوليمر ذاتية الرص.أظهرت نتائج فحص الخرسانة ذاتية الرص والخرسانة المعدلة بالبوليمر ذاتية الرص المغمورة بشكل مستمر في الماء تطوراً في خواصها الميكانيكية عند زيادة فترة الغمر بالماء . بينما تأثرت الخواص الميكانيكية للخرسانة ذاتية الرص والخرسانة المعدلة بالبوليمر ذاتية الرص المعرضة بشكل مستمر للمشتقات النفطية سلبياً.سجلت نتائج فحص الخرسانة المعدلة بالبوليمر ذاتية الرص المعرضة للمنتجات النفطية ادني تدهور في قيم مقاومة الانضغاط من الخرسانة المرجعية. حيث كانت النسبة المئوية للنقصان في مقاومة الانضغاط (6,03)% ، (9,61)% بعد 180 يوما من التعرض للنفط الأبيض وزيت الغاز على التوالي نسبة الى نفس الخلطة للنماذج المغمورة في الماء, بينما النسبة المئوية للنقصان في مقاومة الانضغاط للخرسانة المرجعية كانت (21,18)% و (25,19)% بعد 180 يوما من التعرض للنفط الأبيض وزيت الغاز على التوالي نسبة إلى نفس الخلطة للنماذج المغمورة في الماء.أظهرت نتائج مقاومه الانحناء إلى حصول تحسن في كل الأعمار وفي جميع نسب البوليمر. أظهرت نتائج امتصاص الماء الكلي للخرسانة المعدلة بالبوليمر ذاتية الرص وبنسبه استبدال 15% من مادة البوليمر إلى الاسمنت أداء أفضل من الخلطة المرجعية عند تعرضها للمنتجات النفطية, حيث كانت نسب الامتصاص الكلي هي (1.34 , 2.21 , 2.17 ) بعد 180 يوما من التعرض للماء والنفط الأبيض وزيت الغاز وبنقصان مقداره (23.86 ، 33.83 ، 31.33)% نسبة إلى الخرسانة ذاتية الرص (الخرسانة المرجعية).


Article
Hydrodesulfurization of Iraqi Atmospheric Gasoil by Ti-Ni-Mo/γ-Al2O3 Prepared Catalyst
أزالة الكبريت بالهيدروجين لزيت الغاز العراقي بواسطة الحفاز المحضر Ti-Ni-Mo/γ-Al2O3

Authors: Tariq Mohammed Naife طارق محمد نايف --- Hussain Kasim Hussain حسين قاسم حسين --- Abdul Halim Abdul Karim Mohammed عبدالحليم عبدالكريم محمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2017 Volume: 23 Issue: 11 Pages: 13-24
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study investigates the improvement of Iraqi atmospheric gas oil characteristics which contains 1.402 wt. % sulfur content and 16.88 wt. % aromatic content supplied from Al-Dura Refinery by using hydrodesulfurization (HDS) process using Ti-Ni-Mo/γ-Al2O3 prepared catalyst in order to achieve low sulfur and aromatic saturation gas oil. Hydrodearomatization (HDA) occurs simultaneously with hydrodesulfurization (HDS) process. The effect of titanium on the conventional catalyst Ni-Mo/γ-Al2O3 was investigated by physical adsorption and catalytic activity test.Ti-Ni-Mo/γ-Al2O3 catalyst was prepared under vacuum impregnation condition to ensure efficient precipitation of metals within the carrier γ-Al2O3. The loading percentage of metals as oxide; titanium oxide 3 wt. %, nickel oxide 5 wt. % and molybdenum oxide 12 wt. %. The performance of the synthesized catalyst for removing sulfur and aromatic saturation were tested at various temperatures 275 to 350°C, LHSV 1 to 4h-1, constant pressure 40 bar and H2/HC ratio 500 ml/ml.Results showed that the sulfur and aromatic content were reduced at all operating conditions. Maximum sulfur removal was 75.52 wt. % in gas oil on Ti-Ni-Mo/γ-Al2O3 at temperature 350˚C, LHSV 1h-1, while minimum aromatic content achieved was 15.6 wt. % at the same conditions.

هذه الدراسة تحقق تحسين من خصائص زيت الغازالعراقي والذي يحتوي 1.402 ٪ نسبة وزنية من الكبريت و16.88 ٪ نسبة وزنية من المركبات الاروماتية والذي تم الحصول عليه من مصفى الدورة عن طريق إدخاله لعملية ازالة الكبريت بالهيدروجين باستخدام الحفاز المحضر Ti-Ni-Mo /γ- Al2O3 لغرض الحصول على زيت غاز عراقي واطئ الكبريت واشباع المركبات الاروماتية ،عملية معالجة المواد الاروماتية بالهيدروجين تحدث تلقائيا مع عملية ازالة الكبريت بالهيدروجين ،تاثير اضافة التيتانيوم على الحفاز التقليدي Ni-Mo/γ- Al2O3 تحقق بواسطة الامتزاز الفيزياوي واختبار اداء الفعالية ، تم تحضير الحفاز تحت ضغط التحميل الفراغي لضمان كفاءة ترسيب المعادن داخل الحامل γ-Al2O3. نسبة تحميل اكاسيد المعادن على الحامل كانت 3 % نسبة وزنية من اوكسيد التياتنيوم و 5 % نسبة وزنية اوكسيد النيكل و 12 % نسبة وزنية من اوكسيد المولوبدنيوم.تم اختبار اداء الحفاز المحضر لازالة الكبريت واشباع المركبات الاروماتية لمختلف درجات الحرارة من 275 – 350 م˚وسرعة حجمية فراغية للسائل من 1- 4 سا -1 ، وضغط 40 بار ونسبة H2/HC 500مل/ مل .اظهرت النتائج أن محتوى الكبريت واشباع المركبات الاروماتية ينخفض في جميع ظروف التشغيل للحفاز المحضر. اعلى نسبة ازالة للكبريت تم الحصول عليها 75.52 % نسبة وزنية لزيت الغاز باستعمال الحفازTi-Ni-Mo/γ-Al2O3 حصلت في درجة حرارة 350م˚وسرعة حجمية فراغية للسائل 1 سا -1 ، بينما اقل قيمة للمحتوى الاروماتي 15.6 % نسبة وزنية وبنفس الظروف التشغيلية.


Article
Activated Bentonite for Removal Nickle and Vanadium from Petroleum Distillates
استخدام البنتونايت في ازالة الفناديوم والنيكل من المقطرات النفطية

Author: Luma Hussein Mahmood لمى حسين محمود
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2019 Volume: 25 Issue: 3 Pages: 11-22
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The present work is to investigate the feasibility of removal vanadium (V) and nickel (Ni) from Iraqi heavy gas oil using activated bentonite. Different operating parameters such as the degree of bentonite activation, activated bentonite loading, and operating time was investigated on the effect of heavy metal removal efficiency. Experimental results of adsorption test show that Langmuir isotherm predicts well the experimental data and the maximum bentonite uptake of vanadium was 30 mg/g. The bentonite activated with 50 wt% H2SO4 shows a (75%) removal for both Ni and V. Results indicated that within approximately 5 hrs, the vanadium removal efficiencies were 33, 45, and 60% at vanadium loadings of 10, 30, and 40 ppm respectively. Further processing of heavy gas oil with 10 ppm vanadium shows a continuous slight increase in metal removal with operating time. At 10, 20, 40, and 50 hrs the removal efficiency was 68, 75, 78 and 78% respectively. Results indicated that an equilibrium concentration of the 10 ppm of vanadium was attained after 30 hrs while for Nickel at a loading of 4 and 7 ppm the equilibrium achieved after 40 hrs. Results depicted that activated bentonite has higher selectivity towards Vanadium. Results depict that activated bentonite (ACB) has a remarkable capacity for removal of (V) and (Ni) from heavy gas oil.

العمل الحالي يهدف الى دراسة امكانية إزالة الفناديوم (V) والنيكل (Ni) من زيت الغاز الثقيل العراقي باستخدام البنتونايت المنشط. تم دراسة ظروف تشغيل مختلفة مثل درجة تنشيط البنتونايت، تحميل البنتونايت المنشط، ووقت التشغيل على تأثير كفاءة إزالة المعادن الثقيلة. أظهرت النتائج التجريبية لاختبار الامتزاز أن ((Langmuir isotherm يتنبأ جيدا بالبيانات التجريبية والحد الأقصى لامتصاص البنتونايت للفناديوم كان 30 ملغ / غم. وقد توضح من النتائج العملية ان البنتونايت المنشط مع 50٪ وزنا H2SO4 اعطى إزالة (75٪) لكل من Ni و V. وأشارت النتائج إلى أنه خلال حوالي 5 ساعات، كانت كفاءة إزالة الفناديوم 33 و 45 و 60٪ عند تركيز الفاناديوم من 10 و 30 و 40 جزء في المليون على التوالي. معالجة زيت الغاز الثقيل العراقي مع 10 جزء في المليون الفناديوم يظهر زيادة مستمرة في إزالة المعادن مع وقت التشغيل. في 10 و 20 و 40 و 50 ساعة حيث كانت كفاءة الإزالة 68 و 75 و 78 و 78٪. أشارت النتائج إلى أن تركيز التوازن ل 10 جزء في المليون من الفاناديوم قد تحقق بعد 30 ساعة بينما بالنسبة للنيكل عند التحميل 4 و 7 جزء في المليون ، يتحقق التوازن بعد 40 ساعة. أظهرت النتائج أن البنتونايت النشط له انتقائية أعلى نحو الفاناديوم. نتائج البحث أكدت أن البنتونايت العراقي المنشط لديه قدرة ملحوظة لإزالة (V) و (Ni) من زيت الغاز الثقيلالعراقي.


Article
The use of Prepared Zeolite Y from Iraqi kaolin for Fluid Catalytic Cracking of Vacuum Gas Oil
استخدام الزيولايت من نوع Y المحضر من الكاؤلين العراقي لعملية التكسير الحفازي المائع لمادة زيت الغاز الفراغي

Authors: Abdul Halim Abdul Karim Mohammed عبدالحليم عبدالكريم محمد --- Ibtehal Kareem Shakir ابتهال كريم شاكر --- Karim Khalifa Esgair كريم خليفة أزغير
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 10 Pages: 1256-1270
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The faujasite type Y zeolite catalyst was prepared from locally available kaolin. For prepared faujasite type NaY zeolite X-ray, FT-IR, BET pore volume and surface area, and silica/ alumina were determined. The X-ray and FT-IR show the compatibility of prepared catalyst with the general structure of standard zeolite Y. BET test shows that the surface area and pore volume of prepared catalyst were 360 m2/g and 0.39 cm3/g respectively. The prepared faujasite type NaY zeolite modified by exchanging sodium ion with ammonium ion using ammonium nitrate and then ammonium ion converted to hydrogen ion. The maximum sodium ion exchange with ammonium ion was 53.6%. The catalytic activity of prepared faujasite type NaY, NaNH4Y and NaHY zeolites was investigated by using the experimental laboratory plant scale of fluidized bed reactor. The cracking process was carried out in the temperature range 440 to 500 oC, weight hourly space velocity (WHSV) range 10 to 25 h-1 ,and atmospheric pressure . The catalytic activities of the prepared faujasite type NaY , NaNH4Y and NaHY zeolites were determined in terms of vacuum gas oil (VGO) conversion, and gasoline yield . The conversion at 500oC and WHSV10 hr-1 by using faujasite type NaY, NaNH4Y and NaHY zeolite were 50.2%, 64.1% and 69.5wt% respectively. The gasoline yield using the same operating conditions were 24.8%, 30.5% and 36.8wt% respectively.

تم تحضيرالعامل المساعد الفيوجيسايت نوع Y زيولايت من الكاؤلين المتوفر محليا. اجريت تحاليل الاشعة السينية , والاشعة تحت الحمراء , والمساحة السطحية و الحجم المسامي , وتحليل نسبة السليكا الى الالومينا للعامل المساعد فيوجيسايت نوع NaY زيولايت.اظهرت تحليلي الاشعة السينية , والاشعة تحت الحمراء توافق العامل المساعد المحضر مع التركيب العام للزيولايت القياسي و كانت المساحة السطحية 360م2 /غم والحجم المسامي 0.39 سم3 /غم .طور العامل المساعد المحضر فيوجيسايت نوع NaY زيولايت و ذلك باستبدال ايون الصوديوم بايون الامونيوم باستعمال نترات الامونيوم ومن ثم جرى تحويل ايون الامونيوم الى ايون الهيدروجين .كانت اعلى نسبة استبدال لايون الصوديوم 53.6% . درست الفعالية الحفازية للفيوجيسايت بصيغة الصوديوم NaY , و صيغة الامونيومNaNH4Y و صيغة الهيدروجين NaHY زيولايت باستخدام وحدة تجريبية بحدود درجات الحرارة بين 440 – 500 oC وسرعة فراغية بين 10 – 25 سا-1 .تم تعيين الفعالية الحفازية للفيوجيسايت بصيغة الصوديوم NaY , و صيغة الامونيومNaNH4Y و صيغة الهيدروجين NaHY زيولايت بصيغة تحويل المتفاعلات الى مختلف النواتج ونسبة الكازولين الناتج .لقد كانت نسبة تحويل المتفاعلات الى نواتج عند درجة حرارة 500 oC وسرعة فراغية 10 سا-1 50.2% و 64.1% و 69.5% على التوالي. وان انتاجية الكازولين لنفس الظروف التشغيلية كانت24.8% و 30.5% و 36.8% على التوالي .


Article
Preparation of bimetallic catalyst ( Ni –Co )for deep oxidative desulfurization
تـحـضيـر عـامـل مساعـد ثنائـي الـمـعـدن ( Ni –Co ) لاستخـدامـه فــي ازالـــة الـكـبـريــت بطريقة الأكسدة

Authors: Jalil R . Ugal --- Asmaa H. Hussein
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2014 Issue: المؤتمر العلمي الثاني لكلية العلوم Pages: 9-15
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

A bimetallic catalyst Ni-Co / γ-Al2O3was prepared by impregnationmethod . Characterizedby atomic absorption (AA) techniqueandXRDdiffraction. Thesurfacearea andpore volume was measuredaccordingthe BETmethod.Thiscatalyst was used in theoxidative desulfurization of gasoil in the presence of hydrogenperoxide H2O2 30% as an oxidizing agent. The results indicated that thecatalystwasefficient to remove sulfur from gas oil depending on temperature, hydrogen peroxide H2O2 30 % , solvent used for extraction. The maximum observed sulfur removal reached 70.44%.

تم خلال البحث تحضير عامل مساعد ثنائي المعدن من نوعNi-Co/γ-Al2O3بطريقة التشبيع وشخص بواسطة تقنيات الامتصاص الذري( AA ),وحيود الاشعة السينية وقياس المساحة السطحية والحجم الحبيبي .استخدم هـذا العامل المساعـد فـي عمليات الاكسدة لإزالة الكبريت من زيت الغاز بوجود بيروكسيد الهيدروجين كعامل مؤكسد.دلت النتائج على أن العامل المساعـد كان كفوءﴽ في ازالة الكبريت وتعتمد كفاءته على درجة الحرارة, وكمية بيروكسيد الهيدروجين وكمية المذيب المستخدم لأغراض الاستخلاص وانافضل ازالة للكبريت بلغت70.44%.


Article
Preparation and Characterization of Bimetallic Catalyst (NiO – CoO) for Desulfurization of Gas Oil
تحضير وتمييز عـامـل مساعـد ثنائـي الـمـعـــدن ( NiO –CoO ) لازالة الـكـبـريــت من زيت الغاز

Authors: Jalil R. Ugal جليل رهيف عكال --- Asmaa H. Hussein اسماء هادي حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2016 Volume: 13 Issue: 2ملحق ابحاث المؤتمر الوطني الثاني للكيمياء Pages: 75-83
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study NiO - CoO bimetallic catalysts are prepared with two Ni/Co ratios (70:30 and 80: 20) using the precipitation method of nitrate salts. The effects of Ni /Co ratio and preparation methods on the catalyst are analyzed by using different characterization techniques, i.e. atomic absorption (AA) , XRD, surface area and pore volume measurements according to the BET method . The results indicate that the best catalyst is the one containing the percentage of Ni :Co ( 70 : 30 ). Experiments indicate that the optimal conditions to prepare catalyst are stirring for three hours at a temperature of 60oC of the preparation , pH= (8-9) , calcination temperature at 400oC for two hours using the impregnation method . The catalyst activity is studied through the application in the process of oxidative desulfurization of gas oil fuel . The optimal conditions for deep oxidative desulfurization processes are : catalysts 3% , 2 gm. Na2 CO3 , refluxe time 3 hours at 400 C , using a mechanical stirrer at moderate speed (700 rpm), the volume ratio of gas oil : H2O2 : acetic acid is 10: 1: 0.5 and extracted with 1:1 ratio of acetonitrile to the gas oil for three times . The results indicate that the catalysts are efficient to remove sulfur from gas oil depending on temperature, time, concentration of hydrogen peroxide H2O2 30 % and solvent used for extraction. The efficiency of the best catalyst gives a maximum sulfur removal reaching 68.97%.

تم تحضير عوامل مساعدة ثنائية المعدن من نوع NiO – CoO وبنسب مختلفة من الكوبلت والنيكل (30:70 و20:80) بطريقة الترسيب باستخدام نترات المعادن وشخصت العوامل المساعدة المحضرة بواسطة تقنيات الامتصاص الذري (AA) وحيود الاشعة السينية وقياس المساحة السطحية والحجم الحبيبي .اشارت النتائج الى ان أفضل العوامل المساعدة هي التي تحتوي على نسبة النيكل : كوبلت (30: 70)دلت التجارب ان أفضل الظروف لتحضير العامل المساعد هي الترسيب بدرجة حرارة 60 م0 و pH تتراوح بين (9-8 ) ويتم التحميص عند درجة حرارة 400 م0 لمدة ساعتين.استخدمت هـذه العوامل المساعـدة المحضرة فـي عمليات الاكسدة لإزالة الكبريت من زيت الغاز gas oil بوجود بيروكسيد الهيدروجين كعامل مؤكسد و حامض الخليك (co-catalyst ).دلت النتائج على أن العامل المساعـد كان كفوءا في ازالة الكبريت وتعتمد كفاءته على درجة الحرارة , كمية بيروكسيد الهيدروجين وكمية المذيب المستخدم لأغراض الاستخلاص وأن الظروف المثلى لعملية الاكسدة هي : 3% من العامل المساعد و2 غرام من كربونات الصوديوم , واستخدام محرك ميكانيكي سرعته 700 دورة بالدقيقة وبنسب زيت الغاز : بيروكسيد الهيدروجين30% : حامض الخـليك (10: 1: 0, 5) اضافة الى استخدام استيونتريل للاستخلاص بنسبة (1:1) ثلاث مرات وكان زمن التصعيد ثلاث ساعات وبدرجة حرارة 40 م0. ولقد بلغت افضل ازالة للكبريت 68.97% .

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (7)

Arabic (1)


Year
From To Submit

2019 (1)

2017 (1)

2016 (2)

2014 (2)

2013 (1)

More...