Article
Using Propylene–Ethylene Grid to Improve the Production of Precast Concret Slabs
استخدام مشبكات البروبلين اثيلين في تطوير صناعة الألواح الخرسانية الجاهزة الصب ( الشتايكر )

Author: Zainab Abdulrdha Thweny
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 4 Part (A) Engineering Pages: 741-751
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The precast concrete roofing slab produced from the local factory were below the Iraqi standard requirement (NO 1107-1988). This study has been made to improve the production of precast concrete slabs by using(propylene – ethylene copolymer grid )which is a waste material produced from the base of polymer boxes . The depended mix of the precast concrete slab in the local factory did not use the correct proportion ,tested mixes were redesigned and prepared to achieve the limited requirements . Propylene – ethylene copolymer grid was used to have better results, less costs, with protection of the environment from pollution ,where there is difficulty to remove it even when it is fully exposed to severe weather conditions .the manufactured slabs had dimensions of (800×800×40)mm and testing program extended to 60 days of age and comprised ,breaking loads, water absorption ,and impact resistance of concrete. The total number of manufactured samples was (55 slabs). The test results indicated that the weigh ted mix proportions ((1:1.5:2.45) cement :sand : gravel ) with w/c=0.41 , superplasticizer(0.75 liter/100 kg of cement )and propylene –ethylene copolymer grid with a dimension (600×600)mm enhances the mechanical properties of concrete . It increased the breaking load by 81 % compared to ordinary production. while the impact resistance increased to 26 blows compared to 3 blows for the ordinary production. However, the polymer grid decreased the width and depth of cracks and maintained the integrity of the slabs after failure .

عند اخذ عينات من الألواح الخرسانية الجاهزة الصب المنتجة في المعامل المحلية تبين بأنها لا تحقق النسب المطلوبة ضمن المواصفات القياسية العراقية (رقم 1107 لسنة 1988) وقد تمت دراسة أمكانيه تحسين وتطوير صناعه قطع الصب الجاهز (الشتايكر) باستخدام مواد متوفرة محليا وهي عبارة عن مشبكات الأقفاص البلاستيكية المتكونة من مادة البروبلين اثيلين كوبوليمر . إن الطريقة المتبعة من قبل المنتج المحلي لا تستخدم النسب الصحيحة للخلط وبذلك تم إعادة تصميم الخلطة الخرسانية للوصول إلى الحدود المطلوبة ضمن المواصفة القياسية العراقية ، كما تم إضافة مشبك بلاستيكي لتعزيز الحصول على نتائج أفضل وبكلفة قليلة مع الحفاظ على البيئة حيث إن المواد البوليميرية يصعب التخلص منها حتى في الظروف الجوية القاسية وقد تم أعداد قطع كونكريتية بإبعاد (800*800*40 ) ملم .وأمتد البرنامج العملي لغاية 60 يوم ، وتم دراسة خواص القطع المنتجة من خلال فحوصات قوة الكسر ، امتصاص الماء ومقاومة الصدم , بلغ العدد الكلي للنماذج المصنعة (55 عينه).وبعد إجراء محاولات عديدة تم التوصل إلى خلطة بنسب وزنيه ( 1 :1.5 :2.45 ) ( الاسمنت : رمل : حصى ) مع مضاف مقلل للماء بنسبة 0.75 لتر لكل 100 كيلو غرام من الاسمنت لتصبح نسبة الماء إلى الاسمنت بما يعادل 0.41 ، واستخدام مشبك بلاستيكي بأبعاد (600* 600 ) ملم قد أعطت لهذه الخلطة زيادة في قوة الكسر بما يعادل 81% عن قطع الخلطة المعتمدة في المعامل المحلية ، بينما ازداد عدد الضربات اللازمة لتحقيق الفشل إلى 26 ضربة بدلا من 3 ضربة بالنسبة للخلطة المحلية .كما تبين إن استخدم المشبك البلاستيكي يقلل من عرض ومن عمق الشقوق المتكونة في القطع الكونكريتية ويقلل من تشظي وتكسر الخرسانة ويساعد على بقاء القطعة ككتلة واحدة .


Article
Structural Behavior Of Self-Compacting Concrete Reinforced T-Beams

Authors: Mohammed M. Salman محمد مصلح سلمان --- Mohammed M. Rasheed --- Yahya S. Khudhair kingconger2000@yahoo.com
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 1 Pages: 284-299
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The study is concerned with the structural behavior of (12) reinforced T-shaped cross-section beams made of self-compacting concrete under flexural with two types of fibers (polypropylene and steel fibers). Compression and tensile strengths, deflection, ductility and cracking behavior are considered. Experimental results are compared with these evaluated based on the (ACI 318 – 08). The variables studied are reinforcing ratio (%ρ) (between %4.4907 - %6.0434) using different sizes of reinforcing steel bars (Ф25mm, Ф20mm, Ф16mm, Ф12mm, Ф6mm, Ф4mm, and Ф6mm wire mesh), in addition to two fibers, [polypropylene (RHEO-FIBERS®) and steel fibers (FIBERFORCE®) at a rate of [(1kg/m3) & (0.5%)], respectively. The tested T-Beams were categorized into three groups, each group includes (4) T-Beams of different steel ratios (ρ %). In Group (G1), polypropylene fibers were used. In Group (G2), steel fibers were used. The reference group (G3) is with the same reinforcement ratios as in the previous two groups. It was concluded that using polypropylene fibers (RHEO-FIBERS®)in addition to (1kg/m3) in self-compacting concrete (SCC) improves the cracking control, ductility by (Δμd = 0.5846 – 4.0514). However, fibers have minor effect on the deflection behavior of T-Beams. On the other hand, when steel fibers type (FIBERFORCE® steel fibers) of a volume rate of (Vf = 0.5% of concrete volume Vc) are used in combination with self-compacting concrete, affects the flexural behavior of T-Beams (reducing deflection, increasing ultimate loads' by (11.02% - 16.80%) and improving the ductility by (Δμd = 4.9232 – 12.1238), but it has a minor effect on reducing the crack width.

أن هذا البحث يهدف ألى دراسة السلوك الأنشائي للعتبات الخرسانية ذات المقاطع بشكل حرف (T) بعدد (12 عتب) والمسلحة بنوعين من الألياف (ألياف البوليمر وألياف الحديد) , وأن دراسة هذا البحث تتضمن برنامج عملي شامل ، مع الأخذ بنظر الأعتبار تأثير أضافة هذين النوعين من الألياف (ألياف البوليبروبيلين وألياف الحديد) على سلوك الخرسانة الذاتية الرص كتأثيرها مثلا على (مقاومة الأنضغاط , ومقاومة الشد , ومقدار الهطول , وتحسين المطيلية ، بالأضافة ألى نمط وعرض التشقق الذي ممكن أن يظهر في الخرسانة الذاتية الرص) ومقارنة النتائج المستحصلة عمليا مع النتائج المحسوبة تخمينيا طبقا للمدونة الأمريكية المرقمة ACI 318) لسنة (2008) , وكل هذا تم دراسته خلال هذا البحث العملي . المتغيرات التي تم دراستها خلال البحث هي نسبة التسليح (ρ%) حيث تم أخذها بنسب تتراوح مابين (4.4907% - 6.0434%) وذلك بأستخدام أقطار مختلفة من قضبان حديد التسليح هي (25 ملم , 20ملم , 16ملم , 12ملم , 6 ملم , 4 ملم , شبكة بقطر 6 ملم) , بالأضافة ألى ذلك أنه تم أستخدام ألياف البوليبروبيلين من نوع (RHEO-FIBER®) بمعدل أضافة مقداره (1كغم / م3) , وألياف الحديد من نوع (FIBERFORCE®) بنسبة أضافة مقدارها (%0.5) كنسبة حجمية من الحجم الكلي للخرسانة الذاتية الرص . كل العتبات ذات المقاطع بشكل حرف (T) تم توزيعها على ثلاث مجاميع , كل مجموعة أستخدم فيها أربع نسب من التسليح بأقطار مختلفة من حديد التسليح , وهذه النسب تم تكرارها على المجاميع الثلاثة مع أستخدام ألياف البوليبروبيلين من نوع(RHEO-FIBERS®) في خلطة الخرسانة الذاتية الرص لعتبات المجموعة الأولى , بينما تم أستخدام ألياف الحديد من النوع (FIBERFORCE®) في خلطة الخرسانة الذاتية الرص لعتبات المجموعة الثانية , أما المجموعة الثالثة فقد تم صبها بدون أستخدام أي نوع من الألياف لكونها المجموعة التي سوف يتم المقارنة معها . وقد أظهرت النتائج العملية لهذا البحث أنه بأضافة ألياف البوليبروبيلين من النوع أعلاه وبنسبة أضافة مقدارها (1كغم / م3) مع الخرسانة الذاتية الرص تؤثر بدرجة كبيرة على تحسين السيطرة على التشققات التي يمكن أن تحصل للخرسانة وتعمل على تقليلها , وكذلك تحسين عامل المطيلية بمقدار يتراوح مابين [التغير بالمطيلية (Δμd) = 2.0356 ألى 4.3515]، بينما يكون تأثيرها على تقليل مقادير الهطول للعتبات الخرسنية الذاتية الرص قليلا . لكن عندما يتم أستخدام ألياف الحديد من النوع (FIBERFORCE®) وبنسبة أضافة حجمية مقدارها (0.5% من الحجم الكلي للخرسانة الذاتية الرص) تظهر تأثيرا كبيرا على تقليل مقادير الهطول وزيادة مقدار الحمل الأقصى لفشل العتب الخرساني بمقادير عالية تتراوح مابين (11.78% ألى 18.42%) مع تحسين عامل المطيلية بمقدار يتراوح مابين [التغر بالمطيلية (Δμd) = 4.9232 ألى 12.1238], ولكنها تكون ذات تأثير قليل على تقليل عرض التشققات التي تظهر على العتبات الخرسانية الذاتية الرص ذات المقاطع بشكل حرف (T).الكلمات الدالة: الخرسانة الذاتية الرص؛ العتب ذو المقطع بشكل (T)؛ ألياف الحديد؛ ألياف البوليمر (البوليبروبيلين)؛ الملدنات المتفوقة؛ مسحوق السيليكا الفعال (مادة بوزولانية ذات خواص أسمنتية)؛ مسحوق حجر النورة الكلسي؛ السلوك المرن؛ سلوك التشقق؛ الهطول؛ عامل المطيلية.