Article
Effect of the Forming Conditions in the Production of Gamma Alumina Catalyst Support on the Crushing Strength Property

Authors: Riad Ahmed Saleh رياض احمد --- Ibrahim Richeh --- Alaa Dhari Jawad علاء ضاري
Journal: Iraqi Journal of Chemical and Petroleum Engineering المجلة العراقية للهندسة الكيمياوية وهندسة النفط ISSN: 19974884/E26180707 Year: 2010 Volume: 11 Issue: 2 Pages: 43-48
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

An investigation was conducted for the determination of the effects of the forming conditions in the production of Gamma Alumina catalyst support on the crushing strength property. Eight variables were studied , they are ;binder content which is the sodium silicate , Solvent content which is the water, speed of mixing , time of mixing, drying temperature , drying time , calcinations temperature and the calcinations time Design of the experiments was made by using the response Surface method in Minitab 15 software which supply us 90 experiments .The results of this investigation show that the crushing strength for the dried Gamma alumina extrudate was affected by the drying temperature and the drying time only and there is no interaction effect between the variables studied.Furthermore, the results show that, the crushing strength for the calcined extrudate was affected by the speed of mixing only and the optimum speed is 900rpm.The maximum crushing strength of 38.38 after calcinations and 11.865 Kg/mm after drying were obtained.


Article
BEHAVIOR OF CONCRETE BEAMS REINFORCED IN SHEAR WITH CARBON FIBER REINFORCED POLYMER

Authors: Amjad H. Abdul-Razaq Al-Modhafer --- Abdul-Muttalib I. Said Al-Mussaue
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2011 Volume: 17 Issue: 1 Pages: 46-61
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Carbon fiber reinforced polymers (CFRP) were widely used in strengthening reinforced concrete members in the last few years, these fibers consist mainly of high strength fibers which increase the member capacity in addition to changing the mode of failure of the reinforced concrete beams. Experimental and theoretical investigations were carried to find the behavior of reinforced concrete beams strengthened by CFRP in shear and bending. The experimental work included testing of 12 beams divided into 4 groups; each group contains 3 beams. The following parameters were taken into consideration:- Concrete crushing strength. - CFRP strengthening location (shear strengthening and both shear and flexure strengthening).Reinforced beams were simply supported subjected to two point loads. Each group consists of three beams; the first beam without CFRP, the second one, is strengthened with CFRP in shear and the third is strengthened with CFRP in both flexure and shear. Four groups with different crushing strength of (12, 20, 30 and 39 MPa). The CFRP sheets are attached externally.It was found that in beam with low crushing strength loads transfer to the CFRP at early stages while in those of high crushing strength, CFRP contribution only starts when full strength of the beam is fulfilled. A full bond between CFRP sheets and the concrete is assumed in the theoretical analysis. Comparison between the theoretical and the experimental results revealed the validity of the numerical analysis and the developed methods such that there was a difference of 13% in the ultimate strength for the tested and analyzed beams.

استعملت العناصر الإنشائية الخرسانية المسلحة المقواة بألياف البوليمر الكاربونية في السنوات الحديثة ، تتألف ألياف التقوية البوليمرية بصورة أساسية من ألياف )عالية المقاومة (حيث تزيد سعة التحمل بالإضافة إلى تغيير أسلوب الفشل للعتبات الخرسانة المسلحة.أجريت تحريات عملية ونظرية لسلوك العتبات الخرسانية المسلحة، لحالتي تقوية العتبات في مناطق فشل القص والانثناء المقواة باستخدام CFRP حيث يتكون البرنامج العملي من 12 عتبة فحص قسمت إلى أربعة مجاميع ،كل مجموعة تضم 3 عتبات. الدراسة أخذت بنظر الاعتبار مقاومة الانضغاط للخرسانة و حالة التقوية ، استعملت مرة للتقوية في منطقة القص وأخرى في منطقتي القص و الانثناء معاً.كل العتبات تم فحصها في فضاء بسيط الإسناد ومتعرض لنقطتي تحميل بينما المتغير الرئيس يمثل مقاومة الانضغاط للخرسانة و موقع . CFRP كل مجموعة تتكون من ثلاثة عتبات الأول وهو النموذج المرجعي وهو خالي من CFRP و الثاني يحتوي على CFRP في منطقة القص و هي عبارة عن سبعة شرائح مائلة بزاوية 45 درجة و الثالث يحتوي على CFRP في منطقتي القص و الانثناء.كل مجموعة لها مقاومة انضغاط مختلفة عن الأخرى وهي (12-20-30-39 MPa ). إستعمل CFRP كمقوي خارجي. أن استعمال CFRP له تأثير على نتائج الحمل الأقصى، شكل التشقق، الهطول. تم اكتشاف إن CFRP يشارك الخرسانة الضعيفة في أوقات مبكرة من الحمل بعكس الخرسانة التي لها قوة انضغاط عالية حيث تتحمل أولا هي لوحدها جميع الاجتهادات ثم تشاركها شرائح CFRP في التحمل.إن أفضل استخدام لشرائح CFRP في منطقة القص بسبب تحول القوى بصورة مباشرة إلى شد على هذه الشرائح. تم استعمال التحليل اللاخطي بواسطة العناصر ثلاثية الإبعاد لتحري أداء العتبات الخرسانية المسلحة المقواة ب CFRP، حيث تم استخدام البرنامج الحاسوبي ANSYS.اعتبرنا هنالك تماس تام بين شرائح CFRP والخرسانة. وتم الحصول على تنبؤ جيد لسلوك ما بعد التصدع. المقارنة بين النتائج النظرية والعملية أكدت صلاحية التحليل العددي و حيث كانت أكبر نسبة فرق في المقاومة القصوى أقل من 13 % لكل العتبات المفحوصة.