Article
Influence of the Mechanical Properties of Composites for Indirect Dental Restorations on Pattern Failure
دراسة تأثير الخواص الميكانيكية للمتراكبات البوليميريه المستخدمة في ترميـــم الأسنان على أنماط الفشل

Loading...
Loading...
Abstract

This study evaluated the fracture pattern of two composites for indirect dental restoration relating to compressive strength and microhardness (Tetric and Tetric- Ceram).Four specimens of each composite polymerized by light were tested in universal testing machine at(1mm/min) crosshead for compressive strength . Microhardness was determined by the Vickers indentation technique. Results obtained show that the compressive strength and microhardness for the (Tetric–Ceram) was more than Tetric and showed partial fracture of the matter.Therefore, indirect composite resin (Tetric-Ceram) materials that guarante both good esthetics and adequate mechanical properties may be considered as substitutes of natural teeth.

في هذه الدراسة تم حساب نمط التكسر لنوعين من المتراكبات لمواد ترميم الأسنان تبعا لفحص الانضغاطية والصلادة ألمجهريه لمادتي (Tetric-Ceram,Tetric). حضرت أربعة نماذج من كل متراكب وتم بلمرتها باستخدام نظام التصلب الضوئي التقليدي و اجري عليها فحص الانضغاطيه باستخدام منظومة فحص الانضغاطيه بسرعة مقدارها( 1ملم دقيقه). قيست الصلادة ألمجهرية للنماذج المحضرة أعلاه باستخدام منظومة الصلادة ألمجهريه (Vickers). من النتائج المستحصله تبين إن متانة الانضغاطيه والصلادة ألمجهريه للمادة (Tetric-Ceram) كانت أعلى مقارنة بمادة إل (Tetric) التي أظهرت فشل جزئي لجسم المادة لذالك فان المواد المتراكبة البوليميريه (Tetric-Ceram) المستخدمة في هذا البحث أعطيت نتائج جيدة وميكانيكيه مقبولة وتكون مناسبة لترميم وتعويض السن الطبيعي.


Article
Investigate the Microstructure and the Mechanical Properties of Ni-Ti-Cu Shape Memory Alloys
التحقيق في البنيه المجهرية والخواص الميكانيكيه لسبائك Ni-Ti-Cu الذاكرة الشكل

Authors: Dania F. Abbas Aljuboori --- Kadhim K.Resan --- Ayad M.Takhakh
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2017 Volume: 20 Issue: 1 Pages: 105-112
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this study a Nickel-Titanium-Cupper shape memory alloys was manufactured by powder metallurgy (PM) technique, powder mixture of 50% Ti , 47% Ni and 3% Cu was prepared by mixing for two hours and compacted in a press machine using various compacting pressure (600, 700 and 800) MPa , sample was then sintered for 5 hrs in an electrical tube vacuum furnace using sintering temperature of (850˚C, 900˚C and 950˚C) .phase analysis of samples was conducted by X-ray diffraction test, the effect of different sintering temperature and compacting pressure on the porosity, microhardness ,compression strength and the shape memory effect (SME) was studied, the result showed decrease in the porosity and increasing in the shape recovery ,compression strength and microhardness with increasing compacting pressure and at lower sintering temperature and hence the best results was at 800MPa compacting pressure and 850˚C sintering temperature.

في هذه الدراسة تم تصنيع سبائك ذاكره الشكل (نيكل – تيتانيوم – نحاس) بواسطة تقنيه ميتالورجيا المساحيق وتم تحضير النماذج بخلط المساحيق بنسب وزنية (50%Ti)، (47%Ni ) و((3%Cu لمدة ساعتين. تم كبس الخليط بضغط 600،700و 800 ميكا بسكال وبعدها أجراء عملية التلبيد باستخدام فرن كهربائي و لمده 5 ساعات وبدرجات حرارة 950,900,850 ˚م. تم دراسة تكون الأطوار باستخدام مطياف الأشعة السينية , ودراسة تأثير حرارة التلبيد وضغوط الكبس المختلفة على المسامية, الانضغاط,الصلادة وقابليه التذكر للسبائك.النتائج العملية أظهرت زيادة قابليه التذكر,الصلادة, قوة الانضغاط ونقصان المسامية بزيادة الضغط ونقصان درجه حرارة التلبيد وبالتالي فأن أفضل النتائج كانت عند ضغط كبس 800 ميكا بسكال وحرارة تلبيد850˚ م.