Article
Numerical Simulation of Three Dimensional Water Flow ThrougSpray Nozzle h

Loading...
Loading...
Abstract

A three dimensional numerical simulation of turbulent water flow through airwasher system nozzles of cylindrical junction with diameters of 2 mm, 3 mm, 4 mm, 5mm respectively and of centered diameter with 4 mm was achieved by using FLUENT software. kεmodel was used in this study. The entrance region of the model wasselected to ensure the constant velocity in the inlet gives results near real solution.Modeling includes the construction of a 3D model with the aid of AUTOCAD and GAMBIT. For the purpose of checking the applicability of the modeling and discovering the best location and diameter of cylindrical junction, five differentlocations and diameters of the cylindrical junction were selected. The present workshows that the best location and diameter are observed for the case of 4 mm. The flowsimulation was achieved by studying the velocity vector plot and contour plot ofpressure in different slices locations through each of 5 geometries. The results wereidentical to the physical phenomenon which was observed in the laboratory of fluidmechanics, where the velocities and pressures are zero at exit cylinder center whichmeans that there is no fluid at center of exit cylinder for 4mm case as shown in Fig(1).The results show also that the maximum skin friction occurs at the peripheralboundaries of the cylindrical junction and exit cylinder.

Keywords

AA


Article
التعقيد في المدينة الكسرية
دراسة تحليلية لجزء من منطقة الاعظمية

Loading...
Loading...
Abstract

The complexity as one of the basic and adequate concepts configuring the structure offragmental city has been considered in this search, where it plays an important role in realizingan essential reality which is human can deal with far of routine and tedium. The search explainsthat the fragmental city as an urban environment is developing gradually due to complexitygrowing up in entire city environment through favorite and multiple planes in the complexity,and presentation of society importance in realizing the complexity socially and physically; aswell as presenting the relation between physical complexity and social complexity whether thecomplexity is declared or hidden. particularly and stands on the fragmental mechanisms, styles,generation methods, important properties, and fragmental linear and nonlinear concepts. Thesearch browses the previous studies that deal with fragmental city concept so that the problemof search (Absence of obvious and scientific concept about complexity role in fragmentalcity as one of fundamental properties configuring the structure of fragmental cities) hasbeen determined where summary and conclusions are provided.. The complexity has been browsed through its role in the fragmental city as a main structure ofsearch where a browsing for its meaning in lingual manner and architecturally, its importantproperties, its role in architectonic generally and urban environment particularly in order to getthe complexity's indications. The indications of complexity will be adopted in the practical partof search and measured to see the role of complexity in the fragmental city and to determine theparticular problem of search (absence of obvious concept of the relation of complexity with ingredients for fragmental city according to its favorite grade and level.then selection andanalysis of region that represents the practical part of search where the particular indications ofcomplexity for fragmental city have been measured depending on the observation study on AlAdamiyacity bysearcher. This leads to therecommendationsand conclusionsthat refer to thepresencea quantityof complexitypresented at a favorite level in the old structures morethaninthemodernstructuresin other words that refersto the presenceof complexityrole in thefragmentalcity.

Keywords

AA


Article
Improvement of Mechanical and Fatigue Properties for Aluminum Alloy 7049 By Using Nano Composites Technique
تحسين الخصائص الميكانيكية و الكلال لسبيكة المنيوم 7049 باستخدام تقنية المركبات النانوية

Loading...
Loading...
Abstract

The aim of present work is to improve mechanical and fatigue properties for Aluminum alloy7049 by using Nano composites technique. The ZrO2 with an average grain diameter of 30-40 nm, was selected as Nano particles, to reinforce Aluminum alloy7049 with different percentage as, 2, 4, 6 and 7 w⁡t%. The Stir casting method was used to fabricate the Nano composites materials due to economical route for improvement and processing of metal matrix composites. The experimental results were shown that the adding of zirconium oxide (ZrO2) as reinforced material leads to improve mechanical properties. The best percentage of improvement of mechanical properties of 7049 AA was with 4% wt. of ZrO2 about (7.76% σ_u) for ultimate tensile stress UTS, (9.62% σ_y) for yield stress YS and (9.92%) for hardness HB than other of adding of 2, 6 and 7% of ZrO2. Also the results shown that the fatigue strength of 7049 AA with 4 w⁡t% ZrO2 nanoparticles is higher than that of 7049 AA under constant loading 9.86% at 108 cycles as well as the fatigue life factor (IFLF %) at different amplitude stress 400, 350, 300 and 250 MPa was improvement in range 66, 115, 63 and 107% respectively.

الهدف من العمل الحالي هو تحسين الخصائص الميكانيكية والكلال لسبائك الألومنيوم 7049 باستخدام تقنية المركبات النانوية. تم اختيار ZrO2 بمتوسط قطر الحبوب 30-40 نانومتر ، كجسيمات نانوية ، لتدعيم سبائك الألومنيوم 7049 بنسب وزنية مئوية مختلفة 2 ، 4 ، 6 و 7٪. تم استخدام طريقة الصب (Stir casting method ) لتصنيع المركبات النانوية بسبب العامل الاقتصادي لتحسين مركبات المصفوفة المعدنية وتصنيعها. أظهرت النتائج العملية أن إضافة أوكسيد الزركونيوم (ZrO2) مادة نانوية مدعمة تؤدي إلى تحسين الخواص الميكانيكية وان أفضل نسبة تحسين في الخواص الميكانيكية لـ 7049 AA كانت بـاستخدام نسبة وزنية 4٪ فكانت نسبة التحسين تساوي (σu 7.76 ٪) و (9.615σy ٪) و (9.92 ٪) للإجهاد الشد الاقصى UTS و للإجهاد الخضوع YSو للصلابة HB على التوالي من غيرها عند استخدام 2 ، 6 و 7 ٪ من ZrO2. كما أظهرت النتائج أن متانة الكلال لسبيكة 7049 AA عند استخدام 4 ٪ من الجسيمات النانوية ZrO2 أعلى بنسبة 9.86 ٪ من متانة الكلال لسبيكة الالمنيوم 7049 AA بدون اضافة اي نسبة من اوكسيد الزركونيوم عند اختبار حمل ثابت عند 108 دورة ، فضلا عن معامل عمر الكلال (IFLF ٪) عند اختبار بإجهادات مختلفة كانت 400 و 350 و 300 و 250 ميكا باسكال تحسنًا بحدود 66 و 115 و 63 و 107٪ على التوالي.

Keywords

Nanomaterial --- 7049 AA --- ZrO2 --- Stir casting.


Article
Experimental and numerical evaluation of friction stirs welding of AA 2024-W aluminum alloy
الحلول العملية والرقمية للحام الاحتكاكي بالمزج (FSW) لسبيكة المنيوم AA2024-W

Authors: Ayad M. Takhakh أياد مراد طخاخ --- Hamzah N. Shakir حمزة نورالدين شاكر
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2012 Volume: 18 Issue: 6 Pages: 717-734
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Friction Stir Welding (FSW) is one of the most effective solid states joining process and has numerous potential applications in many industries. A FSW numerical tool, based on ANSYS F.E software, has been developed. The amount of the heat gone to the tool dictates the life of the tool and the capability of the tool to produce a good processed zone. Hence, understanding the heat transfer aspect of the friction stir welding is extremely important for improving the process. Many research works were carried out to simulate the friction stir welding using various softwares to determine the temperature distribution for a given set of welding conditions. The objective of this research is to develop a finite element simulation of friction stir welding of AA2024-W Aluminium alloy. Numerical simulations are developed for thermal conductivity, specific heat and density to know the relationship of these factors with peak temperature. Variation of temperature with input parameters is observed. The simulation model is tested with experimental results. The results of the simulation are in good agreement with that of experimental results.

يعد اللحام الاحتكاكي بالمزج (FSW) واحد من الطرق الفعالة للحام الحالة الصلبة ويدخل في الكثير من التطبيقات في مختلف الصناعات . تم تطوير حلول رقمية للحام الاحتكاكي بالمزج بالاعتماد علر برنامج ANSYS لحساب كمية الحرارة المتولدة خلال عملية اللحام والتي تؤثر على عمر وجودة منطقة اللحام والعدة، اذ ان من المهم معرفة كيفية انتقال الحرارة خلال اللحام الاحتكاكي بالمزج. عدد من الباحثين درسو توزيع درجات الحرارة خلال هذا النوع من اللحام باستخدام برامجيات متعددة. الغرض من هذا البحث تطوير حلول رقمية باستخدام طريقة العناصر المحددة (FEM) بالاستناد على برنامج ANSYS لسبيكة المنيوم نوع AA2024-W . تم تطوير هذه الحلول بالاعتماد على العلاقة التي تربط خواص التوصيل الحراري و الحرارة النوعية و الكثافة مع درجات الحرارة حيث تتغير هذه الخواص بتغير درجات الحرارة. المحاكة التي تم الحصول عليها تم التحقق عملياً من نتائجها واظهرت نتائج المقارنة وجود توافق جيد .


Article
Binomial Expressions with Reference to Du’aa as-Sabaḥ (The Morning Invocation) by Imam Ali bin Abi Ṭalib (AS)

Author: Ahmed Muhammad Mahdi
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2016 Volume: 24 Issue: 1 Pages: 188-197
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This paper deals with the linguistic phenomenon of ‘binomial expressions’. These are expressions that involve two words belonging to the same word-class. The linkage of the two members of any binomial expression is accomplished through the use of either a preposition or conjunction. There is usually a semantic relation between these members of some sort. The study comprises two sections. The first presents a theoretical background of binomial expressions. Views and opinions of scholars are cited with regard to their treatment of these expressions. In this section, a short survey of the previous research on the topic is presented. This theoretical background is then applied to the Arabic text of Du’aa as-Sabaḥ by Imam Ali bin Abi Ṭalib (PBUH). Instances of binomials in this text are extracted and analyzed in terms of the ordering of occurrence of the members of the binomial expressions. The previous and following discourse (linguistic context( are considered important in the analysis of the ordering. The members of the binomials in the Du’aa are joined by the coordinator (و) .They are predominantly nouns except for only one in which an adjective occurs. Some of the binomials are resistant to reversibility because of religious or cultural constraints.

يتناول هذا البحث الألفاظ الثنائية كظاهرة لغوية. تشتمل هذه الألفاظ على كلمتين من نفس الصنف. ترتبط هاتين الكلمتين مع بعضهما بحرف جر أو عطف و تربطهما علاقة دلالية. قُسم البحث الى جُزأين يُقدم الجُزء الأول خلفية نظرية عن هذه الألفاظ تشمل وجهات نظر واراء الباحثين حول الموضوع. يحتوي هذا الجُزء على عرض مختصر للدراسات السابقة حول الموضوع. طُبقت هذه الآراء على النص العربي لدُعاء الصباح المروي عن أمير المؤمنين علي بن أبي طالب(عليه السلام). تناول البحث بالتحليل الثنائيات التي وردت في الدُعاء الشريف من قبيل ترتيب أو تتابع الكلمتين اللتان تحتويها كُل ثُنائية. يُعد السياق اللغوي عاملاً مُهما يؤثر على تحديد أي من الاسمين اللذين يؤلفان الثُنائية يسبق الاخر في الظهور.


Article
ENHANCEMENT OF CUMULATIVE CORROSION-FATIGUE INTERACTION LIVES OF 6061-T6 ALUMINUM ALLOY USING ULTRASONIC IMPACT PEENING PROCESS

Authors: Hussain Jasem Mohammed Al-Alkawi --- Amer Hameed Majeed --- Saba Farhan Naser
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2019 Volume: 23 Issue: 4 Pages: 132-144
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The fatigue behavior of 6061-T6 aluminum alloy under constant and variable amplitude loading was investigated in air for as-received and pre-corroded specimens in 3.5% NaCl corrosive solution for 77 days. The experimental results presented that the tests of fatigue life on pre-corroded samples with and without ultrasonic peening revealed a significant reduction in life related with the presence of corrosion defects before cyclic loading. In state of unpeened specimens the constant S-N fatigue strength curve was decreased by 4.5% due to immersed the specimens in corrosive 3.5% NaCl solution for 77 days, while in state of ultrasonically peened specimens for 10 sec. per line and 2.5 joul energy the reduction of S-N curve decreased to 2.2% due to the beneficial effect of this treatment for increasing the corrosion-fatigue life. The improvement of fatigue life and corrosion-fatigue life of specimens when applying of ultrasonic peening was 8.69% for dry fatigue life and 2.3% for corrosion-fatigue interaction. The results of cumulative corrosion-fatigue tests indicated that the life of corroded specimens under the effect of ultrasonic peening treatment improved to approximately (3% ـــ 2.25%) for low-high and high-low sequences.


Article
Polymorphism of AA-NAT gene and its relationship with the productive and reproductive performance in Turkish Awassi ewes
المظاهر الوراثية لجين AA-NAT وعلاقتها بالأداء الانتاجي والتناسلي في النعاج العواسي التركي

Authors: Gheni N. Addin غني ناصر الدين طه --- Thair R. Mohammed ثائر رشيد محمد --- Nasr N. Al-Anbari نصر نوري الأنباري
Journal: ANBAR JOURNAL OF AGRICULTURAL SCIENCES مجلة الأنبار للعلوم الزراعية ISSN: PISSN: 19927479 / EISSN: 26176211 Year: 2016 Volume: 14 Issue: 2 Pages: 246-255
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This study was conducted in the sheep farm of Department of Animal Production Sheep Field /Faculty of Agriculture University of Baghdad in the Jadiriyah area, as well as laboratories of Genetic Engineering and the Institute of Life Technologies Graduate Studies-University of Baghdad, during the period from 01/04/2015 to 01/02/2016, in order to identify genetic manifestations gene AA-NAT and its relationship with some of reproductive and productive traits among a sample of 30 Turkish Awassi ewes and offspring of 38 births. There was a genetic variation in polymorphism manifestations of the gene AA-NAT depending on the different genetic packets that generated by enzymatic digestion, which showed to be of three appearances (3 packs AA; 5 packs GA and 4 packs GG). The distribution of genetic manifestations attributed to gene AA-NAT in a sample Awassi sheep 56.67 and 33.33 and 10.00% for each of the genotypes AA and GA and GG respectively, and it was the contrast between these highly significant proportions, it was observed that the influence of appearance hereditary gene AA-NAT in the prolificacy and twining rate highly significant, while there was no significant difference in the fertility percentage. The results of the current study showed that the daily and total milk production of Awassi ewes was morally affected (P <0.05) genotype appearance, as ewes achieved with genotype AA the best rates, while those registered with genotype GG lowest rates. It can be concluded from this study of gene expression for gene AA-NAT possible adoption in the development of genetic improvement strategies for the sheep to maximize the economic returns of the election and crossing genotypes that have achieved the best prolificacy rate, twinning percentage and milk production.

أجري البحث في حقل الاغنام التابع لقسم الإنتاج الحيواني-كلية الزراعة-جامعة بغداد في موقع الجادرية، فضلا عن مختبرات معهد الهندسة الوراثية والتقانات الحياتية للدراسات العليا/جامعة بغداد للمدة من 1/4/2015 ولغاية 1/2/2016، بهدف تحديد المظاهر الوراثية لجين AA-NAT وعلاقتها ببعض الصفات التناسلية والإنتاجية لدى عينة مكونة من 30 نعجة عواسي تركية ومواليدها من الحملان البالغ عددها 38 مولودا. اختلفت المظاهر الوراثية (Polymorphism) للجين AA-NAT تبعا لاختلاف الحزم الوراثية الناتجة عن الهضم الإنزيمي التي بلغت ثلاث مظاهر (3 حزم AA و5 حزم GA و4 حزم GG). كانت نسب توزيع المظاهر الوراثية لجين AA-NAT في عينة الأغنام العواسية 56.67 و33.33 و10.00% لكل من التراكيب الوراثية AA وGA وGG على التوالي، وكان التباين بين هذه النسب عالي المعنوية، وكان تأثير المظهر الوراثي لجين AA-NAT في معدل الخصب ونسبة التوائم عالي المعنوية في حين لم يكن التباين معنويا في نسبة الخصوبة. أظهرت نتائج الدراسة الحالية أن إنتاج الحليب اليومي والكلي للنعاج العواسي كان قد تأثر معنويا (P<0.05) بالمظهر الوراثي، إذ حققت النعاج ذات التركيب الوراثي AA أفضل المعدلات في حين سجلت مثيلاتها ذات التركيب GG أدنى المعدلات. يمكن أن نستنتج من خلال دراسة التعبير الجيني لجين AA-NAT أمكانية اعتماده في وضع استراتيجيات التحسين الوراثي لدى الأغنام لتعظيم العائد الاقتصادي من مشاريع تربيتها بانتخاب وتضريب التراكيب الوراثية التي حققت أفضل معدل خصب ونسبة توائم وإنتاج حليب.


Article
Experimental Study on Tribological Characteristics of AA 6061 Alloy Reinforced with Al2O3 and B4C Particles
دراسة تجريبية للخصائص الترايبولوجية لسبيكةAA 6061 المقوّاة بدقائق Al2O3 و B4C

Authors: Khansa Daood AlShamari خنساء داوود الشمري --- Ihsan Kadhom AlNaimi إحسان كاظم عباس النعيمي --- Raad Hameed Majid رعد حميد ماجد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2018 Volume: 24 Issue: 6 Pages: 1-10
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Two different composite materials were prepared by stir casting method of AA 6061 alloy as a matrix reinforced with two addition different ceramic materials Al2O3 and B4C of grain size 20 µm by 2.5, 5, 7.5 and10% in weight. The composite material with aluminum alloy as a matrix possesses a unique mechanical properties such as: high specific strength and hardness, low density, and high resistance to corrosion and friction wear. This composite is widely used in automotive parts space and marine applications.Pin-on-disc technique was used to calculate the wear rate for each addition of Al2O3 and B4C particles. Rockwell hardness test and optical micrographs examinations were carried out to analyze, compare, and evaluate the addition of reinforced particles. The results of this investigation appeared that the 7.5% of ceramic particles addition give highest values of the hardness and wear resistance.

تم تحضير مادتين مركبة بطريقة السباكة بالمزج لسبيكة ألمُنيوم AA 6061 كمادة أساس مقوّاة بنوعين من الدقائق السيراميكية المضافة Al2O3 و B4C بحجم حبيبي 20 ميكرون وبنسبة وزنية 2.5، 5، 7.5 و 10%. تمتلك المادة المركبة من الألمُنيوم كمادة أساس خواص ميكانيكية فريدة مثل: مقاومة نوعية وصلادة عاليتين، كثافة منخفضة، ومقاومة عالية للتآكل، والتآكل الاحتكاكي. غالباً ما تستعمل هذه المواد المركبة في الفضاء، أجزاء السيارات، والتطبيقات البحرية. تقنية المسمار-على-القرص قد استخدمت لحساب نسبة معدل البلى لكل من الدقائق المضافة Al2O3 و B4C. اختبار روكويل للصلادة وفحص الصور المجهرية تم إجراؤها لتحليل، مقارنة، وتقييم إضافة الدقائق المقوّاة. نتائج هذا البحث أظهرت أن نسبة إضافة 7.5% من الدقائق السيراميكية أعطت قيم عالية للصلادة ومقاومة البلى.


Article
The significance of preoperative white blood cells count and ultrasonography for diagnosis of acute appendicitis

Author: Majeed H. H.AL-amiri مجيد حمود العامري
Journal: Al-Qadisiyah Medical Journal مجلة القادسية الطبية ISSN: 18170153 Year: 2011 Volume: 7 Issue: 12 Pages: 247-253
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Background:Appendicectomy is still the most common surgical procedure; but diagnostic failure may still occur & leads to delay in treatment or negative appendicectomy.Objectives of this study:to evaluate value of preoperative white blood cells count &ultrasonography in diagnosis of acute appendicitisPatients and methods:This study had been carried on 588 cases of acute appendicitis. Appendicectomy done for all cases. Over period of 4 years from January 2006-january 2010. the range of age was between 7-76 years.With mean age of (41.5 years).and median age 25 years old. 366 males (62.244%) and 222 females (37.755). ultrasonography done for all patients by our radiologists. white blood cells count performed in our lab.Results:Negative appendicectomy rate was 102 patients (17.346%) this rate was 42 patients (11.475%) for male and 60 patients (27.027%) for female patients. positive appendicitis in 486Increase white blood cells count for acute appendicitis (histological positive result) in 388 patients (79.835%) from the 486 patients.And increase white blood cells count for non-acute appendicitis (i.e. negative histological result) in 52 patients (50.980) from the 102 patients.Conclusion:In spite of the improvement tests for acute appendicitis we could not sufficiently reduce the negative appendicectomy rate. If there is doubt about the diagnosis although leukocyte levels and altrasonographic result are normal, especially for female patients performing further radiologic examination such as CT can be favorable.

تمت الدراسة على 588 مريض مصاب باعراض التهاب الزائدة الدودية،جميعهم تم لهم استئصال الزائدية الدودية بعملية جراحية ،خلال اربعة سنوات من كانون الثاني 2006- الى كانون الثاني 2010 . 366 مريض ذكر و222 مريضة انثى، اعمارهم تتراوح بين 7-76 سنة. جميعهم يشكون من اعراض التهاب الزائدة الدودية مثلا الم حول السرة او الم اسفل الجهة اليمنى من البطن مع تقيء وعدم الشهية للاكل الخ. وتم اجراء فحص سونار البطن لجميعهم, واجراء فحص عدد كريات الدم البيضاء لهم في شعبة الاشعة وشعبة المختبر التابعين للمستشفى .الهدف من هذة الدراسة لمعرفة اهمية اجراء فحص سونار البطن واجراء الفحص المختبري لعدد كريات الدم البيضاء لغرض تشخيص التهاب الزائدة الدودية.وتم استئصال الزائدة الدودية لكل المرضى وارسلت الزائدة للفحص النسيجي للتاكد من حقيقة التهابها من عدمة. وكان هناك 102 مريض ,كانت نتيجة الفحص النسيجي سالبة اي بنسبة%346. 17. وكانوا 42 مريض ذكر و60 مريضة انثى. وتبين ان نسبة اجراء عملية سالبة تقل كلما كان هناك ارتفاع في عدد كريات الدم البيضاء وهناك دلائل على التهاب الزائدة الدودية بواسطة السونار. وتبين وجود نتيجة للفحص النسيجي موجبة في 486 مريض اي بنسبة%653. 82 . زيادة عدد كريات الدم البيضاء في الدم للحالات الموجبة للزائدة الدودية كانت في 388 مريض اي بنسبة%835 .79. وكانت عدد كريات الدم البيضاء في الدم للحالات السالبة في 52 مريض اي بنسبة%980. 50.في 198 مريض اي بنسبة%673. 33 كان فحص السونار سالب. ومن 198 مريض كان 89 مريض اي بنسبة%949. 44 كانت نتيجة الفحص النسيجي موجبة.و390 مريض اي بنسبة%326. 66 كان فحص السونار موجب والفحص النسيجي ل 45 مريض منهم اي بنسبة%538. 11 سالب .


Article
THE EFFECT OF HEAT TREATMENTS ON MECHANICAL PROPERTIES OF ALUMINUM ALLOY AA 2024-T6
تأثير المعاملات الحرارية على الخواص الميكانيكية لسبيكة الالمنيوم 2024 – T6

Author: Ekhlas Ahmed
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2013 Volume: 13 Issue: 3 Pages: 402-409
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

This paper is aimed to study the effect of solution heat treatment on mechanical properties of Al alloy AA 2024-T6 (Tensile, hardness, wear resistance), many specimens were prepared according to ASTM and then heated to 500ºC for one hour and water quenched.Artificial aging carried out at 190ºC for (1, 2, 5) hours and cooled slowly by air to show the effect of aging time on mechanical properties, many examinations (Microstructure, hardness Tensile and wear test) were done for specimens.From the obtained results it can be see that heat treatment contributed in mechanical properties improvement.

يهدف البحث الى دراسة تأثير المعاملات الحرارية على الخواص الميكانيكية لسبيكة الالمنيوم 2024 T6 AA (مقاومة الشد والصلادة ومقاومة بلى), حيث تم تصنيع عينات وفق المواصفات القياسيةASTM , بعدها اجريت عدة اختبارات قبل وبعد المعاملة المحلولية التي تضمنت تسخين العينات الى حرارة 500ºC ثم التبريد السريع بالماء وبعدها تم اعادة التسخين الى درجة 190ºC لمدة (1, 2, 5) ساعة ومن ثم التبريد البطيء بالهواء لغرض التعتيق الصناعي. النتائج التي تم الحصول عليها اظهرت ان المعاملات الحرارية ساهمت في تحسين الخواص الميكانيكية.

Listing 1 - 10 of 16 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (16)


Language

English (10)

Arabic (3)

Arabic and English (2)


Year
From To Submit

2019 (4)

2018 (1)

2017 (2)

2016 (3)

2013 (2)

More...